CN106853325A - A kind of STEVIA REBAUDIANA anti-blushing agent - Google Patents
A kind of STEVIA REBAUDIANA anti-blushing agent Download PDFInfo
- Publication number
- CN106853325A CN106853325A CN201610949878.9A CN201610949878A CN106853325A CN 106853325 A CN106853325 A CN 106853325A CN 201610949878 A CN201610949878 A CN 201610949878A CN 106853325 A CN106853325 A CN 106853325A
- Authority
- CN
- China
- Prior art keywords
- parts
- stevia rebaudiana
- blushing agent
- kaolin
- mud
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides a kind of STEVIA REBAUDIANA anti-blushing agent, including following weight portion component：Attapulgite modified 20~30 parts, 15~20 parts of kaolin, 20~25 parts of mud liver moss, 8~12 parts of atlapulgite, 12~18 parts of red bentonite, 10~15 parts of carnallite.STEVIA REBAUDIANA anti-blushing agent of the present invention, is combined using the spongy materials of various tools, prepared, and the occurrence of the anti-blushing agent for obtaining can effectively keep protection against the tide of the STEVIA REBAUDIANA during storing to go mouldy, storage is as long as half a year more than the STEVIA REBAUDIANA without the anti-blushing agent.
Description
Technical field
The present invention relates to STEVIA REBAUDIANA storing technology field, in particular it relates to a kind of STEVIA REBAUDIANA anti-blushing agent.
Background technology
STEVIA REBAUDIANA is composite family Stevia herbaceos perennial.The whole strain of STEVIA REBAUDIANA all contains sugar, with the sugariness of blade most
Height, containing glucosides about 14%, the half of the glucosides equivalent to blade of branch stalk, STEVIA REBAUDIANA vanes can work as sugar material after shining dry grinding, pass through
The stevioside that obtains of extraction, sugariness is equivalent to 250-300 times of white granulated sugar, and heat is only the 1/300 of white granulated sugar, not only
In this way, stevioside has no toxic side effect, without carcinogenic substance, edible safety, often eating can preventing hypertension, diabetes, obesity, the heart
The illnesss such as popular name for, carious tooth, are a kind of ideal sweeteners of replacement sucrose.At present, food, beverage, doctor are widely used to
The industries such as medicine, daily-use chemical industry, wine brewing, cosmetics, and relatively use sucrose escapable cost 60%.
STEVIA REBAUDIANA is rich in sugar, if not carrying out damp-proof treatment during storage, easily makes moist, and causes nigrescence to be gone mouldy, influence kind
The plantation income and stevioside for planting family process the economic benefit of enterprise.At present, many use plastics of STEVIA REBAUDIANA are composite braided
Bag and non-toxic plastic bag packaging, tie sack, are preserved, although this kind of storage practice can prevent STEVIA REBAUDIANA to a certain extent
Make moist, but it is unsatisfactory to the long term storage effect of STEVIA REBAUDIANA.
The content of the invention
For the defect that prior art is present, it is an object of the invention to provide a kind of effective, lasting STEVIA REBAUDIANA anti-blushing agent.
To reach above-mentioned purpose, the present invention is adopted the following technical scheme that：A kind of STEVIA REBAUDIANA anti-blushing agent, including following weight portion
Component：Attapulgite modified 20~30 parts, 15~20 parts of kaolin, 20~25 parts of mud liver moss, 8~12 parts of atlapulgite is red
12~18 parts of color bentonite, 10~15 parts of carnallite.
Preferably, the component of the STEVIA REBAUDIANA anti-blushing agent, including following weight portion：Attapulgite modified 25 parts, kaolin
17 parts, 23 parts of mud liver moss, 10 parts of atlapulgite, 15 parts of red bentonite, 12 parts of carnallite.
Preferably, the attapulgite modified preparation method is as follows：Attapulgite is added the iron ore of its weight 3-5%
Ground-slag takes out cooling in 2h is calcined at 800 DEG C, pulverizes, and adds the zinc oxide of its weight 2%, 3% magnesium sulfate, 2%
Basic copper sulfate, 5% China tree powder, it is well mixed obtain final product it is described attapulgite modified.
Preferably, the kaolin is through 600 DEG C of high-temperature calcination.
Preferably, the water content of the mud liver moss is 10~12%.
Preferably, the red bentonitic iron oxide content is 15%~25%.
A kind of preparation method of the anti-blushing agent of STEVIA REBAUDIANA as described is as follows：
（1）Kaolin, mud liver moss, atlapulgite, red bentonite, carnallite are crushed after being dried to water content not at 80 DEG C
More than 3%, then each raw material is mixed, be well mixed；
（2）By the step（1）Each raw material it is well mixed after with non-woven bag or gauze bag, sealing obtains final product the STEVIA REBAUDIANA
Anti-blushing agent.
Compared with prior art, the present invention has following beneficial effect：STEVIA REBAUDIANA anti-blushing agent of the present invention, using many
Plant the spongy material of tool to be combined, prepare, the anti-blushing agent for obtaining can effectively keep protection against the tide of the STEVIA REBAUDIANA during storing
The occurrence of going mouldy, storage is as long as half a year more than the STEVIA REBAUDIANA without the anti-blushing agent.
Specific embodiment
With reference to specific embodiment, the present invention is expanded on further.It should be understood that these embodiments are merely to illustrate the present invention
Rather than limitation the scope of the present invention.
Embodiment 1
STEVIA REBAUDIANA anti-blushing agent described in the present embodiment, including following weight portion component：Attapulgite modified 25 parts, kaolin 17
Part, 23 parts of mud liver moss, 10 parts of atlapulgite, 15 parts of red bentonite, 12 parts of carnallite；The kaolin is through 600 DEG C of high temperature
Calcining；The water content of the mud liver moss is 10%；The red bentonitic iron oxide content is 20%.
The attapulgite modified preparation method is as follows：Attapulgite is added into the iron ore ground-slag of its weight 4% in 800
2h is calcined at DEG C, cooling is taken out, pulverized, add zinc oxide, 3% magnesium sulfate, the 2% alkali formula sulfuric acid of its weight 2%
Copper, 5% China tree powder, it is well mixed obtain final product it is described attapulgite modified.
The preparation method of STEVIA REBAUDIANA anti-blushing agent is as follows as described：
（1）Kaolin, mud liver moss, atlapulgite, red bentonite, carnallite are crushed and is after drying to water content at 80 DEG C
2.5%, then each raw material is mixed, it is well mixed；
（2）By the step（1）Each raw material it is well mixed after with non-woven bag or gauze bag, sealing obtains final product the STEVIA REBAUDIANA
Anti-blushing agent.
The storage of STEVIA REBAUDIANA is used it for, is stored 6 months as long as than the STEVIA REBAUDIANA without the anti-blushing agent more.
Embodiment 2
STEVIA REBAUDIANA anti-blushing agent described in the present embodiment, including following weight portion component：Attapulgite modified 20 parts, kaolin 15
Part, 25 parts of mud liver moss, 8 parts of atlapulgite, 18 parts of red bentonite, 15 parts of carnallite；The kaolin is forged through 600 DEG C of high temperature
Burn；The water content of the mud liver moss is 12%；The red bentonitic iron oxide content is 15%.
The attapulgite modified preparation method is as follows：Attapulgite is added into the iron ore ground-slag of its weight 5% in 800
2h is calcined at DEG C, cooling is taken out, pulverized, add zinc oxide, 3% magnesium sulfate, the 2% alkali formula sulfuric acid of its weight 2%
Copper, 5% China tree powder, it is well mixed obtain final product it is described attapulgite modified.
The preparation method of STEVIA REBAUDIANA anti-blushing agent is as follows as described：
（1）Kaolin, mud liver moss, atlapulgite, red bentonite, carnallite are crushed and is after drying to water content at 80 DEG C
2.5%, then each raw material is mixed, it is well mixed；
（2）By the step（1）Each raw material it is well mixed after with non-woven bag or gauze bag, sealing obtains final product the STEVIA REBAUDIANA
Anti-blushing agent.
The storage of STEVIA REBAUDIANA is used it for, is stored 4 months as long as than the STEVIA REBAUDIANA without the anti-blushing agent more.
Embodiment 3
STEVIA REBAUDIANA anti-blushing agent described in the present embodiment, including following weight portion component：Attapulgite modified 30 parts, kaolin 20
Part, 20 parts of mud liver moss, 12 parts of atlapulgite, 12 parts of red bentonite, 10 parts of carnallite；The kaolin is through 600 DEG C of high temperature
Calcining；The water content of the mud liver moss is 11%；The red bentonitic iron oxide content is 25%.
The attapulgite modified preparation method is as follows：Attapulgite is added into the iron ore ground-slag of its weight 3% in 800
2h is calcined at DEG C, cooling is taken out, pulverized, add zinc oxide, 3% magnesium sulfate, the 2% alkali formula sulfuric acid of its weight 2%
Copper, 5% China tree powder, it is well mixed obtain final product it is described attapulgite modified.
The preparation method of STEVIA REBAUDIANA anti-blushing agent is as follows as described：
（1）Kaolin, mud liver moss, atlapulgite, red bentonite, carnallite are crushed and is after drying to water content at 80 DEG C
3%, then each raw material is mixed, it is well mixed；
（2）By the step（1）Each raw material it is well mixed after with non-woven bag or gauze bag, sealing obtains final product the STEVIA REBAUDIANA
Anti-blushing agent.
The storage of STEVIA REBAUDIANA being used it for, as long as storing 3 first quarter moons than the STEVIA REBAUDIANA without the anti-blushing agent more.
Specific embodiment of the invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can within the scope of the claims make various deformations or amendments, this not shadow
Sound substance of the invention.
Claims (7)
1. a kind of STEVIA REBAUDIANA anti-blushing agent, it is characterised in that the component including following weight portion：Attapulgite modified 20~30 parts,
15~20 parts of kaolin, 20~25 parts of mud liver moss, 8~12 parts of atlapulgite, 12~18 parts of red bentonite, carnallite 10~15
Part.
2. STEVIA REBAUDIANA anti-blushing agent according to claim 1, it is characterised in that the STEVIA REBAUDIANA anti-blushing agent, including following weight
The component of part：Attapulgite modified 25 parts, 17 parts of kaolin, 23 parts of mud liver moss, 10 parts of atlapulgite, 15 parts of red bentonite,
12 parts of carnallite.
3. STEVIA REBAUDIANA anti-blushing agent according to claim 1, it is characterised in that the attapulgite modified preparation method is such as
Under：Add the iron ore ground-slag of its weight 3-5% in 2h is calcined at 800 DEG C attapulgite, take out cooling, pulverize, add
The zinc oxide of its weight 2%, 3% magnesium sulfate, 2% basic copper sulfate, 5% China tree powder, it is well mixed obtain final product it is described modified recessed
Convex rod soil.
4. STEVIA REBAUDIANA anti-blushing agent according to claim 1, it is characterised in that the kaolin is through 600 DEG C of high-temperature calcination.
5. STEVIA REBAUDIANA anti-blushing agent according to claim 1, it is characterised in that the water content of the mud liver moss is 10~12%.
6. STEVIA REBAUDIANA anti-blushing agent according to claim 1, it is characterised in that the red bentonitic iron oxide content is
15%~25%.
7. a kind of preparation method of STEVIA REBAUDIANA anti-blushing agent as claimed in claim 1, it is characterised in that the preparation method is included such as
Lower step：
（1）Kaolin, mud liver moss, atlapulgite, red bentonite, carnallite are crushed after being dried to water content not at 80 DEG C
More than 3%, then each raw material is mixed, be well mixed；
（2）By the step（1）Each raw material it is well mixed after with non-woven bag or gauze bag, sealing obtains final product the STEVIA REBAUDIANA
Anti-blushing agent.