CN105948677A - Anti-cracking encaustic tile and production technique thereof - Google Patents
Anti-cracking encaustic tile and production technique thereof Download PDFInfo
- Publication number
- CN105948677A CN105948677A CN201610477356.3A CN201610477356A CN105948677A CN 105948677 A CN105948677 A CN 105948677A CN 201610477356 A CN201610477356 A CN 201610477356A CN 105948677 A CN105948677 A CN 105948677A
- Authority
- CN
- China
- Prior art keywords
- cement
- parts
- watt
- pigment
- cracking resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses an anti-cracking encaustic tile and a production technique thereof, relating to the field of construction materials. The anti-cracking encaustic tile comprises the following components in parts by weight: 20-30 parts of quicklime, 20-35 parts of clay, 40-50 parts of raw gypsum, 1-2 parts of mixed fiber, 15-20 parts of cement, 25-30 parts of coarse sand, 10-15 parts of fine sand and 9-12 parts of pigment. The production technique disclosed by the technical scheme of the invention has the advantage of high production efficiency. The produced encaustic tile has the advantages of high strength, high safety and reliability, long service life, uniform material distribution and favorable pigment adhesion property, and can prevent cracking.
Description
Technical field
The present invention relates to building materials field, be specifically related to a kind of cracking resistance azulejo watt and production technology thereof.
Background technology
Azulejo watt formal name used at school color concrete watt, is again color cement tile, cement encaustic tile etc..Encaustic tile described on the market is general
Refer both to color cement tile.It is novel roof decorations building materials recent years.Encaustic tile is by after the rational proportion such as cement, sand, logical
Cross mould, form through high pressure compacting, there is compressive resistance strong, bearing capacity advantages of higher.Concerned countries standard has JC/T746-2007
Standard.
The general klining watt of color concrete watt ratio has impervious strong, and bearing capacity is strong, the advantages such as water absorption rate is low.Cement colorful
Watt have that degree of compaction is big, intensity is high, lightweight, the tile-type advantage such as rationally, revolutionize traditional employing dry concrete
, the shortcoming such as intensity low, tile-type dull coarse through the cement tile of rolling-type molding.It has unique waterproof construction, the intensity of superelevation,
Beautiful outward appearance etc..
Patent No. CN 103448139 A discloses the production technology of a kind of azulejo watt, relates to the processing of a kind of construction material
Preparation field, by choosing raw material, molding, drying, dedusting, colouring, final dusting, roasting, cooling, quality inspection, finished product warehouse-in.
Although above-mentioned production technology is novel in design, simple in construction, when processing, whole process uses conveyer belt conveying, automatically
Changing strong, efficiency is high, pollution-free, cost-effective, it is ensured that the qualification rate of azulejo watt, but its azulejo watt produced holds in use
Easy to crack, have impact on promoting the use of of azulejo watt, accordingly, it would be desirable to design a kind of cracking resistance azulejo that can solve the problem that problem above
Watt and production technology.
Summary of the invention
Problem to be solved by this invention is to provide a kind of cracking resistance azulejo watt and production technology thereof.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of cracking resistance azulejo watt, by weight, described cracking resistance azulejo watt includes quick lime 20-30 part, clay 20-
35 parts, Gypsum Fibrosum 40-50 part, composite fibre 1-2 part, cement 15-20 part, coarse sand 25-30 part, fine sand 10-15 part,
Pigment 9-12 part.
Preferably, by weight, described cracking resistance azulejo watt includes quick lime 25 parts, clay 30 parts, Gypsum Fibrosum
45 parts, composite fibre 2 parts, cement 15 parts, coarse sand 25 parts, fine sand 10 parts, pigment 9 parts.
Preferably, described composite fibre includes the component by following weight proportion: high modulus fiber 15-20 part, middle modulus fibre
25-35 part, low modulus fibre 30-40 part, described high modulus fiber uses a length of 2-20mm, and tensile strength is 1500-1750MPa,
Elastic modelling quantity is the Phyllostachys pubescens Mazei ex H.de Lebaie fiber of 23-27GPa, and described middle modulus fibre uses a length of 2-20mm, and tensile strength is 500-
1250MPa, the Chinese Fir for Fibre of elastic modelling quantity 8-20GPa, described low modulus fibre uses a length of 2-5mm, tensile strength 600-
700MPa, elastic modelling quantity is the bleached sulphate softwood pulp fiber of 3.5-4.5GPa.
Preferably, the one during described pigment is red pigment, blue pigment, yellow uitramarine, black pigment.
Preferably, described cement uses silicate or Portland cement.
A kind of production technology of raw cracking resistance azulejo watt, described production technology specifically includes following steps:
A. dispensing: join preparing quick lime 20-30 part, clay 20-35 part, Gypsum Fibrosum 40-50 part, composite fibre by weight
1-2 part, cement 15-20 part, coarse sand 25-30 part, fine sand 10-15 part, pigment 9-12 part, wherein, the fineness of described fine sand
Modulus is inertia sand at 2.3-2.6, the clay content 1% of fine sand, described coarse sand, and the particle diameter fineness of coarse sand 0.5mm with
Under, described strength of cement grade is not less than 32.5, normal consistency water requirement≤27% of cement, and the presetting period of cement >=
45min, the final setting time≤6.5h of cement, the specific surface area >=3000cm of cement2/ g, the 80um square hole screen screen over-size of cement
≤ 10%, the 3d comprcssive strength >=12.0Mpa of cement, the 28d comprcssive strength >=32.5Mpa of cement, cement quick
Resisting and tear intensity >=5.5Mpa open, the 3d of cement is anti-tears intensity >=2.5 open, and the 28d of cement is anti-tears intensity >=5.5 open；
B. stirring: raw material is carried out mix and blend, and mixing time is 3-5min, adds water in whipping process, water and the ratio of raw material
For 1:2；
C. leading watt molding: final mixed material is packed into Wa Monei, final mixed material is squeezed into by watt machine of utilization
Type, watt machine maximum pressure >=120Mpa during molding, presses persistent period: 0.5-0.8s；
D. acrylic acid spraying: poured into by acrylic acid in high pressure conservation tank, opens acrylic acid flusher, adjusts atomization gas simultaneously
Pressure and acrylate pressure regulate spray effect；Described acrylic acid Lacquer finish coating is not more than 1% at the volatility of 105 DEG C；
E. indoor maintenance: the cement tile after spraying is placed in indoor 8 hours of the maintenance of temperature 50-55 DEG C；
F. showering curing: the cement tile after indoor maintenance is carried out showering curing 15 days, and every day, trickle was no less than 2 times；
G. steel ingot cleaning: steel ingot width 1/2 position is cleared up after terminating by ingot slow cool by flame gun, clears up width control
Making at 30-50CM, cleaning severity control is at 5-10mm；
H. spraying: the semi-finished product watt after showering curing are dried, until dry tack free, anhydrous mark, the face that then will modulate
Material is sprayed on semi-finished product watt by rule of operation；
I. dry: watt being also performed on spraying coating line after spraying is dried and surface coating material is dried；
J. check: coating is tested by Quality Inspector, check that device temperature requires to be: preheating chamber temperature is set in 90-120
℃；Hothouse temperature is set in 90-120 DEG C, spraying inspection equipment required for air pressure and blast pressure requirements be: air pressure pressure
Power reaches 0.6-0.8Mpa；Blast pressure reaches more than 0.5Mpa.
Using technical scheme, production efficiency is high, and the azulejo watt intensity height produced, and can prevent cracking, peace
Complete reliable, service life is long, and material is evenly distributed, and pigment adhesiveness is good.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below in conjunction with
Detailed description of the invention, is expanded on further the present invention.
Embodiment 1:
A kind of cracking resistance azulejo watt, by weight, described cracking resistance azulejo watt includes quick lime 20 parts, clay 20 parts, life
40 parts of Gypsum Fibrosum, composite fibre 1 part, cement 15 parts, coarse sand 25 parts, fine sand 10 parts, pigment 9 parts.
Wherein, described composite fibre includes the component by following weight proportion: high modulus fiber 15 parts, middle modulus fibre 25
Part, low modulus fibre 30 parts, described high modulus fiber uses a length of 20mm, and tensile strength is 1750MPa, and elastic modelling quantity is 27GPa
Phyllostachys pubescens Mazei ex H.de Lebaie fiber, described middle modulus fibre uses a length of 20mm, and tensile strength is 1250MPa, and the Lignum seu Ramulus Cunninghamiae Lanceolatae of elastic modelling quantity 20GPa is fine
Dimension, described low modulus fibre uses a length of 5mm, and tensile strength 700MPa, elastic modelling quantity is the bleached sulphate needle of 4.5GPa
Wood pulp cellulose.
Wherein, described pigment is black pigment.
Wherein, described cement uses silicate.
A kind of production technology of raw cracking resistance azulejo watt, described production technology specifically includes following steps:
A. dispensing: join preparing quick lime 20 parts, clay 20 parts, Gypsum Fibrosum 40 parts, composite fibre 1 part, cement by weight
15 parts, coarse sand 25 parts, fine sand 10 parts, pigment 9 parts, wherein, the modulus of fineness of described fine sand 2.6, the clay content of fine sand
1%, described coarse sand is inertia sand, and the particle diameter fineness of coarse sand is at below 0.5mm, and described strength of cement grade is not less than
32.5, the normal consistency water requirement 25% of cement, the presetting period 50min of cement, the final setting time 6.5h of cement, cement
Specific surface area 3000cm2/ g, the 80um square hole screen screen over-size 10% of cement, 3d comprcssive strength 12.0Mpa of cement,
28d comprcssive strength 32.5Mpa of cement, the Fast Anti of cement tears intensity 5.5Mpa open, and the 3d of cement is anti-tears intensity 2.5, water open
The 28d of mud is anti-tears intensity 6.5 open；
B. stirring: raw material is carried out mix and blend, and mixing time is 5min, adds water in whipping process, and water with the ratio of raw material is
1:2；
C. leading watt molding: final mixed material is packed into Wa Monei, final mixed material is squeezed into by watt machine of utilization
Type, watt machine maximum pressure 120Mpa during molding, presses persistent period: 0.6s；
D. acrylic acid spraying: poured into by acrylic acid in high pressure conservation tank, opens acrylic acid flusher, adjusts atomization gas simultaneously
Pressure and acrylate pressure regulate spray effect；Described acrylic acid Lacquer finish coating is not more than 1% at the volatility of 105 DEG C；
E. indoor maintenance: the cement tile after spraying is placed in indoor 8 hours of the maintenance of temperature 50 C；
F. showering curing: the cement tile after indoor maintenance is carried out showering curing 15 days, and every day, trickle was no less than 2 times；
G. steel ingot cleaning: steel ingot width 1/2 position is cleared up after terminating by ingot slow cool by flame gun, clears up width control
Making at 40CM, cleaning severity control is at 8mm；
H. spraying: the semi-finished product watt after showering curing are dried, until dry tack free, anhydrous mark, the face that then will modulate
Material is sprayed on semi-finished product watt by rule of operation；
I. dry: watt being also performed on spraying coating line after spraying is dried and surface coating material is dried；
J. check: coating is tested by Quality Inspector, check that device temperature requires to be: preheating chamber temperature is set in 120 DEG C；Dry
Dry room temperature is set in 90 DEG C, spraying inspection equipment required for air pressure and blast pressure requirements be: atmospheric pressure reaches
0.6Mpa ；Blast pressure reaches 0.5Mpa.
Embodiment 2:
A kind of cracking resistance azulejo watt, by weight, described cracking resistance azulejo watt includes quick lime 30 parts, clay 35 parts, life
50 parts of Gypsum Fibrosum, composite fibre 2 parts, cement 20 parts, coarse sand 30 parts, fine sand 15 parts, pigment 12 parts.
Wherein, described composite fibre includes the component by following weight proportion: high modulus fiber 20 parts, middle modulus fibre 35
Part, low modulus fibre 40 parts, described high modulus fiber uses a length of 2mm, and tensile strength is 1500MPa, and elastic modelling quantity is 23GPa's
Phyllostachys pubescens Mazei ex H.de Lebaie fiber, described middle modulus fibre uses a length of 2mm, and tensile strength is 500MPa, the Chinese Fir for Fibre of elastic modelling quantity 8GPa, institute
Stating low modulus fibre and use a length of 2mm, tensile strength 600MPa, elastic modelling quantity is that the bleached sulphate softwood pulp of 3.5GPa is fine
Dimension.
Wherein, described pigment is red pigment.
Wherein, described cement uses Portland cement.
A kind of production technology of raw cracking resistance azulejo watt, described production technology specifically includes following steps:
A. dispensing: join preparing quick lime 30 parts, clay 35 parts, Gypsum Fibrosum 50 parts, composite fibre 2 parts, cement 20 by weight
Part, coarse sand 30 parts, fine sand 15 parts, pigment 12 parts, wherein, the modulus of fineness of described fine sand 2.4, the clay content 1% of fine sand,
Described coarse sand is inertia sand, and the particle diameter fineness of coarse sand is at 0.5mm, described strength of cement grade 32.5, the normal consistency of cement
Water requirement 27%, the presetting period 45min of cement, the final setting time 6.5h of cement, specific surface area 3000cm of cement2/ g, water
The 80um square hole screen screen over-size 10% of mud, 3d comprcssive strength 12.0Mpa of cement, the 28d comprcssive strength of cement
32.5Mpa, the Fast Anti of cement tears intensity 5.5Mpa open, and the 3d of cement is anti-tears intensity 2.5 open, and the 28d of cement is anti-tears intensity 5.5 open；
B. stirring: raw material is carried out mix and blend, and mixing time is 3min, adds water in whipping process, and water with the ratio of raw material is
1:2；
C. leading watt molding: final mixed material is packed into Wa Monei, final mixed material is squeezed into by watt machine of utilization
Type, watt machine maximum pressure 120Mpa during molding, presses persistent period: 0.5s；
D. acrylic acid spraying: poured into by acrylic acid in high pressure conservation tank, opens acrylic acid flusher, adjusts atomization gas simultaneously
Pressure and acrylate pressure regulate spray effect；Described acrylic acid Lacquer finish coating is at the volatility 1% of 105 DEG C；
E. indoor maintenance: the cement tile after spraying is placed in indoor 8 hours of the maintenance of temperature 55 DEG C；
F. showering curing: the cement tile after indoor maintenance is carried out showering curing 15 days, and every day, trickle was no less than 2 times；
G. steel ingot cleaning: steel ingot width 1/2 position is cleared up after terminating by ingot slow cool by flame gun, clears up width control
Making at 40CM, cleaning severity control is at 8mm；
H. spraying: the semi-finished product watt after showering curing are dried, until dry tack free, anhydrous mark, the face that then will modulate
Material is sprayed on semi-finished product watt by rule of operation；
I. dry: watt being also performed on spraying coating line after spraying is dried and surface coating material is dried；
J. check: coating is tested by Quality Inspector, check that device temperature requires to be: preheating chamber temperature is set in 110 DEG C；Dry
Dry room temperature is set in 110 DEG C, spraying inspection equipment required for air pressure and blast pressure requirements be: atmospheric pressure reaches
0.7Mpa ；Blast pressure reaches more than 0.5Mpa.
Embodiment 3: a kind of cracking resistance azulejo watt, by weight, described cracking resistance azulejo watt include quick lime 25 parts,
Clay 30 parts, Gypsum Fibrosum 45 parts, composite fibre 2 parts, cement 15 parts, coarse sand 25 parts, fine sand 10 parts, pigment 9 parts.
Wherein, described composite fibre includes the component by following weight proportion: high modulus fiber 18 parts, middle modulus fibre 30
Part, low modulus fibre 35 parts, described high modulus fiber uses length 15mm, and tensile strength is 1600MPa, and elastic modelling quantity is 25GPa's
Phyllostachys pubescens Mazei ex H.de Lebaie fiber, described middle modulus fibre uses a length of 15mm, and tensile strength is 1000MPa, the Chinese Fir for Fibre of springform 15GPa,
Described low modulus fibre uses a length of 3mm, and tensile strength 650MPa, elastic modelling quantity is the bleached sulphate softwood pulp of 4.5GPa
Fiber.
Wherein, described pigment is blue pigment.
Wherein, described cement uses silicate.
A kind of production technology of raw cracking resistance azulejo watt, described production technology specifically includes following steps:
A. dispensing: join preparing quick lime 25 parts, clay 30 parts, Gypsum Fibrosum 45 parts, composite fibre 2 parts, cement by weight
15 parts, coarse sand 25 parts, fine sand 10 parts, pigment 9 parts, wherein, the modulus of fineness of described fine sand 2.5, the clay content of fine sand
1%, described coarse sand is inertia sand, and the particle diameter fineness of coarse sand is at 0.5mm, described strength of cement grade 32.5, the mark of cement
Quasi-denseness water requirement 27%, the presetting period 45min of cement, the final setting time 5.5h of cement, the specific surface area of cement
3000cm2/ g, the 80um square hole screen screen over-size 10% of cement, 3d comprcssive strength 12.0Mpa of cement, the 28d of cement
Comprcssive strength 32.5Mpa, the Fast Anti of cement tears intensity 5.5Mpa open, and the 3d of cement is anti-tears intensity 2.5 open, the 28d of cement is anti-tears open strong
Degree 5.5；
B. stirring: raw material is carried out mix and blend, and mixing time is 4min, adds water in whipping process, and water with the ratio of raw material is
1:2；
C. leading watt molding: final mixed material is packed into Wa Monei, final mixed material is squeezed into by watt machine of utilization
Type, watt machine maximum pressure 120Mpa during molding, presses persistent period: 0.6s；
D. acrylic acid spraying: poured into by acrylic acid in high pressure conservation tank, opens acrylic acid flusher, adjusts atomization gas simultaneously
Pressure and acrylate pressure regulate spray effect；Described acrylic acid Lacquer finish coating is not more than 1% at the volatility of 105 DEG C；
E. indoor maintenance: the cement tile after spraying is placed in indoor 8 hours of the maintenance of temperature 53 DEG C；
F. showering curing: the cement tile after indoor maintenance is carried out showering curing 15 days, every day trickle 3 times；
G. steel ingot cleaning: steel ingot width 1/2 position is cleared up after terminating by ingot slow cool by flame gun, clears up width control
Making at 40CM, cleaning severity control is at 8mm；
H. spraying: the semi-finished product watt after showering curing are dried, until dry tack free, anhydrous mark, the face that then will modulate
Material is sprayed on semi-finished product watt by rule of operation；
I. dry: watt being also performed on spraying coating line after spraying is dried and surface coating material is dried；
J. check: coating is tested by Quality Inspector, check that device temperature requires to be: preheating chamber temperature is set in 110 DEG C；Dry
Dry room temperature is set in 110 DEG C, spraying inspection equipment required for air pressure and blast pressure requirements be: atmospheric pressure reaches
0.7Mpa ；Blast pressure reaches 0.5Mpa.
Based on above-mentioned, using technical scheme, production efficiency is high, and the azulejo watt intensity height produced, and can prevent
Only cracking, safe and reliable, service life is long, and material is evenly distributed, and pigment adhesiveness is good.
Obviously the present invention implements and is not subject to the restrictions described above, as long as have employed method design and the skill of the present invention
The improvement of the various unsubstantialities that art scheme is carried out, or the most improved design by the present invention and technical scheme directly apply to it
Its occasion, all within protection scope of the present invention.
Claims (6)
1. a cracking resistance azulejo watt, it is characterised in that by weight, described cracking resistance azulejo watt includes quick lime 20-30
Part, clay 20-35 part, Gypsum Fibrosum 40-50 part, composite fibre 1-2 part, cement 15-20 part, coarse sand 25-30 part, thin
Sand 10-15 part, pigment 9-12 part.
A kind of cracking resistance azulejo watt the most according to claim 1, it is characterised in that: by weight, described cracking resistance is color
Brick and tile include quick lime 25 parts, clay 30 parts, Gypsum Fibrosum 45 parts, composite fibre 2 parts, cement 15 parts, coarse sand 25 parts,
Fine sand 10 parts, pigment 9 parts.
A kind of cracking resistance azulejo watt the most according to claim 1, it is characterised in that: described composite fibre includes by following heavy
The component of amount proportioning: high modulus fiber 15-20 part, middle modulus fibre 25-35 part, low modulus fibre 30-40 part, described high modulus fiber
Using a length of 2-20mm, tensile strength is 1500-1750MPa, and elastic modelling quantity is the Phyllostachys pubescens Mazei ex H.de Lebaie fiber of 23-27GPa, described middle mold
Fiber uses a length of 2-20mm, and tensile strength is 500-1250MPa, the Chinese Fir for Fibre of elastic modelling quantity 8-20GPa, described low mould
Fiber uses a length of 2-5mm, and tensile strength 600-700MPa, elastic modelling quantity is the bleached sulphate needlebush of 3.5-4.5GPa
Pulp fibres.
A kind of cracking resistance azulejo watt the most according to claim 1, it is characterised in that: described pigment is red pigment, blueness
One in pigment, yellow uitramarine, black pigment.
A kind of cracking resistance azulejo watt the most according to claim 1, it is characterised in that: described cement uses silicate or common
Portland cement.
6. the technique of the cracking resistance azulejo watt that a kind produces described in claim 1-5 any one, it is characterised in that described production
Technique specifically includes following steps:
A. dispensing: join preparing quick lime 20-30 part, clay 20-35 part, Gypsum Fibrosum 40-50 part, composite fibre by weight
1-2 part, cement 15-20 part, coarse sand 25-30 part, fine sand 10-15 part, pigment 9-12 part, wherein, the fineness of described fine sand
Modulus is inertia sand at 2.3-2.6, the clay content 1% of fine sand, described coarse sand, and the particle diameter fineness of coarse sand 0.5mm with
Under, described strength of cement grade is not less than 32.5, normal consistency water requirement≤27% of cement, and the presetting period of cement >=
45min, the final setting time≤6.5h of cement, the specific surface area >=3000cm of cement2/ g, the 80um square hole screen screen over-size of cement
≤ 10%, the 3d comprcssive strength >=12.0Mpa of cement, the 28d comprcssive strength >=32.5Mpa of cement, cement quick
Resisting and tear intensity >=5.5Mpa open, the 3d of cement is anti-tears intensity >=2.5 open, and the 28d of cement is anti-tears intensity >=5.5 open；
B. stirring: raw material is carried out mix and blend, and mixing time is 3-5min, adds water in whipping process, water and the ratio of raw material
For 1:2；
C. leading watt molding: final mixed material is packed into Wa Monei, final mixed material is squeezed into by watt machine of utilization
Type, watt machine maximum pressure >=120Mpa during molding, presses persistent period: 0.5-0.8s；
D. acrylic acid spraying: poured into by acrylic acid in high pressure conservation tank, opens acrylic acid flusher, adjusts atomization gas simultaneously
Pressure and acrylate pressure regulate spray effect；Described acrylic acid Lacquer finish coating is not more than 1% at the volatility of 105 DEG C；
E. indoor maintenance: the cement tile after spraying is placed in indoor 8 hours of the maintenance of temperature 50-55 DEG C；
F. showering curing: the cement tile after indoor maintenance is carried out showering curing 15 days, and every day, trickle was no less than 2 times；
G. steel ingot cleaning: steel ingot width 1/2 position is cleared up after terminating by ingot slow cool by flame gun, clears up width control
Making at 30-50CM, cleaning severity control is at 5-10mm；
H. spraying: the semi-finished product watt after showering curing are dried, until dry tack free, anhydrous mark, the face that then will modulate
Material is sprayed on semi-finished product watt by rule of operation；
I. dry: watt being also performed on spraying coating line after spraying is dried and surface coating material is dried；
J. check: coating is tested by Quality Inspector, check that device temperature requires to be: preheating chamber temperature is set in 90-120
℃；Hothouse temperature is set in 90-120 DEG C, spraying inspection equipment required for air pressure and blast pressure requirements be: air pressure pressure
Power reaches 0.6-0.8Mpa；Blast pressure reaches more than 0.5Mpa.