CN106904832A - A kind of high quality glass and its production technology - Google Patents
A kind of high quality glass and its production technology Download PDFInfo
- Publication number
- CN106904832A CN106904832A CN201710178716.4A CN201710178716A CN106904832A CN 106904832 A CN106904832 A CN 106904832A CN 201710178716 A CN201710178716 A CN 201710178716A CN 106904832 A CN106904832 A CN 106904832A
- Authority
- CN
- China
- Prior art keywords
- raw material
- high quality
- glass
- parts
- batch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of high quality glass and its production technology, is related to field of glass production technology, and glass is made up of the raw material of following weight portion：60 75 parts of quartz sand, 14 18 parts of soda ash, 5 10 parts of saltcake, 48 parts of lime stone, 48 parts of cured stone, 28 parts of dolomite, 0.4 0.8 parts of sulfate type fining agent, process of glass is comprised the following steps：(1) raw material preprocessing, the preparation of (2) batch, (3) melt, (4) shaping, (5) annealing.The present invention have the advantages that setting efficient pulverizing and dried process link, composition of raw materials and technique can be adjusted and controlled, low cost.
Description
Technical field
The invention belongs to field of glass production technology, and in particular to a kind of high quality glass and its production technology.
Background technology
The crystalistic sense of glass is good, pollution-free, fashion is strong, moulding is enriched, be widely used, with low cost.The mould of glass
Compact dimensions are accurate, can manufacture light and thin type product, and various colors are changeable, technique is exquisite.
A kind of porcelain white glass of Chinese patent literature and its production technology (Authorization Notice No. of the bulletin of on January 20th, 2016
CN103482870B), the production technology comprises the following steps：(1) prepared by batch；(2) melt：Batch and cullet are thrown
Enter furnace；(3) it is molded：Processing and forming is carried out using glass shaping equipment；(4) anneal：Annealed using annealing kiln.The porcelain
White glass formula is made up of raw material as follows by weight percentage：60-90% batches, 10-40% cullet；The cooperation
Material includes the component of following ratio meter by weight：50-60 parts of quartz sand, 13.5-16 parts of soda ash, 10-12 parts of hydrogen-oxygen
Change aluminium, 9-11 parts of prodan, 5-7 parts of fluorite, 0-1.5 parts of barium sulfate, 0.5-2 parts of sodium nitrate, 0-3 parts of side's solution
Stone, 0.3-0.7 parts of compound clarifier.The invention is by composition of raw materials, the intense adjustment of technological parameter and control, being had
There is the porcelain white glass of ceramic whiteware device appearance high.
But the frit in the invention is much in block and humidity, it is necessary to crush and dried process, not so raw material
Mixing is uneven, and the glass quality for manufacturing is poor.
The content of the invention
In order to solve existing glass and its production technology exist lack crushing and dried process link, to composition of raw materials and
Technique can not be adjusted and controlled, the problem of high cost, it is an object of the invention to provide a kind of high quality glass and its production work
Skill, with setting efficient pulverizing and dried process link, composition of raw materials and technological parameter can accurately be adjusted and controlled, cost
Low advantage.
The invention provides following technical scheme：
A kind of high quality glass, it is made up of the raw material of following weight portion：
Preferably, it is made up of the raw material of following weight portion：
Have the advantages that composition of raw materials can be adjusted and control, low cost.
Preferably, it is made up of the raw material of following weight portion：
With composition of raw materials can be adjusted and control, low cost, make the good advantage of glass quality.
Preferably, the sulfate type fining agent is sodium sulphate, barium sulfate or calcium sulfate, and sulfate type fining agent belongs to high
Warm fining agent, decomposition temperature is higher, there is good clarifying effect.
Preferably, the sulfate type fining agent is sodium sulphate, can effectively facilitate the gas discharge in glass melt.
A kind of production technology of high quality glass, comprises the following steps：
(1) raw material preprocessing：Block stock is crushed using Portable high speed pulverizer, moist raw material is dried；
(2) prepared by batch：Raw material is made batch according to the material rate input batch mixer of the weight portion of glass；
(3) melt：Batch is put into pot furnace and is melted；
(4) it is molded：Processing and forming is carried out to the batch of fusing in step (3) using glass shaping equipment；
(5) anneal：Made annealing treatment using annealing device, obtained glassware.
Preferably, moist raw material is dried using drying machine in the step (1), drying effect is good, efficiency high.
Preferably, the drying machine is vacuum drier, with temperature control it is accurate reliable, the heat time is short, drying effect is good,
The advantage of stable performance.
The beneficial effects of the invention are as follows：
1st, glass of the invention is made up of following parts by weight raw material：Quartz sand 60-75 parts, soda ash 14-18 parts, saltcake 5-
10 parts, lime stone 4-8 parts, cured stone 4-8 parts, dolomite 2-8 parts, 0.4-0.8 parts of sulfate type fining agent, can to composition of raw materials
Adjustment and control；The production technology of high quality glass, comprises the following steps：(1) raw material preprocessing, the preparation of (2) batch, (3)
Melt, (4) shaping, (5) annealing, technique can accurately adjust and control, by setting (1) raw material preprocessing, reach crushing and
The effect of dried process so that raw material is well mixed, and the glass quality for manufacturing is high.
2nd, heretofore described compound clarifier be the sulfate type fining agent be sodium sulphate, barium sulfate or calcium sulfate,
Sulfate type fining agent belongs to high temperature fining agent, and decomposition temperature is higher, there is good clarifying effect.
3rd, heretofore described sulfate type fining agent is sodium sulphate, can effectively facilitate the gas row in glass melt
Go out.
4th, moist raw material is dried using drying machine in heretofore described step (1), drying effect is good, efficiency
It is high.
5th, heretofore described drying machine is vacuum drier, with temperature control it is accurate reliable, the heat time is short, drying effect
The good, advantage of stable performance.
Specific embodiment
Embodiment 1
A kind of high quality glass, it is made up of the raw material of following weight portion：
Sulfate type fining agent belongs to high temperature fining agent for sodium sulphate, and decomposition temperature is higher, there is good clarifying effect,
The gas discharge in glass melt can be effectively facilitated.
A kind of production technology of high quality glass, comprises the following steps：
(1) raw material preprocessing：Block stock is crushed using Portable high speed pulverizer, moist raw material is dried；
(2) prepared by batch：Raw material is made batch according to the material rate input batch mixer of the weight portion of glass；
(3) melt：Batch is put into pot furnace and is melted；
(4) it is molded：Processing and forming is carried out to the batch of fusing in step (3) using glass shaping equipment；
(5) anneal：Made annealing treatment using annealing device, obtained glassware.
Moist raw material is dried using drying machine in step (1), drying effect is good, efficiency high.
Drying machine is vacuum drier, with temperature control it is accurate reliable, the heat time is short, drying effect is good, stable performance
Advantage.
With composition of raw materials and technique can be adjusted and control, low cost, make the good advantage of glass quality.
Embodiment 2
A kind of high quality glass, it is made up of the raw material of following weight portion：
Sulfate type fining agent belongs to high temperature fining agent for sodium sulphate, and decomposition temperature is higher, there is good clarifying effect,
The gas discharge in glass melt can be effectively facilitated.
A kind of production technology of high quality glass, comprises the following steps：
(1) raw material preprocessing：Block stock is crushed using Portable high speed pulverizer, moist raw material is dried；
(2) prepared by batch：Raw material is made batch according to the material rate input batch mixer of the weight portion of glass；
(3) melt：Batch is put into pot furnace and is melted；
(4) it is molded：Processing and forming is carried out to the batch of fusing in step (3) using glass shaping equipment；
(5) anneal：Made annealing treatment using annealing device, obtained glassware.
Moist raw material is dried using drying machine in step (1), drying effect is good, efficiency high.
Drying machine is vacuum drier, with temperature control it is accurate reliable, the heat time is short, drying effect is good, stable performance
Advantage.
With composition of raw materials and technique can be adjusted and control, low cost, make the good advantage of glass quality.
Embodiment 3
A kind of high quality glass, it is made up of the raw material of following weight portion：
Sulfate type fining agent belongs to high temperature fining agent for sodium sulphate, and decomposition temperature is higher, there is good clarifying effect,
The gas discharge in glass melt can be effectively facilitated.
A kind of production technology of high quality glass, comprises the following steps：
(1) raw material preprocessing：Block stock is crushed using Portable high speed pulverizer, moist raw material is dried；
(2) prepared by batch：Raw material is made batch according to the material rate input batch mixer of the weight portion of glass；
(3) melt：Batch is put into pot furnace and is melted；
(4) it is molded：Processing and forming is carried out to the batch of fusing in step (3) using glass shaping equipment；
(5) anneal：Made annealing treatment using annealing device, obtained glassware.
Moist raw material is dried using drying machine in step (1), drying effect is good, efficiency high.
Drying machine is vacuum drier, with temperature control it is accurate reliable, the heat time is short, drying effect is good, stable performance
Advantage.
With composition of raw materials and technique can be adjusted and control, low cost, make the good advantage of glass quality.
The preferred embodiments of the present invention are the foregoing is only, is not intended to limit the invention, although with reference to foregoing reality
Apply example to be described in detail the present invention, for a person skilled in the art, it still can be to foregoing each implementation
Technical scheme described in example is modified, or equivalent is carried out to which part technical characteristic, all in essence of the invention
Within god and principle, any modification, equivalent substitution and improvements made etc. should be included within the scope of the present invention.
Claims (8)
1. a kind of high quality glass, it is characterised in that it is made up of the raw material of following weight portion：
2. high quality glass according to claim 1, it is characterised in that it is made up of the raw material of following weight portion：
3. high quality glass according to claim 2, it is characterised in that it is made up of the raw material of following weight portion：
4. high quality glass according to claim 1, it is characterised in that：The sulfate type fining agent is sodium sulphate, sulphur
Sour barium or calcium sulfate.
5. high quality glass according to claim 1, it is characterised in that：The sulfate type fining agent is sodium sulphate.
6. a kind of production technology of high quality glass as claimed in claim 1, it is characterised in that comprise the following steps：
(1) raw material preprocessing：Block stock is crushed using Portable high speed pulverizer, moist raw material is dried；
(2) prepared by batch：Raw material is made batch according to the material rate input batch mixer of the weight portion of glass；
(3) melt：Batch is put into pot furnace and is melted；
(4) it is molded：Processing and forming is carried out to the batch of fusing in step (3) using glass shaping equipment；
(5) anneal：Made annealing treatment using annealing device, obtained glassware.
7. the production technology of high quality glass according to claim 6, it is characterised in that：Using dry in the step (1)
Dry machine is dried to moist raw material.
8. the production technology of high quality glass according to claim 7, it is characterised in that：The drying machine is vacuum drying
Machine.