CN106830997A - A kind of method for cooking after ceramic utensil glazing - Google Patents
A kind of method for cooking after ceramic utensil glazing Download PDFInfo
- Publication number
- CN106830997A CN106830997A CN201710043191.3A CN201710043191A CN106830997A CN 106830997 A CN106830997 A CN 106830997A CN 201710043191 A CN201710043191 A CN 201710043191A CN 106830997 A CN106830997 A CN 106830997A
- Authority
- CN
- China
- Prior art keywords
- base
- tea set
- glazing
- glaze
- cooking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides the method for cooking after a kind of ceramic utensil glazing, base used and preparation method thereof, the method for cooking is that the tea set that will soak glaze water is placed on base, base is fired again located at the bottom of tea set 1 along 3, and base is tapped after the completion of firing makes it come off；The base includes circular heelpiece and supporting table, and the supporting table is on heelpiece.The tea set that the present invention will have been soaked after glaze water is placed on base and is fired again, by base abate after the completion of firing, so as to can avoid the occurrence of tea set glaze water in sintering procedure flow downward accumulate in tea set bottom occur along 3 glaze water-water reactor product caking phenomenon, bottom can be obtained along 3 tea sets with complete glaze paint, improve the quality of tea set, make tea set glaze paint more complete, improve the integrated ornamental of tea set, the operation that polishing tea set bottom is along 3 is eliminated simultaneously, the production process of tea set is reduced, cost is reduced.
Description
Technical field：
The present invention relates to a kind of preparation method of ceramic utensil, and in particular to a kind of method for cooking after ceramic utensil glazing,
Base used and preparation method thereof.
Background technology：
When being fired after existing ceramic utensil glazing, its glaze water can flow downward and pile up caking or tea along upper at the bottom of tea set bottom
Tool bottom along can adhere on backing plate, cause bottom along the inadequate flat smooth in surface or it is viscous extremely cause substandard products, need to carry out polishing can
Using or directly break into pieces and cause decrease in yield, it is and no longer smooth through the surface on the bottom edge after polishing, reduce tea set overall
Aesthetic feeling, and the desktop that easily weares and teares, its usability are poor, and bottom is along the effect for being also not reaching to complete glaze paint.
The content of the invention：
It is contemplated that in overcoming the deficiencies in the prior art, there is provided a kind of method for cooking after ceramic utensil glazing, used
Base and preparation method thereof, the phenomenon lumpd is accumulated in its bottom along there is glaze water-water reactor after the present invention can avoid tea set from firing.
Method for cooking after ceramic utensil glazing of the invention, the technical scheme of use is：The tea of glaze water will have been soaked
Tool is placed on base, and base is fired again located at the bottom of tea set 1 along interior being fired again, and base is tapped after the completion of firing makes it
Come off.
Ceramic utensil glazing firing base of the invention, the technical scheme of use is：The base includes circular
Heelpiece and supporting table, the supporting table is on heelpiece.
The preparation method of above-mentioned base is：Dried after the completion of the disposable roll forming of base or manual slip casting, it is desirable to base
Body Heshui rate deviation is less than ± 15%.
The beneficial effects of the invention are as follows：The tea set that the present invention will have been soaked after glaze water is placed on base and is fired again, burns
By base abate after the completion of system, the bottom edge of tea set is accumulated in so as to tea set glaze water in sintering procedure can be avoided the occurrence of and flowed downward
Above there is the phenomenon of glaze water-water reactor product caking or cause porcelain to cause decrease in yield with backing plate adhesion, can obtain bottom edge has had
The tea set of whole glaze paint, improves the quality of tea set, makes tea set glaze paint more complete, improves the integrated ornamental of tea set, while saving
The operation on polishing tea set bottom edge has been omited, the production process of tea set has been reduced, cost has been reduced.
Brief description of the drawings：
Fig. 1 is structural representation of the invention,
Fig. 2 is understructure figure of the invention.
Specific embodiment：
Reference picture 1, the method for cooking after the ceramic utensil glazing is that the tea set 1 that will soak glaze water is placed on base, base
It is fired again along 3 located at the bottom of tea set 1, base is tapped after the completion of firing makes it come off.
The ceramic utensil glazing firing base, including circular heelpiece 2 and supporting table 4, the supporting table 4 are located at heelpiece
On 2.
The preparation method of above-mentioned base is：First pass through rolling mill or slip casting to complete the shaping of base substrate branch, drying after forming makes
Its moisture content is consistent with tea set base substrate moisture content.
Claims (3)
1. the method for cooking after a kind of ceramic utensil glazing, it is characterised in that：The tea set 1 that glaze water will have been soaked is placed on base
On, base is fired again located at the bottom of tea set 1 along 3, and base is tapped after the completion of firing makes it come off.
2. a kind of ceramic utensil glazing firing base, it is characterised in that：The base includes circular heelpiece 2 and supporting table 4,
The supporting table 4 is on heelpiece 2.
3. a kind of preparation method of ceramic utensil glazing firing base, it is characterised in that：The disposable roll forming of base or hand
Dried after the completion of work slip casting.