CN106833199A - A kind of environment protecting water-based paint and preparation method thereof - Google Patents

A kind of environment protecting water-based paint and preparation method thereof Download PDF

Info

Publication number
CN106833199A
CN106833199A CN201710063531.9A CN201710063531A CN106833199A CN 106833199 A CN106833199 A CN 106833199A CN 201710063531 A CN201710063531 A CN 201710063531A CN 106833199 A CN106833199 A CN 106833199A
Authority
CN
China
Prior art keywords
parts
agent
based paint
environment protecting
trifluoroacetylacetone
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710063531.9A
Other languages
Chinese (zh)
Inventor
姚孝国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Huasheng Coating Co Ltd
Original Assignee
Anhui Huasheng Coating Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Huasheng Coating Co Ltd filed Critical Anhui Huasheng Coating Co Ltd
Priority to CN201710063531.9A priority Critical patent/CN106833199A/en
Publication of CN106833199A publication Critical patent/CN106833199A/en
Pending legal-status Critical Current

Abstract

A kind of environment protecting water-based paint and preparation method thereof, is related to coating material production processing technique field.It is made up of the raw material of following weight portion：20 40 parts of aqueous acrylic emulsion, 5 12 parts of trifluoroacetylacetone (TFA) iron, 6 11 parts of flame retardant, 5 12 parts of butyl glycol ether, 4 10 parts of ethyl acetate, 5 12 parts of dilauryl thiodipropionate, 5 10 parts of aluminium triphosphate, 5 12 parts of titanium dioxide, 7 12 parts of trbasic zinc phosphate, 5 11 parts of anti-corrosive aids, 6 12 parts of levelling agent, 59 parts of defoamer, 3 12 parts of nano titanium oxide, 58 parts of calcium carbonate, 4 12 parts of talcum powder, 5 10 parts of curing agent, 3 13 parts of wetting agent, 5 11 parts of dispersant, 2 12 parts of adhesive agent, 4 10 parts of Herba Asari extract, 10 15 parts of deionized water.Environment protecting water-based paint, it is environmentally friendly, in the absence of harm environment and the component of air.Rationally, production efficiency is high for preparation method technological design.

Description

A kind of environment protecting water-based paint and preparation method thereof
Technical field
The present invention relates to a kind of environment protecting water-based paint and preparation method thereof, it is related to coating material production processing technique field.
Background technology
Atmosphere pollution enters air (input) by artificial source or natural source, the cyclic process of air is participated in, by one After the fixed holdup time, (output) is removed from air further through the sedimentation of the chemical reaction in air, biological activity and physics. If the speed of output is less than the speed of input, relative in an atmosphere will gather, cause the concentration liter of certain material in air It is high.When concentration is raised to a certain extent, acute, chronic hazard directly or indirectly will be caused to people, biological or material etc., Air is just contaminated.
With industrial expansion, coating is widely used in all trades and professions of life.Due to most coating composition In all there is organic solvent so that coating persistently can cause irreversible during using process and follow-up repair and maintenance to air Harm.
The content of the invention
In order to overcome the above-mentioned technical problem in the presence of prior art, it is an object of the invention to provide a kind of environment-protective water Property coating and preparation method thereof.
To achieve the above object, present invention employs following technical scheme：
A kind of environment protecting water-based paint, is made up of the raw material of following weight portion：
Aqueous acrylic emulsion 20-40 parts,
5-12 parts of trifluoroacetylacetone (TFA) iron,
Flame retardant 6-11 parts,
Butyl glycol ether 5-12 parts,
Ethyl acetate 4-10 parts,
Dilauryl thiodipropionate 5-12 parts,
Aluminium triphosphate 5-10 parts,
Titanium dioxide 5-12 parts,
Trbasic zinc phosphate 7-12 parts,
Anti-corrosive aids 5-11 parts,
Levelling agent 6-12 parts,
Defoamer 5-9 parts,
Nano titanium oxide 3-12 parts,
Calcium carbonate 5-8 parts,
Talcum powder 4-12 parts,
Curing agent 5-10 parts,
Wetting agent 3-13 parts,
Dispersant 5-11 parts,
Adhesive agent 2-12 parts,
Herba Asari extract 4-10 parts,
Deionized water 10-15 parts.
Preferably, a kind of environment protecting water-based paint of the invention, is made up of the raw material of following weight portion：
30 parts of aqueous acrylic emulsion,
8 parts of trifluoroacetylacetone (TFA) iron,
9 parts of flame retardant,
7 parts of butyl glycol ether,
7 parts of ethyl acetate,
6 parts of dilauryl thiodipropionate,
9 parts of aluminium triphosphate,
8.5 parts of titanium dioxide,
9.5 parts of trbasic zinc phosphate,
10 parts of anti-corrosive aids,
11 parts of levelling agent,
7.5 parts of defoamer,
8 parts of nano titanium oxide,
6.5 parts of calcium carbonate,
8 parts of talcum powder,
8 parts of curing agent,
7 parts of wetting agent,
8 parts of dispersant,
6.5 parts of adhesive agent,
7.5 parts of Herba Asari extract,
12.5 parts of deionized water.
The preparation method of environment protecting water-based paint of the invention, step is as follows：
1), to sequentially adding aqueous acrylic emulsion, trifluoroacetylacetone (TFA) iron, flame retardant, ethylene glycol in dosing apparatus Butyl ether, ethyl acetate, dilauryl thiodipropionate, aluminium triphosphate, titanium dioxide, trbasic zinc phosphate, warming while stirring to 75 DEG C, Then stirring mixing 0.5 hour；
2), keeping temperature be 75 DEG C, sequentially add anti-corrosive aids, levelling agent, defoamer, nano titanium oxide, calcium carbonate, Talcum powder, curing agent, wetting agent, dispersant, adhesive agent, Herba Asari extract, deionized water, stirring mixing 2 hours.
Beneficial effects of the present invention are mainly manifested in：
Environment protecting water-based paint, it is environmentally friendly, in the absence of harm environment and the component of air.Preparation method technological design is closed Reason, production efficiency is high.
Specific embodiment
Embodiment 1
A kind of environment protecting water-based paint, is made up of the raw material of following weight portion：
30 parts of aqueous acrylic emulsion,
8 parts of trifluoroacetylacetone (TFA) iron,
9 parts of flame retardant,
7 parts of butyl glycol ether,
7 parts of ethyl acetate,
6 parts of dilauryl thiodipropionate,
9 parts of aluminium triphosphate,
8.5 parts of titanium dioxide,
9.5 parts of trbasic zinc phosphate,
10 parts of anti-corrosive aids,
11 parts of levelling agent,
7.5 parts of defoamer,
8 parts of nano titanium oxide,
6.5 parts of calcium carbonate,
8 parts of talcum powder,
8 parts of curing agent,
7 parts of wetting agent,
8 parts of dispersant,
6.5 parts of adhesive agent,
7.5 parts of Herba Asari extract (by asarum plus its 5 times of water of weight, is decocted, filtrate is condensed into stream leaching after filtering Cream, then dries and obtains powdered extract),
12.5 parts of deionized water.
The preparation method of environment protecting water-based paint, step is as follows：
1), to sequentially adding aqueous acrylic emulsion, trifluoroacetylacetone (TFA) iron, flame retardant, ethylene glycol in dosing apparatus Butyl ether, ethyl acetate, dilauryl thiodipropionate, aluminium triphosphate, titanium dioxide, trbasic zinc phosphate, warming while stirring to 75 DEG C, Then stirring mixing 0.5 hour；
2), keeping temperature be 75 DEG C, sequentially add anti-corrosive aids, levelling agent, defoamer, nano titanium oxide, calcium carbonate, Talcum powder, curing agent, wetting agent, dispersant, adhesive agent, Herba Asari extract, deionized water, stirring mixing 2 hours.
Embodiment 2
A kind of environment protecting water-based paint, is made up of the raw material of following weight portion：
20 parts of aqueous acrylic emulsion,
12 parts of trifluoroacetylacetone (TFA) iron,
6 parts of flame retardant,
12 parts of butyl glycol ether,
4 parts of ethyl acetate,
12 parts of dilauryl thiodipropionate,
5 parts of aluminium triphosphate,
12 parts of titanium dioxide,
7 parts of trbasic zinc phosphate,
11 parts of anti-corrosive aids,
6 parts of levelling agent,
9 parts of defoamer,
3 parts of nano titanium oxide,
8 parts of calcium carbonate,
4 parts of talcum powder,
10 parts of curing agent,
3 parts of wetting agent,
11 parts of dispersant,
2 parts of adhesive agent,
10 parts of Herba Asari extract,
15 parts of deionized water.
Preparation method is with embodiment 1.
Embodiment 3
A kind of environment protecting water-based paint, is made up of the raw material of following weight portion：
40 parts of aqueous acrylic emulsion,
5 parts of trifluoroacetylacetone (TFA) iron,
11 parts of flame retardant,
5 parts of butyl glycol ether,
10 parts of ethyl acetate,
5 parts of dilauryl thiodipropionate,
10 parts of aluminium triphosphate,
5 parts of titanium dioxide,
12 parts of trbasic zinc phosphate,
5 parts of anti-corrosive aids,
12 parts of levelling agent,
5 parts of defoamer,
12 parts of nano titanium oxide,
5 parts of calcium carbonate,
12 parts of talcum powder,
5 parts of curing agent,
13 parts of wetting agent,
5 parts of dispersant,
12 parts of adhesive agent,
4 parts of Herba Asari extract,
10 parts of deionized water.
Preparation method is with embodiment 1.
Below with reference to embodiment, the present invention is described in detail.But, embodiment content is only to this hair Bright example and explanation, affiliated those skilled in the art do various repairing to described specific embodiment Change or supplement or using similar mode substitute, without departing from invention design or surmount defined in the claims Scope, all should belong to protection scope of the present invention.

Claims (3)

1. a kind of environment protecting water-based paint, it is characterised in that：It is made up of the raw material of following weight portion：
Aqueous acrylic emulsion 20-40 parts,
5-12 parts of trifluoroacetylacetone (TFA) iron,
Flame retardant 6-11 parts,
Butyl glycol ether 5-12 parts,
Ethyl acetate 4-10 parts,
Dilauryl thiodipropionate 5-12 parts,
Aluminium triphosphate 5-10 parts,
Titanium dioxide 5-12 parts,
Trbasic zinc phosphate 7-12 parts,
Anti-corrosive aids 5-11 parts,
Levelling agent 6-12 parts,
Defoamer 5-9 parts,
Nano titanium oxide 3-12 parts,
Calcium carbonate 5-8 parts,
Talcum powder 4-12 parts,
Curing agent 5-10 parts,
Wetting agent 3-13 parts,
Dispersant 5-11 parts,
Adhesive agent 2-12 parts,
Herba Asari extract 4-10 parts,
Deionized water 10-15 parts.
2. a kind of environment protecting water-based paint as claimed in claim 1, it is characterised in that be made up of the raw material of following weight portion：
30 parts of aqueous acrylic emulsion,
8 parts of trifluoroacetylacetone (TFA) iron,
9 parts of flame retardant,
7 parts of butyl glycol ether,
7 parts of ethyl acetate,
6 parts of dilauryl thiodipropionate,
9 parts of aluminium triphosphate,
8.5 parts of titanium dioxide,
9.5 parts of trbasic zinc phosphate,
10 parts of anti-corrosive aids,
11 parts of levelling agent,
7.5 parts of defoamer,
8 parts of nano titanium oxide,
6.5 parts of calcium carbonate,
8 parts of talcum powder,
8 parts of curing agent,
7 parts of wetting agent,
8 parts of dispersant,
6.5 parts of adhesive agent,
7.5 parts of Herba Asari extract,
12.5 parts of deionized water.
3. a kind of method for preparing environment protecting water-based paint as claimed in claim 1 or 2, it is characterised in that step is as follows：
1), to sequentially added in dosing apparatus aqueous acrylic emulsion, trifluoroacetylacetone (TFA) iron, flame retardant, butyl glycol ether, Ethyl acetate, dilauryl thiodipropionate, aluminium triphosphate, titanium dioxide, trbasic zinc phosphate, warming while stirring to 75 DEG C, then Stirring mixing 0.5 hour；
2), keeping temperature is 75 DEG C, sequentially adds anti-corrosive aids, levelling agent, defoamer, nano titanium oxide, calcium carbonate, talcum Powder, curing agent, wetting agent, dispersant, adhesive agent, Herba Asari extract, deionized water, stirring mixing 2 hours.
CN201710063531.9A 2017-02-03 2017-02-03 A kind of environment protecting water-based paint and preparation method thereof Pending CN106833199A (en)