CN106832116A - 一种氨氮去除剂的制备方法 - Google Patents
一种氨氮去除剂的制备方法 Download PDFInfo
- Publication number
- CN106832116A CN106832116A CN201710134569.0A CN201710134569A CN106832116A CN 106832116 A CN106832116 A CN 106832116A CN 201710134569 A CN201710134569 A CN 201710134569A CN 106832116 A CN106832116 A CN 106832116A
- Authority
- CN
- China
- Prior art keywords
- parts
- added
- hours
- ammonia nitrogen
- nitrogen removal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种氨氮去除剂的制备方法,包括向反应釜中加入三羟甲基丙烷10‑18份,升温到60℃熔化;加入3‑5份乙醇胺,慢慢加入20‑40份马来酸酐,约1‑1.5小时加完;加完升温至100‑110℃,反应3‑5小时,降温至80‑85℃;加入100份蒸馏水,溶解后,向溶液中加入1‑3份十二醇马来酸酯钠;然后在80‑85℃下同时滴加丙烯酸羟丙酯6‑12份,丙烯酰胺水溶液18‑30份,引发剂溶液3‑5份,约3小时滴加完毕;保温反应2小时后,升温至90‑92℃反应0.5小时,然后降温至50‑60℃;加入四羟甲基硫酸磷‑尿素缩合物10‑15份,过碳酸钠2‑4份,反应1‑1.5小时,降至室温,出料。与现有技术相比,本发明的方法工艺流程少,步骤简单,操作简便,从而能够提高氨氮去除剂的制备效率,具有推广应用的价值。
Description
技术领域
本发明涉及一种化学药物制作技术,尤其涉及一种氨氮去除剂的制备方法。
背景技术
氨氮去除剂是污水处理中专门去除废水中氨氮的药剂总称。污水处理中专门去除废水中氨氮的药剂总称。氨氮去除剂主要有两类.一类是化学药剂.另一类是微生物药剂。化学药剂:通过投加化学药剂,使废水中的氨氮发生化学反应,此类方法较多,原理不一,比如磷酸钠和氯化镁属于常规的沉淀法,MT-501属于催化氧化法,氯气属于折点加氯法,但最终目的都是使废水氨氮降低。这种方法叫物化法。微生物药剂:微生物药剂通过投加经过人工驯化的,专门分解氨氮的微生物来去污.这种方法叫微生物法。现有技术中,氨氮去除剂的制备方法繁琐,制备效率低,因此,需要一种新的方法诞生。
发明内容
本发明的目的就在于为了解决上述问题而提供一种氨氮去除剂的制备方法。
本发明通过以下技术方案来实现上述目的:
本发明包括以下步骤:
(1)向反应釜中加入三羟甲基丙烷10-18份,升温到60℃熔化;
(2)加入3-5份乙醇胺,慢慢加入20-40份马来酸酐,约1-1.5小时加完;
(3)加完升温至100-110℃,反应3-5小时,降温至80-85℃;
(4)加入100份蒸馏水,溶解后,向溶液中加入1-3份十二醇马来酸酯钠;
(5)然后在80-85℃下同时滴加丙烯酸羟丙酯6-12份,丙烯酰胺水溶液18-30份,引发剂溶液3-5份,约3小时滴加完毕;
(6)保温反应2小时后,升温至90-92℃反应0.5小时,然后降温至50-60℃;
(7)加入四羟甲基硫酸磷-尿素缩合物10-15份,过碳酸钠2-4份,反应1-1.5小时,降至室温,出料。
具体地,所述步骤(5)中丙烯酰胺水溶液的质量百分比分数为30%。所述引发剂溶液的质量百分比为10%。
本发明的有益效果在于:
本发明是一种氨氮去除剂的制备方法,与现有技术相比,本发明的方法工艺流程少,步骤简单,操作简便,从而能够提高氨氮去除剂的制备效率,具有推广应用的价值。
具体实施方式
下面对本发明作进一步说明:
本发明包括以下步骤:
(1)向反应釜中加入三羟甲基丙烷10-18份,升温到60℃熔化;
(2)加入3-5份乙醇胺,慢慢加入20-40份马来酸酐,约1-1.5小时加完;
(3)加完升温至100-110℃,反应3-5小时,降温至80-85℃;
(4)加入100份蒸馏水,溶解后,向溶液中加入1-3份十二醇马来酸酯钠;
(5)然后在80-85℃下同时滴加丙烯酸羟丙酯6-12份,丙烯酰胺水溶液18-30份,引发剂溶液3-5份,约3小时滴加完毕;
(6)保温反应2小时后,升温至90-92℃反应0.5小时,然后降温至50-60℃;
(7)加入四羟甲基硫酸磷-尿素缩合物10-15份,过碳酸钠2-4份,反应1-1.5小时,降至室温,出料。
具体地,所述步骤(5)中丙烯酰胺水溶液的质量百分比分数为30%。所述引发剂溶液的质量百分比为10%。
以上显示和描述了本发明的基本原理和主要特征及本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (3)
1.一种氨氮去除剂的制备方法,其特征在于,包括以下步骤:
(1)向反应釜中加入三羟甲基丙烷10-18份,升温到60℃熔化;
(2)加入3-5份乙醇胺,慢慢加入20-40份马来酸酐,约1-1.5小时加完;
(3)加完升温至100-110℃,反应3-5小时,降温至80-85℃;
(4)加入100份蒸馏水,溶解后,向溶液中加入1-3份十二醇马来酸酯钠;
(5)然后在80-85℃下同时滴加丙烯酸羟丙酯6-12份,丙烯酰胺水溶液18-30份,引发剂溶液3-5份,约3小时滴加完毕;
(6)保温反应2小时后,升温至90-92℃反应0.5小时,然后降温至50-60℃;
(7)加入四羟甲基硫酸磷-尿素缩合物10-15份,过碳酸钠2-4份,反应1-1.5小时,降至室温,出料。
2.根据权利要求1所述的氨氮去除剂的制备方法,其特征在于:所述步骤(5)中丙烯酰胺水溶液的质量百分比分数为30%。
3.根据权利要求1所述的氨氮去除剂的制备方法,其特征在于:所述步骤(5)中引发剂溶液的质量百分比为10%。