CN107187140A - A kind of root resistant waterproof roll and preparation method thereof - Google Patents
A kind of root resistant waterproof roll and preparation method thereof Download PDFInfo
- Publication number
- CN107187140A CN107187140A CN201710395526.8A CN201710395526A CN107187140A CN 107187140 A CN107187140 A CN 107187140A CN 201710395526 A CN201710395526 A CN 201710395526A CN 107187140 A CN107187140 A CN 107187140A
- Authority
- CN
- China
- Prior art keywords
- waterproof roll
- root
- layer
- pitch
- resistant waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of root resistant waterproof roll and preparation method thereof, it is related to field of waterproof materials, solves the technical problem of existing waterproof material root-resistant puncturing ability.The waterproof roll of the application includes successively from top to bottom：First separation layer, the first bitumen layer, the first tire basic unit, zine plate layer, the second bitumen layer and the second separation layer, wherein, the first bitumen layer is identical with the composition of the second bitumen layer.The present invention is used for the root-resistant puncturing ability for improving waterproof roll.
Description
Technical field
The present invention relates to waterproof material technical field, and in particular to a kind of root resistant waterproof roll and preparation method thereof.
Background technology
With the development and progress of society, planting on roof is widely used.Roof greening is increasingly
The concern of society is caused more.The extensive use of planting on roof, it is necessary to waterproof, the production of root-resistant puncturing coiled material,
High standards is given by construction enterprises.
But present waterproof roll bad adaptability, can not meet different roofings to the material waterproofing of waterproof roll, intensity,
The requirement of root-resistant puncturing, causes the phenomenon of the waterproof effect difference of construction wall or roofing.
The content of the invention
It is an object of the invention to provide a kind of root resistant waterproof roll and preparation method thereof, for improving waterproof roll
Root-resistant puncturing ability.
To reach above-mentioned purpose, root resistant waterproof roll provided by the present invention is adopted the following technical scheme that：
The root resistant waterproof roll includes successively from top to bottom：First separation layer, the first bitumen layer, the first tire basic unit,
Zine plate layer, the second bitumen layer and the second separation layer, wherein, the first bitumen layer is identical with the composition of the second bitumen layer.
Alternatively, the composition of the first bitumen layer and the second bitumen layer, is calculated by weight, including：32~36 parts of pitch；
SBS10~20 part；POE10~20 part；0.5~1 part of solubilizer；1~3 part of accelerator；2~5 parts of activating agent；Stabilizer 0.002
~0.004 part；1~1.4 part of root resistance agent.
Alternatively, pitch is 70# pitches.
Alternatively, the material of the first tire basic unit is the one or more in polyester fiber, glass fibre or composite fibre.
Alternatively, the thickness of waterproof roll is 3mm~5mm.
Waterproof roll provided by the present invention, on the basis of existing waterproof roll, adds zine plate layer, and to bitumen layer
It is modified so that waterproof roll has stronger impact resistance, oxidative resistance, is difficult to be worn by root system of plant during use
Thoroughly, good water-proof effect, service life are long.
In addition, present invention also offers a kind of preparation method of root resistant waterproof roll, the preparation method includes following
Step:
Step 1, according to parts by weight by pitch, SBS, POE, solubilizer, accelerator, activating agent, stabilizer and root resistance agent
It is put into agitator tank and is mixed, is stirred；
Step 2, by the material stirred in agitator tank by after extruder by mould extrusion forming, the thing after shaping
Expect the blank for flat；
Step 3, the first tire basic unit, zine plate layer prolonged into machine roll-forming by rolling, obtain tire basic unit precast body；
Step 4, mixed material and the tire basic unit precast body of gained in agitator tank are prolonged into machine by rolling roll one-shot forming；
Step 5, the upper surface for the material being combined in calendering isolate with forming the first separation layer and second on lower surface respectively
Layer；
Step 6, structure progress roll-in and roller cooling to being formed after step 5, form pitch band；
Step 7, the pitch band after spraying is dried, wound.
Alternatively, the parts by weight of each component in step 1 are according to 32~36 parts of pitch；SBS10~20 part；POE10~
20 parts；0.5~1 part of solubilizer；1~3 part of accelerator；2~5 parts of activating agent；0.002~0.004 part of stabilizer；Root resistance agent 1~
1.4 parts are prepared.
Alternatively, temperature when pitch is added in agitator tank in step 1 is 180 DEG C.
Alternatively, pitch is 70# pitches.
Alternatively, the thickness of waterproof roll is 3mm~5mm.
The preparation method of root resistant waterproof roll provided by the present invention, the waterproof roll of formation is wrapped successively from top to bottom
Include：First separation layer, the first bitumen layer, the first tire basic unit, zine plate layer, the second bitumen layer and the second separation layer, the first tire basic unit
New tire basic unit is formed with zine plate layer combination, and bitumen layer is modified so that waterproof roll has stronger shock resistance
Property, oxidative resistance, be difficult to be penetrated by root system of plant during use, good water-proof effect, service life it is long.
Brief description of the drawings
, below will be to embodiment or existing in order to illustrate more clearly of the embodiment of the present application or technical scheme of the prior art
There is the accompanying drawing used required in technology description to be briefly described, it should be apparent that, drawings in the following description are only this
Some embodiments described in application, for those of ordinary skill in the art, can also obtain other according to these accompanying drawings
Accompanying drawing.
Fig. 1 is the structural representation of the root resistant waterproof roll of the embodiment of the present invention.
Description of reference numerals：
1-the first separation layer；2-the first bitumen layer；3-the first tire basic unit；4-zine plate layer；5-the second bitumen layer；6—
Second separation layer.
Embodiment
With reference to the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Ground is described, it is clear that described embodiment is a part of embodiment of the invention, rather than whole embodiments.Based on the present invention
In embodiment, the every other implementation that those of ordinary skill in the art are obtained under the premise of creative work is not made
Example, belongs to the scope of protection of the invention.
Embodiment one
The embodiments of the invention provide a kind of root resistant waterproof roll, Fig. 1 is that the root-resistant puncturing of the embodiment of the present invention is prevented
The structural representation of water coiled material, as shown in figure 1, the waterproof roll includes successively from top to bottom：First separation layer 1, the first pitch
The 2, first tire basic unit 3 of layer, zine plate the 4, second bitumen layer 5 of layer and the second separation layer 6.Wherein, the first bitumen layer 2 and the second bitumen layer
5 composition is identical.
Waterproof roll provided by the present invention, on the basis of existing waterproof roll, adds zine plate layer 4, and to pitch
Layer is modified so that waterproof roll has stronger impact resistance, oxidative resistance, is difficult during use by root system of plant
Penetrate, good water-proof effect, service life it is long.
Preferably, the composition of the first bitumen layer 2 and the second bitumen layer 5, is calculated by weight, including：Pitch 32~36
Part；SBS10~20 part；POE10~20 part；0.5~1 part of solubilizer；1~3 part of accelerator；2~5 parts of activating agent；Stabilizer
0.002~0.004 part；1~1.4 part of root resistance agent.Exemplarily, solubilizer is naphthenic rubber oil or aromatic radical rubber oil；Promote
Enter agent for M, i.e. 2- benzothiazolyl mercaptans；Activating agent is stearic acid；Stabilizer is sulphur powder；Root resistance agent is cupric oxide powder
End.SBS, POE are added in pitch, and solubilizer and accelerator cause SBS, POE are evengranular to be dispersed in pitch, activating agent
Coordinate with stabilizer so that SBS and POE macromolecules cross-linkings, constitutionally stable mixture is mixed to form with pitch；Root resistance agent can
Suppress root system of plant and penetrate bitumen layer, making the root-resistant puncturing ability of waterproof roll is improved.
Alternatively, pitch is 70# pitches, and softening point temperature is high, and the higher area of preference temperature is used, and 70# pitches
Cost is low, can reduce the production cost of waterproof roll.
Exemplarily, the first bitumen layer 2 and the second bitumen layer 5 are according to parts by weight：34 parts of pitch；SBS10 parts；POE12
Part；0.8 part of solubilizer；2 parts of accelerator；3 parts of activating agent；0.004 part of stabilizer；When 1.19 parts of root resistance agent is prepared, gained
Mixture composition the first bitumen layer 2 and the second bitumen layer 5 root-resistant puncturing degree it is preferable.
Alternatively, the material of the first tire basic unit 3 is the one or more in polyester fiber, glass fibre or composite fibre.
Preferably, zine plate layer 4 improves the root-resistant puncturing degree of planted roof root resistant waterproof roll, improves waterproof
The water resistance of coiled material.Zine plate can have good dimensional stability, be difficult for synthesis zine plate or synthesis zinc paper tinsel, synthesis zine plate
Corrosion, and there is good normal temperature mechanical performance and wearability at normal temperatures so that the root-resistant puncturing degree of bitumen layer is carried
Height, improves the waterproof degree of waterproof roll.
Alternatively, the thickness of waterproof roll is 3mm~5mm, is consistent substantially with the thickness of existing waterproof roll.
The root resistant waterproof roll of the present invention, on the one hand, add SBS, POE in modified asphalt layer so that waterproof is rolled up
The dimensional stability of material is improved, and extends the service life of waterproof roll；On the one hand, work is added in modified asphalt layer
Property agent, stabilizer and root resistance agent so that bitumen layer SBS and POE formation crosslinking, increase the tensile strength of modified asphalt layer,
Root-resistant puncturing ability is improved, and improves the water resistance of waterproof roll；On the other hand, the addition of zine plate layer 4 so that waterproof roll
Root-resistant puncturing degree improve, improve the water resistance of waterproof roll.
Embodiment two
The embodiments of the invention provide a kind of preparation method of root resistant waterproof roll, this method comprises the following steps：
Step 1, according to parts by weight by pitch, SBS, POE, solubilizer, accelerator, activating agent, stabilizer and root resistance agent
It is put into agitator tank and is mixed, is stirred；
Step 2, by the material stirred in agitator tank by after extruder by mould extrusion forming, the thing after shaping
Expect the blank for flat；
Step 3, the first tire basic unit 3, zine plate layer 4 prolonged into machine roll-forming by rolling, obtain tire basic unit precast body；
Step 4, mixed material and the tire basic unit precast body of gained in agitator tank are prolonged into machine by rolling roll one-shot forming；
Step 5, the upper surface for the material being combined in calendering isolate with forming the first separation layer 1 and second on lower surface respectively
Layer 6；
Step 6, structure progress roll-in and roller cooling to being formed after step 5, form pitch band；
Step 7, the pitch band after spraying is dried, wound.
The preparation method of root resistant waterproof roll provided by the present invention, the waterproof roll of formation is wrapped successively from top to bottom
Include：First separation layer 1, the first bitumen layer 2, the first tire basic unit 3, zine plate the 4, second bitumen layer 5 of layer and the second separation layer 6, this hair
The waterproof roll that bright embodiment is provided, bitumen layer and tire basic unit to existing waterproof roll are modified so that waterproof is rolled up
The root-resistant puncturing degree of material in use is improved, and improves the waterproof degree of waterproof roll.
Alternatively, the parts by weight of each component in step 1 are according to 32~36 parts of pitch；SBS10~20 part；POE10~
20 parts；0.5~1 part of solubilizer；1~3 part of accelerator；2~5 parts of activating agent；0.002~0.004 part of stabilizer；Root resistance agent 1~
1.4 parts are prepared.
Alternatively, temperature when pitch is added in agitator tank in step 1 is 180 DEG C.
Preferably, when pitch is 70# pitches, the better performances of the first bitumen layer 2 and the second bitumen layer 5.
Alternatively, the material of the first tire basic unit 3 is the one or more in polyester fiber, glass fibre or composite fibre.
Alternatively, the thickness of the waterproof roll of the application is 3mm~5mm, is protected substantially with the thickness of existing waterproof roll
Hold consistent.Exemplarily, the thickness range of the first separation layer 1 and the second separation layer 6 is 0.3mm~0.5mm；First tire basic unit 3
Thickness range be 0.7~1.2mm；The thickness range of zine plate layer 4 is 0.05mm~0.1mm；First bitumen layer 2 and the second pitch
The thickness range of layer 5 is 0.8mm~1.5mm.
Preferably, the first separation layer 1, the first bitumen layer 2, the first tire basic unit 3, zine plate the 4, second bitumen layer 5 and second of layer
The thickness of separation layer 6 is respectively：When 0.4mm, 1.0mm, 0.8mm, 0.08mm, 1.0mm, 0.4mm, the waterproof roll of the application
Root-resistant puncturing best results.
Alternatively, when the drying temperature in above-mentioned steps 7 is 55 DEG C~75 DEG C, waterproof roll can be dried rapidly
It is dry, rapidly it is shaped to waterproof roll.
Although having been described for the preferred embodiment of the application, those skilled in the art once know basic creation
Property concept, then can make other change and modification to these embodiments.So, appended claims are intended to be construed to include excellent
Select embodiment and fall into having altered and changing for the application scope.Obviously, those skilled in the art can be to the application
Various changes and modification are carried out without departing from spirit and scope.So, if these modifications and variations of the application
Belong within the scope of the application claim and its equivalent technologies, then the application is also intended to exist comprising these changes and modification
It is interior.
Claims (10)
1. a kind of root resistant waterproof roll, it is characterised in that include successively from top to bottom：First separation layer, the first bitumen layer,
First tire basic unit, zine plate layer, the second bitumen layer and the second separation layer, wherein, the composition phase of the first bitumen layer and the second bitumen layer
Together.
2. root resistant waterproof roll as claimed in claim 1, it is characterised in that the group of the first bitumen layer and the second bitumen layer
Into, calculate by weight, including：32~36 parts of pitch；SBS10~20 part；POE10~20 part；0.5~1 part of solubilizer；Promote
Enter 1~3 part of agent；2~5 parts of activating agent；0.002~0.004 part of stabilizer；1~1.4 part of root resistance agent.
3. root resistant waterproof roll as claimed in claim 1, it is characterised in that pitch is 70# pitches.
4. root resistant waterproof roll as claimed in claim 1, it is characterised in that the material of the first tire basic unit is that polyester is fine
One or more in dimension, glass fibre or composite fibre.
5. root resistant waterproof roll as claimed in claim 1, it is characterised in that the thickness of waterproof roll is 3mm~5mm.
6. a kind of preparation method of root resistant waterproof roll, it is characterised in that comprise the following steps：
Step 1, according to parts by weight pitch, SBS, POE, solubilizer, accelerator, activating agent, stabilizer and root resistance agent are put into
Mixed, stirred in agitator tank；
Step 2, by the material stirred in agitator tank by the way that, by mould extrusion forming, the material after shaping is after extruder
The blank of flat；
Step 3, the first tire basic unit, zine plate layer prolonged into machine roll-forming by rolling, obtain tire basic unit precast body；
Step 4, mixed material and the tire basic unit precast body of gained in agitator tank are prolonged into machine by rolling roll one-shot forming；
The first separation layer and the second separation layer are formed respectively on step 5, the upper surface for the material being combined in calendering and lower surface；
Step 6, structure progress roll-in and roller cooling to being formed after step 5, form pitch band；
Step 7, the pitch band after spraying is dried, wound.
7. the preparation method of root resistant waterproof roll as claimed in claim 6, it is characterised in that each component in step 1
Parts by weight according to 32~36 parts of pitch；SBS10~20 part；POE10~20 part；0.5~1 part of solubilizer；Accelerator 1~3
Part；2~5 parts of activating agent；0.002~0.004 part of stabilizer；1~1.4 part of root resistance agent is prepared.
8. the preparation method of root resistant waterproof roll as claimed in claim 6, it is characterised in that in step 1 in agitator tank
Temperature when pitch is added is 180 DEG C.
9. the preparation method of root resistant waterproof roll as claimed in claim 6, it is characterised in that pitch is 70# pitches.
10. the preparation method of root resistant waterproof roll as claimed in claim 6, it is characterised in that the thickness of waterproof roll
For 3mm~5mm.