CN106966637A - A kind of coloured ceramic water-permeable brick and preparation method thereof - Google Patents
A kind of coloured ceramic water-permeable brick and preparation method thereof Download PDFInfo
- Publication number
- CN106966637A CN106966637A CN201710219142.0A CN201710219142A CN106966637A CN 106966637 A CN106966637 A CN 106966637A CN 201710219142 A CN201710219142 A CN 201710219142A CN 106966637 A CN106966637 A CN 106966637A
- Authority
- CN
- China
- Prior art keywords
- permeable
- coloured ceramic
- permeable brick
- coupling agent
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of coloured ceramic water-permeable brick, and it includes porous base course and the permeable top layer being covered on the porous base course；The permeable top layer is formed according to each feed proportioning of following parts by weight：150 parts of coloured ceramic particle, 5~15 parts of Resin adhesive, 0.5~1 part of surfactant, 0.05~0.1 part of coupling agent；The preparation method of the coloured ceramic water-permeable brick is disclosed simultaneously.Not only preparation technology is simple by the present invention, be easy to large-scale production; and while realizing that compression strength is high low with cost; with permeable timeliness is longer, frost resistance is good, wearability is good and feature not easy to fade bright in luster, the problem of preferably enough solving existing water-permeable brick wearability deficiency, single color, fugitive color.
Description
【Technical field】
The invention belongs to building material field, and in particular to a kind of coloured ceramic water-permeable brick and preparation method thereof.
【Background technology】
At present, application of the permeable pavement such as water-permeable brick material in sponge urban construction is more and more extensive, common water-permeable brick
Mostly pervious concrete road pavement brick, its primer is porous base course mostly cement concrete, and surface material is that permeable top layer is more
For by cement, toner, sand mix mortar；Such water-permeable brick has the low feature of simple production process, cost, but in reality
The permeable timeliness in the permeable top layer of generally existing is short during the engineer applied of border, frost resistance is not enough, wearability is not enough and color is single etc.
Problem.
【The content of the invention】
One of technical problems to be solved by the invention are to provide a kind of coloured ceramic water-permeable brick, with permeable timeliness compared with
It is long, frost resistance is good, wearability is good, rich color and non-fading feature..
The two of the technical problems to be solved by the invention are to provide a kind of preparation method of coloured ceramic water-permeable brick, its work
Skill is simple, be easy to large-scale production.
The present invention is to solve one of above-mentioned technical problem by the following technical programs：A kind of coloured ceramic water-permeable brick, should
Water-permeable brick includes porous base course and the permeable top layer being covered on the porous base course；The permeable top layer is according to following parts by weight
Each feed proportioning form：
150 parts of coloured ceramic particle；
5~15 parts of Resin adhesive；
0.5~1 part of surfactant；
0.05~0.1 part of coupling agent.
Further, the particle diameter of the coloured ceramic particle is one of 0.5~1mm, 1~2mm or combination and the color ceramic
The color of matter particle is at least one of red, yellow, green, blueness, grey.
Further, the Resin adhesive is epoxy resin adhesive, adhesive for polyurethane or acrylic resin gluing
Agent.
Further, the surfactant is dodecyl sodium sulfate, lauryl sodium sulfate or triethanolamine soap.
Further, the coupling agent is at least one in chromium complex coupling agent, silane coupler, titanate coupling agent
Kind.
The present invention is to solve the two of above-mentioned technical problem by the following technical programs：A kind of system of coloured ceramic water-permeable brick
Preparation Method, the preparation method is first to prepare porous base course, after porous base course is molded, and carries out the cloth on permeable top layer, this is permeable
The cloth concrete operations on top layer are：First prepare each raw material of following weight parts：150 parts of coloured ceramic particle, Resin adhesive 5~
0.05~0.1 part of 10 parts, 0.5~1 part of surfactant and coupling agent；Then by Resin adhesive, surfactant and coupling
Agent is mixed evenly；Coloured ceramic is added and uniform mixing afterwards, permeable top layer material is obtained；Then by the saturating of preparation
Surface layer of water material is distributed on the top of the porous base course after shaping, die head and brushes releasing agent；It is last compressing, and briquetting pressure
For 8.0~10.0MPa, the dwell time is 5s.
Further, the color of the coloured ceramic particle is at least one in red, yellow, green, blueness, grey
Kind；And the particle diameter of the coloured ceramic particle is one of 0.5~1mm, 1~2mm or combination.
Further, the Resin adhesive is epoxy resin adhesive, adhesive for polyurethane or acrylic resin gluing
Agent；The surfactant is dodecyl sodium sulfate, lauryl sodium sulfate or triethanolamine soap；The coupling agent is chromium network
At least one of compound coupling agent, silane coupler, titanate coupling agent.
The beneficial effects of the present invention are：
Not only preparation technology is simple for coloured ceramic water-permeable brick of the present invention, be easy to large-scale production, and is realizing pressure resistance
While degree height and low cost, with permeable timeliness is longer, frost resistance is good, wearability is good and bright in luster not easy to fade
Feature, the problem of preferably enough solving existing water-permeable brick wearability deficiency, single color, fugitive color.
【Embodiment】
A kind of coloured ceramic water-permeable brick of the present invention, the water-permeable brick includes porous base course and is covered on the porous base course
Permeable top layer；The permeable top layer is formed according to each feed proportioning of following parts by weight：
150 parts of coloured ceramic particle；
5~15 parts of Resin adhesive；
0.5~1 part of surfactant；
0.05~0.1 part of coupling agent.
Simultaneously, disclosed herein the preparation method of above-mentioned coloured ceramic water-permeable brick, specifically, the preparation method is
Porous base course is first prepared, after porous base course is molded, the cloth on permeable top layer is carried out；The cloth concrete operations on the permeable top layer
For：First prepare each raw material of following weight parts：150 parts of coloured ceramic particle, 5~10 parts of Resin adhesive, surfactant 0.5
~1 part and 0.05~0.1 part of coupling agent；Then Resin adhesive, surfactant and coupling agent are mixed evenly；
Coloured ceramic particle is added and uniform mixing afterwards, permeable top layer material is obtained；Then the permeable top layer material of gained is distributed in
Releasing agent is brushed on the top of porous base course after shaping, die head；It is last compressing, and briquetting pressure be 8.0~
10.0MPa, the dwell time is 5s.In the present invention, the color of coloured ceramic particle is in red, yellow, green, blueness, grey
At least one；And the particle diameter of coloured ceramic particle is one of 0.5~1mm, 1~2mm or combination；Resin adhesive selects epoxy
Resin adhesive, adhesive for polyurethane or acrylic resin adhesive；Surfactant is dodecyl sodium sulfate, dodecyl
Sodium sulphate or triethanolamine soap；The coupling agent be chromium complex coupling agent, silane coupler, titanate coupling agent at least
It is a kind of.
In order to be preferably described to the present invention, applicant gives following several specific embodiments.And this hair
The preparation moulding process of bright middle porous base course belong to it is existing routinely, system with the porous base course of existing ordinary cement water-permeable brick
Standby moulding process is consistent.
Embodiment 1
Porous base course is prepared, after porous base course is molded；Ceramic granule that weigh red and that particle diameter is 1~2mm
150kg, adhesive for polyurethane 5kg, dodecyl sodium sulfate 0.6kg and silane coupler 0.06kg, first by the polyurethane weighed
Adhesive, dodecyl sodium sulfate and silane coupler are mixed evenly, and then red ceramic granule is added simultaneously
Attached adhesive for polyurethane, dodecyl sodium sulfate and silane coupler are uniformly wrapped up in uniform mixing, i.e. red ceramic granule surface
The mixture being mixed to form, obtains permeable top layer material；Then permeable top layer material is distributed in the top of the porous base course after shaping,
Releasing agent is brushed on die head；It is last compressing, and briquetting pressure is 8.0MPa, the dwell time is 5s, so as to obtain red ceramic
Water-permeable brick.
After tested, the red ceramic water-permeable brick obtained by the present embodiment preparation is bright in colour, and its average tensile splitting strength
For 3.5MPa, coefficient of permeability is 0.40mm/s, and mill hole length is 26mm, and BPN values are 72.
Embodiment 2
Porous base course is prepared, after porous base course is molded；Ceramic granule that weigh yellow and that particle diameter is 0.5~1mm
150kg, adhesive for polyurethane 10kg, lauryl sodium sulfate 1kg and chromium complex coupling agent 0.1kg, first by the poly- ammonia weighed
Ester adhesive, lauryl sodium sulfate and chromium complex coupling agent are mixed evenly, then the ceramic granule of yellow
Add and attached adhesive for polyurethane, lauryl sodium sulfate and chromium network are uniformly wrapped up in the ceramic granule surface of uniform mixing, i.e. yellow
The mixture that compound coupling agent is mixed to form, obtains permeable top layer material；Then permeable top layer material is distributed in permeable after shaping
Releasing agent is brushed on the top of basic unit, die head；It is last compressing, and briquetting pressure is 10MPa, the dwell time is 5s, so that
Obtain yellow ceramic water-permeable brick.
After tested, the yellow ceramic water-permeable brick obtained by the present embodiment preparation is bright in colour, and its average tensile splitting strength
For 4.8MPa, coefficient of permeability is 0.35mm/s, and mill hole length is 23mm, and BPN values are 78.
Embodiment 3
Porous base course is prepared, after porous base course is molded；Weigh green and particle diameter be 1~2mm ceramic granule 150kg,
Acrylic resin adhesive 15kg, triethanolamine soap 0.75kg and titanate coupling agent 0.08kg, first by the acrylic acid tree weighed
Fat adhesive, triethanolamine soap and titanate coupling agent are mixed evenly, and then the ceramic granule of green is added simultaneously
Uniform mixing, i.e. green ceramic granule surface are uniformly wrapped up in attached acrylic resin adhesive, triethanolamine soap and titanate esters and are coupled
The mixture that agent is mixed to form, obtains permeable top layer material；Then permeable top layer material is distributed in the top of the porous base course after shaping
Releasing agent is brushed on portion, die head；It is last compressing, and briquetting pressure is 8.0MPa, the dwell time is 5s, so as to obtain green ceramic
Water-permeable brick.
After tested, the yellow ceramic water-permeable brick obtained by the present embodiment preparation is bright in colour, and its average tensile splitting strength
For 5.3MPa, coefficient of permeability is 0.30mm/s, and mill hole length is 18mm, and BPN values are 83.
To sum up, the coloured ceramic water-permeable brick obtained by present invention preparation is realizing compression strength height, simple production process, cost
, can be compared with permeable timeliness is longer, frost resistance is good, wearability is good and feature not easy to fade bright in luster while low
The problems such as enough solving existing water-permeable brick wearability deficiency, single color, fugitive color well.
Claims (8)
1. a kind of coloured ceramic water-permeable brick, the water-permeable brick includes porous base course and the permeable table being covered on the porous base course
Layer；It is characterized in that：The permeable top layer is formed according to each feed proportioning of following parts by weight：
150 parts of coloured ceramic particle；
5~15 parts of Resin adhesive；
0.5~1 part of surfactant；
0.05~0.1 part of coupling agent.
2. a kind of coloured ceramic water-permeable brick according to claim 1, it is characterised in that：The particle diameter of the coloured ceramic particle
For one of 0.5~1mm, 1~2mm or combination；And the color of coloured ceramic particle is in red, yellow, green, blueness, grey
At least one.
3. a kind of coloured ceramic water-permeable brick according to claim 1, it is characterised in that：The Resin adhesive is asphalt mixtures modified by epoxy resin
Fat adhesive, adhesive for polyurethane or acrylic resin adhesive.
4. a kind of coloured ceramic water-permeable brick according to claim 1, it is characterised in that：The surfactant is dodecane
Base sodium sulfonate, lauryl sodium sulfate or triethanolamine soap.
5. a kind of coloured ceramic water-permeable brick according to claim 1, it is characterised in that：The coupling agent is that chromium complex is even
Join at least one of agent, silane coupler, titanate coupling agent.
6. the preparation method of coloured ceramic water-permeable brick described in a kind of claim 1, the preparation method is first to prepare porous base course, when
After porous base course shaping, the cloth on permeable top layer is carried out, it is characterised in that：The cloth concrete operations on the permeable top layer are：It is first accurate
Each raw material of standby following weight parts：150 parts of coloured ceramic particle, 5~15 parts of Resin adhesive, 0.5~1 part of surfactant and
0.05~0.1 part of coupling agent；Then Resin adhesive, surfactant and coupling agent are mixed evenly；Afterwards will
Coloured ceramic is added and uniform mixing, obtains permeable top layer material；Then the permeable top layer material of preparation is distributed in saturating after shaping
Releasing agent is brushed on the top of water-base, die head；It is last compressing, and briquetting pressure is 8.0~10.0MPa, dwell time
For 5s.
7. a kind of index method of coloured ceramic water-permeable brick according to claim 7, it is characterised in that：The coloured ceramic
Color is at least one of red, yellow, green, blueness, grey；And the particle diameter of the coloured ceramic be 0.5~1mm, 1~
One of 2mm or combination.
8. a kind of index method of coloured ceramic water-permeable brick according to claim 7, it is characterised in that：The Resin adhesive
For epoxy resin adhesive, adhesive for polyurethane or acrylic resin adhesive；The surfactant is dodecyl sodium sulfonate
In sodium, lauryl sodium sulfate or triethanolamine soap；The coupling agent is chromium complex coupling agent, silane coupler, titanate esters
At least one of coupling agent.