CN106832945A - A kind of anti-aging cable cover(ing) formula of high temperature resistant - Google Patents
A kind of anti-aging cable cover(ing) formula of high temperature resistant Download PDFInfo
- Publication number
- CN106832945A CN106832945A CN201611262395.8A CN201611262395A CN106832945A CN 106832945 A CN106832945 A CN 106832945A CN 201611262395 A CN201611262395 A CN 201611262395A CN 106832945 A CN106832945 A CN 106832945A
- Authority
- CN
- China
- Prior art keywords
- parts
- ing
- formula
- high temperature
- temperature resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-aging cable cover(ing) formula of high temperature resistant, including phenylate support silicon rubber, phenylene silicone rubber, fire retardant, antioxidant, plasticizer, antistatic additive and foaming agent, the phenylate support silicon rubber is 50 80 parts, phenylene silicone rubber is 20 30 parts, the fire retardant is 10 20 parts, the antioxidant is 5 10 parts, the plasticizer is 38 parts, and the antistatic additive is 13 parts, and the foaming agent is 15 parts.The cable product that the present invention is made is fire-retardant, anti-aging, durable, economical and practical.
Description
Technical field
The present invention relates to a kind of anti-aging cable cover(ing) formula of high temperature resistant, belong to field of cable technology.
Background technology
Cable is the basis of modern society's electric power, and electric power is the basis for bringing up modern civilization society, with modern society
Development, requirement to cable height all the more, it is necessary to cable has high temperature resistant, the advantages of fire-retardant.
The content of the invention
To overcome above-mentioned deficiency, the object of the invention to provide a kind of anti-aging cable cover(ing) formula of high temperature resistant.
The solution of the present invention is as follows：A kind of anti-aging cable cover(ing) formula of high temperature resistant, including phenylate support silicon rubber, penylene
Silicon rubber, fire retardant, antioxidant, plasticizer, antistatic additive and foaming agent, the phenylate support silicon rubber is 50-80 parts, penylene
Silicon rubber is 20-30 parts, and the fire retardant is 10-20 parts, the antioxidant is 5-10 parts, and the plasticizer is 3-8 parts, institute
It is 1-3 parts to state antistatic additive, and the foaming agent is 1-5 parts, and the fire retardant is by 10-15 parts of MAP and 5-10 parts of hydrogen-oxygen
Change magnesium composition, the antioxidant is that, by 3-8 parts of dibutyl hydroxy toluene and 1-5 portions of propylgallate, the plasticizer is
It is made up of 1-5 parts of diisobutyl phthalate and 2-6 parts of phthalic acid quinoline ester, the antistatic additive is by 1-2 parts of ethoxy
Base alkylamine and the 0.5-1.5 parts of cruel amine composition of ethyoxyl bay, the foaming agent is by 1-3 parts of calcium carbonate and 2-4 parts of trichlorine
Difluoromethane is constituted, and a kind of anti-aging cable cover(ing) formula of high temperature resistant is to support silicon rubber, 25 parts of penylene silicon by 60 parts of phenylates
Rubber, 12 parts of MAPs, 8 parts of magnesium hydroxides, 4 parts of dibutyl hydroxy toluenes, 3 portions of propylgallates, 2 parts of phthalic acids
Diisobutyl ester, 3 parts of phthalic acid quinoline esters, 1 part of ethoxylated alkylamine, 1 part of cruel amine of ethyoxyl bay, 1 part of calcium carbonate and 2 parts
Three dichlorodifluoromethanes are constituted.
Beneficial effects of the present invention：The cable product that the present invention is made is fire-retardant, anti-aging, durable, high temperature resistant.
Specific embodiment
A kind of anti-aging cable cover(ing) formula of high temperature resistant, including phenylate support silicon rubber, phenylene silicone rubber, fire retardant, antioxygen
Agent, plasticizer, antistatic additive and foaming agent, the phenylate support silicon rubber is 50-80 parts, and phenylene silicone rubber is 20-30 parts, institute
Fire retardant is stated for 10-20 parts, the antioxidant are 5-10 parts, the plasticizer is 3-8 parts, and the antistatic additive is 1-3 parts,
The foaming agent is 1-5 parts, and the fire retardant is made up of 10-15 parts of MAP and 5-10 parts of magnesium hydroxide, the antioxygen
Agent is that, by 3-8 parts of dibutyl hydroxy toluene and 1-5 portions of propylgallate, the plasticizer is by 1-5 parts of phthalic acid
Diisobutyl ester and 2-6 parts of phthalic acid quinoline ester composition, the antistatic additive is by 1-2 parts of ethoxylated alkylamine and 0.5-
1.5 parts of cruel amine compositions of ethyoxyl bay, the foaming agent is made up of 1-3 parts of calcium carbonate and 2-4 parts of three dichlorodifluoromethanes, described
A kind of anti-aging cable cover(ing) formula of high temperature resistant is to support silicon rubber, 25 parts of phenylene silicone rubbers, 12 parts of phosphoric acid one by 60 parts of phenylates
Ammonium, 8 parts of magnesium hydroxides, 4 parts of dibutyl hydroxy toluenes, 3 portions of propylgallates, 2 parts of diisobutyl phthalates, 3 parts of neighbours
Phthalic acid quinoline ester, 1 part of ethoxylated alkylamine, 1 part of cruel amine of ethyoxyl bay, 1 part of calcium carbonate and 2 part of three dichlorodifluoromethane group
Into.
Although detailed description being given to specific embodiment of the invention above and being illustrated, it should be noted that
We can carry out various equivalent changes and modification to above-mentioned implementation method according to conception of the invention, and the function produced by it is made
With still without departing from specification covered it is spiritual when, all should be within protection scope of the present invention.
Claims (7)
1. it is a kind of anti-aging cable cover(ing) formula of high temperature resistant, including phenylate support silicon rubber, phenylene silicone rubber, fire retardant, anti-oxidant
Agent, plasticizer, antistatic additive and foaming agent, it is characterised in that：The phenylate support silicon rubber is 50-80 parts, and phenylene silicone rubber is
20-30 parts, the fire retardant is 10-20 parts, the antioxidant is 5-10 parts, and the plasticizer is 3-8 parts, described antistatic
Agent is 1-3 parts, and the foaming agent is 1-5 parts.
2. the anti-aging cable cover(ing) formula of a kind of high temperature resistant according to claim 1, it is characterised in that：The fire retardant is
It is made up of 10-15 parts of MAP and 5-10 parts of magnesium hydroxide.
3. the anti-aging cable cover(ing) formula of a kind of high temperature resistant according to claim 1, it is characterised in that：The antioxidant
It is by 3-8 parts of dibutyl hydroxy toluene and 1-5 portions of propylgallate.
4. the anti-aging cable cover(ing) formula of a kind of high temperature resistant according to claim 1, it is characterised in that：The plasticizer is
It is made up of 1-5 parts of diisobutyl phthalate and 2-6 parts of phthalic acid quinoline ester.
5. the anti-aging cable cover(ing) formula of a kind of high temperature resistant according to claim 1, it is characterised in that：The antistatic additive
It is made up of 1-2 parts of ethoxylated alkylamine and the 0.5-1.5 parts of cruel amine of ethyoxyl bay.
6. the anti-aging cable cover(ing) formula of a kind of high temperature resistant according to claim 1, it is characterised in that：The foaming agent is
It is made up of 1-3 parts of calcium carbonate and 2-4 parts of three dichlorodifluoromethanes.
7. the anti-aging cable cover(ing) formula of a kind of high temperature resistant according to claim 1, it is characterised in that：A kind of resistance to height
The anti-aging cable cover(ing) formula of temperature is to support silicon rubber, 25 parts of phenylene silicone rubbers, 12 parts of MAPs, 8 parts of hydrogen-oxygens by 60 parts of phenylates
Change magnesium, 4 parts of dibutyl hydroxy toluenes, 3 portions of propylgallates, 2 parts of diisobutyl phthalates, 3 parts of phthalic acid quinolines
Ester, 1 part of ethoxylated alkylamine, 1 part of cruel amine of ethyoxyl bay, 1 part of calcium carbonate and 2 part of three dichlorodifluoromethane composition.