CN106906550A - A kind of bamboo section pattern yarn - Google Patents
A kind of bamboo section pattern yarn Download PDFInfo
- Publication number
- CN106906550A CN106906550A CN201710079810.4A CN201710079810A CN106906550A CN 106906550 A CN106906550 A CN 106906550A CN 201710079810 A CN201710079810 A CN 201710079810A CN 106906550 A CN106906550 A CN 106906550A
- Authority
- CN
- China
- Prior art keywords
- speed
- revs
- cashmere
- spun silk
- silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of bamboo section pattern yarn, by spun silk, cashmere, A100 is tencel blended forms, and by weight percentage, each raw material components proportioning is as follows：Spun silk 5~20%, cashmere 5~15%, A100 tencels 65~90%.The present invention is soft, ventilative good, full color, gloss is soft, pendency is excellent, dimensionally stable, comfortable and easy to wear, good hygroscopicity, good permeability, distinct style；The advantage of spun silk, cashmere and A100 tencels is provided simultaneously with, while respective shortcoming is compensate for, with wider array of range of application and market prospects.
Description
Technical field
The present invention relates to spinninging technical field, more particularly to a kind of bamboo section pattern yarn.
Background technology
Spun silk is broadly divided into mulberry silk and tussah silk, wherein on tussah growth toothed oak tree in the wild, tussah silk it is average carefully
It is 3.1dtex (monofilament) to spend, thicker than mulberry silk.Its length spring cocoon about 600m, reelability wire length 360-490m, autumn cocoon length degree 700-
1000m, reelability wire length is all 360-490m, and its section is sharp triangle, flat in wedge-like.Tussah silk is weaving silk fabric, decoration
Silk fabric and some industry, raw materials of national defence silk goods, are generally used for weaving medium-thick type silk goods.Mulberry silk is domestic silk,
Fed with mulberry leaves.Mulberry cocoon ecto-entad is divided into husks, cocoon layer and the part of pelettes three.Wherein cocoon layer can be used to do silk weaving original
Material, because thin, fragility can be used as silk spinning raw material to husks with pelettes.Mulberry silk fineness is about 2.64-3.74dtex (mariages), and its is thin
Spend with the discharge successively difference of silk, with the stage casing of the middle level of cocoon and silk for most thin and uniformly, and triangle character is bright
It is aobvious.Silk is mainly fibroin albumen, next to that silk gum, also contains a small amount of impurity such as pigment, wax, fat, inorganic matter.The present invention
Using mulberry silk.Substantially, mulberry silk is finer and smoother, and tussah silk is simpleer and more unsophisticated, and gloss is soft, and feel is smooth for spun silk kind style and features,
To skin compatibility very well, it is very high-grade spinning material.But because spun silk is excessively soft and smooth, jewelry, expensive clothing and other valuables, and exist obvious quiet
Electrical phenomena, Spinning process is very difficult on cotton system does, and the requirement for the treatment of and technology to raw material is very high.
Cashmere is the fine hair of goat, and color point is white, purple, cyan., without medullary substance, Qiang Shenxing, elasticity are better than identical for cashmere
The sheep's wool of fineness.The ring-type of scale is obvious with integrity feature, and big and dilute, is close to hair shaft, and soft cunning is glutinous.Averagely
Fineness is generally 14-16um (belonging to 80/90S maos), is most thin, length 35-45mm, short flannel 18-20% in animal origin.Goat
The soft cunning of suede light weight, warmth retention property is especially excellent, good to skin compatibility, but easily crispaturas, and has obvious electrostatic phenomenon, on cotton system
Production is very difficult to be done.In mixing because the excessive curling of cashmere is difficult to be well mixed, and due to expensive, production process
Middle management and control is careless slightly will to cause huge loss.There is technical threshold very high using cashmere as cotton spinning raw material.
Tencel is the regenerated celulose fibre of the newer type that Austrian Lenzin company develops.Its fibre property is very excellent
It is good：Dry, wet strength greatly, does strong close to terylene, and in 4cn/Dtex or so, even more high is wet about to do strong 80% by force；Introductory die
Amount is high, and the shrinkage factor in water is small, good stability of the dimension.Plain edition (G100) fiber has very prominent fibrillation phenomenon.Crosslinking
Type (A100) fiber is difficult pilling almost without fibrillation phenomenon during taking.LF tencels are then using without formaldehyde
Organic solvent, harmless, fibrillation phenomenon is lighter, is typically used for bed necessaries, and feel is slided glutinous, compares " enervated ".Tencel
Because rigidity is big, surface is smooth, it is easy to point comb, but easily brittle failure, and because the smooth cohesive force in surface is poor, spinning difficulty is higher,
It is the raw material for being most difficult to control resultant yarn index in common man-made cellulose fibers.
In view of with three kinds of excellent in performance of raw material, having neutralized two kinds of natural top grade protein fibres and a kind of regeneration of high-performance
The advantage of cellulose fibre, performance is more remarkable, along with being given to the obvious style characteristic of product fabric using ring yarn process,
The existing spun silk of fabric made it is fine and smooth soft and smooth, have the plentiful fluffy of cashmere again, the texture of also tencel is wide.By three kinds completely
Different raw material styles is rubbed and is integrated, recycle slub the additional style of moire hollow out, alone become a high-end, function, fashion,
The product of characteristic.But, there are excessively a softer and smoother touch, electrostatic distinct issues in spinning process in spun silk.Cashmere carries curling
It is excessive to be difficult to stretch, and because soft cohesive force is poor.Tencel rigidity is big, and combing difficult processing is grasping product.At present, not on
Spun silk, cashmere, the relevant report of Modal blended bamboo node fancy yarn
The content of the invention
It is an object of the invention to provide a kind of bamboo section pattern yarn, soft, ventilative good, full color, gloss are soft
With, dangle excellent, dimensionally stable, comfortable and easy to wear, good hygroscopicity, good permeability, distinct style；It is provided simultaneously with spun silk, goat
The advantage of suede and A100 tencels, while respective shortcoming is compensate for, with wider array of range of application and market prospects.
The technical solution adopted for the present invention to solve the technical problems is：
A kind of bamboo section pattern yarn, by spun silk, cashmere, A100 is tencel blended forms, by weight percentage, each raw material group
Distribution ratio is as follows：Spun silk 5~20%, cashmere 5~15%, A100 tencels 65~90%.Spun silk of the present invention is made using mulberry silk
It is raw material.Cashmere of the present invention is using most high-grade white middle white goat wool as raw material.A100 tencels of the present invention are used without fibril
The A100 raw materials of change.
Before the present invention, and in the absence of the technique for preparing spun silk, cashmere, A100 tencel blended bamboo node fancy yarns；This hair
It is bright by analysing in depth the performance and spinnability of raw material, while carried out numerous studies experiment, it is achieved thereby that preparing spun silk, mountain
The technique of cashmere, A100 tencel blended bamboo node fancy yarns.Technique of the invention, successfully solves：Spun silk excessively soft, light
Sliding, electrostatic is big, easily winding, and cashmere is excessively soft, disaster is stretched, cohesive force is small, electrostatic is big, easy damaged for curling, A tencel rigidity
Greatly, the problem of easy brittle failure；While reducing to fibre damage, also with the advantage of spinnability between each fiber of mediation；Successfully
Prepare and be provided simultaneously with spun silk, cashmere, the spun silk of the advantage of A100 tencels, cashmere, A100 tencel blended bamboo node fancy yarns.
The present invention passes through modified technique (cotton cleaning process：Using specified raw material handling process and the mixed technique of bag；Change cotton carding work
The technological parameter of sequence, Roving Frames and spinning process, designs specific random ring) successfully solve：Spun silk excessively soft, light
Sliding, electrostatic is big, easily winding, and cashmere is excessively soft, disaster is stretched, cohesive force is small, electrostatic is big, easy damaged for curling, A tencel rigidity
Greatly, the problem of easy brittle failure；While reducing to fibre damage, also with the advantage of spinnability between each fiber of mediation；Successfully
Prepare and be provided simultaneously with spun silk, cashmere, the advantage of A100 tencels, while compensate for the spun silk of respective shortcoming, cashmere, A100
Tencel blended bamboo node fancy yarn.Mixed yarn good hand feeling of the invention is fine and smooth, a softer and smoother touch, ventilative good, full color, gloss
It is soft, unique style, comfortable and easy to wear.Preferably, by weight percentage, each raw material components proportioning is as follows：Spun silk 10%, mountain
Cashmere 10%, A100 tencels 80%.
Preferably, ring is irregular at random.
A kind of preparation method of bamboo section pattern yarn, comprises the following steps：
(1) Feedstock treating：The antistatic additive aqueous solution is uniformly sprayed on spun silk and cashmere respectively, seal it is vexed put 12~
Used after 48h；Enter cotton cleaning process (the mixed technique of bag) after the mixing of spun silk, cashmere and A100 tencels；
(2) cotton cleaning process：450~500 revs/min of opener Beater Speed, single beater scutcher Beater Speed 900~1000
Rev/min, lap roller speed：10~12 revs/min；
(3) carding step：300~360 revs/min of cylinder speed, 16~22 revs/min of doffer speed, licker-in speed：550~
750 revs/min；
(4) mixing in doubling step：Slubbing drafting：170~200 ms/min of speed, 1.25~1.40 times of first break draft；
Two road draftings：160~190 ms/min of speed, 1.20~1.35 times of first break draft；
Extreme trace drafting：150~180 ms/min of speed, 1.20~1.30 times of first break draft；
(5) Roving Frames：700~800 revs/min of rove ingot speed, back area draft：1.2~1.35；
(6) spinning process：13500~15000 revs/min of spun yarn spindle speed, back area draft：1.15~1.35.
(7) ring operation：Average section 9~25cm long, mean pitch：6~70cm, saves thick 1.6~2.2 times, random ring.
Preferably, cotton cleaning process：480 revs/min of opener Beater Speed, single beater scutcher synthesis Beater Speed 950
Rev/min, 11 revs/min of lap roller speed；Carding step：330 revs/min of cylinder speed, 18 revs/min of doffer speed, licker-in speed
700 revs/min.
Preferably, mixing in doubling step：
Slubbing drafting：190 ms/min of speed, 1.35 times of first break draft；
Two road draftings：170 ms/min of speed, 1.30 times of first break draft；
Extreme trace drafting：150 ms/min of speed, 1.25 times of first break draft.
Preferably, Roving Frames：750 revs/min of rove ingot speed, 1.26 times of back area draft；Spinning process：Spun yarn spindle speed
13500 revs/min, 1.20 times of first break draft.
Preferably, ring operation：Average section length：16cm, mean pitch 33cm, section are thick：2.2 times, random ring.
Preferably, the mass concentration of the antistatic additive aqueous solution is 5~15% in step (1), the antistatic additive aqueous solution
Consumption is respectively the 5~15% of spun silk weight, the 5~15% of cashmere weight.
The beneficial effects of the invention are as follows：
Spun silk of the present invention, cashmere, A100 tencel blended bamboo node fancy yarns have advantages below：It is soft, ventilative good
Good, full color, gloss is soft, pendency is excellent, dimensionally stable, comfortable and easy to wear, good hygroscopicity, good permeability, distinct style；I.e.
Be provided simultaneously with the advantage of spun silk, cashmere and A100 tencels, while compensate for respective shortcoming, with wider array of range of application and
Market prospects.
Specific embodiment
Below by specific embodiment, technical scheme is described in further detail.
In the present invention, if not refering in particular to, raw material and equipment for being used etc. is commercially available or commonly used in the art.
Method in following embodiments, unless otherwise instructed, is the conventional method of this area.
In following embodiments and comparative example, raw material sources：Spun silk is A grades of silk tops；Cashmere specification be 16um*41mm it is white in
White goat wool；The specification of A100 tencels is 1.25dtex*38mm.
Embodiment 1.1
Raw material：Spun silk 10kg, cashmere 10kg, A100 tencel 80kg；
Production technology：
(1) Feedstock treating：Spun silk and cashmere are pressed using the 10% antistatic additive aqueous solution (antistatic additive model FK-305)
10% weight is uniformly sprayed on spun silk and cashmere, seal it is vexed to put feed intake after 24h use；Spun silk, cashmere and A100 tencels
Enter cotton cleaning process after mixing；
(2) cotton cleaning process：480 revs/min of opener Beater Speed, single beater scutcher 950 revs/min of Beater Speed of synthesis,
11 revs/min of lap roller speed；
(3) carding step：330 revs/min of cylinder speed, 18 revs/min of doffer speed, 700 revs/min of licker-in speed；
(4) mixing in doubling step：Slubbing drafting：190 ms/min of speed, 1.35 times of first break draft；
Two road draftings：170 ms/min of speed, 1.30 times of first break draft；
Extreme trace drafting：150 ms/min of speed, 1.25 times of first break draft；
(4) Roving Frames：650 revs/min of rove ingot speed, 1.26 times of back area draft；
(5) spinning process：13500 revs/min of spun yarn spindle speed, 1.20 times of later stage drawing-off.
(6) ring technique：Average section length：16cm, mean pitch 33cm, section are thick：2.2 times, random ring.
Embodiment 1.2
Raw material：Spun silk 10kg, cashmere 10kg, A100 tencel 80kg；
Production technology：
(1) Feedstock treating：Thin,tough silk is uniformly sprayed at by spun silk and the weight of cashmere 15% using the 15% antistatic additive aqueous solution
On silk and cashmere, seal it is vexed to put feed intake after 36h use；Enter cotton cleaning process after the mixing of spun silk, cashmere and A100 tencels；
(2) cotton cleaning process：450 revs/min of opener Beater Speed, single beater scutcher 900 revs/min of Beater Speed of synthesis,
10 revs/min of lap roller speed；
(3) carding step：330 revs/min of cylinder speed, 16 revs/min of doffer speed, 550 revs/min of licker-in speed；
(4) mixing in doubling step：Slubbing drafting：180 ms/min of speed, 1.32 times of first break draft；
Two road draftings：160 ms/min of speed, 1.25 times of first break draft；
Extreme trace drafting：150 ms/min of speed, 1.21 times of first break draft；
(4) Roving Frames：600 revs/min of rove ingot speed, 1.21 times of back area draft；
(5) spinning process：13500 revs/min of spun yarn spindle speed, 1.17 times of later stage drawing-off.
(6) ring technique：Average section length：18cm, mean pitch 42cm, section are thick：2.0 times, random ring.
Embodiment 1.3
Raw material：Spun silk 10kg, cashmere 10kg, A100 tencel 80kg；
Production technology：
(1) Feedstock treating：Thin,tough silk is uniformly sprayed at by spun silk and the weight of cashmere 10% using the 10% antistatic additive aqueous solution
On silk and cashmere, seal it is vexed to put feed intake after 48h use；Enter cotton cleaning process after the mixing of spun silk, cashmere and A100 tencels；
(2) cotton cleaning process：500 revs/min of opener Beater Speed, single beater scutcher 1000 revs/min of Beater Speed of synthesis,
12 revs/min of lap roller speed；
(3) carding step：360 revs/min of cylinder speed, 22 revs/min of doffer speed, 750 revs/min of licker-in speed；
(4) mixing in doubling step：Slubbing drafting：200 ms/min of speed, 1.40 times of first break draft；
Two road draftings：180 ms/min of speed, 1.35 times of first break draft；
Extreme trace drafting：160 ms/min of speed, 1.26 times of first break draft；
(4) Roving Frames：700 revs/min of rove ingot speed, 1.26 times of back area draft；
(5) spinning process：15000 revs/min of spun yarn spindle speed, 1.24 times of later stage drawing-off.
(6) ring technique：Average section length：10cm, mean pitch 22cm, section are thick：1.6 times, random ring.
Comparative example 1-1
Raw material：Spun silk 10kg, cashmere 10kg, A100 tencel 80kg；
Production technology：
(1) Feedstock treating：Thin,tough silk is uniformly sprayed at by spun silk and the weight of cashmere 10% using the 15% antistatic additive aqueous solution
On silk and cashmere, seal it is vexed to put feed intake after 24h use；Enter cotton cleaning process after the mixing of spun silk, cashmere and A100 tencels；
(2) cotton cleaning process：550 revs/min of opener Beater Speed, single beater scutcher 1050 revs/min of Beater Speed of synthesis,
13 revs/min of lap roller speed；
(3) carding step：330 revs/min of cylinder speed, 18 revs/min of doffer speed, 700 revs/min of licker-in speed；
(4) mixing in doubling step：Slubbing drafting：200 ms/min of speed, 1.35 times of first break draft；
Two road draftings：180 ms/min of speed, 1.35 times of first break draft；
Extreme trace drafting：160 ms/min of speed, 1.26 times of first break draft；
(4) Roving Frames：750 revs/min of rove ingot speed, 1.26 times of back area draft；
(5) spinning process：13500 revs/min of spun yarn spindle speed, 1.20 times of later stage drawing-off.
(6) ring technique：Average section length：16cm, mean pitch 33cm, section are thick：2.2 times, random ring.
Comparative example 1-2
Raw material：Spun silk 10kg, cashmere 10kg, A100 tencel 80kg；
Production technology：
(1) Feedstock treating：Thin,tough silk is uniformly sprayed at by spun silk and the weight of cashmere 10% using the 10% antistatic additive aqueous solution
On silk and cashmere, seal it is vexed to put feed intake after 24h use；Enter cotton cleaning process after the mixing of spun silk, cashmere and A100 tencels；
(2) cotton cleaning process：480 revs/min of opener Beater Speed, single beater scutcher 950 revs/min of Beater Speed of synthesis,
11 revs/min of lap roller speed；
(3) carding step：380 revs/min of cylinder speed, 22 revs/min of doffer speed, 800 revs/min of licker-in speed；
(4) mixing in doubling step：Slubbing drafting：190 ms/min of speed, 1.40 times of first break draft；
Two road draftings：170 ms/min of speed, 1.35 times of first break draft；
Extreme trace drafting：150 ms/min of speed, 1.26 times of first break draft；
(4) Roving Frames：750 revs/min of rove ingot speed, 1.26 times of back area draft；
(5) spinning process：13500 revs/min of spun yarn spindle speed, 1.20 times of later stage drawing-off.
(6) ring technique：Average section length：18cm, mean pitch 42cm, section are thick：2.0 times, random ring.
Comparative example 1-3
Raw material：Spun silk 10kg, cashmere 10kg, A100 tencel 80kg；
Production technology：
(1) Feedstock treating：Thin,tough silk is uniformly sprayed at by spun silk and the weight of cashmere 10% using the 10% antistatic additive aqueous solution
On silk and cashmere, seal it is vexed to put feed intake after 24h use；Enter cotton cleaning process after the mixing of spun silk, cashmere and A100 tencels；
(2) cotton cleaning process：480 revs/min of opener Beater Speed, single beater scutcher 950 revs/min of Beater Speed of synthesis,
11 revs/min of lap roller speed；
(3) carding step：380 revs/min of cylinder speed, 22 revs/min of doffer speed, 800 revs/min of licker-in speed；
(4) mixing in doubling step：Slubbing drafting：190 ms/min of speed, 1.35 times of first break draft；
Two road draftings：170 ms/min of speed, 1.32 times of first break draft；
Extreme trace drafting：150 ms/min of speed, 1.21 times of first break draft；
(4) Roving Frames：850 revs/min of rove ingot speed, 1.36 times of back area draft；
(5) spinning process：13500 revs/min of spun yarn spindle speed, 1.20 times of later stage drawing-off.
(6) ring technique：Average section length：10cm, mean pitch 22cm, section are thick：1.6 times, random ring.
Comparative example 1-4
Raw material：Spun silk 10kg, cashmere 10kg, A100 tencel 80kg；
Production technology：
(1) Feedstock treating：Thin,tough silk is uniformly sprayed at by spun silk and the weight of cashmere 10% using the 10% antistatic additive aqueous solution
On silk and cashmere, seal it is vexed to put feed intake after 24h use；Enter cotton cleaning process after the mixing of spun silk, cashmere and A100 tencels；
(2) cotton cleaning process is entered after the mixing of spun silk, cashmere and A100 tencels：480 revs/min of opener Beater Speed, it is single
Hired roughneck's lapper 950 revs/min of Beater Speed of synthesis, 11 revs/min of lap roller speed；
(3) carding step：330 revs/min of cylinder speed, 18 revs/min of doffer speed, 700 revs/min of licker-in speed；
(4) mixing in doubling step：Slubbing drafting：190 ms/min of speed, 1.35 times of first break draft；
Two road draftings：170 ms/min of speed, 1.31 times of first break draft；
Extreme trace drafting：150 ms/min of speed, 1.21 times of first break draft；
(4) Roving Frames：750 revs/min of rove ingot speed, 1.26 times of back area draft；
(5) spinning process：15500 revs/min of spun yarn spindle speed, 1.26 times of later stage drawing-off.
(6) ring technique：Average section length：10cm, mean pitch 22cm, section are thick：1.8 times, random ring.
Embodiment 2
Raw material：Spun silk 15kg, cashmere 15kg, A100 tencel 70kg；Technique according to embodiment 1.1 carries out blended bamboo node
Fancy yarn.
Embodiment 3
Raw material：Spun silk 5kg, cashmere 5kg, A100 tencel 90kg；Technique according to embodiment 1.1 carries out blended bamboo node flower
Formula yarn.
Quality testing is carried out to the blended bamboo node fancy yarn that above-described embodiment, comparative example are obtained：
The project of predominantly detecting includes：Single thread ultimate strength；Single thread force CV；Unevenness CV；Km details (- 50%) number；
Km slubbing (+50%) number；Km cotton knot (+200%) number.
Detection method and concrete operations：1st, each scheme of single thread force samples 20 cops, and each cop tests 3 sections strong
Power, adds up each scheme and tests 60 sections of strengths, asks its average value and the coefficient of variation, and strength machine uses domestic strength machine.2nd, bar is done
The test of CV%, thickness section and cotton knot is to sample 10 cops according to each scheme, and evenness meter uses domestic Chang Ling instrument.
Testing result is as shown in table 1；
Table 1
Blending is carried out to spun silk, cashmere, A100 tencels using the blended weave closest with the present invention and there is resultant yarn
Index and production efficiency more or less have too late this technique.And the parameter only to a certain operation of existing process is adjusted,
Preferable effect cannot equally be obtained.Only use blended weave of the invention, cooperation and ring wind by each operation parameter
The design of lattice, can be only achieved the product style of preferably yarn quality and uniqueness, meets that client is increasingly stricter, specializes
Use requirement.
Embodiment described above is a kind of preferably scheme of the invention, not makees any formal to the present invention
Limitation, also has other variants and remodeling on the premise of without departing from the technical scheme described in claim.
Claims (9)
1. a kind of bamboo section pattern yarn, it is characterised in that by spun silk, cashmere, A100 is tencel blended forms, by weight percentage
Meter, each raw material components proportioning is as follows：Spun silk 5~20%, cashmere 5~15%, A100 tencels 65~90%.
2. a kind of bamboo section pattern yarn according to claim 1, it is characterised in that by weight percentage, each raw material components
Proportioning is as follows：Spun silk 10%, cashmere 10%, A100 tencels 80%.
3. a kind of bamboo section pattern yarn according to claim 1 and 2, it is characterised in that ring is irregular at random.
4. a kind of preparation method of bamboo section pattern yarn as claimed in claim 1, it is characterised in that comprise the following steps：
(1) Feedstock treating：The antistatic additive aqueous solution is uniformly sprayed on spun silk and cashmere respectively, sealing is vexed to put 12~48h
After use；Enter cotton cleaning process after the mixing of spun silk, cashmere and A100 tencels；
(2) cotton cleaning process：450~500 revs/min of opener Beater Speed, 900~1000 turns of single beater scutcher Beater Speed/
Point, lap roller speed：10~12 revs/min；
(3) carding step：300~360 revs/min of cylinder speed, 16~22 revs/min of doffer speed, licker-in speed：550~750
Rev/min；
(4) mixing in doubling step：Slubbing drafting：170~200 ms/min of speed, 1.25~1.40 times of first break draft；
Two road draftings：160~190 ms/min of speed, 1.20~1.35 times of first break draft；
Extreme trace drafting：150~180 ms/min of speed, 1.20~1.30 times of first break draft；
(5) Roving Frames：700~800 revs/min of rove ingot speed, back area draft：1.2~1.35；
(6) spinning process：13500~15000 revs/min of spun yarn spindle speed, back area draft：1.15~1.35.
(7) ring operation：Average section 9~25cm long, mean pitch：6~70cm, saves thick 1.6~2.2 times, random ring.
5. preparation method according to claim 4, it is characterised in that cotton cleaning process：480 revs/min of opener Beater Speed,
Single beater scutcher 950 revs/min of Beater Speed of synthesis, 11 revs/min of lap roller speed；Carding step：330 turns of cylinder speed/
Point, 18 revs/min of doffer speed, 700 revs/min of licker-in speed.
6. preparation method according to claim 4, it is characterised in that mixing in doubling step：
Slubbing drafting：190 ms/min of speed, 1.35 times of first break draft；
Two road draftings：170 ms/min of speed, 1.30 times of first break draft；
Extreme trace drafting：150 ms/min of speed, 1.25 times of first break draft.
7. preparation method according to claim 4, it is characterised in that Roving Frames：750 revs/min of rove ingot speed, back zone is led
Stretch 1.26 times；Spinning process：13500 revs/min of spun yarn spindle speed, 1.20 times of first break draft.
8. preparation method according to claim 4, it is characterised in that ring operation：Average section length：16cm, mean pitch
33cm, section is thick：2.2 times, random ring.
9. preparation method according to claim 4, it is characterised in that the quality of the antistatic additive aqueous solution is dense in step (1)
It is 5~15% to spend, and the consumption of the antistatic additive aqueous solution is respectively the 5~15% of spun silk weight, the 5~15% of cashmere weight.