CN106863952A - A kind of planted roof root resistant waterproof roll and preparation method thereof - Google Patents

A kind of planted roof root resistant waterproof roll and preparation method thereof Download PDF

Info

Publication number
CN106863952A
CN106863952A CN201710112094.5A CN201710112094A CN106863952A CN 106863952 A CN106863952 A CN 106863952A CN 201710112094 A CN201710112094 A CN 201710112094A CN 106863952 A CN106863952 A CN 106863952A
Authority
CN
China
Prior art keywords
waterproof roll
layer
basic unit
parts
planted roof
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710112094.5A
Other languages
Chinese (zh)
Inventor
邱明轩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Zhonglian Tiansheng Engineering Material Co Ltd
Original Assignee
Beijing Zhonglian Tiansheng Engineering Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Zhonglian Tiansheng Engineering Material Co Ltd filed Critical Beijing Zhonglian Tiansheng Engineering Material Co Ltd
Priority to CN201710112094.5A priority Critical patent/CN106863952A/en
Publication of CN106863952A publication Critical patent/CN106863952A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of planted roof root resistant waterproof roll and preparation method thereof, it is related to field of waterproof materials, solves the technical problem of existing waterproof material root-resistant puncturing ability.The waterproof roll of the application includes successively from top to bottom：First separation layer, the first bitumen layer, the first tire basic unit, copper foil layer, second fetus basic unit, the second bitumen layer and the second separation layer, wherein, the first bitumen layer is identical with the composition of the second bitumen layer.The present invention is used to improve the root-resistant puncturing ability of waterproof roll.

Description

A kind of planted roof root resistant waterproof roll and preparation method thereof
Technical field
The present invention relates to waterproof material technical field, and in particular to a kind of planted roof root resistant waterproof roll and its system Preparation Method.
Background technology
With the development and progress of society, planting on roof is widely used.Roof greening is increasingly The concern of society is caused more.The extensive use of planting on roof, it is necessary to waterproof, the production of root-resistant puncturing coiled material, Construction enterprises give high standards.
But present waterproof roll bad adaptability, can not meet different roofings to the material waterproofing of waterproof roll, intensity, The requirement of root-resistant puncturing, causes the Seepage of construction wall or roofing.
The content of the invention
It is an object of the invention to provide a kind of planted roof root resistant waterproof roll and preparation method thereof, for improving The root-resistant puncturing ability of waterproof roll.
To reach above-mentioned purpose, planted roof root resistant waterproof roll provided by the present invention uses following technical side Case：
The waterproof roll includes successively from top to bottom：First separation layer, the first bitumen layer, the first tire basic unit, copper foil layer, Two tire basic units, the second bitumen layer and the second separation layer, wherein, the first bitumen layer is identical with the composition of the second bitumen layer.
Alternatively, the composition of the first bitumen layer and the second bitumen layer, calculates by weight, including：60~80 parts of pitch； HDPE10~20 part；5~10 parts of compound lard；3~6 parts of fire retardant；ZnO10~40 part；11~20 parts of chemical root resistance agent.
Alternatively, pitch include 200# road asphalts and with 60# road asphalts, 200# road asphalts and 60# road asphalts Mixing ratio by weight example be 7：3.
Alternatively, the material of the first tire basic unit and second fetus basic unit is in polyester fiber, glass fibre or composite fibre One or more.
Alternatively, the thickness of waterproof roll is 3mm~5mm.
Waterproof roll provided by the present invention, on the basis of existing waterproof roll, increased copper foil layer and second fetus base Layer, and bitumen layer is modified so that waterproof roll has stronger impact resistance, corrosion resistance, during use not Easily penetrated by root system of plant, good water-proof effect, long service life.
Additionally, present invention also offers a kind of preparation method of planted roof root resistant waterproof roll, the preparation method Comprise the following steps:
Step 1, that pitch, HDPE, compound lard, fire retardant, ZnO and chemical root resistance agent are put into 1# according to parts by weight is close Mill is mixed, and is stirred；
Step 2, by the material stirred in 1# banburies by after extruder by mould extrusion forming, after shaping Material is the blank of flat；
Step 3, the first tire basic unit, copper foil layer and second fetus basic unit are prolonged into machine roll-forming by rolling, obtain tire basic unit prefabricated Body；
Step 4, the mixed material obtained by 1# banburies and tire basic unit precast body are prolonged into machine rolling one-shot forming by rolling；
Step 5, the upper surface of the material being combined in calendering isolate with the first separation layer and second is formed on lower surface respectively Layer；
Step 6, the structure to being formed after step 5 carry out roll-in and roller cooling, form pitch band；
Step 7, the pitch band after spraying is dried, wound.
Alternatively, the parts by weight of each component in step 1 are according to 60~80 parts of pitch；HDPE10~20 part；Miscella 5~10 parts of fat；3~6 parts of fire retardant；ZnO10~40 part；11~20 parts of chemical root resistance agent is prepared.
Alternatively, the temperature that 1# banburies set in step 1 is 85 DEG C~90 DEG C.
Alternatively, pitch includes 200# road asphalts and 60# road asphalts, 200# road asphalts and 60# road asphalts Mixing ratio by weight example is 7：3.
Alternatively, the thickness of waterproof roll is 3mm~5mm.
The preparation method of planted roof root resistant waterproof roll provided by the present invention, the waterproof roll of formation is from up to Under include successively：First separation layer, the first bitumen layer, the first tire basic unit, copper foil layer, second fetus basic unit, the second bitumen layer and Two separation layers, the tire basic unit of the combination formation of the first tire basic unit, Copper Foil and second fetus basic unit, and bitumen layer is modified, So that waterproof roll has stronger impact resistance, corrosion resistance, it is difficult to be penetrated by root system of plant during use, waterproof effect Good, long service life.
Brief description of the drawings
In order to illustrate more clearly of the embodiment of the present application or technical scheme of the prior art, below will be to embodiment or existing The accompanying drawing to be used needed for having technology description is briefly described, it should be apparent that, drawings in the following description are only this Some embodiments described in application, for those of ordinary skill in the art, can also obtain other according to these accompanying drawings Accompanying drawing.
Fig. 1 is the structural representation of the planted roof root resistant waterproof roll of the embodiment of the present invention.
Description of reference numerals：
1-the first separation layer；2-the first bitumen layer；3-the first tire basic unit；4-copper foil layer；5-second fetus basic unit；6— Second bitumen layer；7-the second separation layer.
Specific embodiment
With reference to the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete Ground description, it is clear that described embodiment is a part of embodiment of the invention, rather than whole embodiments.Based on the present invention In embodiment, the every other implementation that those of ordinary skill in the art are obtained under the premise of creative work is not made Example, belongs to the scope of protection of the invention.
Embodiment one
A kind of planted roof root resistant waterproof roll is the embodiment of the invention provides, Fig. 1 is the kind of the embodiment of the present invention The structural representation of roofing root resistant waterproof roll is planted, as shown in figure 1, the waterproof roll includes successively from top to bottom：First Separation layer 1, the first bitumen layer 2, the first tire basic unit 3, copper foil layer 4, second fetus basic unit 5, the second bitumen layer 6 and the second separation layer 7. Wherein, the first bitumen layer 2 is identical with the composition of the second bitumen layer 6.
Waterproof roll provided by the present invention, on the basis of existing waterproof roll, increased copper foil layer 4 and second fetus base Layer 5, and bitumen layer is modified so that waterproof roll has stronger impact resistance, corrosion resistance, during use not Easily penetrated by root system of plant, good water-proof effect, long service life.
Preferably, the composition of the first bitumen layer 2 and the second bitumen layer 6, calculates by weight, including：Pitch 60~80 Part；HDPE10~20 part；5~10 parts of compound lard；3~6 parts of fire retardant；ZnO10~40 part；11~20 parts of chemical root resistance agent. Chemical root resistance agent is cupric oxide powder.Pitch, HDPE and compound lard, fire retardant, ZnO, chemical root resistance agent in the case where high temperature mixes, Obtain finely dispersed high intensity mixture.Chemical root resistance agent and the addition of ZnO so that the viscosity of mixture is improved, improved The high-temperature stability of mixture, the toughness for increasing pitch, meanwhile, there is quantitative metal ion in mixture so that drip The root-resistant puncturing degree of cyan layer is improved, and improves the waterproof degree of waterproof roll.
Exemplarily, the first bitumen layer 2 and the second bitumen layer 6 are according to parts by weight：60 parts of pitch；HDPE10 parts；Mixing 10 parts of grease；5 parts of fire retardant；ZnO20 parts；When 15 parts of chemical root resistance agent is prepared, the first drip of the mixture composition of gained The root-resistant puncturing degree of the bitumen layer 6 of cyan layer 2 and second is preferable.
Preferably, pitch includes 200# road asphalts and 60# road asphalts, 200# road asphalts and 60# road asphalts Mixing ratio by weight example is 7：3.The softening point temperature of 200# pitches is low, and the softening point temperature of 60# pitches is high, 60# pitches and 200# When pitch mixes, can quickly elevate the temperature, bitumen layer each component is melted rapidly, be well mixed.By testing crew Test of many times show that the Mixing ratio by weight example of 200# road asphalts and 60# road asphalts is 7:3, the first bitumen layer 2 and second The better performances of bitumen layer 6.
Alternatively, compound lard includes biodiesel, paraffin oil and epoxidized soybean oil, and Mixing ratio by weight example is 4:3:2, make The each component for obtaining bitumen layer is uniformly dispersed, and improves the resistance to low temperature of bitumen layer.
Alternatively, the material of the first tire basic unit 3 and second fetus basic unit 5 is in polyester fiber, glass fibre or composite fibre One or more.
Preferably, copper foil layer 4 improves the root-resistant puncturing degree of planted roof root resistant waterproof roll, improves waterproof The water resistance of coiled material.
Alternatively, the thickness of waterproof roll is 3mm~5mm, and the thickness with existing waterproof roll is consistent substantially.
Root resistant waterproof roll of the invention, on the one hand, add HDPE, compound lard in modified asphalt layer so that The lower temperature resistance of waterproof roll is improved, and extends the service life of waterproof roll；On the one hand, added in modified asphalt layer ZnO and chemical root resistance agent so that the root-resistant puncturing degree of bitumen layer is improved, improve the water resistance of waterproof roll； On the other hand, the addition of copper foil layer 4 so that the root-resistant puncturing degree of waterproof roll is improved, and improves the water proofing property of waterproof roll Energy.
Embodiment two
The embodiment of the invention provides a kind of preparation method of planted roof root resistant waterproof roll, the method include with Lower step：
Step 1, that pitch, HDPE, compound lard, fire retardant, ZnO and chemical root resistance agent are put into 1# according to parts by weight is close Mill is mixed, and is stirred；
Step 2, by the material stirred in 1# banburies by after extruder by mould extrusion forming, after shaping Material is the blank of flat；
Step 3, the first tire basic unit 3, copper foil layer 4 and second fetus basic unit 5 are prolonged into machine roll-forming by rolling, obtain tire basic unit pre- Body processed；
Step 4, the mixed material obtained by 1# banburies and tire basic unit precast body are prolonged into machine rolling one-shot forming by rolling；
Step 5, the upper surface of the material being combined in calendering isolate with the first separation layer 1 and second is formed on lower surface respectively Layer 7；
Step 6, the structure to being formed after step 5 carry out roll-in and roller cooling, form pitch band；
Step 7, the pitch band after spraying is dried, wound.
The preparation method of planted roof root resistant waterproof roll provided by the present invention, the waterproof roll of formation is from up to Under include successively：First separation layer 1, the first bitumen layer 2, the first tire basic unit 3, copper foil layer 4, second fetus basic unit 5, the second bitumen layer 6 and second separation layer 7, the waterproof roll that the embodiment of the present invention is provided, bitumen layer and tire basic unit to existing waterproof roll It is modified so that waterproof roll root-resistant puncturing degree in use is improved, and improves the waterproof of waterproof roll Degree.
Alternatively, the parts by weight of each component in step 1 are according to 60~80 parts of pitch；HDPE10~20 part；Miscella 5~10 parts of fat；3~6 parts of fire retardant；ZnO10~40 part；11~20 parts of chemical root resistance agent is prepared.
Alternatively, the temperature that 1# banburies set in step 1 is 85 DEG C~90 DEG C.
Preferably, pitch includes 200# road asphalts and 60# road asphalts, 200# road asphalts and 60# road asphalts Mixing ratio by weight example is 7：3, Mixing ratio by weight example is 7:When 3, the better performances of the first bitumen layer 2 and the second bitumen layer 6.
Alternatively, the material of the first tire basic unit 3 and second fetus basic unit 5 is in polyester fiber, glass fibre or composite fibre One or more.
Alternatively, the thickness of the waterproof roll of the application is 3mm~5mm, and the thickness with existing waterproof roll is protected substantially Hold consistent.Exemplarily, the thickness range of the first separation layer 1 and the second separation layer 7 is 0.1mm~0.3mm；First tire basic unit 3, The thickness range of second fetus basic unit 5 is 0.5~1.0mm；The thickness range of copper foil layer 4 is 0.05mm~0.1mm；First bitumen layer 2 and second bitumen layer 6 thickness range be 0.8mm~1.2mm.
Preferably, the first separation layer 1, the first bitumen layer 2, the first tire basic unit 3, copper foil layer 4, second fetus basic unit 5, second drip The thickness of the separation layer 7 of cyan layer 6 and second is respectively：When 0.2mm, 1.0mm, 0.8mm, 0.06mm, 0.8mm, 1.0mm, 0.2mm, The root-resistant puncturing best results of the waterproof roll of the application.
Alternatively, when the drying temperature in above-mentioned steps 7 is 55 DEG C~75 DEG C, can cause that waterproof roll dries rapidly It is dry, rapidly it is shaped to waterproof roll.
Although having been described for the preferred embodiment of the application, those skilled in the art once know basic creation Property concept, then can make other change and modification to these embodiments.So, appended claims are intended to be construed to include excellent Select embodiment and fall into having altered and changing for the application scope.Obviously, those skilled in the art can be to the application Various changes and modification are carried out without deviating from spirit and scope.So, if these modifications of the application and modification Belong within the scope of the application claim and its equivalent technologies, then the application is also intended to exist comprising these changes and modification It is interior.

Claims (10)

1. a kind of planted roof root resistant waterproof roll, it is characterised in that include successively from top to bottom：First separation layer, One bitumen layer, the first tire basic unit, copper foil layer, second fetus basic unit, the second bitumen layer and the second separation layer, wherein, the first bitumen layer Composition with the second bitumen layer is identical.
2. planted roof root resistant waterproof roll as claimed in claim 1, it is characterised in that the first bitumen layer and the second drip The composition of cyan layer, calculates by weight, including：60~80 parts of pitch；HDPE10~20 part；5~10 parts of compound lard；It is fire-retardant 3~6 parts of agent；ZnO10~40 part；11~20 parts of chemical root resistance agent.
3. planted roof root resistant waterproof roll as claimed in claim 1, it is characterised in that pitch includes the drip of 200# roads The Mixing ratio by weight example of blue or green and 60# road asphalts, 200# road asphalts and 60# road asphalts is 7：3.
4. planted roof root resistant waterproof roll as claimed in claim 1, it is characterised in that the first tire basic unit and second fetus The material of basic unit is one or more in polyester fiber, glass fibre or composite fibre.
5. planted roof root resistant waterproof roll as claimed in claim 1, it is characterised in that the thickness of waterproof roll is 3mm~5mm.
6. a kind of preparation method of planted roof root resistant waterproof roll, it is characterised in that comprise the following steps：
Step 1, pitch, HDPE, compound lard, fire retardant, ZnO and chemical root resistance agent are put into 1# banburies according to parts by weight Mixed, stirred；
Step 2, by the material stirred in 1# banburies by after extruder by mould extrusion forming, the material after shaping It is the blank of flat；
Step 3, the first tire basic unit, copper foil layer and second fetus basic unit are prolonged into machine roll-forming by rolling, obtain tire basic unit precast body；
Step 4, the mixed material obtained by 1# banburies and tire basic unit precast body are prolonged into machine rolling one-shot forming by rolling；
The first separation layer and the second separation layer are formed respectively on step 5, the upper surface of the material being combined in calendering and lower surface；
Step 6, the structure to being formed after step 5 carry out roll-in and roller cooling, form pitch band；
Step 7, the pitch band after spraying is dried, wound.
7. the preparation method of planted roof root resistant waterproof roll as claimed in claim 6, it is characterised in that in step 1 Each component parts by weight according to 60~80 parts of pitch；HDPE10~20 part；5~10 parts of compound lard；3~6 parts of fire retardant； ZnO10~40 part；11~20 parts of chemical root resistance agent is prepared.
8. the preparation method of planted roof root resistant waterproof roll as claimed in claim 6, it is characterised in that in step 1 The temperature that 1# banburies set is 85 DEG C~90 DEG C.
9. the preparation method of planted roof root resistant waterproof roll as claimed in claim 6, it is characterised in that pitch includes The Mixing ratio by weight example of 200# road asphalts and 60# road asphalts, 200# road asphalts and 60# road asphalts is 7：3.
10. the preparation method of planted roof root resistant waterproof roll as claimed in claim 6, it is characterised in that waterproof is rolled up The thickness of material is 3mm~5mm.
CN201710112094.5A 2017-02-28 2017-02-28 A kind of planted roof root resistant waterproof roll and preparation method thereof Withdrawn CN106863952A (en)