CN107056051A - A kind of production technology of ground glass - Google Patents
A kind of production technology of ground glass Download PDFInfo
- Publication number
- CN107056051A CN107056051A CN201710016719.8A CN201710016719A CN107056051A CN 107056051 A CN107056051 A CN 107056051A CN 201710016719 A CN201710016719 A CN 201710016719A CN 107056051 A CN107056051 A CN 107056051A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass
- gob
- ground glass
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of production technology of ground glass, it is related to glass production processing technique field, comprises the following steps, 1) dispensing：Quartz sand, soda ash, lime stone, saltcake nitrifies salt, and manganese powder, indium powder, glass fibre, bamboo charcoal powder, bonding agent, cosolvent, opacifiers, epoxy resin prepares raw material for standby；2) found：It will be mixed with the raw material got ready, carry out high-temperature heating thawing using melting furnace, be allowed to form uniform liquid glass；3) it is molded：Liquid glass after thawing is subjected to forming processes using grinding tool, pickling is carried out to gob with acid solution, gob is made；4) clean；5) it is heat-treated, both obtains ground glass.The present invention can improve the intensity of ground glass by indium powder and glass fibre, enhance the impact resistance of glass, it is not likely to produce glass broken, the surface that epoxy resin is sprayed on ground glass can strengthen its intensity, and ground glass frosted finish effect produced by the present invention is preferable.
Description
Technical field
The present invention relates to glass production processing technique field, a kind of production technology of ground glass is particularly belonged to.
Background technology
Ground glass rough surface, makes light produce diffusing reflection, the characteristics of not had an X-rayed with printing opacity, and make indoor light soft
With.It is commonly used for the cut-off of toilet, bathroom, lavatory, office, corridor etc., can also make the plate face of blackboard, general mill
Sand glass is made up of quartz sand, soda ash, lime stone and saltcake raw material, and this ground glass intensity is not high, is produced by minor impact
Raw crackle.
The content of the invention
In view of the above-mentioned problems, it is an object of the invention to provide a kind of production technology of ground glass, overcoming existing skill
The deficiency of art.
The technical solution adopted by the present invention is as follows：
A kind of production technology of ground glass, comprises the following steps：
(1) dispensing：By following weight raw material, 40~60 parts of quartz sand, 10~20 parts of soda ash, lime stone 6~
13 parts, 2~8 parts of saltcake nitrifies 5~15 parts of salt, 5~10 parts of manganese powder, 5~10 parts of indium powder, 4~8 parts of glass fibre, bamboo charcoal powder 2
~8 parts, 5~10 parts of bonding agent, 5~10 parts of cosolvent, 5~10 parts of opacifiers, 4~8 parts of epoxy resin prepares raw material for standby；
(2) found：It will be mixed with the raw material got ready, 1500~1700 DEG C of heating and meltings of high temperature carried out using melting furnace, when
Between be 30~60 minutes, be allowed to form uniform liquid glass；
(3) it is molded：Liquid glass after thawing is subjected to forming processes using grinding tool, gob carried out with acid solution
Pickling, soak time is 10~20 minutes, and gob is made；
(4) clean：Gob is first cleaned up with clear water, then soaked with concentration for 2%~6% sodium bicarbonate solution
10~20 minutes；
(5) it is heat-treated：The gob of shaping is quenched, annealing process, both ground glass.
Further, the cosolvent is potassium oxide or sodium oxide molybdena.
Compared with the prior art, beneficial effects of the present invention are as follows：
The present invention can improve the intensity of ground glass by indium powder and glass fibre, enhance the shock resistance of glass
Property, it is not likely to produce glass broken, the surface that epoxy resin is sprayed on ground glass can strengthen its intensity, it is produced by the present invention
Ground glass frosted finish effect is preferable.
Embodiment
Embodiment one, a kind of production technology of ground glass, comprise the following steps：
(1) dispensing：By following weight raw material, 45 parts of quartz sand, 15 parts of soda ash, 8 parts of lime stone, 4 parts of saltcake,
Nitrify 10 parts of salt, 7 parts of manganese powder, 7 parts of indium powder, 6 parts of glass fibre, 4 parts of bamboo charcoal powder, 7 parts of bonding agent, 7 parts of cosolvent, opacifiers 7
Part, 6 parts of epoxy resin prepares raw material for standby；
(2) found：It will be mixed with the raw material got ready, carry out 1500 DEG C of heating and meltings of high temperature using melting furnace, the time is 40
Minute, it is allowed to form uniform liquid glass；
(3) it is molded：Liquid glass after thawing is subjected to forming processes using grinding tool, gob carried out with acid solution
Pickling, soak time is 15 minutes, and gob is made；
(4) clean：Gob is first cleaned up with clear water, then 15 points are soaked with the sodium bicarbonate solution that concentration is 4%
Clock；
(5) it is heat-treated：The gob of shaping is quenched, annealing process, both ground glass.
Embodiment two, a kind of production technology of ground glass, comprise the following steps：
(1) dispensing：By following weight raw material, 55 parts of quartz sand, 18 parts of soda ash, 11 parts of lime stone, saltcake 6
Part, nitrify 13 parts of salt, 8 parts of manganese powder, 8 parts of indium powder, 7 parts of glass fibre, 6 parts of bamboo charcoal powder, 8 parts of bonding agent, 8 parts of cosolvent, milkiness
8 parts of agent, 7 parts of epoxy resin, prepares raw material for standby；
(2) found：It will be mixed with the raw material got ready, carry out 1600 DEG C of heating and meltings of high temperature using melting furnace, the time is 50
Minute, it is allowed to form uniform liquid glass；
(3) it is molded：Liquid glass after thawing is subjected to forming processes using grinding tool, gob carried out with acid solution
Pickling, soak time is 18 minutes, and gob is made；
(4) clean：Gob is first cleaned up with clear water, then 18 points are soaked with the sodium bicarbonate solution that concentration is 5%
Clock；
(5) it is heat-treated：The gob of shaping is quenched, annealing process, both ground glass.
Embodiment three, a kind of production technology of ground glass, comprise the following steps：
(1) dispensing：By following weight raw material, 60 parts of quartz sand, 20 parts of soda ash, 12 parts of lime stone, saltcake 7
Part, 15 parts of salt of nitrification, 10 parts of manganese powder, 10 parts of indium powder, 8 parts of glass fibre, 8 parts of bamboo charcoal powder, 10 parts of bonding agent, 10 parts of cosolvent,
10 parts of opacifiers, 8 parts of epoxy resin, prepares raw material for standby；
(2) found：It will be mixed with the raw material got ready, carry out 1700 DEG C of heating and meltings of high temperature using melting furnace, the time is 60
Minute, it is allowed to form uniform liquid glass；
(3) it is molded：Liquid glass after thawing is subjected to forming processes using grinding tool, gob carried out with acid solution
Pickling, soak time is 20 minutes, and gob is made；
(4) clean：Gob is first cleaned up with clear water, then 20 points are soaked with the sodium bicarbonate solution that concentration is 5%
Clock；
(5) it is heat-treated：The gob of shaping is quenched, annealing process, both ground glass.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (2)
1. a kind of production technology of ground glass, it is characterised in that comprise the following steps：
(1) dispensing：By following weight raw material, 40~60 parts of quartz sand, 10~20 parts of soda ash, 6~13 parts of lime stone,
2~8 parts of saltcake, 5~15 parts of salt of nitrification, 5~10 parts of manganese powder, 5~10 parts of indium powder, 4~8 parts of glass fibre, 2~8 parts of bamboo charcoal powder,
5~10 parts of bonding agent, 5~10 parts of cosolvent, 5~10 parts of opacifiers, 4~8 parts of epoxy resin prepares raw material for standby；
(2) found：It will be mixed with the raw material got ready, using melting furnace progress 1500~1700 DEG C of heating and meltings of high temperature, the time is
30~60 minutes, it is allowed to form uniform liquid glass；
(3) it is molded：Liquid glass after thawing is subjected to forming processes using grinding tool, acid is carried out to gob with acid solution
Wash, soak time is 10~20 minutes, and gob is made；
(4) clean：Gob is first cleaned up with clear water, then with concentration for 2%~6% sodium bicarbonate solution immersion 10~
20 minutes；
(5) it is heat-treated：The gob of shaping is quenched, annealing process, both ground glass.
2. a kind of production technology of ground glass according to claim 1, it is characterised in that：The cosolvent is potassium oxide
Or sodium oxide molybdena.