CN106883695A - 行道树涂料及其制备方法 - Google Patents
行道树涂料及其制备方法 Download PDFInfo
- Publication number
- CN106883695A CN106883695A CN201710091907.7A CN201710091907A CN106883695A CN 106883695 A CN106883695 A CN 106883695A CN 201710091907 A CN201710091907 A CN 201710091907A CN 106883695 A CN106883695 A CN 106883695A
- Authority
- CN
- China
- Prior art keywords
- component
- shade tree
- coating
- coating according
- tree coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种行道树涂料及其制备方法。所述行道树涂料主要包括拟除虫菊酯组分、反光组分、隔热组分、水性合成树脂乳液组分、涂料膜结构改善组分、光稳定组分等。采用拟驱虫菊酯、玻璃微珠、水性合成树脂乳液、硅藻土或高岭土、纳米氧化锌制备得到的行道树涂料不仅具有良好长久的驱虫效果，而且能够有效保温，减少树木受到寒冷的侵袭，同时能够有效反射光，行道树能够起到良好的交通引导作用，大大提高道路交通安全。
Description
技术领域
本申请属于水性涂料领域，具体涉及一种行道树涂料及其制备方法。
背景技术
目前的园林、果园、行道树、景观绿化等树木都需要进行涂料涂刷，对树木进行一定程度的保护。尤其是，行道树的保护、美化和道路指引作用，尤为突出。
行道树是指种在道路两旁及分车带，给车辆和行人遮荫并构成街景的树种。行道树已经与人们生活融为一体，成为一座城市的象征，是地域文化中不可或缺的一部分，但是行道树经常饱受低温冷冻害及其病虫害的侵袭。尤其在我国北方冬季，夜晚温度很低；到了白天，受到阳光的照射，气温升高，而树干呈深色，易於吸收热量，树干温度上升很快。这样冷热交替，使树干容易冻裂。尤其是大树，树干粗，颜色深，而且组织韧性比较差，更容易裂开，影响景观绿化的美观。
种植在公路两旁的行道树，尤其在没设路灯的区域，行道树有着道路指引的作用，尤其在夜间行车时，对行车道路的指引和交通安全有重要的作用，但是行道树树干与环境相容性好，色差小，道路指引作用不明显。
目前多采用生石灰水涂刷树干来保护树木，但其防虫效果差、容易脱落、有效时间短等，已不能满足现实使用要求。显然更不适合于行道树使用。
公开号为CN106085073A的发明专利申请公开了“一种园林绿化用环保涂料及其制备方法”，公开了一种利用异噻唑啉酮为有效成分的杀虫涂料。
公开号为CN1308863A的发明专利申请公开说明书公开了“一种昆虫驱虫剂组合物和含有该组合物的驱虫涂料组合物”，采用的昆虫驱虫剂成分包括拟除虫菊酯，其目的主要是解决了除虫菊酯等有效成分在环境中由于紫外线、热、风等自然环境的影响在短时间内丧失功能，利用光吸收剂消除环境紫外线的影响，利用光稳定剂消除空气中自由基的影响，进而提高拟除虫菊酯的环境稳定性。但是该涂料主要针对建筑物等环境驱虫使用，而且光吸收剂和稳定剂对组合物使用寿命的延长受其含量的限制，其环境稳定性并不理想，而且并不是针对树木保护之目的，不适合用于保护种植在道路旁的行道树。
公开号为CN1693378A的发明专利申请公开了“一种环保型杀虫涂料及其制备工艺”，公开了水性涂料和杀虫剂组成的环保型杀虫涂料，采用的杀虫剂为拟除虫菊酯。
但是，以上涂料或者功能单一，或者不适合于树木，或者不适合于寒冷天气使用，而且都无法实现涂覆于行道树上后的道路指引作用。
发明内容
目前，行道树树木驱虫效果不佳，且驱虫效果不持久，北方冬天寒冷侵袭树木，树木表皮损伤，影响城市市容美观度，公路两旁的行道树与环境颜色接近，起不到良好的交通标识作用，尤其在没设路灯的公路上，行道树对夜间行车安全性贡献不大。
为了解决至少一种现有问题，本申请主要提供如下所述的内容。
本发明的一方面，提供行道树涂料，该涂料包括驱虫剂组分、反光组分、隔热组分、水性合成树脂乳液组分、涂料膜结构改善组分和光稳定组分。在某些实施方案中，驱虫剂组分是拟除虫菊酯。优选地，拟除虫菊酯可以是选自胺菊酯、右旋胺菊酯、右旋苄呋菊酯、炔呋菊酯、丙炔菊酯、丙烯菊酯、右旋丙烯菊酯、右旋反式丙烯菊酯、氯菊酯、菊酯、顺式氯氰菊酯和高效顺反氯氰菊酯中的至少一种。优选地，拟驱虫菊酯以溶解在醇中的拟驱虫菊酯醇溶液的形式提供。
在某些实施方案中，拟驱虫聚酯是氯氰菊酯。
在某些实施方案中，反光组分是实心玻璃微珠。
在某些实施方案中，隔热组分是空心玻璃微珠。
在某些实施方案中，光稳定组分是纳米氧化锌。
在某些实施方案中，涂料膜结构改善组分是硅藻土和/高岭土。
在某些实施方案中，采用水性合成树脂乳液作为主要成膜物质。
本发明的另一方面，提供行道树涂料的制备方法，其包括：
(1)将拟除虫菊酯和醇溶液按比例加入反应罐，搅拌均匀，得到预制驱虫液，备用；
(2)将反光组分、隔热组分按比例加入装有水性合成树脂乳液的反应罐中，搅拌均匀，得到涂料预混液；
(3)在反应罐中依次缓慢加入去离子水、增稠剂、润湿分散剂、杀菌剂、pH调节剂、成膜助剂和消泡剂，混合，搅拌至均匀；
(4)在步骤(3)的反应罐中，依次缓慢加入颜填料、光稳定组分、硅藻土/煅烧高岭土，以搅拌至均匀；
(5)在步骤(4)的反应罐中，将预制驱虫液、涂料预混液依次缓慢加入，搅拌，加入增稠剂调整粘度，得到行道树涂料。
具体实施方式
通过解释以下本申请的优选实施方案，本发明的其他目的和优点将变得清楚。
应理解本发明中所述的术语仅仅是为描述特别的实施方式，并非用于限制本发明。另外，对于本发明中的数值范围，应理解为还具体公开了该范围的上限和下限之间的每个中间值。在任何陈述值或陈述范围内的中间值以及任何其他陈述值或在所述范围内的中间值之间的每个较小的范围也包括在本发明内。这些较小范围的上限和下限可独立地包括或排除在范围内。
另外，为了更好地说明本发明的内容，在下文的具体实施例中给出了众多的具体细节。本领域技术人员应当理解，没有某些具体细节，本发明同样可以实施。在另外一些实施例中，对于本领域技术人员熟知的方法、手段未作详细描述，以便于凸显本发明的主旨。
除非另有说明，否则本文使用的所有技术和科学术语具有本发明所属技术领域的常规技术人员通常理解的相同含义。
本发明中，术语“主要包括”是指所包括的物质占总量(例如，体积或重量)的至少约50％，例如75％、85％、95％或98％以上，或者包括的物质为起积极作用的或有效作用的成分。
本发明中，术语“水性涂料”也称作“水性组合物”，有时也简称为“本发明的涂料”，是指以水作为溶剂的组合物或涂料，包括但不限于水稀释性涂料和水分散涂料(或水分散性涂料)。
作为水稀释性涂料是指后乳化乳液为成膜物配制的涂料，在施工中可用水来稀释。其中后乳化液是指使溶剂型树脂溶在有机溶剂中，然后在乳化剂的帮助下靠强烈的机械搅拌使树脂分散在水中形成的乳液。
作为水分散涂料是指以合成树脂乳液为成膜物配制的涂料。乳液是指在乳化剂存在下，在机械搅拌的过程中，不饱和乙烯基单体在一定温度条件下聚合而成的小粒子团分散在水中组成的分散乳液。
本发明中，术语“水性合成树脂乳液”是指干燥时用于使涂料成膜的任何成分。树脂乳液可以将水性组合物中的其它成分(包括添加剂)粘合/粘结到一起，并在干燥后赋予膜特定的性质。本发明中的合成树脂包括但不限于烯类聚合物，例如丙烯酸酯类、醋酸乙烯酯类及二者共聚类、氯化聚丙烯、氯乙烯-醋酸乙烯共聚物、氯醚树脂、聚乙烯醇、苯乙烯-丙烯酸酯共聚物。合成树脂还包括有机硅氧烷和丙烯酸酯等缩聚而成的聚合物。本发明的合成树脂还包括上述树脂的改性树脂。
在某些实施方案中，使用醋酸乙烯-乙烯共聚物(EVA)作为成膜物质，其使涂层不至于过于致密，致使杀虫剂有效成分不能随水汽运动散发，同时涂层不会过于松散，导致杀虫剂有效成分过快衰减，达到长时间保持良好驱虫效果的作用。并且水性合成树脂乳液成膜后具有一定的弹性，能够弥补细小的裂纹。当作为行道树涂料应用于树干时，在外界环境作用下有所变形时并不能破坏涂层膜的整体完整性，增强涂料的观赏性。
本发明中优选使用的拟除虫菊酯，是一类能防治多种害虫的广谱杀虫剂，对昆虫具有强烈的触杀作用。其作用机理是扰乱昆虫神经的正常生理，使之由兴奋、痉挛到麻痹而死亡。拟除虫菊酯具有用量小、使用浓度低，故对人畜较安全，对环境的污染很小等优点。使用拟除虫菊酯能有效杀灭害虫，阻断土壤里过冬害虫通过树干爬到树上的通道，从而达到保护树木免受病虫害侵袭的目的。
本发明中，拟驱虫菊酯包括但不限于胺菊酯、右旋胺菊酯、右旋苄呋菊酯、炔呋菊酯、丙炔菊酯、丙烯菊酯、右旋丙烯菊酯、右旋反式丙烯菊酯、氯菊酯、氯氰菊酯、顺式氯氰菊酯和高效顺反氯氰菊酯。上述化合物可单独使用或组合使用其中的两种以上。
驱虫剂组分可以单独的成分提供，或以溶液的形式提供。例如拟驱虫菊酯可以溶解在乙醇中得到拟驱虫菊酯乙醇溶液的形式提供。
在某些实施方案中，驱虫菊酯溶液是氯氰菊酯与95％乙醇混合得到的乙醇溶液。
在某些实施方案中，拟除虫菊酯乙醇溶液通过下述方法制得：氯氰菊酯和95％乙醇按体积比1:1的比例混合均匀，即得到拟除虫菊酯乙醇溶液。
本发明中，术语“反光组分”是指单向照射的光照射到该组分后，能够将反射光线返回到照射方向的组分，一般该组分具有良好的光折射率，而且与水性涂料有良好的相容性，能够均匀分散在水性涂料成膜后的涂料膜中；所述反光组分包括但不限于实心玻璃微珠。
本发明中，术语“隔热组分”是指有效隔离热量传递的组分，通常该隔热组分的热传导系数低，能够与水性涂料有良好的相容性，均匀分散在水性涂料成膜后的涂料中。所述隔热组分包括但不限于空心玻璃微珠。
在某些实施方案中，玻璃微珠为直径在数微米至数毫米范围内的实心玻璃微珠和空心玻璃微珠混合物。玻璃微珠直径可以分布在40-125μm之间，可以选择直径分布在56-100μm之间的玻璃微珠，也可以选择直径在70-90μm之间，也可以选择直径在70-90μm之间。
在某些实施方案中，实心玻璃微珠的光折射率在1.40以上，可选光折射率在1.64以上，也可选光折射率在1.80以上。
玻璃微珠具有光学性能好、导热系数低等特点。本发明实施例涂料中使用实心和空心玻璃微珠球体的混合体，涂料成膜后，实心玻璃微珠和中空玻璃微珠混合均匀，在涂料膜中紧密排列，形成一个完整的隔离层，其中的空心玻璃微珠具有良好的隔热效果，还具有优异的隔音效果；实心玻璃微珠的透明度良好、折射率高，能定向反射照射的光源。本实施例涂料涂覆于行道树上后，白天有效反射阳光，夜间隔离热传递，减小树木昼夜温差，保护树木不被冻裂。同时，夜间能够反射汽车灯光，反光度高，定向反射性能优良，明显标示道路宽度位置，有效起到道路引导作用，提高夜间道路交通安全。
本发明中，术语“光稳定剂”是指能够增加涂料中特定功能组分的耐受太阳光稳定性的组分。所述光稳定剂分包括但不限于纳米氧化锌。
众所周知，太阳光是由不同波长的电磁波组合而成，其中紫外线是一种高能粒子，能引起物质变质、分解、失效、变色、老化等。紫外线根据其波长大小可分为：长波紫外线(UVA)(波长320～400nm)、中波紫外线(UVB)(波长280～320nm)和短波紫外线(UVC)(波长200～275nm)等。在某些实施方案中，纳米氧化锌粒径在1-100nm之间，平均粒径80nm，小于紫外线的半波长。纳米粒子可将作用于其上的紫外线向各个方向散射从而减少照射方向的紫外线强度，这种散射紫外线的规律符合光散射定律。纳米氧化锌对紫外线有优异的吸收和反射效应，具有很好的紫外线屏蔽作用。
另外本发明中的玻璃微珠，尤其是实心玻璃微珠，有很好的光学性能可以很好的反射紫外线与氧化锌起到协同作用，共同起到稳定剂的作用，从而使驱虫剂能稳定存在于本涂料中。
本发明中，术语“涂料膜结构改善组分”是指能够改善涂料膜微观结构的材料组分，包括但不限于多孔材料，其可渗透使得流体(例如，气体等)可通过孔或其它通道而移动通过。涂料膜结构改善组分的实例包括纤维素材料、石材、硅藻土、高岭土、陶瓷及其衍生物。纤维素材料是指包括纤维素作为结构组分的材料。纤维素材料的实例包括木材、纸、纺织物、绳、刨花板以及其它生物和合成材料。本发明可任意使用上述材料中的一种或多种。
在某些实施方案中，本发明的涂料膜结构改善组分为硅藻土和/或煅烧高岭土。硅藻土、煅烧高岭土等作为填充料配入涂层体系中，利用硅藻土、煅烧高岭土疏松多孔、吸水率高的特性，增强涂层内部与表面的水汽交换和迁移，提高杀虫剂有效成分从涂层内部相表面迁移的效率，提高涂层防蚊虫的效果。优选地，硅藻土和/或煅烧高岭土的平均粒径为5-10μm，也可为6-9μm，例如7μm或8μm。
本发明的水性涂料进一步包括其它成分，其它成分的实例包括pH调节剂、颜填料、消泡剂、增稠剂、杀菌剂、成膜助剂等。
pH值调节剂用于至少部分地中和成膜物质的羧酸部分以使水性涂料稳定。pH值调节剂是其中与羧酸的反应可能导致盐形成的任何物质。pH值调节剂的实例包括但不限于碱金属氢氧化物、氨或其有机衍生物(包括胺)。在某些实施方案中，pH值调节剂是强碱或弱碱。例如，pH值调节剂可以是氢氧化钠、氢氧化钾、氨或胺，例如单乙醇胺(MEA)、三乙醇胺(TEA)、二乙基乙醇胺(DEEA)或二甲基氨基乙醇(DMEA)。pH值对于稳定水性涂料是重要的。在某些实施方案中，水性组合物的pH在6.0-7.0之间，优选6.2-6.8之间，例如，6.3、6.4、6.5、6.6和6.7。如果pH值过低，则水性涂料不稳定，易于发生凝聚，甚至发生沉淀(即，破乳)。如果pH值过高，水性涂料的驱虫效果变差。在某些实施方案中，水性涂料中5至100摩尔百分数的-COOH基团被pH值调节剂中和。在某些实施方案中，10至80摩尔百分数的-COOH基团被中和。在某些实施方案中，20至70摩尔百分数的-COOH基团被中和。
本发明中，颜填料为本领域内通常使用的任何物质。优选为二氧化钛、重质碳酸钙和石英粉中的至少一种。
本发明中，消泡剂为本领域内通常使用的任何物质。优选为星型结构分子级消泡剂。
本发明中，增稠剂为本领域内通常使用的任何物质。优选为无溶剂聚氨酯类增稠剂。
本发明中，杀菌剂为本领域内通常使用的任何物质。优先为杂环化合物或取代芳烃类化合物。
本发明中，成膜助剂为本领域内通常使用的任何物质。优选为酮类或乙二醇醚酯类成膜助剂。
本发明中，水性涂料的制备可使用本领域内已知的任何方法。作为示例性方法，本发明例举如下步骤：
(1)将驱虫剂和乙醇溶液按一定比例加入反应罐，以一定的速度搅拌均匀，得到预制驱虫液，备用；
(2)将反光组分、隔热组分按一定比例加入装有水性合成树脂乳液的反应罐中，以一定速度搅拌均匀，得到涂料预混液；
(3)在反应罐中依次缓慢加入去离子水、增稠剂、润湿分散剂、杀菌剂、pH调节剂、成膜助剂和消泡剂，混合，以一定速度搅拌至均匀；
(4)在步骤(3)的反应罐中，依次缓慢加入颜填料、光稳定剂、硅藻土/煅烧高岭土，以一定速度搅拌至均匀；
(5)在步骤(4)的反应罐中，将预制驱虫液、涂料预混液依次缓慢加入，在一定速度下搅拌，加入增稠剂调整其到一定的粘度，得到本发明的水性涂料。
步骤(1)中搅拌速度为100-200rpm；步骤(2)中搅拌速度为200-300rpm；步骤(3)中搅拌速度为500-600rpm，搅拌时间为2-12min；步骤(4)的搅拌速度为800-1000rpm,搅拌时间为1-30min，搅拌至粒度小于等于100μm；步骤(5)的搅拌速度为400-600rpm，搅拌时间1-5min，环境温度为25℃时调整粘度在100-150KU之间。
在制备本发明的水性涂料时，各成分的重量份组成，例如，可如下所示：
上述成分中，部分成分例如pH调节剂、颜填料、消泡剂、增稠剂、杀菌剂、成膜助剂等为任选成分。
本发明的水性涂料可应用于各种领域，优选应用于园林、果园、行道树、景观绿化等树木，对树木进行一定程度的保护。尤其是，行道树的保护、美化和道路指引作用，尤为突出。
本发明提供的行道树涂料的具体应用方法，例如可以如下所示：
在秋末冬初，将行道树上树干的粗翘皮及其他物质清除干净，之后在每棵树上做标记，用胶带在树干距地面约150cm处缠绕一周，之后用刷子蘸取本发明涂料，涂覆于标记下方的树干上即可，涂覆量以将标记树干全部涂覆均匀为准。
本发明提供的行道树涂料涂敷在行道树干上，可以长期有效保护行道树木免受病虫害，在寒冷的北方冬季，有效隔离冷空气对树木的侵袭，减少寒冷对树木的损伤，行道树涂料在白天保持良好完整的外观，长时间内具有很高的观赏性，特别地，在夜间能够有效反射灯光，能够作为道路标识，充分发挥其道路指引作用，大大提高道路交通安全。
下面，将参考下列具体实施例、比较例详细解释本发明一种行道树涂料的制备方法。
实施例
本实施例共列举4例用以说明该涂料的性能，各组份和重量份配方如表1。各组分计量单位为重量份。
表1
具体制备步骤：
(1)将高效氯氟氰菊酯水乳液、高效氯氰菊酯水乳液或联苯菊酯水乳液和95％乙醇溶液按体积比1:1的比例加入反应罐，以10rpm速度搅拌均匀，得到预制驱虫液，备用；
(2)将反光组分、隔热组分加入到装有水性合成树脂乳液的反应罐中，以200rpm速度搅拌10min至均匀，得到涂料预混液；
(3)在反应罐中依次缓慢加入去离子水、增稠剂、润湿分散剂、杀菌剂、pH调节剂、成膜助剂和消泡剂，混合，以500rpm速度搅拌至均匀；
(4)在步骤(3)的反应罐中，依次缓慢加入颜填料、光稳定组分、硅藻土/煅烧高岭土，以1000rpm速度搅拌30min至均匀；
(5)在步骤(4)的反应罐中，将预制驱虫液、涂料预混液依次缓慢加入，在500rpm速度下搅拌2min，加入增稠剂调整其粘度为80KU，得到本发明的水性涂料1。
步骤(1)中搅拌速度为100-200rpm；步骤(2)中搅拌速度为200-300rpm；步骤(3)中搅拌速度为500-600rpm，搅拌时间为2-12min；步骤(4)的搅拌速度为800-1000rpm,搅拌时间为1-30min，搅拌至粒度小于等于100μm；步骤(5)的搅拌速度为400-600rpm，搅拌时间1-5min，环境温度为25℃时调整粘度在100-150KU之间。
本发明对于上述实施例1-4所制作的涂料进行性能检测，测得的各项技术指标见表2。检测方法参照相关涂料国家标准GB/T 9755-2014，逆反射系数测试方法参照GB/T18833-2012《道路交通反光膜》中规定的方法执行。
表2实施例1-4性能测试结果
通过上述实施例可注意到本发明行道树涂料能够满足施工使用要求。另外逆反射系数均在150cd·lx-1·m-2以上，可知该行道树涂料在夜间能够有效反射光，起到良好的交通引导作用。
比较例
本比较例共列举8例，其中比较例1-4是为了选择合适的昆虫驱虫剂成分；比较例5-7是为了说明光稳定性和涂料膜结构改善组分，对昆虫趋避效果耐久性的影响；比较例8是为了说明对隔热组分对涂料保温隔热的影响。
比较例1-4各组份配方表3，各单位为重量份。
说明：具有驱虫作用的拟除虫菊酯有很多种，本比较例选用了山东中农联合生物科技股份有限公司生产的高效氯氟氰菊酯水乳液、高效氯氰菊酯水乳液和联苯菊酯水乳液。
表3比较例1-4的拟除虫菊酯组成及配方
| 驱虫剂成分 | 比较例1 | 比较例2 | 比较例3 | 比较例4 |
| 高效氯氟氰菊酯水乳液 | 0 | 0 | 6 | 6 |
| 高效氯氰菊酯水乳液 | 6 | 6 | 0 | 6 |
| 联苯菊酯水乳液 | 0 | 6 | 6 | 0 |
比较例1-4按照实施例1中的方法、各组分含量，分别制得行道树涂料。
注：比较例1-4中驱虫剂量与实施例1驱虫剂量相同，为24个单位。
测试比较例1-4、实施例1中的行道树涂料的驱虫/杀虫效力，观察到的结果列于表4。每种涂料组合物的昆虫趋避力的测试方法如下进行。将涂料涂布在每只测试盒(30cm*30*cm*20cm)的除了上表面外的五个内表面上。上表面用昆虫控制网盖住。将50只德国蟑螂(German roach)成虫投入盒中，该昆虫具有很强的繁殖力并且是公用的测试昆虫。在每只盒子的内壁上设置隔离栏使蟑螂不能沿壁爬出。控制湿度保持在50-70％，温度25±2℃。提供固体饲料和糖水。投入蟑螂后，根据时间和推移计算蟑螂的数目。
根据文献，可采用各种方式测试昆虫趋避力。杀虫效力通常用LD50(中致死量)和LC50(中致死浓度)代表。他们用相对剂量和浓度的致死率代表，用S特性曲线表示。致死率折合成剂量和浓度对数，在图表上用点表示。将如此得到的点连接起来，得到直线。该直线被称作致死率相对于剂量和浓度的回归直线，并代表杀虫效力的参照。
为了表示立即的结果，使用了KT50(中击倒时间)，KT50代表使用昆虫驱虫剂成分后50％蟑螂表现出反常反应的时间。残留特性代表昆虫趋避效力的持久时间。驱出效力用FOT50(中驱出时间)代表，表示隐藏处的蟑螂开始被驱出的时间。
在这一试验中，根据时间计数盒中死亡的蟑螂数，累加死亡的蟑螂数目，得到表4中所列值。
表4蟑螂驱出效力实验结果
| 时间(小时) | 比较例1 | 比较例2 | 比较例3 | 比较例4 | 实施例1 |
| 1 | 0 | 1 | 0 | 1 | 1 |
| 2 | 0 | 4 | 1 | 5 | 5 |
| 5 | 1 | 10 | 4 | 9 | 12 |
| 8 | 3 | 14 | 9 | 13 | 18 |
| 12 | 7 | 17 | 15 | 18 | 35 |
| 24 | 10 | 25 | 23 | 26 | 48 |
| 36 | 15 | 39 | 30 | 38 | 50 |
| 48 | 20 | 48 | 38 | 47 | 50 |
| 60 | 28 | 50 | 48 | 50 | 50 |
| 72 | 36 | 50 | 50 | 50 | 50 |
从结果中可以证明实施例1制备的组合物的昆虫趋避剂效力具有优异效果，8-12小时杀死半数蟑螂，36小时内将蟑螂全部杀死；比较例2和实施例4效果良好，12-24小时杀死半数蟑螂，60小时内将蟑螂全部杀死；比较例3效果一般，24-36小时杀死半数蟑螂，72小时内将将蟑螂全部杀死；比较例1驱虫效果不合格，48-60小时杀死半数蟑螂，在72小时内只杀死36只蟑螂。结合各实施例、比较例驱虫剂成分分析，不难得出结论：氯氰菊酯相对其他拟除虫菊酯类驱虫剂是一种高效驱虫剂。从简化涂料配方和成本考虑，氯氰菊酯是一种理想的驱虫剂，应作为本行道涂料的最优选。
下面将使用高效氯氰菊酯水乳液作为驱虫剂成分，在涂料膜结构改善组分、光稳定剂有无的情况下，进行该昆虫驱虫剂效力的持久实验。
比较例5-7各组份配方表5，各单位为重量份。
表5比较例5-7中光稳定剂及涂膜结构改善组分列表
| 涂料膜结构改善组分/光稳定剂 | 比较例5 | 比较例6 | 比较例7 |
| 硅藻土(涂料膜结构改善组分) | 0 | 80 | 0 |
| 纳米氧化锌(光稳定剂) | 80 | 0 | 0 |
比较例5-7按照实施例1中的方法、各组分含量，分别制得行道树涂料。硅藻土、纳米氧化锌不足部分由CC-1000等量代替。
将实施例1、比较例5、比较例6、比较例7制得的涂料暴露在自然环境，进行驱虫效力测试。
将上述各涂料涂布在石板上，暴露在阳光、风、雨、露、霜、雪等自然环境中。平板从2015年11月1日起暴露至2016年10月30日。使用这种平板制造具有同样尺寸和形状的用于测试昆虫趋避力效力的盒子。将50只德国蟑螂成虫投入盒中并观察。结果列于表6。其中数值代表死亡蟑螂的累加值。
表6比较例5-7及实施例1蟑螂驱出效力实验结果
| 时间(小时) | 比较例5 | 比较例6 | 比较例7 | 实施例1 |
| 1 | 0 | 0 | 0 | 0 |
| 2 | 1 | 1 | 0 | 1 |
| 5 | 2 | 3 | 1 | 3 |
| 8 | 5 | 6 | 2 | 7 |
| 12 | 9 | 9 | 4 | 10 |
| 24 | 11 | 12 | 9 | 15 |
| 36 | 15 | 16 | 15 | 19 |
| 48 | 20 | 19 | 21 | 25 |
| 60 | 24 | 26 | 26 | 36 |
| 72 | 37 | 35 | 30 | 43 |
从结果中可以证实使用实验例1制备的涂料可得到最有效的结果，该组合物中含有防晒剂纳米二氧化锌和涂料膜结构改善组分硅藻土。
综上，根据本发明人实验，可以保证本发明的行道树涂料驱虫效力可保持约12个月。通常，行道树大约在每年秋末冬初进行涂刷一次，用以保护行道树免受病虫害的侵袭。因此该涂料的驱虫持久度还是令人满意的。
下面将使用介绍在有无隔热组分的情况下，进行行道树涂料保温隔热效果试验。
比较例8，其组成不含玻璃微珠，其余组分与实施例1相同。
涂料的隔热效果测试方法如下进行。将涂料涂布在每只测试盒(30cm*30*cm*20cm)的除了下表面外的五个外表面上。在距测试盒上方15cm处安装200w的电烤灯。电烤灯正下方在测试盒外表面、测试盒内中心安装热电偶温度测试装置，温度精度为1℃。控制室温保持在25±2℃，打开电烤灯开始计时，并记录温度变化值。结果列于表7。
表7比较例8和实施例1保温效果测试
从结果中可以证实使用了隔热组分(空心玻璃微珠)的实施例1比没有使用隔热组分的比较例8的隔热效果要好的多。同理，在冬季该涂料的保温效果也很好。综上，使用该隔热组分可以有效保温，减少树木受到寒冷的侵袭。
Claims (13)
1.一种行道树涂料，其特征在于：主要包括拟除虫菊酯组分、反光组分、隔热组分、水性合成树脂乳液组分、涂料膜结构改善组分和光稳定组分。
2.根据权利要求1所述的行道树涂料，其特征在于：所述反光组分是实心玻璃微珠。
3.根据权利要求1所述的行道树涂料，其特征在于：所述隔热组分是空心玻璃微珠。
4.根据权利要求1所述的行道树涂料，其特征在于：所述水性合成树脂乳液为醋酸乙烯-乙烯共聚物的水分散乳液。
5.根据权利要求1所述的行道树涂料，其特征在于：所述涂料膜结构改善组分为硅藻土和/或高岭土。
6.根据权利要求1所述的行道树涂料，其特征在于：所述光稳定组分为纳米氧化锌。
7.根据权利要求1所述的行道树涂料，其特征在于：所述拟驱虫菊酯为溶解在醇中得到的拟驱虫菊酯醇溶液。
8.根据权利要求7所述的行道树涂料，其特征在于：所述拟驱虫菊酯选自胺菊酯、右旋胺菊酯、右旋苄呋菊酯、炔呋菊酯、丙炔菊酯、丙烯菊酯、右旋丙烯菊酯、右旋反式丙烯菊酯、氯菊酯、氯氰菊酯、顺式氯氰菊酯和高效顺反氯氰菊酯组成的组中的至少一种。
9.根据权利要求8所述的行道树涂料，其特征在于：所述拟驱虫菊酯醇溶液是氯氰菊酯与95％乙醇混合得到的乙醇溶液。
10.根据权利要求1-9任一项所述的行道树涂料，其特征在于：还包括润湿分散剂、pH调节剂、颜填料、消泡剂、增稠剂、杀菌剂、成膜助剂和去离子水。
11.根据权利要求10所述的行道树涂料，其特征在于：所述组分重量份比例为:
12.一种根据权利要求1-11任一项所述的行道树涂料的制备方法，包括如下步骤：
(1)将拟除虫菊酯和醇溶液按比例加入反应罐，搅拌均匀，得到预制驱虫液，备用；
(2)将反光组分、隔热组分按比例加入装有水性合成树脂乳液的反应罐中，搅拌均匀，得到涂料预混液；
(3)在反应罐中依次缓慢加入去离子水、增稠剂、润湿分散剂、杀菌剂、pH调节剂、成膜助剂和消泡剂，混合，搅拌至均匀；
(4)在步骤(3)的反应罐中，依次缓慢加入颜填料、硅藻土、光稳定组分，以搅拌至均匀；
(5)在步骤(4)的反应罐中，将预制驱虫液、涂料预混液依次缓慢加入，搅拌，加入增稠剂调整粘度，得到行道树涂料。
13.根据权利要求12所述的制备方法，其特征在于：步骤(1)中搅拌速度为100-200rpm；步骤(2)中搅拌速度为200-300rpm；步骤(3)中搅拌速度为500-600rpm，搅拌时间为2-12min；步骤(4)的搅拌速度为800-1000rpm，搅拌时间为1-30min，搅拌至粒度小于等于100μm；步骤(5)的搅拌速度为400-600rpm，搅拌时间1-5min，环境温度为25℃时调整粘度在100-150KU之间。