CN106833236A - The preparation method of the construction coating for internal wall of containing diatomite - Google Patents

The preparation method of the construction coating for internal wall of containing diatomite Download PDF

Info

Publication number
CN106833236A
CN106833236A CN201710187947.1A CN201710187947A CN106833236A CN 106833236 A CN106833236 A CN 106833236A CN 201710187947 A CN201710187947 A CN 201710187947A CN 106833236 A CN106833236 A CN 106833236A
Authority
CN
China
Prior art keywords
solution
added
diatomite
internal wall
construction coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710187947.1A
Other languages
Chinese (zh)
Inventor
不公告发明人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710187947.1A priority Critical patent/CN106833236A/en
Publication of CN106833236A publication Critical patent/CN106833236A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of preparation method of containing diatomite construction coating for internal wall, it is characterized in that：First, diatomite through ball milling sieve after, be added in ethanol, ultrasonic disperse, be filtrated to get removal organic impurities purified silicious earth A；Secondly, A, water-bath temperature control is added to be separately added into binding agent, thickener and surfactant in water, stirring obtains mixed solution B；Organic titanate and calcium nitrate are sequentially added in nitric acid, is stirred vigorously, obtain solution C；Then, solution C is poured into solution B, stands, adjusts solution ph to neutrality, obtain solution D, transfer is put in reactor, and temperature control stands；Then, solution D is filtrated to get wet cake, solid E is obtained through oven drying；Finally, solid E is proportionally added into emulsion, stirring is obtained containing diatomite construction coating for internal wall.The construction coating for internal wall is widely used, it is adaptable to multiple coating, and the peculiar smell such as PARA FORMALDEHYDE PRILLS(91,95) has relatively strong absorption and removal ability.

Description

The preparation method of the construction coating for internal wall of containing diatomite
Technical field
The present invention relates to paint field, particularly a kind of containing diatomite construction coating for internal wall.
Background technology
With the quickening of urbanization process, human living standard's more and more higher, environmental issue turns into public's growing interest Major issue.Home decoration in daily life, people would generally select green, environmentally friendly, environment amenable material, these materials Price general charged is expensive, actual most of decorative building materials for using would generally more or less composition containing formaldehyde, such as in dalle Binding agent.Formaldehyde is a kind of colourless gas with intense irritation smell, serious to harm, easily causes all kinds of diseases Disease, such as：Alimentary canal, respiratory tract, skin, cancer, abnormal property etc..
The A of CN 103923536 report a kind of preparation method of net taste ecology damping antibacterial inner wall paint, and formula is main Component contains emulsion, titanium dioxide, diatomite, nano titanium oxide etc.；The A of CN 103741545 report a kind of antibacterial diatomite Base coating and its preparation method and application, both of which is to prepare containing diatomite coating by physical mixed method.And chemical method is A kind of cheap, device simple, the effective ways for preparing multifunctional composite, are more and more paid attention to.
Therefore, finding a kind of environmental protection, the construction coating for internal wall of effectively removal formaldehyde has turned into interior wall construction material neck A kind of active demand in domain.
The content of the invention
It is an object of the invention to：A kind of preparation method of containing diatomite construction coating for internal wall is provided, with reference to organic chemistry The advantageous property of modification technology and inorganic material, rapid batch prepares compound diatomite, titanium oxide, the emulsion coatings of calcium oxide.
Technical scheme：First, after diatomite sieves through ball milling, it is added in ethanol, during one section of ultrasonic disperse Between after, be filtrated to get removal organic impurities purified silicious earth A；Secondly, A, water-bath temperature control is added to add respectively in a certain amount of water Enter binding agent polyvinyl alcohol, thickener hydroxyethyl cellulose and Surfactant SDS and odium stearate, stir Obtain mixed solution B；Again, organic titanate and calcium nitrate are sequentially added in finite concentration nitric acid, when being stirred vigorously one section Between after, obtain solution C；Then, solution C is poured into solution B, after standing a period of time, regulation solution ph is obtained to neutrality Solution D, transfer is put in reactor, and temperature control stands a period of time；Then, solution D is filtrated to get wet cake, it is solid through being dried to obtain Body E；Finally, solid E is proportionally added into emulsion, is stirred, containing diatomite construction coating for internal wall is obtained.
The present invention compared with prior art, with remarkable advantage：One, the construction coating for internal wall are to adsorb with diatomite Agent, titanium dioxide is photochemical catalyst, and the peculiar smell such as PARA FORMALDEHYDE PRILLS(91,95) has relatively strong absorption and removal ability；Second, the construction coating for internal wall Diatomite, titanium dioxide, calcium oxide, binding agent, thickener, surfactant are compounded with, are widely used, it is adaptable to various paintings Material.
Specific embodiment
Technical solution of the invention is illustrated with reference to specific embodiment, these embodiments are it is not intended that to technology The limitation of scheme.
Embodiment 1：A kind of containing diatomite construction coating for internal wall is prepared according to step in detail below.
Step 1, the diatomite that 100g crosses 80 mesh sieves through ball milling is taken, be added in ethanol, after ultrasonic disperse 3h, be filtrated to get Purified silicious earth A；
Step 2, A is added in 400mL water, water-bath temperature control 60oC, adds polyvinyl alcohol 15g, hydroxyethyl cellulose 2g, dodecane Base sodium sulphate 5g and odium stearate 5g, stirs 6h, obtains mixed solution B；
Step 3, the nitric acid of 40mL mass concentrations 60% is taken, wherein adding organic titanate 10g and calcium nitrate 5g, be stirred vigorously 1h, obtained To solution C；
Step 4, solution C is poured into solution B, stand 12h, sodium hydroxide solution adjusts solution ph to neutrality, obtains solution D, is transferred in reactor, temperature control 150oC, places 4h；
Step 5, solution D is filtrated to get wet cake, through 110oC oven drying 12h, obtain solid E；
Step 6,20g solids E is added in 400g styrene-acrylic emulsions, stirs 4h, containing diatomite construction coating for internal wall is obtained.
Embodiment 2：A kind of containing diatomite construction coating for internal wall is prepared according to step in detail below.
Step 1, the diatomite that 100g crosses 80 mesh sieves through ball milling is taken, be added in ethanol, after ultrasonic disperse 6h, be filtrated to get Purified silicious earth A；
Step 2, A is added in 400mL water, water-bath temperature control 80oC, adds polyvinyl alcohol 30g, hydroxyethyl cellulose 5g, dodecane Base sodium sulphate 10g and odium stearate 10g, stirs 12h, obtains mixed solution B；
Step 3, the nitric acid of 60mL mass concentrations 60% is taken, wherein adding organic titanate 20g and calcium nitrate 10g, is stirred vigorously 3h, Obtain solution C；
Step 4, solution C is poured into solution B, stand 36h, sodium hydroxide solution adjusts solution ph to neutrality, obtains solution D, is transferred in reactor, temperature control 250oC, places 8h；
Step 5, solution D is filtrated to get wet cake, through 130oC oven drying 24h, obtain solid E；
Step 6,20g solids E is added in 100g acrylic emulsions, stirs 4h, containing diatomite construction coating for internal wall is obtained.
Embodiment 3：A kind of containing diatomite construction coating for internal wall is prepared according to step in detail below.
Step 1, the diatomite that 100g crosses 80 mesh sieves through ball milling is taken, be added in ethanol, after ultrasonic disperse 4h, be filtrated to get Purified silicious earth A；
Step 2, A is added in 400mL water, water-bath temperature control 70oC, adds polyvinyl alcohol 20g, hydroxyethyl cellulose 3g, dodecane Base sodium sulphate 8g and odium stearate 6g, stirs 8h, obtains mixed solution B；
Step 3, the nitric acid of 50mL mass concentrations 60% is taken, wherein adding organic titanate 15g and calcium nitrate 7g, be stirred vigorously 2h, obtained To solution C；
Step 4, solution C is poured into solution B, stand 24h, sodium hydroxide solution adjusts solution ph to neutrality, obtains solution D, is transferred in reactor, temperature control 200oC, places 6h；
Step 5, solution D is filtrated to get wet cake, through 120oC oven drying 16h, obtain solid E；
Step 6,20g solids E is added in 200g silicone acrylic emulsions, stirs 4h, containing diatomite construction coating for internal wall is obtained.

Claims (1)

1. a kind of preparation method of containing diatomite construction coating for internal wall, it is characterized in that the preparation method is comprised the following steps：
Step 1, the diatomite that 100g crosses 80 mesh sieves through ball milling is taken, be added in ethanol, after ultrasonic disperse 3h, be filtrated to get purifying Diatomite A；
Step 2, A is added in 400mL water, water-bath temperature control 60oC, adds polyvinyl alcohol 15g, hydroxyethyl cellulose 2g, dodecane Base sodium sulphate 5g and odium stearate 5g, stirs 6h, obtains mixed solution B；
Step 3, the nitric acid of 40mL mass concentrations 60% is taken, wherein adding organic titanate 10g and calcium nitrate 5g, be stirred vigorously 1h, obtained To solution C；
Step 4, solution C is poured into solution B, stand 12h, sodium hydroxide solution adjusts solution ph to neutrality, obtains solution D, is transferred in reactor, temperature control 150oC, places 4h；
Step 5, solution D is filtrated to get wet cake, through 110oC oven drying 12h, obtain solid E；
Step 6,20g solids E is added in 400g styrene-acrylic emulsions, stirs 4h, containing diatomite construction coating for internal wall is obtained.
CN201710187947.1A 2015-08-19 2015-08-19 The preparation method of the construction coating for internal wall of containing diatomite Withdrawn CN106833236A (en)