CN107057281A - A kind of fire retarding epoxide resin fiberglass - Google Patents
A kind of fire retarding epoxide resin fiberglass Download PDFInfo
- Publication number
- CN107057281A CN107057281A CN201611239382.9A CN201611239382A CN107057281A CN 107057281 A CN107057281 A CN 107057281A CN 201611239382 A CN201611239382 A CN 201611239382A CN 107057281 A CN107057281 A CN 107057281A
- Authority
- CN
- China
- Prior art keywords
- epoxide resin
- fire retarding
- retarding epoxide
- resin fiberglass
- fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides fire retarding epoxide resin fiberglass, it includes the raw material of following parts by weight：Epoxy resin 70~90, curing agent 10~15, releasing agent 2~5, filler 15~30, toughener 5~10, diluent 2~5, reinforcing material 10~25, fire retardant 15~25.The characteristics of fire retarding epoxide resin fiberglass of the present invention, excellent mechanical property, resistance to surface leakage, good impact resistance, good fire resistance.
Description
Technical field
The present invention relates to field of compound material, more particularly to a kind of fire retarding epoxide resin fiberglass.
Background technology
Glass-reinforced plastic material is to be embedded in cured thermosetting resin by fiber glass reinforcement or be wrapped to form by it
The material of composite construction.It is molded in the market more than the glass-reinforced plastic material of production and application using resin Sized glass cloth material.
This method effect of impregnation is good, and prepared content of glass fiber is high.But due to being limited by glass cloth volume and shape, make it special
The product that uniform-compression is difficult for pipe joint, tee pipe fitting, bend pipe tools etc. is not suitable with.In addition, prepared by this method
Glass-reinforced plastic material its impact resistance it is poor, and laminated face is easily layered.In order to solve the above problems, there is researcher by glass
It is that 1000 or so, length is 3~5mm glass fiber powders that glass fiber, which cuts into Fiber Aspect Ratio, then puts into glass fiber powder
Into the mixed liquor being made up of epoxy resin, plasticizer, silane coupler, then it is the addition filler that stirs in ball mill, solid
Agent, is thus prepared into a kind of glass-reinforced plastic material without glass cloth laying.Although the glass-reinforced plastic material gram that this method is provided
Glass cloth caused defect in itself has been taken, but because glass fibre is cut into powdery, thus its fiber is specific in itself
Physical characteristic is also weakened severely.Mode as composite absorbs impact energy is often deformed with Crack Extension extremely by resin
Fracture, fiber are extracted out, 3 kinds of modes of fibrous fracture.Thus it is not difficult to find out when the glass fibre in composite is embedded in powdery
In the thermosetting resin of solidification, when by external impacts, mealiness fiber can absorb energy when no longer there is fiber to extract out
Effect, while the energy that can be absorbed when also losing fibrous fracture.
The content of the invention
It is an object of the present invention in view of the shortcomings of the prior art there is provided a kind of fire retarding epoxide resin fiberglass, to solve
Above-mentioned technical problem.
The technical scheme that is used to achieve the above object of the present invention for：
A kind of fire retarding epoxide resin fiberglass, it includes the raw material of following parts by weight：
Preferably, described diluent is diepoxy propane ethylether.
Preferably, solidfied material is peroxide.
Preferably, described toughener is dioctyl phthalate.
Preferably, described releasing agent is zinc stearate or calcium stearate.
Preferably, described reinforcing material is organic fiber.
Preferably, described reinforcing material is Graphite cloth's band.
Preferably, described reinforcing material is glass rove.
Preferably, described fire retardant is melamine cyanurate.
The fire retarding epoxide resin fiberglass that the present invention is provided, with excellent mechanical property, resistance to surface leakage, impact resistance
Well, the characteristics of good fire resistance.
Embodiment
Embodiment 1
A kind of fire retarding epoxide resin fiberglass is provided, it includes the raw material of following parts by weight：
It is beaten when it is implemented, the epoxy resin, hydrogen peroxide, dioctyl phthalate of above-mentioned weight are added first
In machine, quick stirring 10 minutes.Mediate 5 minutes, then sequentially add next, the slurry stirred is moved into kneader
Mediated 20 minutes after the components such as zinc stearate, calcium carbonate, the melamine cyanurate of above-mentioned weight, be eventually adding diepoxy propane
Continue to mediate 5 minutes after ethylether, organic fiber composition by weight.Obtain the fire retarding epoxide resin glass-reinforced plastic material of true qualities.Root
According to client need that corresponding color masterbatch can also be added to be made into the color of needs.
Embodiment 2
A kind of fire retarding epoxide resin fiberglass is provided, it includes the raw material of following parts by weight：
When it is implemented, the epoxy resin, cumyl peroxide, dioctyl phthalate of above-mentioned weight are added first
Enter in beater, quick stirring 10 minutes.Next, will the slurry that stirred move into kneader in mediate 5 minutes, then according to
Mediated 20 minutes after the components such as secondary calcium stearate, barium sulfate, the melamine cyanurate for adding above-mentioned weight, be eventually adding two rings
Continue to mediate 5 minutes after Ethylene Oxide ethylether, Graphite cloth's band composition by weight.Obtain the fire retarding epoxide resin glass steel of true qualities
Material.According to client need that corresponding color masterbatch can also be added to be made into the color of needs.
Embodiment 3
A kind of fire retarding epoxide resin fiberglass is provided, it includes the raw material of following parts by weight：
When it is implemented, the epoxy resin, cumyl peroxide, dioctyl phthalate of above-mentioned weight are added first
Enter in beater, quick stirring 10 minutes.Next, will the slurry that stirred move into kneader in mediate 5 minutes, then according to
Mediated 20 minutes after the components such as secondary zinc stearate, calcium sulfate, the melamine cyanurate for adding above-mentioned weight, be eventually adding two rings
Continue to mediate 5 minutes after Ethylene Oxide ethylether, glass rove composition by weight.Obtain the fire retarding epoxide resin glass steel of true qualities
Material.According to client need that corresponding color masterbatch can also be added to be made into the color of needs.
There is the performance shown in following table after tested as the unsaturated polyester die plastic obtained by above example：
Certainly, this invention can also have other conversion, it is not limited to which above-mentioned embodiment, those skilled in the art are had
Standby knowledge, can also various changes can be made without departing from the inventive concept of the premise, such change all should fall in this hair
In bright protection domain.
Claims (9)
1. a kind of fire retarding epoxide resin fiberglass, it is characterised in that it includes the raw material of following parts by weight：
。
2. fire retarding epoxide resin fiberglass according to claim 1, it is characterised in that described diluent is diepoxy third
Alkane ethylether.
3. fire retarding epoxide resin fiberglass according to claim 1, it is characterised in that solidfied material is peroxide.
4. fire retarding epoxide resin fiberglass according to claim 1, it is characterised in that described toughener is O-phthalic
Dioctyl phthalate.
5. fire retarding epoxide resin fiberglass according to claim 1, it is characterised in that described releasing agent is zinc stearate
Or calcium stearate.
6. fire retarding epoxide resin fiberglass according to claim 1, it is characterised in that described reinforcing material is organic fibre
Dimension.
7. fire retarding epoxide resin fiberglass according to claim 1, it is characterised in that described reinforcing material is Graphite cloth
Band.
8. fire retarding epoxide resin fiberglass according to claim 1, it is characterised in that described reinforcing material is that glass is thick
Yarn.
9. fire retarding epoxide resin fiberglass according to claim 1, it is characterised in that described fire retardant is melamine
Lithate.