CN106827703B - Macromolecule viscosity waterproof roll - Google Patents
Macromolecule viscosity waterproof roll Download PDFInfo
- Publication number
- CN106827703B CN106827703B CN201611073689.6A CN201611073689A CN106827703B CN 106827703 B CN106827703 B CN 106827703B CN 201611073689 A CN201611073689 A CN 201611073689A CN 106827703 B CN106827703 B CN 106827703B
- Authority
- CN
- China
- Prior art keywords
- layer
- waterproof roll
- upside
- downside
- modified asphalt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to waterproof roll fields, more particularly to a kind of macromolecule viscosity waterproof roll, including tire base, the upside of the tire base is equipped with the first modified asphalt layer, the upside of first modified asphalt layer is equipped with nonwoven layer, the upside of the nonwoven layer is equipped with separating film layer, the upside of the separating film layer is equipped with SBR layers, the downside of the tire base is equipped with the second modified asphalt layer, the downside of second modified asphalt layer is equipped with PVC alloy-layer, the downside of the PVC alloy-layer is equipped with SBS layers, SBS layers of the downside is equipped with fiberglass cloth, the downside of the fiberglass cloth is equipped with polyvinyl acetate layer.The waterproof roll tensile strength is high, and self-healing ability and root puncture resistant ability are strong, long service life.
Description
Technical field
The invention belongs to waterproof roll fields, and in particular to a kind of macromolecule viscosity waterproof roll.
Background technique
Waterproof roll is mainly used for construction wall, roofing and tunnel, highway, refuse landfill etc., plays and resists
The rollable flexible building material product at web-like of one kind of extraneous rainwater, underground water leakage, as between engineering foundation and building
Ne-leakage connection, is the first barrier of entire engineering waterproofing, plays a crucial role to entire engineering.Waterproof roll is
Pitch class or high score subclass waterproof material be immersed in and is fabricated on carcass.The tear-proof of waterproof roll in the prior art,
Puncture resistant is indifferent, affects the waterproofness durability of waterproof roll entirety.
Authorized announcement date is on 2 20th, 2013, and Authorization Notice No. is the Chinese utility model patent of CN202742739U,
A kind of planted roof root puncture waterproof roll is disclosed, the two sides of the compound plies of copper foil are respectively equipped with SBS modified pitch
The outer surface of layer, the SBS modified asphalt layer is equipped with protective layer;The SBS modified asphalt layer is by added with chemical root resistance agent
SBS modified pitch composition.The waterproof roll has waterproof and prevents the dual function of plant root puncture, but its tear-proof,
Self-healing property, acid and alkali-resistance and resistance to chemical corrosion are poor.
Data of publication of application is on March 25th, 2015, and application publication number is the Chinese invention patent application of CN104441859A,
A kind of waterproof roll, including waterproof layer are disclosed, the upper and lower surface of waterproof layer is respectively equipped with needle thorn nonwoven polypropylene fabric layer, knit stitch
Pierce nonwoven polypropylene fabric layer;Upper needle thorn nonwoven polypropylene fabric layer is equipped with insulating layer, and insulating layer is equipped with aluminium foil layer;Knit stitch pierce polypropylene fibre without
The lower surface of woven fabric layer is equipped with SBS modified asphalt layer, and the lower surface of SBS modified asphalt layer is equipped with anti-aging layer.Invention enhancing
The resistance performance of waterproof roll and extend service life, but its tensile strength, puncture resistance are unsatisfactory.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of macromolecule viscosity waterproof rolls, to improve waterproof roll
Tensile strength and puncture resistance.
In order to solve the above-mentioned technical problem, the technical solution of the present invention is as follows:
Macromolecule viscosity waterproof roll, including tire base, the upside of the tire base is equipped with the first modified asphalt layer, described
The upside of first modified asphalt layer is equipped with nonwoven layer, and the upside of the nonwoven layer is equipped with separating film layer, the separating film layer
Upside be equipped with SBR (butadiene-styrene rubber) layer, the downside of the tire base is equipped with the second modified asphalt layer, second modified pitch
The downside of layer is equipped with PVC alloy-layer, and the downside of the PVC alloy-layer is equipped with SBS (s-B-S block copolymerization
Object) layer, the downside of SBS (Styrene-Butadiene-Styrene Block Copolymer) layer is equipped with fiberglass cloth, the glass
The downside of glass scrim cloth is equipped with polyvinyl acetate layer.
In macromolecule viscosity waterproof roll provided by the invention, it is preferable that the tire base is plant bast fiber layer.
The plant bast fiber can be also possible to sisal fiber selected from flax, hemp, ramie and jute etc..Plant bast fiber
Have the characteristics that anti-corrosion, wear-resisting, tough and tensile, anti-aging, stretch-proof and service life are long.Select plant bast fiber Zuo Tai base that can increase
Add the tensile strength of waterproof roll, extend the service life of waterproof roll.
In macromolecule viscosity waterproof roll provided by the invention, it is preferable that the isolation film is PP or PE film.
In macromolecule viscosity waterproof roll provided by the invention, it is preferable that the separating film layer and SBR (butadiene-styrene rubber)
Biological stopping area is additionally provided between layer.
In macromolecule viscosity waterproof roll provided by the invention, it is preferable that the nonwoven layer is polyester felt foundation.
The polyester felt foundation has the function of chemical root resistance.
In macromolecule viscosity waterproof roll provided by the invention, it is preferable that set on the upside of SBR (butadiene-styrene rubber) layer
It is equipped with flame-retardant layer;It is further preferred that the flame-retardant layer is fire-retardant polyphosphoric acid amine or flame-retardant acrylic fibre or fire resistance fibre or fire-retardant ring
Oxygen resin.Flame-retardant layer is provided in waterproof roll, so that waterproof roll also has fireproof performance.
In macromolecule viscosity waterproof roll provided by the invention, it is preferable that in the biological stopping area and separating film layer
Between be provided with third modified asphalt layer and the first copper foil, first copper foil is located at the upside of the third modified asphalt layer;
It is further preferred that being additionally provided with self-adhesive layer on the downside of the polyvinyl acetate layer.Biological stopping area and the first copper foil combine, more
Effective root puncture resistant.
In macromolecule viscosity waterproof roll provided by the invention, it is preferable that in the polyvinyl acetate layer and self-adhesion
The second copper foil is additionally provided between layer.The second copper foil being arranged herein has the function of that termite-proof, preventing microorganism corrodes.
By adopting the above technical scheme, due to using plant bast fiber Zuo Tai base, the stretch-proof of waterproof roll is increased
Intensity and the service life for extending waterproof roll;It is provided with three layers of modified asphalt layer in waterproof roll, increases waterproof roll
Self-healing ability;The combination of nonwoven layer, biological stopping area and the first copper foil, improves the root puncture resistant ability of waterproof roll.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of the macromolecule viscosity waterproof roll of one embodiment in the present invention;
Fig. 2 is the structural schematic diagram of the macromolecule viscosity waterproof roll of another embodiment in the present invention;
In figure: 1- plant bast fiber layer, the first modified asphalt layer of 2-, 3- polyester oil carpet veneer, 41-PP film layer, 42-PE
Film layer, 5-SBR layers, the second modified asphalt layer of 6-, 7-PVC alloy-layer, 8-SBS layers, 9- glass layer, 10- polyvinyl acetate
Ester layer, the fire-retardant polyacids amine layer of 11-, 12- biology stopping area, 13- third modified asphalt layer, the first copper foil of 14-, the second copper foil of 15-,
16- self-adhesive layer.
Specific embodiment
Specific embodiments of the present invention will be further explained with reference to the accompanying drawing.It should be noted that for
The explanation of these embodiments is used to help understand the present invention, but and does not constitute a limitation of the invention.In addition, disclosed below
The each embodiment of the present invention involved in technical characteristic can be combined with each other as long as they do not conflict with each other.
Embodiment 1
A kind of macromolecule viscosity waterproof roll is present embodiments provided, as shown in Figure 1, include plant bast fiber layer 1,
The upside of plant bast fiber layer 1 is equipped with the first modified asphalt layer 2, and the upside of the first modified asphalt layer 2 is equipped with polyester malthoid base
Layer 31 is equipped with PP film layer 41 in the upside of polyester malthoid base 31, and the upside of PP film layer 41 is equipped with SBR layer 5, plant bast fiber
The downside of layer 1 is equipped with the second modified asphalt layer 6, and the downside of the second modified asphalt layer 6 is equipped with PVC alloy-layer 7, in PVC alloy-layer 7
Downside be equipped with SBS layer 8, the downside of SBS layer 8 be equipped with fiberglass cloth 9, the downside of fiberglass cloth 9 equipped with gather
Vinyl acetate 10.
Embodiment 2
A kind of macromolecule viscosity waterproof roll is present embodiments provided, as shown in Fig. 2, include plant bast fiber layer 1,
The upside of plant bast fiber layer 1 is equipped with the first modified asphalt layer 2, and the upside of the first modified asphalt layer 2 is equipped with polyester malthoid base
Layer 3 is equipped with PE film layer 42 in the upside of polyester malthoid base 3, and the upside of PE film layer 42 is equipped with SBR layer 5, in the upside of SBR layer 5
It is provided with fire-retardant polyacids amine layer 11, biological stopping area 12 is provided between PE film layer 42 and fire-retardant polyacids amine layer 11, in PE film
It is provided with third modified asphalt layer 13 and the first copper foil 14 between 42 layers and biological stopping area 12, the first copper foil 14 changes positioned at third
Property bitumen layer 13 upside, the downside of plant bast fiber layer 1 be equipped with the second modified asphalt layer 6, the second modified asphalt layer 6
Downside is equipped with PVC alloy-layer 7, is equipped with SBS layer 8 in the downside of PVC alloy-layer 7, is equipped with glass fabric in the downside of SBS layer 8
Layer 9 is equipped with polyvinyl acetate layer 10 in the downside of fiberglass cloth 9, is equipped with certainly in the downside of polyvinyl acetate layer 10
Adhesion coating 16 is additionally provided with the second copper foil 15 between polyvinyl acetate layer 10 and self-adhesive layer 16.
Comparative example 1
It will be changed to mylar in plant bast fiber layer 1 in embodiment 1, remaining is consistent with embodiment 1.
Comparative example 2
Without the second modified asphalt layer 6, remaining is consistent with embodiment 1.
Comparative example 3
Without the second modified asphalt layer 6 and third modified asphalt layer 13, remaining is consistent with embodiment 2.
Comparative example 4
Without the first copper foil 14, remaining is consistent with embodiment 2.
Comparative example 5
Inanimate object stopping area 12 and the first copper foil 14, remaining is consistent with embodiment 2.
Test example
In order to verify technical effect of the invention, spy does following inspection:
As can be seen from the above table, the tensile strength of the product in comparative example 1 either laterally will be much small or longitudinal
Elongation percentage and tearing strength are also far smaller than other products when other products, maximum pull.Therefore, plant bast fiber
Elongation percentage and tearing strength when significantly improving tensile strength, the maximum pull of waterproof roll.
The puncture resistant ability of embodiment 2 and comparative example 3 is most strong, is secondly embodiment and comparative example 4, followed by comparative example 1
With 2, the puncture resistant ability of comparative example 5 is worst, and therefore, the combination of nonwoven layer, biological stopping area and the first copper foil can be significant
Raising waterproof roll puncture resistant ability.
Embodiment 2, comparative example 4 and 5 the self-healing time be substantially less than embodiment 1, comparative example 1,2 and 3, wherein comparative example
3 self-healing time longest.Therefore, the second modified asphalt layer and third modified asphalt layer improve the self-healing energy of waterproof roll
Power.
In conjunction with attached drawing, the embodiments of the present invention are described in detail above, but the present invention is not limited to described implementations
Mode.For a person skilled in the art, in the case where not departing from the principle of the invention and spirit, to these embodiments
A variety of change, modification, replacement and modification are carried out, are still fallen in protection scope of the present invention.
Claims (5)
1. macromolecule viscosity waterproof roll, which is characterized in that including tire base, the upside of the tire base is equipped with the first modified drip
Cyan layer, the upside of first modified asphalt layer are equipped with nonwoven layer, and the upside of the nonwoven layer is equipped with separating film layer, described
The upside of separating film layer is equipped with SBR layers, and the downside of the tire base is equipped with the second modified asphalt layer, second modified asphalt layer
Downside be equipped with PVC alloy-layer, the downside of the PVC alloy-layer is equipped with SBS layer, and SBS layers of the downside is equipped with glass fibre
The downside of layer of cloth, the fiberglass cloth is equipped with polyvinyl acetate layer;
The tire base is plant bast fiber layer;
Biological stopping area is additionally provided between the separating film layer and SBR layers;
SBR layers of the upside is provided with flame-retardant layer;
Third modified asphalt layer and the first copper foil, first copper foil are provided between the biological stopping area and separating film layer
Positioned at the upside of the third modified asphalt layer;
The flame-retardant layer is fire-retardant polyphosphoric acid amine or flame-retardant acrylic fibre or fire resistance fibre or fire retarding epoxide resin.
2. macromolecule viscosity waterproof roll according to claim 1, which is characterized in that the isolation film is PP or PE film.
3. macromolecule viscosity waterproof roll according to claim 1, which is characterized in that the nonwoven layer is polyester malthoid
Base fabric.
4. macromolecule viscosity waterproof roll according to claim 1, which is characterized in that under the polyvinyl acetate layer
Side is additionally provided with self-adhesive layer.
5. macromolecule viscosity waterproof roll according to claim 1, which is characterized in that in the polyvinyl acetate layer and
The second copper foil is additionally provided between self-adhesive layer.