CN106853992A - 锐钛型钛白粉盐处理剂 - Google Patents
锐钛型钛白粉盐处理剂 Download PDFInfo
- Publication number
- CN106853992A CN106853992A CN201510904160.3A CN201510904160A CN106853992A CN 106853992 A CN106853992 A CN 106853992A CN 201510904160 A CN201510904160 A CN 201510904160A CN 106853992 A CN106853992 A CN 106853992A
- Authority
- CN
- China
- Prior art keywords
- white powder
- treatment agent
- salt treatment
- thpe white
- anatase thpe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及锐钛型钛白粉盐处理剂,属于钛白粉添加剂技术领域。本发明所要解决的技术问题提供一种可以提高锐钛型钛白粉遮盖力的锐钛型钛白粉盐处理剂。本发明锐钛型钛白粉盐处理剂由如下重量配比的组分组成:硫酸钾0.4-2份,磷酸0.2-0.35份,氯化铝0.8-1.0份。
Description
技术领域
本发明涉及锐钛型钛白粉盐处理剂,属于钛白粉添加剂技术领域。
背景技术
钛白粉是一种重要的化工原料,广泛应用于涂料、塑料、油墨、造纸、化妆品、颜料等技术领域。钛白粉主要分为金红石型和锐钛型两大类。在钛白粉生产过程中,为了提高钛白粉的性能,需要对漂洗后的偏钛酸进行盐处理,然后经煅烧制得钛白粉。
传统的钛白粉盐处理剂主要有磷酸和碳酸钾,加入磷酸可以改善钛白粉白度,提高其耐候性,使煅烧后的钛白粉松软易碎;而加入碳酸钾可以提高钛白粉的白度,还可以阻隔小粒子团聚,避免煅烧过程中细粒子被烧结。
但是,传统的钛白粉盐处理剂对钛白粉的其他性能如:消色力、分散性、遮盖力等指标改善幅度较小。
发明内容
本发明所要解决的技术问题提供一种可以提高锐钛型钛白粉遮盖力的锐钛型钛白粉盐处理剂。
本发明锐钛型钛白粉盐处理剂由如下重量配比的组分组成:硫酸钾0.4-2份,磷酸0.2-0.35份,氯化铝0.8-1.0份。
其中,本发明锐钛型钛白粉盐处理剂优选由如下重量配比的组分组成:硫酸钾0.8-1.5份,磷酸0.25-0.3份,氯化铝0.85-0.95份。
进一步的,本发明锐钛型钛白粉盐处理剂最优选由如下重量配比的组分组成:硫酸钾1.2份,磷酸0.28份,氯化铝0.9份。
本发明锐钛型钛白粉盐处理剂通过将各组分按重量配比混匀即可,使用时一次性加入,相比传统方法的先加入碳酸钾后加入磷酸,其使用更方便。按重量配比,以二氧化钛计,每100份的偏钛酸,加入硫酸钾0.4-2份,磷酸0.2-0.35份,氯化铝0.8-1.0份即可。
本发明锐钛型钛白粉盐处理剂相比传统的盐处理剂,其锐钛型钛白粉遮盖力提高明显,耐候性更好。本发明为本领域提供了一种新的锐钛型钛白粉盐处理剂,具有广阔的应用前景。
具体实施方式
本发明锐钛型钛白粉盐处理剂由如下重量配比的组分组成:硫酸钾0.4-2份,磷酸0.2-0.35份,氯化铝0.8-1.0份。
其中,本发明锐钛型钛白粉盐处理剂优选由如下重量配比的组分组成:硫酸钾0.8-1.5份,磷酸0.25-0.3份,氯化铝0.85-0.95份。
进一步的,本发明锐钛型钛白粉盐处理剂最优选由如下重量配比的组分组成:硫酸钾1.2份,磷酸0.28份,氯化铝0.9份。
下面结合实施例对本发明的具体实施方式做进一步的描述,并不因此将本发明限制在所述的实施例范围之中。
实施例1本发明锐钛型钛白粉盐处理剂的制备
取硫酸钾0.8kg,磷酸0.35kg,氯化铝0.85kg,混匀,制得本发明锐钛型钛白粉盐处理剂。
实施例2本发明锐钛型钛白粉盐处理剂的制备
取硫酸钾1.2kg,磷酸0.28kg,氯化铝0.9kg,混匀,制得本发明锐钛型钛白粉盐处理剂。
实施例3本发明锐钛型钛白粉盐处理剂的制备
取硫酸钾1.5kg,磷酸0.2kg,氯化铝0.95kg,混匀,制得本发明锐钛型钛白粉盐处理剂。
试验例1
取硫酸钾2.1kg,磷酸0.15kg,氯化铝1.05kg,混匀,制得锐钛型钛白粉盐处理剂。
试验例2
取硫酸钾0.75kg,磷酸0.4kg,氯化铝0.75kg,混匀,制得锐钛型钛白粉盐处理剂。
试验例3
取硫酸钾2.1kg,磷酸0.45kg,混匀,制得锐钛型钛白粉盐处理剂。
分别取漂洗后的偏钛酸100kg(以二氧化钛含量计),各加入实施例1-3制备的本发明锐钛型钛白粉盐处理剂和试验例1-3制备的锐钛型钛白粉盐处理剂(均完全加入),煅烧,制得锐钛型钛白粉。同时,直接煅烧漂洗后的偏钛酸,不添加盐处理剂,制得锐钛型钛白粉。测定所得锐钛型钛白粉的性能,结果如表1所示。
表1
编号 | 煅烧温度(℃) | 白度 | |
实施例1 | 850 | 104 | 44 |
实施例2 | 850 | 107 | 46 |
实施例3 | 850 | 105 | 44 |
试验例1 | 850 | 101.4 | 39 |
试验例2 | 850 | 101.4 | 40 |
试验例3 | 850 | 101.5 | 35 |
不加处理剂 | 960 | 100 | 25 |
从表1可以看出,采用本发明实施例1-3制备的锐钛型钛白粉盐处理剂生产的锐钛型钛白粉的遮盖力明显更好,特别是实施例2制备的锐钛型钛白粉盐处理剂生产的锐钛型钛白粉的性能最好。
Claims (3)
1.锐钛型钛白粉盐处理剂,其特征在于由如下重量配比的组分组成:硫酸钾0.4-2份,磷酸0.2-0.35份,氯化铝0.8-1.0份。
2.根据权利要求1所述的锐钛型钛白粉盐处理剂,其特征在于由如下重量配比的组分组成:硫酸钾0.8-1.5份,磷酸0.25-0.3份,氯化铝0.85-0.95份。
3.根据权利要求1所述的锐钛型钛白粉盐处理剂,其特征在于由如下重量配比的组分组成:硫酸钾1.2份,磷酸0.28份,氯化铝0.9份。