CN106995280A - Ground glass - Google Patents
Ground glass Download PDFInfo
- Publication number
- CN106995280A CN106995280A CN201710168111.7A CN201710168111A CN106995280A CN 106995280 A CN106995280 A CN 106995280A CN 201710168111 A CN201710168111 A CN 201710168111A CN 106995280 A CN106995280 A CN 106995280A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass
- ground glass
- calcite
- quartz sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of ground glass, a kind of ground glass, by weight including following each component：50 70 parts of quartz sand, 40 48 parts of calcite, 10 15 parts of ammonium fluoride, 40 50 parts of paper fiber, 20 30 parts of ammonium acid fluoride, 15 20 parts of sodium oxide molybdena, 13 parts of fining agent；Ground glass is made by crushing, mixing, heat treatment, applique, sandblasting.Addition paper fiber and calcite can increase the intensity of ground glass to the present invention in the feed, and the intensity of ground glass can be increased in glass surface spraying diamond dust；The present invention passes through scientific matching, optimize technique so that the ground glass finish produced is good, block vision is preferable.
Description
Technical field
The present invention relates to field of glass production technology, and in particular to a kind of ground glass.
Background technology
Ground glass is usually to carry out frosted processing on the surface of common common glass, can not only cause the outer of glass
Surface has plus good-looking frosted decorative pattern, and main purpose is can to reduce the permeability of glass so that more difficult phase inside and outside glass
Mutually it is clear that existing ground glass is generally after frosted processing is carried out at frosted is rendered as white, existing white is weaker, from
Glass side still can see offside, and the finish of frosting is poor.
The content of the invention
The purpose of the present invention be overcome in place of above-mentioned the deficiencies in the prior art there is provided a kind of finish preferably, block vision
Preferably, the high ground glass of intensity.
To reach above-mentioned purpose, the present invention is adopted the following technical scheme that：A kind of ground glass, by weight including following
Component：50-70 parts of quartz sand, 40-48 parts of calcite, 10-15 parts of ammonium fluoride, 40-50 parts of paper fiber, 20-30 parts of ammonium acid fluoride,
15-20 parts of sodium oxide molybdena, 1-3 parts of fining agent；
The preparation method of the ground glass is：Quartz sand, calcite are put into pulverizer and crushed first, is obtained
Crushed material；Clout is well mixed with crushed material again, input melting furnace in be heated to 1480-1510 DEG C, in heating process with
50-100r/min rotating speeds are stirred, and are allowed to form uniform liquid glass；Liquid glass by calendering technology is obtained into glass big,
Glass is big by annealing process, eliminates stress, split-phase or the crystallization of inside glass so that the configuration state of glass changes；In glass
Put up decorative pattern on glass is big with paper, then diamond dust sprayed to glass with air compressor machine, glass sand face is occurred, produce ground glass.
Further, the crushed material is 10-30 mesh.
Further, each component of the ground glass is calculated by weight is：50 parts of quartz sand, 40 parts of calcite, fluorine
Change 12 parts of ammonium, 42 parts of paper fiber, 20 parts of ammonium acid fluoride, 15 parts of sodium oxide molybdena, 1 part of fining agent.
Further, each component of the ground glass is calculated by weight is：70 parts of quartz sand, 48 parts of calcite, fluorine
Change 15 parts of ammonium, 50 parts of paper fiber, 30 parts of ammonium acid fluoride, 15 parts of sodium oxide molybdena, 3 parts of fining agent.
Further, each component of the ground glass is calculated by weight is：57 parts of quartz sand, 43 parts of calcite, fluorine
Change 10 parts of ammonium, 40 parts of paper fiber, 25 parts of ammonium acid fluoride, 18 parts of sodium oxide molybdena, 2 parts of fining agent.
Beneficial effects of the present invention：Addition paper fiber and calcite can increase the strong of ground glass to the present invention in the feed
Degree, the intensity of ground glass can be increased in glass surface spraying diamond dust；The present invention is by scientific matching, and optimize technique makes
The ground glass finish that must produce is good, block vision is preferable.
Further advantage, target and the feature of the present invention embodies part by following explanation, and part will also be by this
The research and practice of invention and be understood by the person skilled in the art.
Embodiment
With reference to the following example, the present invention is described in further detail, to make those skilled in the art with reference to specification
Word can be implemented according to this.
Embodiment 1
The each component of ground glass of the present invention is calculated by weight is：50 parts of quartz sand, 40 parts of calcite, ammonium fluoride 12
Part, 42 parts of paper fiber, 20 parts of ammonium acid fluoride, 15 parts of sodium oxide molybdena, 1 part of fining agent.
The production method of the ground glass is as follows：
Step 1：Quartz sand, calcite are put into pulverizer and crushed first, the crushed material of 10 mesh is obtained；
Step 2：Clout is well mixed with crushed material again, 1480 DEG C are heated in input melting furnace, in heating process
Stirred with 50r/min rotating speeds, be allowed to form uniform liquid glass；
Step 3：Liquid glass by calendering technology is obtained into glass big, glass is big by annealing process, eliminates in glass
Stress, split-phase or the crystallization in portion so that the configuration state of glass changes；
Step 4：Put up decorative pattern with paper on glass is big, then diamond dust sprayed to glass with air compressor machine, glass sand is occurred
Face, produces ground glass.
Embodiment 2
The each component of ground glass of the present invention is calculated by weight is：70 parts of quartz sand, 48 parts of calcite, ammonium fluoride 15
Part, 50 parts of paper fiber, 30 parts of ammonium acid fluoride, 15 parts of sodium oxide molybdena, 3 parts of fining agent.
The production method of the ground glass is as follows：
Step 1：Quartz sand, calcite are put into pulverizer and crushed first, the crushed material of 20 mesh is obtained；
Step 2：Clout is well mixed with crushed material again, 1492 DEG C are heated in input melting furnace, in heating process
Stirred with 70r/min rotating speeds, be allowed to form uniform liquid glass；
Step 3：Liquid glass by calendering technology is obtained into glass big, glass is big by annealing process, eliminates in glass
Stress, split-phase or the crystallization in portion so that the configuration state of glass changes；
Step 4：Put up decorative pattern with paper on glass is big, then diamond dust sprayed to glass with air compressor machine, glass sand is occurred
Face, produces ground glass.
Embodiment 3
The each component of ground glass of the present invention is calculated by weight is：57 parts of quartz sand, 43 parts of calcite, ammonium fluoride 10
Part, 40 parts of paper fiber, 25 parts of ammonium acid fluoride, 18 parts of sodium oxide molybdena, 2 parts of fining agent.
The production method of the ground glass is as follows：
Step 1：Quartz sand, calcite are put into pulverizer and crushed first, the crushed material of 30 mesh is obtained；
Step 2：Clout is well mixed with crushed material again, 1510 DEG C are heated in input melting furnace, in heating process
Stirred with 100r/min rotating speeds, be allowed to form uniform liquid glass；
Step 3：Liquid glass by calendering technology is obtained into glass big, glass is big by annealing process, eliminates in glass
Stress, split-phase or the crystallization in portion so that the configuration state of glass changes；
Step 4：Put up decorative pattern with paper on glass is big, then diamond dust sprayed to glass with air compressor machine, glass sand is occurred
Face, produces ground glass.
Although embodiment of the present invention is disclosed as above, it is not restricted in specification and embodiment listed
With it can be applied to various suitable the field of the invention completely, can be easily for those skilled in the art
Other modification is realized, therefore under the universal limited without departing substantially from claim and equivalency range, the present invention is not limited
In specific details and shown here as the embodiment with description.
Claims (5)
1. a kind of ground glass, it is characterised in that by weight including following each component：50-70 parts of quartz sand, calcite 40-48
Part, 10-15 parts of ammonium fluoride, 40-50 parts of paper fiber, 20-30 parts of ammonium acid fluoride, 15-20 parts of sodium oxide molybdena, 1-3 parts of fining agent；
The preparation method of the ground glass is：Quartz sand, calcite are put into pulverizer and crushed first, is crushed
Material；Clout is well mixed with crushed material again, 1480-1510 DEG C is heated in input melting furnace, with 50- in heating process
100r/min rotating speeds are stirred, and are allowed to form uniform liquid glass；Liquid glass by calendering technology is obtained into glass big, glass
It is big to pass through annealing process, stress, split-phase or the crystallization of elimination inside glass so that the configuration state of glass changes；It is big in glass
On put up decorative pattern with paper, then diamond dust sprayed to glass with air compressor machine, glass sand face is occurred, produce ground glass.
2. ground glass according to claim 1, it is characterised in that：The crushed material is 10-30 mesh.
3. ground glass according to claim 1, it is characterised in that：The each component of the ground glass is calculated by weight
For：50 parts of quartz sand, 40 parts of calcite, 12 parts of ammonium fluoride, 42 parts of paper fiber, 20 parts of ammonium acid fluoride, 15 parts of sodium oxide molybdena, fining agent
1 part.
4. ground glass according to claim 1, it is characterised in that：The each component of the ground glass is calculated by weight
For：70 parts of quartz sand, 48 parts of calcite, 15 parts of ammonium fluoride, 50 parts of paper fiber, 30 parts of ammonium acid fluoride, 15 parts of sodium oxide molybdena, fining agent
3 parts.
5. ground glass according to claim 1, it is characterised in that：The each component of the ground glass is calculated by weight
For：57 parts of quartz sand, 43 parts of calcite, 10 parts of ammonium fluoride, 40 parts of paper fiber, 25 parts of ammonium acid fluoride, 18 parts of sodium oxide molybdena, fining agent
2 parts.