CN106893409A - A kind of biological environmental production pigment for artistic design - Google Patents
A kind of biological environmental production pigment for artistic design Download PDFInfo
- Publication number
- CN106893409A CN106893409A CN201710187075.9A CN201710187075A CN106893409A CN 106893409 A CN106893409 A CN 106893409A CN 201710187075 A CN201710187075 A CN 201710187075A CN 106893409 A CN106893409 A CN 106893409A
- Authority
- CN
- China
- Prior art keywords
- parts
- pigment
- powder
- alar
- biological environmental
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of biological environmental production pigment for artistic design, it is made up of the following raw material according to weight portion：5 12 parts of Tissuemat E, 23 31 parts of glycerine, 37 parts of dioctyl phthalate, 51 59 parts of pigment, 11 19 parts of smoke sheet rubber, 15 parts of alar-85,8 16 parts of titanium dioxide, 80 90 parts of distilled water.Polyethylene wax powder and titanium oxide powder are inserted in glycerin solution and is stirred, add the stirring of smoked sheet rubber powder, alar-85 powder is added to be stirred with pigment, then dioctyl phthalate is being added dropwise, it is then sonicated 24 26min, slurry is obtained, slurry is ground to fineness biological environmental production pigment is obtained final product more than 1000 mesh.Biological environmental production pigment prepared by the present invention meets that illumination is difficult for drop-off and discoloration, resistance to steam and wet environment, without harmful substance, human contact is not injured, environment friendly and pollution-free.Raw material that the present invention is used is simple, be easy to get, and low cost, preparation process is simple, storage stability reaches more than 3 years, reaches international standards, and is suitable to industrialized production.
Description
Technical field
The present invention relates to painting supply technical field, specifically a kind of biological environmental production pigment for artistic design.
Background technology
Pigment is divided into two kinds of inorganic pigment and organic pigment, and organic pigment extracts pigment from plant and is made, without to people
Body harmful element, belongs to environmental-friendly pigment.And inorganic pigment extracts pigment from mineral matter, more containing chemical element, such as selenium, cadmium, chromium
Deng element, human body is sucked for a long time, or works long hours in such a case, and the element such as selenium, cadmium is easily by respiratory tract or skin
Enter blood of human body etc. approach, cause people's mechanism body to lack or MSOF.Why claim inorganic pigment poisonous, be not real
Poisonous in meaning, inorganic pigment part can influence human normal function containing selenium, cadmium, chromium pigment, cause MSOF.
So people's custom is referred to as " poisonous ".With expanding economy, growth in the living standard, the environmental consciousness of people gradually strengthens,
Requirement more and more higher to coating, does not require nothing more than that its product is attractive in appearance, performance is good, also requires that its pollution is small.Water-base pigment is a kind of
Novel environment friendly pigment, compares with conventional pigment, it have it is nontoxic, odorlessness, environmental protection the advantages of.But existing water-base pigment is applied
Crow shines easy to fall off long in the presence of chance illumination mostly after paper, intolerant to steam and humidity etc., contains harmful substance not enough environmental protection etc.
Defect.
The content of the invention
Illumination difficult for drop-off and discoloration, resistance to steam and wet environment, environmentally friendly nothing are met it is an object of the invention to provide one kind
The biological environmental production pigment for artistic design of pollution, to solve the problems, such as to be proposed in above-mentioned background technology.
To achieve the above object, the present invention provides following technical scheme：
A kind of biological environmental production pigment for artistic design, is made up of the following raw material according to weight portion：Tissuemat E 5-
12 parts, glycerine 23-31 parts, dioctyl phthalate 3-7 parts, pigment 51-59 parts, smoke sheet rubber 11-19 parts, alar-85 1-5 parts,
Titanium dioxide 8-16 parts, distilled water 80-90 parts.
As further scheme of the invention：The biological environmental production pigment for artistic design, by following according to weight
The raw material composition of part：Tissuemat E 7-10 parts, glycerine 25-29 parts, dioctyl phthalate 4-6 parts, pigment 53-57 parts,
Smoke sheet rubber 13-17 parts, alar-85 2-4 parts, titanium dioxide 10-14 parts, distilled water 82-88 parts.
As further scheme of the invention：The biological environmental production pigment for artistic design, by following according to weight
The raw material composition of part：8 parts of Tissuemat E, 27 parts of glycerine, 5 parts of dioctyl phthalate, pigment yellow 155 part, 15 parts of smoke sheet rubber,
3 parts of alar-85,12 parts of titanium dioxide, 85 parts of distilled water.
As further scheme of the invention：The biological environmental production pigment for artistic design, using following steps system
：
1) by Tissuemat E ultramicro grinding, 10-25 μm of polyethylene wax powder is obtained；By smoke sheet rubber, alar-85, titanium dioxide difference
200 mesh sieves were crushed, smoked sheet rubber powder, alar-85 powder, titanium oxide powder was obtained；Glycerine is mixed with distilled water, glycerine is obtained molten
Liquid；
2) polyethylene wax powder and titanium oxide powder are inserted in glycerin solution, after stirring 10-15min, is warming up to 58 DEG C, and
Add smoked sheet rubber powder while stirring at such a temperature, mixing speed is 60-100r/min, smoked sheet rubber powder is added in 1min follow-up continuous
Stirring 20-25min, then heats to 65 DEG C, and adds alar-85 powder and pigment while stirring at such a temperature, and mixing speed is
150-200r/min, 3-4min continue to stir 30min after adding alar-85 powder and pigment, then pungent in dropwise addition phthalic acid two
Ester, is then sonicated 24-26min, and slurry is obtained, and slurry is ground into fineness biological environmental production pigment is obtained final product more than 1000 mesh.
As further scheme of the invention：Smoked sheet rubber powder is added while stirring, and mixing speed is 80r/min.
As further scheme of the invention：Alar-85 powder and pigment are added while stirring, and mixing speed is 175r/min.
As further scheme of the invention：Ultrasonic power is 800W.
As further scheme of the invention：Sonication treatment time is 25min.
Compared with prior art, the beneficial effects of the invention are as follows：
The biological environmental production pigment that the present invention is prepared using raw materials such as Tissuemat E, smoke sheet rubber, alar-85, titanium dioxides, in each original
Make its chance illumination difficult for drop-off under the interaction of material and discoloration, resistance to steam and wet environment, without harmful substance, human body is connect
Touch without injury, green safety is environment friendly and pollution-free.The present invention with the addition of smoke sheet rubber, alar-85 and dioctyl phthalate, improve
The decentralization and adhesive force of pigment；And improve moisture resistance heat resistance with titanium dioxide by adding Tissuemat E.The present invention
The raw material of use is simple, be easy to get, and low cost, preparation process is simple, storage stability reaches more than 3 years, reaches international standards,
Energy-conserving and environment-protective, are suitable to industrialized production.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, a kind of biological environmental production pigment for artistic design is made up of following raw material：Tissuemat E
5g, glycerine 23g, dioctyl phthalate 3g, pigment 51g, smoke sheet rubber 11g, alar-85 1g, titanium dioxide 8g, distilled water 80g.
By Tissuemat E ultramicro grinding, 10-25 μm of polyethylene wax powder is obtained；By smoke sheet rubber, alar-85, titanium dioxide difference powder
The mesh sieve of broken mistake 200, is obtained smoked sheet rubber powder, alar-85 powder, titanium oxide powder；Glycerine is mixed with distilled water, glycerin solution is obtained.
Polyethylene wax powder and titanium oxide powder are inserted in glycerin solution, after stirring 10min, 58 DEG C, and side at such a temperature is warming up to
Stirring side adds smoked sheet rubber powder, and mixing speed is 60r/min, and smoked sheet rubber powder follow-up continuous stirring 20min, Ran Housheng are added in 1min
Temperature adds alar-85 powder and pigment while stirring at such a temperature to 65 DEG C, and mixing speed is 150r/min, and 3min adds alar-85
Continue to stir 30min after powder and pigment, dioctyl phthalate then is being added dropwise, be then sonicated 24min, ultrasonic power is
800W, is obtained slurry, slurry is ground into fineness biological environmental production pigment is obtained final product more than 1000 mesh.
Embodiment 2
In the embodiment of the present invention, a kind of biological environmental production pigment for artistic design is made up of following raw material：Tissuemat E
12g, glycerine 31g, dioctyl phthalate 7g, pigment 59g, smoke sheet rubber 19g, alar-85 5g, titanium dioxide 16g, distilled water
90g。
By Tissuemat E ultramicro grinding, 10-25 μm of polyethylene wax powder is obtained；By smoke sheet rubber, alar-85, titanium dioxide difference powder
The mesh sieve of broken mistake 200, is obtained smoked sheet rubber powder, alar-85 powder, titanium oxide powder；Glycerine is mixed with distilled water, glycerin solution is obtained.
Polyethylene wax powder and titanium oxide powder are inserted in glycerin solution, after stirring 15min, 58 DEG C, and side at such a temperature is warming up to
Stirring side adds smoked sheet rubber powder, and mixing speed is 100r/min, the follow-up continuous stirring 25min of smoked sheet rubber powder is added in 1min, then
65 DEG C are warming up to, and add alar-85 powder and pigment while stirring at such a temperature, mixing speed is 200r/min, and 4min adds ratio
Continue to stir 30min after long powder and pigment, dioctyl phthalate then is being added dropwise, be then sonicated 26min, ultrasonic power
It is 800W, slurry is obtained, slurry is ground to fineness biological environmental production pigment is obtained final product more than 1000 mesh.
Embodiment 3
In the embodiment of the present invention, a kind of biological environmental production pigment for artistic design is made up of following raw material：Tissuemat E
7g, glycerine 25g, dioctyl phthalate 4g, pigment 53g, smoke sheet rubber 13g, alar-85 2g, titanium dioxide 10g, distilled water 82g.
By Tissuemat E ultramicro grinding, 10-25 μm of polyethylene wax powder is obtained；By smoke sheet rubber, alar-85, titanium dioxide difference powder
The mesh sieve of broken mistake 200, is obtained smoked sheet rubber powder, alar-85 powder, titanium oxide powder；Glycerine is mixed with distilled water, glycerin solution is obtained.
Polyethylene wax powder and titanium oxide powder are inserted in glycerin solution, after stirring 12min, 58 DEG C, and side at such a temperature is warming up to
Stirring side adds smoked sheet rubber powder, and mixing speed is 80r/min, and smoked sheet rubber powder follow-up continuous stirring 22min, Ran Housheng are added in 1min
Temperature adds alar-85 powder and pigment while stirring at such a temperature to 65 DEG C, and mixing speed is 175r/min, and 3.5min adds ratio
Continue to stir 30min after long powder and pigment, dioctyl phthalate then is being added dropwise, be then sonicated 25min, ultrasonic power
It is 800W, slurry is obtained, slurry is ground to fineness biological environmental production pigment is obtained final product more than 1000 mesh.
Embodiment 4
In the embodiment of the present invention, a kind of biological environmental production pigment for artistic design is made up of following raw material：Tissuemat E
10g, glycerine 29g, dioctyl phthalate 6g, pigment 57g, smoke sheet rubber 17g, alar-85 4g, titanium dioxide 14g, distilled water
88g。
By Tissuemat E ultramicro grinding, 10-25 μm of polyethylene wax powder is obtained；By smoke sheet rubber, alar-85, titanium dioxide difference powder
The mesh sieve of broken mistake 200, is obtained smoked sheet rubber powder, alar-85 powder, titanium oxide powder；Glycerine is mixed with distilled water, glycerin solution is obtained.
Polyethylene wax powder and titanium oxide powder are inserted in glycerin solution, after stirring 12min, 58 DEG C, and side at such a temperature is warming up to
Stirring side adds smoked sheet rubber powder, and mixing speed is 80r/min, and smoked sheet rubber powder follow-up continuous stirring 22min, Ran Housheng are added in 1min
Temperature adds alar-85 powder and pigment while stirring at such a temperature to 65 DEG C, and mixing speed is 175r/min, and 3.5min adds ratio
Continue to stir 30min after long powder and pigment, dioctyl phthalate then is being added dropwise, be then sonicated 25min, ultrasonic power
It is 800W, slurry is obtained, slurry is ground to fineness biological environmental production pigment is obtained final product more than 1000 mesh.
Embodiment 5
In the embodiment of the present invention, a kind of biological environmental production pigment for artistic design is made up of following raw material：Tissuemat E
8g, glycerine 27g, dioctyl phthalate 5g, pigment yellow 155 g, smoke sheet rubber 15g, alar-85 3g, titanium dioxide 12g, distilled water 85g.
By Tissuemat E ultramicro grinding, 10-25 μm of polyethylene wax powder is obtained；By smoke sheet rubber, alar-85, titanium dioxide difference powder
The mesh sieve of broken mistake 200, is obtained smoked sheet rubber powder, alar-85 powder, titanium oxide powder；Glycerine is mixed with distilled water, glycerin solution is obtained.
Polyethylene wax powder and titanium oxide powder are inserted in glycerin solution, after stirring 12min, 58 DEG C, and side at such a temperature is warming up to
Stirring side adds smoked sheet rubber powder, and mixing speed is 80r/min, and smoked sheet rubber powder follow-up continuous stirring 22min, Ran Housheng are added in 1min
Temperature adds alar-85 powder and pigment while stirring at such a temperature to 65 DEG C, and mixing speed is 175r/min, and 3.5min adds ratio
Continue to stir 30min after long powder and pigment, dioctyl phthalate then is being added dropwise, be then sonicated 25min, ultrasonic power
It is 800W, slurry is obtained, slurry is ground to fineness biological environmental production pigment is obtained final product more than 1000 mesh.
Embodiment 6
Biological environmental production pigment obtained in embodiment of the present invention 1-5 carries out following performance parameter detection.
Light resistance is tested：Q-SUN weatherabilities tester (model Xe-1-S), X-RITE color density instrument, measurement scribble paper
Color density change before and after Q-SUN irradiates 1000 hours.
Evaluation criterion：A：Less than 10%；B：10-30%；C：More than 30%.After testing：Prepared by embodiment of the present invention 1-5
Biological environmental production pigment is A grades.
Wet-hot aging performance is tested：Dried biological environmental production pigment is placed in hygrothermal environment (relative humidity 90% and temperature
In 60 DEG C of environment), its color change is detected, it is shown in Table 1：
Table 1
Meanwhile, have detected the drying time (GB/T1728) of the biological environmental production pigment of embodiment of the present invention 1-5 preparations；It is shown in Table
2。
Table 2
| Drying time | Surface drying (min) | Do solid work (h) |
| Embodiment 1 | 12 | 6.8 |
| Embodiment 2 | 11 | 6.5 |
| Embodiment 3 | 9.5 | 6.2 |
| Embodiment 4 | 9 | 6.0 |
| Embodiment 5 | 9 | 5.8 |
Additionally, pigment prepared by the present invention is also equipped with bactericidal function (with reference to the resistance to mould determination method GB1741-79 of coating
(89) national standard), can preserve steadily in the long term.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be in other specific forms realized.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires to be limited rather than described above, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each implementation method is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should
Specification an as entirety, the technical scheme in each embodiment can also be formed into those skilled in the art through appropriately combined
May be appreciated other embodiment.
Claims (8)
1. a kind of biological environmental production pigment for artistic design, it is characterised in that be made up of the following raw material according to weight portion：It is poly-
Ethylene waxes 5-12 parts, glycerine 23-31 parts, dioctyl phthalate 3-7 parts, pigment 51-59 parts, smoke sheet rubber 11-19 parts, ratio
1-5 parts, titanium dioxide 8-16 parts, distilled water 80-90 parts long.
2. the biological environmental production pigment for artistic design according to claim 1, it is characterised in that by following according to weight
The raw material composition of part：Tissuemat E 7-10 parts, glycerine 25-29 parts, dioctyl phthalate 4-6 parts, pigment 53-57 parts,
Smoke sheet rubber 13-17 parts, alar-85 2-4 parts, titanium dioxide 10-14 parts, distilled water 82-88 parts.
3. the biological environmental production pigment for artistic design according to claim 1, it is characterised in that by following according to weight
The raw material composition of part：8 parts of Tissuemat E, 27 parts of glycerine, 5 parts of dioctyl phthalate, pigment yellow 155 part, 15 parts of smoke sheet rubber,
3 parts of alar-85,12 parts of titanium dioxide, 85 parts of distilled water.
4. according to any described biological environmental production pigment for artistic design of claim 1-3, it is characterised in that using following
Step is obtained：
1) by Tissuemat E ultramicro grinding, 10-25 μm of polyethylene wax powder is obtained；Smoke sheet rubber, alar-85, titanium dioxide are crushed respectively
200 mesh sieves are crossed, smoked sheet rubber powder, alar-85 powder, titanium oxide powder is obtained；Glycerine is mixed with distilled water, glycerin solution is obtained；
2) polyethylene wax powder and titanium oxide powder are inserted in glycerin solution, after stirring 10-15min, is warming up to 58 DEG C, and at this
At a temperature of add smoked sheet rubber powder while stirring, mixing speed is 60-100r/min, and the follow-up continuous stirring of smoked sheet rubber powder is added in 1min
20-25min, then heats to 65 DEG C, and adds alar-85 powder and pigment while stirring at such a temperature, and mixing speed is 150-
200r/min, 3-4min continue to stir 30min after adding alar-85 powder and pigment, then in dropwise addition dioctyl phthalate, then
Ultrasonically treated 24-26min, is obtained slurry, slurry is ground into fineness biological environmental production pigment is obtained final product more than 1000 mesh.
5. the biological environmental production pigment for artistic design according to claim 4, it is characterised in that add cigarette while stirring
Piece rubber powder, mixing speed is 80r/min.
6. the biological environmental production pigment for artistic design according to claim 4, it is characterised in that add ratio while stirring
Long powder and pigment, mixing speed is 175r/min.
7. the biological environmental production pigment for artistic design according to claim 4, it is characterised in that ultrasonic power is
800W。
8. the biological environmental production pigment for artistic design according to claim 4, it is characterised in that sonication treatment time is
25min。