CN106832841A - A kind of unsaturated polyester resin fiberglass preparation method - Google Patents
A kind of unsaturated polyester resin fiberglass preparation method Download PDFInfo
- Publication number
- CN106832841A CN106832841A CN201611238250.4A CN201611238250A CN106832841A CN 106832841 A CN106832841 A CN 106832841A CN 201611238250 A CN201611238250 A CN 201611238250A CN 106832841 A CN106832841 A CN 106832841A
- Authority
- CN
- China
- Prior art keywords
- polyester resin
- unsaturated polyester
- preparation
- resin fiberglass
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides unsaturated polyester resin fiberglass preparation method, its raw material for including following parts by weight:Unsaturated polyester resin 60~90, shrinking agent 8~20, curing agent 1~5, releasing agent 6~8, filler 15~30, reinforcing material 30~50, the characteristics of unsaturated polyester resin fiberglass of the invention has that intensity is good, shrinks low, good impact resistance.
Description
Technical field
The present invention relates to field of compound material, more particularly to a kind of unsaturated polyester resin fiberglass preparation method.
Background technology
Polyester fiberglass steel composite material generally refers to one kind chemistry obtained with glass fiber reinforced unsaturated polyester resin
Composite.The unsaturated polyester die plastic of glass fiber reinforcement, it is high with intensity, the characteristics of excellent electrical property, but solidification
Its property is crisp afterwards and impact resistance it is not high be its shortcoming, therefore for being used in during impact structure part, often ftracture, it is disconnected
The phenomenon such as split.It is difficult to meet the requirement that some special occasions are used, such as Aero-Space, automobile, building, body-building apparatus.
The content of the invention
It is an object of the present invention in view of the shortcomings of the prior art, there is provided prepared by a kind of unsaturated polyester resin fiberglass
Method, to solve above-mentioned technical problem.
The technical scheme that is used to achieve the above object of the present invention for:
A kind of unsaturated polyester resin fiberglass preparation method, its raw material for including following parts by weight:
Its preparation method is as follows:Unsaturated polyester resin, curing agent first above-mentioned weight are added in beater, quickly
Stirring 4~6 minutes, the curing agent for being subsequently adding above-mentioned weight continues to stir 10~15 minutes, next, by the slurry for stirring
Material is mediated 3~5 minutes in moving into kneader, then sequentially add and mediate after hard releasing agent, the filler component of above-mentioned weight 15~
20 minutes, continue to mediate 5~10 minutes after being eventually adding reinforcing material composition by weight, that is, obtain unsaturated polyester resin glass
Steel.
Preferably, described unsaturated polyester resin is metaphenylene unsaturated polyester resin.
Preferably, described unsaturated polyester resin is m-phthalate unsaturated polyester resin.
Preferably, described shrinking agent is polymethyl methacrylate type shrinking agent.
Preferably, described solidfied material is peroxide.
Preferably, described releasing agent is zinc stearate or calcium stearate.
Preferably, described reinforcing material is organic fiber.
Preferably, described reinforcing material is Graphite cloth's band.
Preferably, described reinforcing material is glass rove.
Unsaturated polyester resin fiberglass obtained in the unsaturated polyester resin fiberglass preparation method that the present invention is provided, tool
The characteristics of having good intensity, low contraction, good impact resistance.Can be used to impact and require part high.
Specific embodiment
Embodiment 1
A kind of unsaturated polyester resin fiberglass preparation method, its raw material for including following parts by weight are provided:
During specific implementation, the metaphenylene unsaturated polyester resin, polymethyl methacrylate type first above-mentioned weight are low
Contracting agent is added in beater, quick stirring 4 minutes, is subsequently adding cumyl peroxide of above-mentioned weight etc. and is continued to stir 15
Minute.Next, being mediated 5 minutes during the slurry for stirring is moved into kneader, the tristearin of above-mentioned weight is then sequentially added
Mediated 20 minutes after the components such as sour zinc, precipitated calcium carbonate, continue to mediate 5 minutes after being eventually adding organic fiber composition by weight.I.e.
Obtain the unsaturated polyester resin fiberglass preparation method material of true qualities.According to client need can also add corresponding color masterbatch with
It is made into the color of needs.
Embodiment 2
A kind of unsaturated polyester resin fiberglass preparation method, its raw material for including following parts by weight are provided:
During specific implementation, the metaphenylene unsaturated polyester resin, polymethyl methacrylate type first above-mentioned weight are low
Contracting agent is added in beater, quick stirring 4 minutes, is subsequently adding cumyl peroxide of above-mentioned weight etc. and is continued to stir 15
Minute.Next, being mediated 5 minutes during the slurry for stirring is moved into kneader, the tristearin of above-mentioned weight is then sequentially added
Mediated 20 minutes after the components such as sour calcium, precipitated calcium carbonate, continue to mediate 5 minutes after being eventually adding Graphite cloth's band component.Obtain
The unsaturated polyester resin fiberglass preparation method material of true qualities.Needed to add corresponding color masterbatch to be made into according to client
The color of needs.
Embodiment 3
A kind of unsaturated polyester resin fiberglass preparation method, its raw material for including following parts by weight are provided:
During specific implementation, the m-phthalate unsaturated polyester resin, polymethyl methacrylate type first above-mentioned weight are low
Contracting agent is added in beater, quick stirring 4 minutes, is subsequently adding cumyl peroxide of above-mentioned weight etc. and is continued to stir 15
Minute.Next, being mediated 5 minutes during the slurry for stirring is moved into kneader, the tristearin of above-mentioned weight is then sequentially added
Mediated 20 minutes after the components such as sour zinc, precipitated calcium carbonate, continue to mediate 5 minutes after being eventually adding glass rove component.Obtain
The unsaturated polyester resin fiberglass preparation method material of true qualities.Needed to add corresponding color masterbatch to be made into according to client
The color of needs.
There is the performance shown in following table after tested as the unsaturated polyester die plastic obtained by above example:
Certainly, this invention can also have other to convert, it is not limited to which above-mentioned implementation method, those skilled in the art are had
Standby knowledge, can also various changes can be made without departing from the inventive concept of the premise, such change all should fall in this hair
In bright protection domain.
Claims (9)
1. a kind of unsaturated polyester resin fiberglass preparation method, it is characterised in that its raw material for including following parts by weight:
Unsaturated polyester resin 60~90
Shrinking agent 8~20
Curing agent 1~5
Releasing agent 6~8
Filler 15~30
Reinforcing material 30~50
Its preparation method is as follows:Unsaturated polyester resin, curing agent first above-mentioned weight are added in beater, quick stirring
4~6 minutes, the curing agent for being subsequently adding above-mentioned weight continued to stir 10~15 minutes, next, the slurry for stirring is moved
Enter in kneader and mediate 3~5 minutes, 15~20 points are mediated after then sequentially adding hard releasing agent, the filler component of above-mentioned weight
Clock, continues to mediate 5~10 minutes after being eventually adding reinforcing material composition by weight, that is, obtain unsaturated polyester resin fiberglass.
2. unsaturated polyester resin fiberglass preparation method according to claim 1, it is characterised in that described unsaturation
Polyester resin is metaphenylene unsaturated polyester resin.
3. unsaturated polyester resin fiberglass preparation method according to claim 1, it is characterised in that described unsaturation
Polyester resin is m-phthalate unsaturated polyester resin.
4. unsaturated polyester resin fiberglass preparation method according to claim 1, it is characterised in that described lower shrinkage
Agent is polymethyl methacrylate type shrinking agent.
5. unsaturated polyester resin fiberglass preparation method according to claim 1, it is characterised in that described solidfied material
It is peroxide.
6. unsaturated polyester resin fiberglass preparation method according to claim 1, it is characterised in that described releasing agent
It is zinc stearate or calcium stearate.
7. unsaturated polyester resin fiberglass preparation method according to claim 1, it is characterised in that described strengthening material
Expect to be organic fiber.
8. unsaturated polyester resin fiberglass preparation method according to claim 1, it is characterised in that described strengthening material
Expect to be Graphite cloth's band.
9. unsaturated polyester resin fiberglass preparation method according to claim 1, it is characterised in that described strengthening material
Expect to be glass rove.