CN106853990A - 生产高遮盖力钛白粉的方法 - Google Patents
生产高遮盖力钛白粉的方法 Download PDFInfo
- Publication number
- CN106853990A CN106853990A CN201510903050.5A CN201510903050A CN106853990A CN 106853990 A CN106853990 A CN 106853990A CN 201510903050 A CN201510903050 A CN 201510903050A CN 106853990 A CN106853990 A CN 106853990A
- Authority
- CN
- China
- Prior art keywords
- titanium dioxide
- parts
- covering power
- high covering
- terms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及生产高遮盖力钛白粉的方法，属于钛白粉技术领域。本发明所要解决的技术问题提供一种生产高遮盖力钛白粉的方法。本发明生产高遮盖力钛白粉的方法包括如下步骤：按重量配比取漂洗后以二氧化钛含量计的偏钛酸100份，加入钛白粉组合盐促进剂，于830-860℃煅烧，制得金红石钛白粉；所述钛白粉组合盐促进剂由如下重量配比的组分组成：硫酸钾0.3-0.7份，磷酸0.01-0.02份，硫酸锌0.1-0.3份，氯化铝以三氧化二铝计0.8-1.0份。
Description
技术领域
本发明涉及生产高遮盖力钛白粉的方法，属于钛白粉技术领域。
背景技术
钛白粉是一种重要的化工原料，广泛应用于涂料、塑料、油墨、造纸、化妆品、颜料等技术领域。钛白粉主要分为金红石型和锐钛型两大类。在钛白粉生产过程中，为了促进金红石晶型的转化，同时也为了提高金红石钛白粉的性能，需要对漂洗后的偏钛酸进行盐处理，然后经煅烧制得金红石钛白粉。
传统的金红石盐处理剂为磷酸和碳酸钾，加入磷酸可以改善钛白粉白度，提高其耐候性，使煅烧后的钛白粉松软易碎；而加入碳酸钾可以提高钛白粉的白度，还可以阻隔小粒子团聚，避免煅烧过程中细粒子被烧结。另外，也有加入金红石组合盐处理剂：硫酸锌、碳酸钾和磷酸的报道。
但是，传统的钛白粉组合盐促进剂对钛白粉的其他性能如：消色力、分散性、遮盖力等指标改善幅度较小。
发明内容
本发明所要解决的技术问题提供一种生产高遮盖力钛白粉的方法。
本发明生产高遮盖力钛白粉的方法包括如下步骤：按重量配比取漂洗后以二氧化钛含量计的偏钛酸100份，加入钛白粉组合盐促进剂，于830-860℃煅烧，制得金红石钛白粉；所述钛白粉组合盐促进剂由如下重量配比的组分组成：硫酸钾0.3-0.7份，磷酸0.01-0.02份，硫酸锌0.1-0.3份，氯化铝以三氧化二铝计0.8-1.0份。
其中，上述钛白粉组合盐促进剂优选由如下重量配比的组分组成：硫酸钾0.4-0.6份，磷酸0.012-0.018份，硫酸锌0.15-0.25份，氯化铝以三氧化二铝计0.85-0.95份。
进一步的，上述钛白粉组合盐促进剂最优选由如下重量配比的组分组成：硫酸钾0.5份，磷酸0.015份，硫酸锌0.2份，氯化铝以三氧化二铝计0.9份。
本发明方法生产金红石钛白粉时，所用调整剂使用时一次性加入，相比传统方法的先加入碳酸钾后加入磷酸，其操作更简单更方便。
本发明方法相比传统方法生产的金红石白粉，其遮盖力更高，综合性能更好。本发明为本领域提供了一种新的金红石钛白粉的生产方法，具有广阔的应用前景。
具体实施方式
本发明生产高遮盖力钛白粉的方法包括如下步骤：按重量配比取漂洗后以二氧化钛含量计的偏钛酸100份，加入钛白粉组合盐促进剂，于830-860℃煅烧，制得金红石钛白粉；所述钛白粉组合盐促进剂由如下重量配比的组分组成：硫酸钾0.3-0.7份，磷酸0.01-0.02份，硫酸锌0.1-0.3份，氯化铝以三氧化二铝计0.8-1.0份。
其中，上述钛白粉组合盐促进剂优选由如下重量配比的组分组成：硫酸钾0.4-0.6份，磷酸0.012-0.018份，硫酸锌0.15-0.25份，氯化铝以三氧化二铝计0.85-0.95份。
进一步的，上述钛白粉组合盐促进剂最优选由如下重量配比的组分组成：硫酸钾0.5份，磷酸0.015份，硫酸锌0.2份，氯化铝以三氧化二铝计0.9份。
本发明方法生产金红石钛白粉时，所用调整剂使用时一次性加入，相比传统方法的先加入碳酸钾后加入磷酸，其操作更简单更方便。
下面结合实施例对本发明的具体实施方式做进一步的描述，并不因此将本发明限制在所述的实施例范围之中。
实施例1采用本发明方法生产金红石钛白粉
取硫酸钾0.3kg，磷酸0.02kg，硫酸锌0.15kg，氯化铝以三氧化二铝计0.8kg，混匀，制得钛白粉组合盐促进剂。
取漂洗后的偏钛酸100kg(以二氧化钛含量计)，加入制得的钛白粉组合盐促进剂，850℃煅烧，制得金红石钛白粉。
实施例2采用本发明方法生产金红石钛白粉
取硫酸钾0.5kg，磷酸0.015kg，硫酸锌0.2kg，氯化铝以三氧化二铝计0.9kg，混匀，制得钛白粉组合盐促进剂。
取漂洗后的偏钛酸100kg(以二氧化钛含量计)，加入制得的钛白粉组合盐促进剂，850℃煅烧，制得金红石钛白粉。
实施例3采用本发明方法生产金红石钛白粉
取硫酸钾0.7kg，磷酸0.012kg，硫酸锌0.3kg，氯化铝以三氧化二铝计1.0kg，混匀，制得钛白粉组合盐促进剂。
取漂洗后的偏钛酸100kg(以二氧化钛含量计)，加入制得的钛白粉组合盐促进剂，850℃煅烧，制得金红石钛白粉。
试验例1
取硫酸钾0.2kg，磷酸0.03kg，硫酸锌0.4kg，氯化铝以三氧化二铝计0.6kg，混匀，制得钛白粉组合盐促进剂。
取漂洗后的偏钛酸100kg(以二氧化钛含量计)，加入制得的钛白粉组合盐促进剂，850℃煅烧，制得金红石钛白粉。
试验例2
取硫酸钾0.8kg，磷酸0.01kg，硫酸锌0.08kg，氯化铝以三氧化二铝计1.1kg，混匀，制得钛白粉组合盐促进剂。
取漂洗后的偏钛酸100kg(以二氧化钛含量计)，加入制得的钛白粉组合盐促进剂，850℃煅烧，制得金红石钛白粉。
试验例3
取硫酸钾0.5kg，磷酸0.015kg，硫酸锌0.2kg，混匀，制得钛白粉组合盐促进剂。
取漂洗后的偏钛酸100kg(以二氧化钛含量计)，加入制得的钛白粉组合盐促进剂，850℃煅烧，制得金红石钛白粉。
另外，直接煅烧漂洗后的偏钛酸，不添加盐处理剂，制得钛白粉。测定所得金红石钛白粉的性能，结果如表1所示。
表1
| 编号 | 金红石晶型转化率/％ | 白度 | |
| 实施例1 | 99.65 | 108 | 50 |
| 实施例2 | 99.77 | 109 | 53 |
| 实施例3 | 99.61 | 106 | 51 |
| 试验例1 | 99.5 | 101 | 45 |
| 试验例2 | 99.2 | 99 | 46 |
| 试验例3 | 99.1 | 103 | 37 |
| 不加处理剂 | 35 | 100 | 25 |
从表1可以看出，采用本发明实施例1-3制备的钛白粉遮盖力明显更好，金红石晶型转化率高，特别是实施例2制备的钛白粉性能最好。
Claims (3)
1.生产高遮盖力钛白粉的方法，其特征在于包括如下步骤：按重量配比取漂洗后以二氧化钛含量计的偏钛酸100份，加入钛白粉组合盐促进剂，于830-860℃煅烧，制得金红石钛白粉；所述钛白粉组合盐促进剂由如下重量配比的组分组成：硫酸钾0.3-0.7份，磷酸0.01-0.02份，硫酸锌0.1-0.3份，氯化铝以三氧化二铝计0.8-1.0份。
2.根据权利要求1所述的生产高遮盖力钛白粉的方法，其特征在于所述钛白粉组合盐促进剂由如下重量配比的组分组成：硫酸钾0.4-0.6份，磷酸0.012-0.018份，硫酸锌0.15-0.25份，氯化铝以三氧化二铝计0.85-0.95份。
3.根据权利要求1所述的生产高遮盖力钛白粉的方法，其特征在于所述钛白粉组合盐促进剂由如下重量配比的组分组成：硫酸钾0.5份，磷酸0.015份，硫酸锌0.2份，氯化铝以三氧化二铝计0.9份。