CN101260269A - Water aluminum powder paint and preparation method thereof - Google Patents
Water aluminum powder paint and preparation method thereof Download PDFInfo
- Publication number
- CN101260269A CN101260269A CNA2008100235459A CN200810023545A CN101260269A CN 101260269 A CN101260269 A CN 101260269A CN A2008100235459 A CNA2008100235459 A CN A2008100235459A CN 200810023545 A CN200810023545 A CN 200810023545A CN 101260269 A CN101260269 A CN 101260269A
- Authority
- CN
- China
- Prior art keywords
- agent
- water
- raw material
- add
- alcohol ester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to environment-friendly anticorrosive paint, in particular to aqueous silver paint and a preparation method thereof. The product is formed by inorganic raw materials which comprise deionized water, aqueous acrylic emulsion, inorganically coating aqueous silver paste, nontoxic and high-efficient anticorrosive pigment, aluminum triphosphate, zinc phosphate, zinc oxide, flash-rust inhibitor, surfactant, surface smooth and scratch-resistant agent, pH value regulator, alcohol ester 12 film forming aid, defoaming agent and thickening agent, does not perform an oxidization reaction with trace elements in the atmosphere, can be silvery white and bright for a long time, does not get dark and fade, belongs to a penetration type product, has strong adhesive force, does not peel and fall off, is high temperature resistant, and can be painted on the layers with higher surface temperature, such as high-temperature metal parts of motorcycles, automobile vent pipes, internal combustion engine shells, barbecue ovens, electromagnetic ovens, heat exchangers, smoke box inner walls, and heating oven inner walls and so on.
Description
Technical field
The present invention relates to a kind of environment friendly corrosion protection coating, specifically a kind of water aluminum powder paint and preparation method thereof.
Background technology
Traditional dissolvent type silver powder paint belongs to the covering type, and silver powder easily comes off, employing be organic material, oxidation blackening phenomena such as usually occur to send out crow, fade.Be simple decorative effect, only make finish paint and use.Used thinner is organic solvents such as dimethylbenzene, gasoline, irritating smell is bigger, and is inflammable and explosive, the heavy metal content severe overweight that volatile organic compounds and lead, mercury, chromium etc. are pernicious to people, human body and environment are caused great harm, do not have good terms of settlement so far.
Summary of the invention
The purpose of this invention is to provide a kind of rust-stabilising pigment that contains, brushing is at the existing decorative effect in steel construction surface, have anticorrosion again, rust inhibition, can with the matching used water aluminum powder paint of any priming paint, this product is made of inorganic raw material, not with atmosphere in trace element produce oxidizing reaction, the permanent silvery white light that keeps, do not send out crow, do not fade, belong to the osmosis type product, strong adhesion, non-scale, do not come off, and high temperature resistant, can brush on the higher aspect of surface temperature, as motorcycle, automobile exhaust pipe, the oil engine shell, oven, electromagnetic oven, heat exchanger, cigarette, on the high temperature metal partss such as baking oven inwall, overcome the deficiencies in the prior art part.
The objective of the invention is to realize with following technical scheme: a kind of water aluminum powder paint is characterized in that:
(1) component of the present invention is: deionized water, aqueous acrylic emulsion, inorganic coating water-based silver slurry, non-toxic efficient corrosion-inhibiting pigment, aluminium triphosphate, zinc phosphate, zinc oxide, anti-rust agent, tensio-active agent, the smooth and anti-zoned trace agent in surface, pH value conditioning agent, alcohol ester 12 film coalescence aid, defoamer, the thickening material of dodging;
(2) main raw material weight part of the present invention is: deionized water 38-40 part, aqueous acrylic emulsion 40-42 part, inorganic coating water-based silver slurry 8-10 part, non-toxic efficient corrosion-inhibiting pigment 0.4-0.5 part, aluminium triphosphate 0.6-0.7 part, 0.4 part of zinc phosphate, 0.5 part in zinc oxide, 2 parts of anti-sudden strain of a muscle rust agent, tensio-active agent 1.1-1.2 part, 0.5 part of the smooth and anti-zoned trace agent in surface, pH value conditioning agent 0.8-0.9 part, alcohol ester 12 film coalescence aid 1.8-2 parts, 0.5 part of defoamer, thickening material 0.9-1 part.
The preparation method of described a kind of water aluminum powder paint carries out as follows;
(1) weighs desired raw material on request;
(2) add the non-toxic efficient corrosion-inhibiting pigment in deionized water, aluminium triphosphate, zinc phosphate, zinc oxide, the agent of anti-sudden strain of a muscle rust mix;
(3) raw material that above-mentioned warp was fully stirred is roughly ground sand, fine grinding sand;
(4) in the raw material behind sand milling, add the aqueous acrylic emulsion stirring and slowly add tensio-active agent, inorganic coating water-based silver slurry, the smooth and anti-zoned trace agent in surface, defoamer, pH value conditioning agent, alcohol ester 12 film coalescence aid more in order, add thickening material at whipping process when spending when temperature reaches 35-40 ℃, regulate required viscosity;
(5) finished product is crossed 220 mesh sieves, after can, put in storage.
Advantage of the present invention is: 1, environmental protection, and nonpoisonous and tasteless, thinner is a water, content of volatile organic compound is zero, does not contain harmful heavy metal, has solved the harm problem to human body and environment well.2, strong adhesion, and acid-fast alkali-proof, salt spray resistance can be secular high temperature resistant, overcome the disadvantage that traditional silver paint is not practicable for the high temperature surface.3, can keep silvery white light, high gloss for a long time, avoid the oxidation blackening phenomena, be ornamental splendid, anticorrosion better Green Product.
The invention will be further described below in conjunction with embodiment;
Embodiment 1.
A kind of water aluminum powder paint is characterized in that:
(1) component of the present invention is: deionized water, aqueous acrylic emulsion, inorganic coating water-based silver slurry, non-toxic efficient corrosion-inhibiting pigment, aluminium triphosphate, zinc phosphate, zinc oxide, anti-rust agent, tensio-active agent, the smooth and anti-zoned trace agent in surface, pH value conditioning agent, alcohol ester 12 film coalescence aid, defoamer, the thickening material of dodging;
(2) main raw material weight part of the present invention is: 39 parts of deionized waters, 41 parts of aqueous acrylic emulsions, 9 parts in inorganic coating water-based silver slurry, 0.4 part of non-toxic efficient corrosion-inhibiting pigment, 0.6 part of aluminium triphosphate, 0.4 part of zinc phosphate, 0.5 part in zinc oxide, anti-2 parts of agent of rust, 1.1 parts in tensio-active agent, 0.5 part of the smooth and anti-zoned trace agent in surface, 0.8 part of pH value conditioning agent, 1.8 parts of alcohol ester 12 film coalescence aid, 0.5 part of defoamer, 0.9 part of the thickening material of dodging.
The preparation method of described a kind of water aluminum powder paint carries out as follows;
(1) weighs desired raw material on request;
(2) add the non-toxic efficient corrosion-inhibiting pigment in deionized water, aluminium triphosphate, zinc phosphate, zinc oxide, the agent of anti-sudden strain of a muscle rust mix;
(3) raw material that above-mentioned warp was fully stirred is roughly ground sand, fine grinding sand;
(4) adding aqueous acrylic emulsion in the raw material behind sand milling stirs, slowly add tensio-active agent, inorganic coating water-based silver slurry, the smooth and anti-zoned trace agent in surface, defoamer, pH value conditioning agent, alcohol ester 12 film coalescence aid more in order, add thickening material at whipping process when spending when temperature reaches 35 ℃, regulate required viscosity;
(5) finished product is crossed 220 mesh sieves, after can, put in storage.
Embodiment 2.
A kind of water aluminum powder paint is characterized in that:
(1) component of the present invention is: deionized water, aqueous acrylic emulsion, inorganic coating water-based silver slurry, non-toxic efficient corrosion-inhibiting pigment, aluminium triphosphate, zinc phosphate, zinc oxide, anti-rust agent, tensio-active agent, the smooth and anti-zoned trace agent in surface, pH value conditioning agent, alcohol ester 12 film coalescence aid, defoamer, the thickening material of dodging;
(2) main raw material weight part of the present invention is: 40 parts of deionized waters, 42 parts of aqueous acrylic emulsions, 10 parts in inorganic coating water-based silver slurry, 0.5 part of non-toxic efficient corrosion-inhibiting pigment, 0.7 part of aluminium triphosphate, 0.4 part of zinc phosphate, 0.5 part in zinc oxide, anti-2 parts of agent of rust, 1.2 parts in tensio-active agent, 0.5 part of the smooth and anti-zoned trace agent in surface, 0.9 part of pH value conditioning agent, 2 parts of alcohol ester 12 film coalescence aid, 0.5 part of defoamer, 1 part of the thickening material of dodging.
The preparation method of described a kind of water aluminum powder paint carries out as follows;
(1) weighs desired raw material on request;
(2) add the non-toxic efficient corrosion-inhibiting pigment in deionized water, aluminium triphosphate, zinc phosphate, zinc oxide, the agent of anti-sudden strain of a muscle rust mix;
(3) raw material that above-mentioned warp was fully stirred is roughly ground sand, fine grinding sand;
(4) in the raw material behind sand milling, add the aqueous acrylic emulsion stirring and slowly add tensio-active agent, inorganic coating water-based silver slurry, the smooth and anti-zoned trace agent in surface, defoamer, pH value conditioning agent, alcohol ester 12 film coalescence aid more in order, add thickening material at whipping process when spending when temperature reaches 40 ℃, regulate required viscosity;
(5) finished product is crossed 220 mesh sieves, after can, put in storage.
Claims (2)
1, a kind of water aluminum powder paint is characterized in that: (1) component of the present invention is: deionized water, aqueous acrylic emulsion, inorganic coating water-based silver slurry, non-toxic efficient corrosion-inhibiting pigment, aluminium triphosphate, zinc phosphate, zinc oxide, anti-rust agent, tensio-active agent, the smooth and anti-zoned trace agent in surface, pH value conditioning agent, alcohol ester 12 film coalescence aid, defoamer, the thickening material of dodging;
(2) main raw material weight part of the present invention is: deionized water 38-40 part, aqueous acrylic emulsion 40-42 part, inorganic coating water-based silver slurry 8-10 part, non-toxic efficient corrosion-inhibiting pigment 0.4-0.5 part, aluminium triphosphate 0.6-0.7 part, 0.4 part of zinc phosphate, 0.5 part in zinc oxide, 2 parts of anti-sudden strain of a muscle rust agent, tensio-active agent 1.1-1.2 part, 0.5 part of the smooth and anti-zoned trace agent in surface, pH value conditioning agent 0.8-0.9 part, alcohol ester 12 film coalescence aid 1.8-2 parts, 0.5 part of defoamer, thickening material 0.9-1 part.
2, the preparation method of the described a kind of water aluminum powder paint of a kind of claim 1 is characterized in that: carry out as follows;
(2) weigh desired raw material on request;
(2) add the non-toxic efficient corrosion-inhibiting pigment in deionized water, aluminium triphosphate, zinc phosphate, zinc oxide, the agent of anti-sudden strain of a muscle rust mix;
(3) raw material that above-mentioned warp was fully stirred is roughly ground sand, fine grinding sand;
(4) in the raw material behind sand milling, add the aqueous acrylic emulsion stirring and slowly add tensio-active agent, inorganic coating water-based silver slurry, the smooth and anti-zoned trace agent in surface, defoamer, pH value conditioning agent, alcohol ester 12 film coalescence aid more in order, add thickening material at whipping process when spending when temperature reaches 35-40 ℃, regulate required viscosity;
(5) finished product is crossed 220 mesh sieves, after can, put in storage.