CN106866033A - A kind of artificial quartz in lump leopard card and preparation method thereof - Google Patents
A kind of artificial quartz in lump leopard card and preparation method thereof Download PDFInfo
- Publication number
- CN106866033A CN106866033A CN201710162104.6A CN201710162104A CN106866033A CN 106866033 A CN106866033 A CN 106866033A CN 201710162104 A CN201710162104 A CN 201710162104A CN 106866033 A CN106866033 A CN 106866033A
- Authority
- CN
- China
- Prior art keywords
- parts
- leopard
- resin
- auxiliary agent
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to artificial quartz in lump plate technique field, and in particular to a kind of synthetic quartz parmelia saxatilis leopard card and preparation method thereof, including the following each component counted by weight：40~55 parts of cullet sheet of particles, 6~12 parts of unsaturated-resin, 6~12 parts of epoxy resin, 5~8 parts of leopard line solid material, 600 25~32 parts of mesh washed ore powder, 0.3~1.2 part of auxiliary agent, wherein, the auxiliary agent includes curing agent and accelerator.Artificial quartz in lump leopard card of the invention has the advantages that environmentally friendly, bright and lustrous bright, easy to clean, fire-retardant.
Description
Technical field
The present invention relates to building material technical field, and in particular to a kind of artificial quartz in lump leopard card and preparation method thereof.
Background technology
The artificial quartz stone checkered plate of prior art is bonding agent typically by unsaturated-resin, with quartz sand, pigment
Artificial quartz stone checkered plate is directly prepared into etc. baking after being stirred.The usual color of quartz diamond plate obtained in prior art
Not distinct bright, the color of decorative pattern is typically embodied by quartz sand and pigment color in itself, the flower of such quartz diamond plate
The color of line is stiff to be discord.
The content of the invention
In order to solve the above problems, the present invention provides a kind of artificial quartz in lump leopard card and preparation method thereof, with unsaturation
Resin is jointing material, with quartz sand, mix after mill base, auxiliary agent etc. stir, then through overbaking, strike off, polish
Operation is obtained the artificial quartz in lump leopard card, bad with the transparency for solving existing artificial quartz stone checkered plate, and decorative pattern is dull
Discordant technological deficiency.
A kind of leopard line glass particle that the present invention is provided, including the following each component counted by weight：Cullet particle
40~55 parts of piece, 6~12 parts of unsaturated-resin, 6~12 parts of epoxy resin, 5~8 parts of leopard line solid material, 600 mesh washed ore powder 25
~32 parts, 0.3~1.2 part of auxiliary agent, wherein, the auxiliary agent includes curing agent and accelerator.
The method for preparing above-mentioned leopard line glass particle is as follows：By cullet sheet of particles, unsaturated-resin, epoxy resin, leopard
After the mixing and stirring such as line solid material and 600 mesh washed ore powder, auxiliary agent moderate-speed mixer 1min is added, is subsequently poured into mould,
60min is toasted under the conditions of 50~70 DEG C, is rubbed scattered, sieved with the screen cloth of 2~4 mesh, be then fabricated to sample, be molded, quality inspection.
The artificial quartz in lump leopard card made using above-mentioned leopard line glass particle, including count by weight it is following each
Component：8~13 parts of unsaturated-resin, 8~12 parts of epoxy resin, 23~33 parts of purity quartzite, 23~34 parts of silica flour, pigment
0.7~1.2 part of powder, 24~36 parts of leopard line glass particle, 0.3~1.5 part of auxiliary agent, wherein, the auxiliary agent includes curing agent and rush
Enter agent.
Preferably, the pigment powder includes the following component counted by weight, 14~15 parts of carbon black powder, iron oxide yellow pigments powder
60~62 parts, 24~25 parts of cologne earth pigment powder.
The preparation technology of the artificial quartz in lump leopard card that above-mentioned leopard line glass particle makes is as follows：By leopard line glass particle,
Unsaturated-resin, epoxy resin, purity quartzite, silica flour mix 4min, spray pigment powder, add auxiliary agent stirring
30s, is sieved once with 2 eye mesh screens, suppresses 180~220S, and 90min is then toasted under conditions of 80~100 DEG C, realizes solidification
Shaping, then through scraping, polishing, finishing process.
The present invention has advantages below compared with prior art：
Artificial quartz stone checkered plate of the invention with unsaturated-resin as jointing material, with quartz sand, mix mill base, auxiliary agent
After stirring, then through overbaking, strike off, the operation such as polish the artificial quartz stone checkered plate is obtained.It is described artificial
The color clear of quartz diamond plate is bright, and leopard line thereon is good with the degrees of coordination of synthetic quartz slabstone, natural harmony.
Specific embodiment
The technical scheme in the embodiment of the present invention is clearly and completely described below in conjunction with the embodiment of the present invention,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention
Embodiment, all other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of the present invention.
Embodiment one：
A kind of artificial quartz in lump leopard card, including the following each component counted by weight：13 parts of unsaturated-resin, epoxy
12 parts of resin, 24 parts of purity quartzite, 25 parts of silica flour, 0.7 part of pigment powder, 25 parts of leopard line glass particle, 0.3 part of auxiliary agent, its
In, the auxiliary agent includes curing agent and accelerator.
Wherein, the leopard line glass particle, including the following each component counted by weight：45 parts of cullet sheet of particles,
10 parts of unsaturated-resin, 9 parts of epoxy resin, 5 parts of leopard line solid material, 600 30 parts of mesh washed ore powder, 1 part of auxiliary agent, wherein, it is described
Auxiliary agent includes curing agent and accelerator.
The pigment powder includes the following component counted by weight, 15 parts of carbon black powder, 60 parts of iron oxide yellow pigments powder, cologne earth face
25 parts of feed powder.
Above-mentioned curing agent is vinyl triamine, and the accelerator is resorcinol.
The preparation method of described leopard line glass particle is as follows：By cullet sheet of particles, unsaturated-resin, epoxy resin,
After the mixing and stirring such as leopard line solid material and 600 mesh washed ore powder, auxiliary agent moderate-speed mixer 1min is added, be subsequently poured into mould
Tool, 60min is toasted under the conditions of 50~70 DEG C, is rubbed scattered, and is sieved with the screen cloth of 2~4 mesh, is then fabricated to sample, is molded, matter
Inspection.
The preparation technology of the artificial quartz in lump leopard card that described leopard line glass particle makes is as follows：By leopard line glass
Grain, unsaturated-resin, epoxy resin, purity quartzite, silica flour mix 4min, spray pigment powder, add auxiliary agent and stir
30s is mixed, is sieved once with 2 eye mesh screens, suppress 180~220S, 90min is then toasted under conditions of 80~100 DEG C, realized solid
Chemical conversion type, then through scraping, polishing, finishing process.
Embodiment two：
A kind of artificial quartz in lump leopard card, including the following each component counted by weight：12 parts of unsaturated-resin, epoxy
12 parts of resin, 25 parts of purity quartzite, 26 parts of silica flour, 0.7 part of pigment powder, 24 parts of leopard line glass particle, 0.3 part of auxiliary agent, its
In, the auxiliary agent includes curing agent and accelerator.
Wherein, the leopard line glass particle, including the following each component counted by weight：46 parts of cullet sheet of particles,
9 parts of unsaturated-resin, 9 parts of epoxy resin, 6 parts of leopard line solid material, 600 29 parts of mesh washed ore powder, 1 part of auxiliary agent, wherein, it is described to help
Agent includes curing agent and accelerator.
The pigment powder includes the following component counted by weight, 14 parts of carbon black powder, 61 parts of iron oxide yellow pigments powder, cologne earth face
25 parts of feed powder.
Above-mentioned curing agent is vinyl triamine, and the accelerator is resorcinol.
The preparation method of described leopard line glass particle is as follows：By cullet sheet of particles, unsaturated-resin, epoxy resin,
After the mixing and stirring such as leopard line solid material and 600 mesh washed ore powder, auxiliary agent moderate-speed mixer 1min is added, be subsequently poured into mould
Tool, 60min is toasted under the conditions of 50~70 DEG C, is rubbed scattered, and is sieved with the screen cloth of 2~4 mesh, is then fabricated to sample, is molded, matter
Inspection.
The preparation technology of the artificial quartz in lump leopard card that described leopard line glass particle makes is as follows：By leopard line glass
Grain, unsaturated-resin, epoxy resin, purity quartzite, silica flour mix 4min, spray pigment powder, add auxiliary agent and stir
30s is mixed, is sieved once with 2 eye mesh screens, suppress 180~220S, 90min is then toasted under conditions of 80~100 DEG C, realized solid
Chemical conversion type, then through scraping, polishing, finishing process.
Embodiment three：
A kind of artificial quartz in lump leopard card, including the following each component counted by weight：11 parts of unsaturated-resin, epoxy
12 parts of resin, 26 parts of purity quartzite, 25 parts of silica flour, 0.7 part of pigment powder, 25 parts of leopard line glass particle, 0.3 part of auxiliary agent, its
In, the auxiliary agent includes curing agent and accelerator.
Wherein, the leopard line glass particle, including the following each component counted by weight：47 parts of cullet sheet of particles,
8 parts of unsaturated-resin, 9 parts of epoxy resin, 6 parts of leopard line solid material, 600 29 parts of mesh washed ore powder, 1 part of auxiliary agent, wherein, it is described to help
Agent includes curing agent and accelerator.
The pigment powder includes the following component counted by weight, 14 parts of carbon black powder, 61.5 parts of iron oxide yellow pigments powder, cologne earth
24.5 parts of pigment powder.
Above-mentioned curing agent is vinyl triamine, and the accelerator is resorcinol.
The preparation method of described leopard line glass particle is as follows：By cullet sheet of particles, unsaturated-resin, epoxy resin,
After the mixing and stirring such as leopard line solid material and 600 mesh washed ore powder, auxiliary agent moderate-speed mixer 1min is added, be subsequently poured into mould
Tool, 60min is toasted under the conditions of 50~70 DEG C, is rubbed scattered, and is sieved with the screen cloth of 2~4 mesh, is then fabricated to sample, is molded, matter
Inspection.
The preparation technology of the artificial quartz in lump leopard card that described leopard line glass particle makes is as follows：By leopard line glass
Grain, unsaturated-resin, epoxy resin, purity quartzite, silica flour mix 4min, spray pigment powder, add auxiliary agent and stir
30s is mixed, is sieved once with 2 eye mesh screens, suppress 180~220S, 90min is then toasted under conditions of 80~100 DEG C, realized solid
Chemical conversion type, then through scraping, polishing, finishing process.
Example IV：
A kind of artificial quartz in lump leopard card, including the following each component counted by weight：10 parts of unsaturated-resin, epoxy
12 parts of resin, 27 parts of purity quartzite, 25 parts of silica flour, 0.7 part of pigment powder, 25 parts of leopard line glass particle, 0.3 part of auxiliary agent, its
In, the auxiliary agent includes curing agent and accelerator.
Wherein, the leopard line glass particle, including the following each component counted by weight：48 parts of cullet sheet of particles,
7 parts of unsaturated-resin, 9 parts of epoxy resin, 6 parts of leopard line solid material, 600 29 parts of mesh washed ore powder, 1 part of auxiliary agent, wherein, it is described to help
Agent includes curing agent and accelerator.
The pigment powder includes the following component counted by weight, 14.5 parts of carbon black powder, 61.5 parts of iron oxide yellow pigments powder, iron
24 parts of brown pigment powder.
Above-mentioned curing agent is vinyl triamine, and the accelerator is resorcinol.
The preparation method of described leopard line glass particle is as follows：By cullet sheet of particles, unsaturated-resin, epoxy resin,
After the mixing and stirring such as leopard line solid material and 600 mesh washed ore powder, auxiliary agent moderate-speed mixer 1min is added, be subsequently poured into mould
Tool, 60min is toasted under the conditions of 50~70 DEG C, is rubbed scattered, and is sieved with the screen cloth of 2~4 mesh, is then fabricated to sample, is molded, matter
Inspection.
The preparation technology of the artificial quartz in lump leopard card that described leopard line glass particle makes is as follows：By leopard line glass
Grain, unsaturated-resin, epoxy resin, purity quartzite, silica flour mix 4min, spray pigment powder, add auxiliary agent and stir
30s is mixed, is sieved once with 2 eye mesh screens, suppress 180~220S, 90min is then toasted under conditions of 80~100 DEG C, realized solid
Chemical conversion type, then through scraping, polishing, finishing process.
Unsaturated-resin in above-described embodiment can be such as in phenolic resin, epoxy resin, unsaturated polyester resin
One or more combination.The unsaturated-resin has good adhesive property as bonding agent, while so that artificial
Quartz leopard card has good transparency so that the decorative pattern clear and natural on quartz leopard line card；And artificial quartz in lump
Quartz leopard card after causing to be molded due to the addition for having unsaturated-resin in plate has good hot property, its line is swollen system
It is small, it is close with common metal material, can so reduce the internal stress produced by expanded by heating；Processing technology is excellent, can make
The artificial quartz in lump leopard line card temperature that is molded successively and is molded is not high, be conducive to energy saving；
Quartz sand and silica flour in artificial quartz stone checkered plate of the invention are Inorganic Non-metallic Materials, with good
Fire prevention and etch-proof performance.
Synthetic quartz slabstone for being provided the embodiment of the present invention above and preparation method thereof is described in detail, herein
In apply specific case principle of the invention and implementation method be set forth, the explanation of above example is only intended to side
Assistant solves core concept of the invention；Simultaneously for those of ordinary skill in the art, according to thought of the invention and method,
Will change in specific embodiments and applications, in sum, this specification content should not be construed as to this
The limitation of invention.
Claims (5)
1. a kind of leopard line glass particle, it is characterised in that including the following each component counted by weight：Cullet sheet of particles 40
~55 parts, 6~12 parts of unsaturated-resin, 6~12 parts of epoxy resin, 5~8 parts of leopard line solid material, 600 mesh washed ore powder 25~32
Part, 0.3~1.2 part of auxiliary agent, wherein, the auxiliary agent includes curing agent and accelerator.
2. leopard line glass particle according to claim 1, it is characterised in that its preparation method is as follows：By cullet particle
After the mixing and stirrings such as piece, unsaturated-resin, epoxy resin, leopard line solid material and 600 mesh washed ore powder, in adding auxiliary agent
Speed stirring 1min, is subsequently poured into mould, and 60min is toasted under the conditions of 50~70 DEG C, rubs scattered, and is sieved with the screen cloth of 2~4 mesh, so
After be fabricated to sample, be molded, quality inspection.
3. the artificial quartz in lump leopard card that leopard line glass particle according to claim 1 makes, it is characterised in that including pressing
The following each component of parts by weight meter：8~13 parts of unsaturated-resin, 8~12 parts of epoxy resin, 23~33 parts of purity quartzite,
23~34 parts of silica flour, 0.7~1.2 part of pigment powder, 24~36 parts of leopard line glass particle, 0.3~1.5 part of auxiliary agent, wherein, it is described
Auxiliary agent includes curing agent and accelerator.
4. the artificial quartz in lump leopard card that leopard line glass particle according to claim 3 makes, it is characterised in that the face
Feed powder includes the following component counted by weight, 14~15 parts of carbon black powder, 60~62 parts of iron oxide yellow pigments powder, cologne earth pigment powder 24
~25 parts.
5. the artificial quartz in lump leopard card that leopard line glass particle according to claim 4 makes, it is characterised in that its preparation
Technique is as follows：Leopard line glass particle, unsaturated-resin, epoxy resin, purity quartzite, silica flour are mixed into 4min, spray
Pigment powder is spilt, auxiliary agent stirring 30s is added, is sieved once with 2 eye mesh screens, 180~220S is suppressed, then at 80~100 DEG C
Under the conditions of toast 90min, realize curing molding, then through scraping, polishing, finishing process.