CN107162418A - A kind of glass and its production technology - Google Patents
A kind of glass and its production technology Download PDFInfo
- Publication number
- CN107162418A CN107162418A CN201710514854.5A CN201710514854A CN107162418A CN 107162418 A CN107162418 A CN 107162418A CN 201710514854 A CN201710514854 A CN 201710514854A CN 107162418 A CN107162418 A CN 107162418A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- glass
- production technology
- batch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of glass and its production technology, is related to decorative materials technology, glass includes the raw material of following parts by weight:0.4 0.6 parts of 60 70 parts of silica sand, 30 50 parts of sandstone, 14 18 parts of soda ash, 59 parts of anorthite, 68 parts of albite, 79 parts of kaolin, 46 parts of lime stone, 24 parts of dolomite and compound clarifier;Production technology comprises the following steps:(1) raw material, (2) raw material preprocessing, the preparation of (3) batch, (4) melt, (5) shaping, (6) annealing are weighed.The present invention solves the problem of existing glass generally existing poor soundproof effect, effect of heat insulation difference and low intensity.
Description
Technical field
The invention belongs to decorative materials technology, and in particular to a kind of glass and its production technology.
Background technology
The crystalistic sense of glass is good, pollution-free, fashion is strong, moulding is enriched, be widely used, with low cost.The mould of glass
Compact dimensions are accurate, can manufacture light and thin type product, and various colors are changeable, technique is exquisite.
But existing glass generally existing poor soundproof effect, effect of heat insulation difference and low intensity.
The content of the invention
In order to solve the problem of existing glass generally existing poor soundproof effect, effect of heat insulation difference and low intensity, this hair
Bright purpose is to provide a kind of glass and its production technology, has the advantages that good soundproof effect, good heat-insulation effect and intensity are high.
The invention provides following technical scheme:
A kind of glass, includes the raw material of following parts by weight:60-70 parts of silica sand, 30-50 parts of sandstone, 14-18 parts of soda ash, calcium
5-9 parts of feldspar, 6-8 parts of albite, 7-9 parts of kaolin, 4-6 parts of lime stone, 2-4 parts of dolomite and compound clarifier 0.4-0.6
Part.
Preferably, the raw material of following parts by weight is included:65 parts of silica sand, 40 parts of sandstone, 16 parts of soda ash, 7 parts of anorthite, sodium are long
0.5 part of 7 parts of stone, 8 parts of kaolin, 5 parts of lime stone, 3 parts of dolomite and compound clarifier.
Preferably, the compound clarifier is without arsenic compound clarifier.
A kind of production technology of glass, comprises the following steps:
(1) raw material is weighed:Raw material is weighed according to the parts by weight of frit;
(2) raw material preprocessing:Block stock is crushed, moist raw material is dried;
(3) prepared by batch:Batch is made in raw material input high-speed mixer;
(4) melt:Batch is put into kiln and melted, fusion temperature is controlled at 1560-1590 DEG C, is produced molten
Material;
(5) it is molded:Processing and forming is carried out to melting charge using glass shaping equipment;
(6) anneal:Made annealing treatment using annealing device, obtain glassware.
Preferably, block stock is ground into 400-500 mesh powders using pulverizer in the step (2).
Preferably, the pulverizer is Portable high speed pulverizer.
Preferably, moist raw material is dried using drying machine in the step (2).
Preferably, the drying machine is vertical drier.
The beneficial effects of the invention are as follows:
1st, the present invention solves existing glass generally existing and asking for poor soundproof effect, effect of heat insulation difference and low intensity
Topic.
2nd, heretofore described compound clarifier is that no arsenic compound clarifier is new generation of green ring without arsenic compound clarifier
Guarantor's type glass fining agent, with green, environmentally friendly, safe and efficient advantage.
3rd, block stock is ground into 400-500 mesh powders, pulverizer using pulverizer in heretofore described step (2)
Crushing effect relative to other crushing measures will get well, and have the advantages that efficiency high, cost are low;Block stock is ground into 300-
500 mesh powders, can preferably make to be well mixed between raw material so that the quality better of the glass manufactured.
4th, heretofore described pulverizer be Portable high speed pulverizer, Portable high speed pulverizer have it is simple in construction,
Light weight, effect be high, without dust, easy to operate, noise is low, performance is stable, fineness can accurately reconcile the advantage of energy-conservation.
5th, moist raw material is dried using drying machine in heretofore described step (2), drying efficiency height and raw material
Dry is uniform.
6th, heretofore described drying machine is vertical drier, and vertical drier has simple to operate, easy to maintenance, mitigation
Labor intensity, the advantage for saving manpower and efficiency high.
Embodiment
Embodiment 1
A kind of glass, includes the raw material of following parts by weight:65 parts of silica sand, 40 parts of sandstone, 16 parts of soda ash, 7 parts of anorthite, sodium
0.5 part of 7 parts of feldspar, 8 parts of kaolin, 5 parts of lime stone, 3 parts of dolomite and compound clarifier.
Compound clarifier is without arsenic compound clarifier.
A kind of production technology of glass, comprises the following steps:
(1) raw material is weighed:Raw material is weighed according to the parts by weight of frit;
(2) raw material preprocessing:Block stock is crushed, moist raw material is dried;
(3) prepared by batch:Batch is made in raw material input high-speed mixer;
(4) melt:Batch is put into kiln and melted, fusion temperature is controlled at 1560-1590 DEG C, is produced molten
Material;
(5) it is molded:Processing and forming is carried out to melting charge using glass shaping equipment;
(6) anneal:Made annealing treatment using annealing device, obtain glassware.
Block stock is ground into 400-500 mesh powders using pulverizer in step (2).
Pulverizer is Portable high speed pulverizer.
Moist raw material is dried using drying machine in step (2).
Drying machine is vertical drier.
Embodiment 2
A kind of glass, includes the raw material of following parts by weight:60 parts of silica sand, 30 parts of sandstone, 14 parts of soda ash, 5 parts of anorthite, sodium
0.4 part of 6 parts of feldspar, 7 parts of kaolin, 4 parts of lime stone, 2 parts of dolomite and compound clarifier.
Compound clarifier is without arsenic compound clarifier.
A kind of production technology of glass, comprises the following steps:
(1) raw material is weighed:Raw material is weighed according to the parts by weight of frit;
(2) raw material preprocessing:Block stock is crushed, moist raw material is dried;
(3) prepared by batch:Batch is made in raw material input high-speed mixer;
(4) melt:Batch is put into kiln and melted, fusion temperature is controlled at 1560-1590 DEG C, is produced molten
Material;
(5) it is molded:Processing and forming is carried out to melting charge using glass shaping equipment;
(6) anneal:Made annealing treatment using annealing device, obtain glassware.
Block stock is ground into 400-500 mesh powders using pulverizer in step (2).
Pulverizer is Portable high speed pulverizer.
Moist raw material is dried using drying machine in step (2).
Drying machine is vertical drier.
Embodiment 3
A kind of glass, includes the raw material of following parts by weight:70 parts of silica sand, 50 parts of sandstone, 18 parts of soda ash, 9 parts of anorthite, sodium
0.6 part of 8 parts of feldspar, 9 parts of kaolin, 6 parts of lime stone, 4 parts of dolomite and compound clarifier.
Compound clarifier is without arsenic compound clarifier.
A kind of production technology of glass, comprises the following steps:
(1) raw material is weighed:Raw material is weighed according to the parts by weight of frit;
(2) raw material preprocessing:Block stock is crushed, moist raw material is dried;
(3) prepared by batch:Batch is made in raw material input high-speed mixer;
(4) melt:Batch is put into kiln and melted, fusion temperature is controlled at 1560-1590 DEG C, is produced molten
Material;
(5) it is molded:Processing and forming is carried out to melting charge using glass shaping equipment;
(6) anneal:Made annealing treatment using annealing device, obtain glassware.
Block stock is ground into 400-500 mesh powders using pulverizer in step (2).
Pulverizer is Portable high speed pulverizer.
Moist raw material is dried using drying machine in step (2).
Drying machine is vertical drier.
Existing glass in glass and comparative example 1 is made in embodiment 1, embodiment 2 and embodiment 3 and carries out performance test, is obtained
To following test result, as shown in table 1:
Index | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 |
Compression strength (Mpa) | 721 | 696 | 636 | 520 |
Thermal conductivity factor (w/m ﹒ k) | 0.023 | 0.030 | 0.036 | 0.067 |
Acoustical ratings | One-level | One-level | One-level | Two grades |
From the data of table 1 compare as can be seen that it is an advantage of the invention that:
1st, a kind of glass and its production technology, from the compression strength measured as can be seen that embodiment 1-3 compression strength is equal
Higher than comparative example 1, illustrate that the compression strength of glass of the present invention is high.
2nd, a kind of glass and its production technology, from the thermal conductivity factor measured as can be seen that embodiment 1-3 thermal conductivity factor is equal
Less than comparative example 1, illustrate the heat-insulated good of glass of the present invention.
3rd, a kind of glass and its production technology, can be with from the acoustical ratings measured according to Code for sound insulation design of civil buildings
Find out, embodiment 1-3 acoustical ratings are superior to comparative example 1, illustrate that the sound insulation value of glass of the present invention is good.
4th, a kind of glass and its production technology, from the data of each index measured as can be seen that embodiment 1 is superior to reality
Example 2, embodiment 3 and comparative example 1 are applied, illustrates the composition of raw materials of glass of the present invention and the reasonability of production technology.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality
Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation
Technical scheme described in example is modified, or equivalent substitution, all essences in the present invention are carried out to which part technical characteristic
God is with principle, and any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (8)
1. a kind of glass, it is characterised in that include the raw material of following parts by weight:60-70 parts of silica sand, 30-50 parts of sandstone, soda ash
14-18 parts, 5-9 parts of anorthite, 6-8 parts of albite, 7-9 parts of kaolin, 4-6 parts of lime stone, 2-4 parts of dolomite and composite clarification
0.4-0.6 parts of agent.
2. glass according to claim 1, it is characterised in that include the raw material of following parts by weight:65 parts of silica sand, sandstone 40
Part, 16 parts of soda ash, 7 parts of anorthite, 7 parts of albite, 8 parts of kaolin, 5 parts of lime stone, 3 parts of dolomite and compound clarifier 0.5
Part.
3. glass according to claim 1, it is characterised in that:The compound clarifier is without arsenic compound clarifier.
4. the production technology of a kind of glass as described in claim 1-3 any one, it is characterised in that comprise the following steps:
(1) raw material is weighed:Raw material is weighed according to the parts by weight of frit;
(2) raw material preprocessing:Block stock is crushed, moist raw material is dried;
(3) prepared by batch:Batch is made in raw material input high-speed mixer;
(4) melt:Batch is put into kiln and melted, fusion temperature is controlled at 1560-1590 DEG C, produces fusing
Material;
(5) it is molded:Processing and forming is carried out to melting charge using glass shaping equipment;
(6) anneal:Made annealing treatment using annealing device, obtain glassware.
5. the production technology of glass according to claim 4, it is characterised in that:Block stock is used in the step (2)
Pulverizer is ground into 400-500 mesh powders.
6. the production technology of glass according to claim 5, it is characterised in that:The pulverizer is crushed for Portable high speed
Machine.
7. the production technology of glass according to claim 4, it is characterised in that:Drying machine pair is used in the step (2)
Moist raw material is dried.
8. the production technology of glass according to claim 7, it is characterised in that:The drying machine is vertical drier.