CN106942782A - 一种高留着的再造烟叶纸基制备方法 - Google Patents

一种高留着的再造烟叶纸基制备方法 Download PDF

Info

Publication number
CN106942782A
CN106942782A CN201710202801.XA CN201710202801A CN106942782A CN 106942782 A CN106942782 A CN 106942782A CN 201710202801 A CN201710202801 A CN 201710202801A CN 106942782 A CN106942782 A CN 106942782A
Authority
CN
China
Prior art keywords
paper substrate
reconstituted tobacco
parts
tobacco paper
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201710202801.XA
Other languages
English (en)
Other versions
CN106942782B (zh
Inventor
陈长兵
阮学良
王铜根
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianchang Tianda Carton And Paper Product Factory
Original Assignee
Tianchang Tianda Carton And Paper Product Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianchang Tianda Carton And Paper Product Factory filed Critical Tianchang Tianda Carton And Paper Product Factory
Priority to CN201710202801.XA priority Critical patent/CN106942782B/zh
Publication of CN106942782A publication Critical patent/CN106942782A/zh
Application granted granted Critical
Publication of CN106942782B publication Critical patent/CN106942782B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高留着的再造烟叶纸基制备方法，先将魔芋胶用双氧水进行氧化，与植物蛋白、硫酸铝混合后对碳酸钙进行改性，然后与烟草浆料混合经过抄片、真空干燥、烘干工序，得到再造烟叶纸基。本发明的生产工艺流程简单、易于操作，能有效降低成本、节约原料，生产得到的再造烟叶纸基具有优良的物理性能指标和外观质量，同时不影响再造烟叶的吸味品质，实用性强。

Description

一种高留着的再造烟叶纸基制备方法
技术领域
本发明涉及烟叶生产技术领域，尤其涉及一种高留着的再造烟叶纸基制备方法。
背景技术
造纸法再造烟叶(又称“薄片”)是指按再造烟叶原料配方要求，将烟末、烟梗等原料用溶剂浸泡提取后，分离出可溶性物质和不溶性物质，将不溶性物质用造纸的方法制成像原纸一样的烟片基，然后存该片基上加入浓缩后的可溶性物质和添加剂，干燥后成为再造烟叶。与辊压法和稠浆法薄片相比，造纸法再造烟叶具有填充性能好、焦油释放量低等优点，具有广阔的发展前景。目前再造烟叶纸基生产常用的填料为沉淀碳酸钙，其在再造烟叶纸基中的留着率低，不仅造成浆料的利用率低，还会影响再造烟叶的产量和质量。因此，提高浆料留着率已经成为备受关注的研究课题。
CN103859576A通过天然马铃薯淀粉对填料进行表面包裹或部分包裹、调节表面电荷、然后将包裹的填料加入烟草浆料中生产造纸法再造烟叶，有效提高了浆料中纤维和填料的留着，提高了原料的利用率，并对烟草薄片品质无影响。然而这种方法仅改善了浆料留着率，对再造烟叶纸基的物理性能指标并没有提升，同时马铃薯淀粉作为包裹剂，对填料以及纤维的附着性较低，对浆料留着率的提高有限。因此，仍需作出进一步改进。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种原料利用率高、产品物理性能指标优良的再造烟叶纸基生产工艺。
本发明是通过以下技术方案实现的：
一种高留着的再造烟叶纸基制备方法，包括以下步骤：
（1）先将3-5重量份魔芋胶加入60-80重量份水中于60-80℃充分搅拌1-2h，然后用氢氧化钠将pH调至9-9.5，加入1-1.5重量份双氧水继续搅拌0.5-1h，冷却后得改性魔芋胶溶液；
（2）将20-30重量份碳酸钙与10-15重量份步骤（1）的改性魔芋胶溶液充分混合，再加入0.1-0.15重量份植物蛋白继续搅拌，然后加入0.1-0.15重量份硫酸铝高速混合并研磨均匀，得改性碳酸钙；
（3）将80-100重量份烟梗、烟末打浆制得的烟草浆料与40-80重量份步骤（2）的改性碳酸钙混合均匀，经过抄片、真空干燥、烘干工序，即得再造烟叶纸基。
所述双氧水的质量分数为20-30%。
所述植物蛋白为花生蛋白、小麦蛋白、大豆蛋白中的一种或者混合。
所述碳酸钙为400-600目。
所述步骤（3）真空干燥工序的压力为0.08-0.1MPa。
所述步骤（3）烘干工序的温度为100-105℃。
本发明的优点是：
本发明先将魔芋胶用双氧水进行氧化，与植物蛋白、硫酸铝混合后对碳酸钙进行改性，然后与烟草浆料混合经过抄片、真空干燥、烘干工序，得到再造烟叶纸基。本发明利用植物蛋白与铝离子的螯合、植物蛋白与氧化魔芋胶之间交联、铝离子与氧化魔芋胶之间络合的效应得到多元助留体系，不仅能能提高碳酸钙与烟草浆料纤维的结合力，使碳酸钙能有效附着在浆料纤维上，从而改善浆料的留着性能，提高原料利用率，而且能增加浆料加工得到的纸基的韧性和强度。本发明的制备方法流程简单、易于操作，能有效降低成本、节约原料，生产得到的再造烟叶纸基具有优良的物理性能指标和外观质量，同时不影响再造烟叶的吸味品质，实用性强。
具体实施方式
一种高留着的再造烟叶纸基制备方法，包括以下步骤：
（1）先将3kg魔芋胶加入60kg水中于60℃充分搅拌1h，然后用氢氧化钠将pH调至9，加入1kg双氧水继续搅拌0.5h，冷却后得改性魔芋胶溶液；
（2）将20kg碳酸钙与10kg步骤（1）的改性魔芋胶溶液充分混合，再加入0.1kg植物蛋白继续搅拌，然后加入0.1kg硫酸铝高速混合并研磨均匀，得改性碳酸钙；
（3）将80kg烟梗、烟末打浆制得的烟草浆料与40kg步骤（2）的改性碳酸钙混合均匀，经过抄片、真空干燥、烘干工序，即得再造烟叶纸基。
所述双氧水的质量分数为20%。
所述植物蛋白为花生蛋白。
所述碳酸钙为400目。
所述步骤（3）真空干燥工序的压力为0.08MPa。
所述步骤（3）烘干工序的温度为100℃。

Claims (6)

1.一种高留着的再造烟叶纸基制备方法，其特征在于，包括以下步骤：
（1）先将3-5重量份魔芋胶加入60-80重量份水中于60-80℃充分搅拌1-2h，然后用氢氧化钠将pH调至9-9.5，加入1-1.5重量份双氧水继续搅拌0.5-1h，冷却后得改性魔芋胶溶液；
（2）将20-30重量份碳酸钙与10-15重量份步骤（1）的改性魔芋胶溶液充分混合，再加入0.1-0.15重量份植物蛋白继续搅拌，然后加入0.1-0.15重量份硫酸铝高速混合并研磨均匀，得改性碳酸钙；
（3）将80-100重量份烟梗、烟末打浆制得的烟草浆料与40-80重量份步骤（2）的改性碳酸钙混合均匀，经过抄片、真空干燥、烘干工序，即得再造烟叶纸基。
2.根据权利要求1所述的一种高留着的再造烟叶纸基制备方法，其特征在于，所述双氧水的质量分数为20-30%。
3.根据权利要求1所述的一种高留着的再造烟叶纸基制备方法，其特征在于，所述植物蛋白为花生蛋白、小麦蛋白、大豆蛋白中的一种或者混合。
4.根据权利要求1所述的一种高留着的再造烟叶纸基制备方法，其特征在于，所述碳酸钙为400-600目。
5.根据权利要求1所述的一种高留着的再造烟叶纸基制备方法，其特征在于，所述步骤（3）真空干燥工序的压力为0.08-0.1MPa。
6.根据权利要求1所述的一种高留着的再造烟叶纸基制备方法，其特征在于，所述步骤（3）烘干工序的温度为100-105℃。
CN201710202801.XA 2017-03-30 2017-03-30 一种高留着的再造烟叶纸基制备方法 Active CN106942782B (zh)