CN106827703A - Macromolecule viscosity waterproof roll - Google Patents

Macromolecule viscosity waterproof roll Download PDF

Info

Publication number
CN106827703A
CN106827703A CN201611073689.6A CN201611073689A CN106827703A CN 106827703 A CN106827703 A CN 106827703A CN 201611073689 A CN201611073689 A CN 201611073689A CN 106827703 A CN106827703 A CN 106827703A
Authority
CN
China
Prior art keywords
layer
waterproof roll
layers
downside
modified asphalt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201611073689.6A
Other languages
Chinese (zh)
Other versions
CN106827703B (en
Inventor
刘冠麟
樊哲新
黎家国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yunnan Glad City Defence Water Science And Technology Ltd
Original Assignee
Yunnan Glad City Defence Water Science And Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yunnan Glad City Defence Water Science And Technology Ltd filed Critical Yunnan Glad City Defence Water Science And Technology Ltd
Priority to CN201611073689.6A priority Critical patent/CN106827703B/en
Publication of CN106827703A publication Critical patent/CN106827703A/en
Application granted granted Critical
Publication of CN106827703B publication Critical patent/CN106827703B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention belongs to waterproof roll field, specifically related to a kind of macromolecule viscosity waterproof roll, including tire basic unit, the first modified asphalt layer is provided with the upside of the tire basic unit, nonwoven layer is provided with the upside of first modified asphalt layer, separating film layer is provided with the upside of the nonwoven layer, SBR layers is provided with the upside of the separating film layer, the second modified asphalt layer is provided with the downside of the tire basic unit, PVC alloy-layers are provided with the downside of second modified asphalt layer, SBS layers is provided with the downside of the PVC alloy-layers, described SBS layers downside is provided with fiberglass cloth, polyvinyl acetate layer is provided with the downside of the fiberglass cloth.The waterproof roll tensile strength is high, and self-healing ability and root puncture resistant ability are strong, long service life.

Description

Macromolecule viscosity waterproof roll
Technical field
The invention belongs to waterproof roll field, and in particular to a kind of macromolecule viscosity waterproof roll.
Background technology
Waterproof roll is mainly used for construction wall, roofing and tunnel, highway, refuse landfill etc., plays and resists A kind of rollable flexible building material product into web-like of extraneous rainwater, underground water seepage, as between engineering foundation and building Ne-leakage is connected, and is first barrier of whole engineering waterproofing, and vital effect is played to whole engineering.Waterproof roll is Pitch class or high score subclass waterproof material are immersed in what is be fabricated on carcass.The tear-proof of waterproof roll of the prior art, Puncture resistant is indifferent, have impact on the overall water proofing property durability of waterproof roll.
Authorized announcement date is on 2 20th, 2013, and Authorization Notice No. is the Chinese utility model patent of CN202742739U, A kind of planted roof root puncture waterproof roll is disclosed, the two sides of the compound plies of the Copper Foil are respectively equipped with SBS modified pitch Layer, the outer surface of the SBS modified asphalt layers is provided with overcoat；The SBS modified asphalt layers are by being added with chemical root resistance agent SBS modified pitch composition.The waterproof roll has waterproof and prevents the dual-use function of plant root puncture, but its tear-proof, Self-healing property, acid and alkali-resistance and resistance to chemical corrosion are poor.
Shen Qing Publication day is on March 25th, 2015, and application publication number is the Chinese invention patent application of CN104441859A, A kind of waterproof roll, including waterproof layer are disclosed, the upper and lower surface of waterproof layer is respectively equipped with acupuncture nonwoven polypropylene fabric layer, lower pin Thorn nonwoven polypropylene fabric layer；Upper acupuncture nonwoven polypropylene fabric layer is provided with heat-insulation layer, and heat-insulation layer is provided with aluminium foil layer；Lower acupuncture polypropylene fibre without The lower surface for spinning layer of cloth is provided with SBS modified asphalt layers, and the lower surface of SBS modified asphalt layers is provided with anti-aging layer.The invention strengthens The resistance performance of waterproof roll and extend service life, but its tensile strength, puncture resistance are unsatisfactory.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of macromolecule viscosity waterproof roll, is used to improve waterproof roll Tensile strength and puncture resistance.
In order to solve the above-mentioned technical problem, the technical scheme is that：
Macromolecule viscosity waterproof roll, including tire basic unit, are provided with the first modified asphalt layer on the upside of the tire basic unit, described Nonwoven layer is provided with the upside of first modified asphalt layer, separating film layer, the separating film layer are provided with the upside of the nonwoven layer Upside be provided with SBR (butadiene-styrene rubber) layer, the second modified asphalt layer, second modified pitch are provided with the downside of the tire basic unit The downside of layer is provided with PVC alloy-layers, and SBS (s-B-S block copolymerizations are provided with the downside of the PVC alloy-layers Thing) layer, it is provided with fiberglass cloth, the glass on the downside of SBS (SBS) layer Polyvinyl acetate layer is provided with the downside of glass scrim cloth.
In the macromolecule viscosity waterproof roll that the present invention is provided, it is preferable that the tire basic unit is plant bast fiber layer. The plant bast fiber can be selected from flax, hemp, ramie and jute etc., or sisal fiber.Plant bast fiber The characteristics of with anti-corrosion, wear-resisting, tough and tensile, anti-aging, stretch-proof and long lifespan.Can be increased from plant bast fiber Zuo Tai basic units Plus tensile strength, the service life of extension waterproof roll of waterproof roll.
In the macromolecule viscosity waterproof roll that the present invention is provided, it is preferable that the barrier film is PP or PE films.
In the macromolecule viscosity waterproof roll that the present invention is provided, it is preferable that the separating film layer and SBR (butadiene-styrene rubber) Biological stopping area is additionally provided between layer.
In the macromolecule viscosity waterproof roll that the present invention is provided, it is preferable that the nonwoven layer is polyester felt foundation. The polyester felt foundation has the effect of chemical root resistance.
In the macromolecule viscosity waterproof roll that the present invention is provided, it is preferable that set on the upside of SBR (butadiene-styrene rubber) layer It is equipped with flame-retardant layer；It is further preferred that the flame-retardant layer is fire-retardant polyphosphoric acid amine or flame-retardant acrylic fibre or fire resistance fibre or fire-retardant ring Oxygen tree fat.Flame-retardant layer is provided with waterproof roll so that waterproof roll also has fireproof performance.
In the macromolecule viscosity waterproof roll that the present invention is provided, it is preferable that in the biological stopping area and separating film layer Between be provided with the 3rd modified asphalt layer and the first Copper Foil, first Copper Foil is located at the upside of the 3rd modified asphalt layer； It is further preferred that being additionally provided with self-adhesive layer on the downside of the polyvinyl acetate layer.Biological stopping area and the first Copper Foil are combined, more Effective root puncture resistant.
In the macromolecule viscosity waterproof roll that the present invention is provided, it is preferable that in the polyvinyl acetate layer and self-adhesion The second Copper Foil is additionally provided between layer.The second Copper Foil for setting herein has the effect that termite-proof, preventing microorganism corrodes.
Using above-mentioned technical proposal, due to using plant bast fiber Zuo Tai basic units, increased the stretch-proof of waterproof roll The service life of intensity and extension waterproof roll；Three layers of modified asphalt layer are provided with waterproof roll, waterproof roll is increased Self-healing ability；The combination of nonwoven layer, biological stopping area and the first Copper Foil, improves the root puncture resistant ability of waterproof roll.
Brief description of the drawings
Fig. 1 is the structural representation of the macromolecule viscosity waterproof roll of one embodiment in the present invention；
Fig. 2 is the structural representation of the macromolecule viscosity waterproof roll of another embodiment in the present invention；
In figure：1- plants bast fiber layer, the modified asphalt layers of 2- first, 3- polyester oil carpet veneers, 41-PP film layers, 42-PE Film layer, 5-SBR layers, the modified asphalt layers of 6- second, 7-PVC alloy-layers, 8-SBS layers, 9- glass layers, 10- polyvinyl acetates Ester layer, the fire-retardant polyacids amine layer of 11-, 12- biology stopping areas, the modified asphalt layers of 13- the 3rd, the Copper Foils of 14- first, the Copper Foils of 15- second, 16- self-adhesive layers.
Specific embodiment
Specific embodiment of the invention is described further below in conjunction with the accompanying drawings.Herein it should be noted that for The explanation of these implementation methods is used to help understand the present invention, but does not constitute limitation of the invention.Additionally, disclosed below As long as each implementation method of the invention in involved technical characteristic do not constitute conflict each other and can just be mutually combined.
Embodiment 1
A kind of macromolecule viscosity waterproof roll is present embodiments provided, as shown in figure 1, include plant bast fiber layer 1, The upside of plant bast fiber layer 1 is provided with the first modified asphalt layer 2, and the upside of the first modified asphalt layer 2 is provided with polyester malthoid base Layer 31, PP film layers 41 are provided with the upside of polyester malthoid basic unit 31, and the upside of PP film layers 41 is provided with SBR layers 5, plant bast fiber The downside of layer 1 is provided with the second modified asphalt layer 6, and the downside of the second modified asphalt layer 6 is provided with PVC alloy-layers 7, in PVC alloy-layers 7 Downside be provided with SBS layers 8, be provided with fiberglass cloth 9 SBS layers 8 of downside, be provided with poly- in the downside of fiberglass cloth 9 Vinyl acetate 10.
Embodiment 2
A kind of macromolecule viscosity waterproof roll is present embodiments provided, as shown in Fig. 2 include plant bast fiber layer 1, The upside of plant bast fiber layer 1 is provided with the first modified asphalt layer 2, and the upside of the first modified asphalt layer 2 is provided with polyester malthoid base Layer 3, PE film layers 42 are provided with the upside of polyester malthoid basic unit 3, and the upside of PE film layers 42 is provided with SBR layers 5, SBR layers 5 of upside Fire-retardant polyacids amine layer 11 is provided with, biological stopping area 12 is provided between PE film layers 42 and fire-retardant polyacids amine layer 11, in PE films The 3rd modified asphalt layer 13 and the first Copper Foil 14 are provided between 42 layers and biological stopping area 12, the first Copper Foil 14 changes positioned at the 3rd Property bitumen layer 13 upside, plant bast fiber layer 1 downside be provided with the second modified asphalt layer 6, the second modified asphalt layer 6 Downside is provided with PVC alloy-layers 7, and SBS layers 8 is provided with the downside of PVC alloy-layers 7, and glass fabric is provided with SBS layers 8 of downside Layer 9, polyvinyl acetate layer 10 is provided with the downside of fiberglass cloth 9, is provided with certainly in the downside of polyvinyl acetate layer 10 Adhesion coating 16, is additionally provided with the second Copper Foil 15 between polyvinyl acetate layer 10 and self-adhesive layer 16.
Comparative example 1
Mylar will be changed in plant bast fiber layer 1 in embodiment 1, remaining is consistent with embodiment 1.
Comparative example 2
Without the second modified asphalt layer 6, remaining is consistent with embodiment 1.
Comparative example 3
Without the second modified asphalt layer 6 and the 3rd modified asphalt layer 13, remaining is consistent with embodiment 2.
Comparative example 4
Without the first Copper Foil 14, remaining is consistent with embodiment 2.
Comparative example 5
The Copper Foil 14 of inanimate object stopping area 12 and first, remaining is consistent with embodiment 2.
Test example
In order to verify technique effect of the invention, spy does following inspection：
As can be seen from the above table, the tensile strength of the product in comparative example 1 either laterally will be much small or longitudinal In other products, elongation percentage and tearing strength are also far smaller than other products during its maximum pull.Therefore, plant bast fiber Elongation percentage and tearing strength when significantly improving tensile strength, the maximum pull of waterproof roll.
The puncture resistant ability of embodiment 2 and comparative example 3 is most strong, is secondly embodiment and comparative example 4, followed by comparative example 1 With 2, the puncture resistant ability of comparative example 5 is worst, therefore, the combination of nonwoven layer, biological stopping area and the first Copper Foil can be notable Raising waterproof roll puncture resistant ability.
Embodiment 2, the self-healing time of comparative example 4 and 5 are substantially less than embodiment 1, wherein comparative example 1,2 and 3, comparative example 3 self-healing time is most long.Therefore, the second modified asphalt layer and the 3rd modified asphalt layer improve the self-healing energy of waterproof roll Power.
Embodiments of the present invention are explained in detail above in association with accompanying drawing, but the invention is not restricted to described implementation Mode.For a person skilled in the art, in the case where the principle of the invention and spirit is not departed from, to these implementation methods Various changes, modification, replacement and modification are carried out, is still fallen within protection scope of the present invention.

Claims (10)

1. macromolecule viscosity waterproof roll, it is characterised in that including tire basic unit, the first modified drip is provided with the upside of the tire basic unit Cyan layer, is provided with nonwoven layer on the upside of first modified asphalt layer, separating film layer is provided with the upside of the nonwoven layer, described SBR layers is provided with the upside of separating film layer, the second modified asphalt layer, second modified asphalt layer are provided with the downside of the tire basic unit Downside be provided with PVC alloy-layers, SBS layers is provided with the downside of the PVC alloy-layers, described SBS layers downside is provided with glass fibre Layer of cloth, polyvinyl acetate layer is provided with the downside of the fiberglass cloth.
2. macromolecule according to claim 1 viscosity waterproof roll, it is characterised in that the tire basic unit is fine plant bast Dimension layer.
3. macromolecule according to claim 1 viscosity waterproof roll, it is characterised in that the barrier film is PP or PE films.
4. macromolecule according to claim 1 viscosity waterproof roll, it is characterised in that the separating film layer and SBR layers Between be additionally provided with biological stopping area.
5. macromolecule according to claim 1 viscosity waterproof roll, it is characterised in that the nonwoven layer is polyester malthoid Base fabric.
6. the sticky waterproof roll of macromolecule according to any one of Claims 1 to 5, it is characterised in that described SBR layers is upper Side is provided with flame-retardant layer.
7. macromolecule according to claim 6 viscosity waterproof roll, it is characterised in that the flame-retardant layer is fire-retardant polyphosphoric acid Amine or flame-retardant acrylic fibre or fire resistance fibre or fire retarding epoxide resin.
8. macromolecule according to claim 6 viscosity waterproof roll, it is characterised in that in the biological stopping area and isolation The 3rd modified asphalt layer and the first Copper Foil are provided between film layer, first Copper Foil is located at the upper of the 3rd modified asphalt layer Side.
9. macromolecule according to claim 8 viscosity waterproof roll, it is characterised in that under the polyvinyl acetate layer Side is additionally provided with self-adhesive layer.
10. macromolecule according to claim 9 viscosity waterproof roll, it is characterised in that in the polyvinyl acetate layer The second Copper Foil is additionally provided with and self-adhesive layer between.
CN201611073689.6A 2016-11-29 2016-11-29 Macromolecule viscosity waterproof roll Active CN106827703B (en)