CN104513537A - Kieselguhr coating - Google Patents
Kieselguhr coating Download PDFInfo
- Publication number
- CN104513537A CN104513537A CN201310460871.7A CN201310460871A CN104513537A CN 104513537 A CN104513537 A CN 104513537A CN 201310460871 A CN201310460871 A CN 201310460871A CN 104513537 A CN104513537 A CN 104513537A
- Authority
- CN
- China
- Prior art keywords
- kieselguhr
- diatomite
- agent
- acrylic emulsion
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kieselguhr coating includes following components, by weight: 40-50% of a styrene-acrylic emulsion, 20-30% of deionized water, 20-30% of an acrylic emulsion, 15-25% of kieselguhr in 400 meshes, 0.1-0.5% of cellulose, 1-3% of wollastonite powder, 2-6% of talcum powder, 1-5% of titanium dioxide, 0.1-0.5% of an anion dispersing agent, 1-5% of an mildew preventive, 10-15% of calcium carbonate, 0.1-0.3% of a defoaming agent, 0.1-0.3% of a contamination-resistant agent, 0.1-1.5% of a thickening agent, 0.1-0.5% of a flatting agent, and 1.5-2% of a film-forming aid. The kieselguhr is ultrafine and is in 400 meshes so that the kieselguhr coating is better in effects of insulating sound and adsorbing contaminants.
Description
Technical field
The present invention relates to a kind of paint, particularly relate to a kind of diatomite paint, belong to chemical field.
Background technology
The sound insulation of metope domestic at present, the effect of absorb polluted matter do not have substantially, have invented this product for addressing this problem.
Summary of the invention
A kind of diatomite paint, component and mass ratio are: the talcum powder of the Mierocrystalline cellulose of the ACRYLIC EMULSION of the benzene emulsion of 40 ~-50%, the deionized water of 20%-30%, 20%-30%, the 400 object diatomite of 15-25,0.1%-0.5%, the wollastonite powder of 1%-3%, 2%-6%, the titanium dioxide of 1%-5%, the anionic dispersing agents of 0.1-0.5%, the mould inhibitor of 1%-5%, the calcium carbonate of 10%-15%, 0.1-0.3% defoamer, the stain resistant agent of 0.1%-0.3%, the thickening material of 0.1%-1.5%, the flow agent of 0.1%-0.5%, the film coalescence aid of 1.5%-2%.The 400 order diatomite that diatomaceous spy used is thin, more can play effect of sound insulation, absorb polluted matter.
embodimenta kind of concrete component of metope antifouling paint, the mass ratio of each component and concrete production technique are as follows:
Take the benzene emulsion of 40%, 20% deionized water, the ACRYLIC EMULSION of 20%, the 400 order diatomite of 15%; The Mierocrystalline cellulose of 0.5%, the wollastonite powder of 3%, 6% talcum powder, 5% titanium dioxide, 0.5% anionic dispersing agents, 5% mould inhibitor, 15% calcium carbonate, 0.3% defoamer, the stain resistant agent of 0.3%, the thickening material of 1.5%, the flow agent of 0.5%, the film coalescence aid of 2%, put into stirred pot to stir, namely can be made into of the present invention kind of metope antifouling paint, indices all detects qualified rear barrelling wait and dispatches from the factory.
Claims (2)
1. a diatomite paint, component and mass ratio are: the talcum powder of the Mierocrystalline cellulose of the ACRYLIC EMULSION of the benzene emulsion of 40 ~-50%, the deionized water of 20%-30%, 20%-30%, the 400 object diatomite of 15-25,0.1%-0.5%, the wollastonite powder of 1%-3%, 2%-6%, the titanium dioxide of 1%-5%, the anionic dispersing agents of 0.1-0.5%, the mould inhibitor of 1%-5%, the calcium carbonate of 10%-15%, 0.1-0.3% defoamer, the stain resistant agent of 0.1%-0.3%, the thickening material of 0.1%-1.5%, the flow agent of 0.1%-0.5%, the film coalescence aid of 1.5%-2%.
2. according to claim 1, a kind of diatomite paint, is characterized in that, the 400 order diatomite that diatomaceous spy used is thin, more can play effect of sound insulation, absorb polluted matter.