CN107879764A - A kind of method for cooking after ceramic utensil glazing - Google Patents
A kind of method for cooking after ceramic utensil glazing Download PDFInfo
- Publication number
- CN107879764A CN107879764A CN201610868439.5A CN201610868439A CN107879764A CN 107879764 A CN107879764 A CN 107879764A CN 201610868439 A CN201610868439 A CN 201610868439A CN 107879764 A CN107879764 A CN 107879764A
- Authority
- CN
- China
- Prior art keywords
- tea set
- base
- glazing
- cooking
- glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides the method for cooking after a kind of ceramic utensil glazing, base used and preparation method thereof, the method for cooking is that the tea set for having soaked glaze water is placed on base, base with located at tea set bottom project through bonding agent it is Nian Jie it is integral after be fired again, percussion base makes it come off after the completion of firing；The base includes circular heelpiece and connected unit, and the connected unit is at the center of heelpiece upper surface.Tea set after having soaked glaze water is placed on base and is fired again by the present invention, by base abate after the completion of firing, flow downward so as to avoiding the occurrence of tea set glaze water in sintering procedure and accumulate in the bottom of tea set along upper and the phenomenon of glaze water-water reactor product caking occur, bottom can be obtained along the tea set with complete glaze paint, the quality of tea set is improved, make tea set glaze paint more complete, improve the integrated ornamental of tea set, the operation on polishing tea set bottom edge is eliminated simultaneously, is reduced the production process of tea set, is reduced cost.
Description
Technical field：
The present invention relates to a kind of preparation method of ceramic utensil, and in particular to method for cooking, institute after a kind of ceramic utensil glazing
With base and preparation method thereof.
Background technology：
When being fired after existing ceramic utensil glazing, its glaze water can flow downward and accumulate caking or tea along upper at the bottom of tea set bottom
Tool bottom along can adhere on backing plate, cause bottom along the inadequate flat smooth in surface or it is viscous extremely cause substandard products, need to carry out polishing can
Using or directly break into pieces and cause decrease in yield, and the surface on the bottom edge after polishing is no longer smooth, and it is overall to reduce tea set
Aesthetic feeling, and desktop is easily worn, its usability is poor.
The content of the invention：
It is contemplated that in overcome the deficiencies in the prior art, there is provided method for cooking, bottom used after a kind of ceramic utensil glazing
Seat and preparation method thereof, there is the phenomenon of glaze water-water reactor product caking in its bottom edge after can avoiding tea set firing by the present invention.
Method for cooking after the ceramic utensil glazing of the present invention, the technical scheme of use are：The tea set of glaze water will be soaked
Be placed on base, base with located at tea set bottom project through bonding agent it is Nian Jie integrally after be fired again, fired
It is set to come off into rear percussion base.
The ceramic utensil glazing firing base of the present invention, the technical scheme of use are：The base includes circular
Heelpiece and connected unit, the connected unit is at the center of heelpiece upper surface.
Further, the connected unit is in truncated cone.
The preparation method of above-mentioned base is：Dried after the completion of the disposable roll forming of base or manual slip casting, it is desirable to base
Body Heshui rate deviation is less than ± 15%.
The beneficial effects of the invention are as follows：Tea set after having soaked glaze water is placed on base and is fired again by the present invention, burns
By base abate after the completion of system, flow downward so as to avoiding the occurrence of tea set glaze water in sintering procedure and accumulate in the bottom edge of tea set
Phenomenon that is upper and that glaze water-water reactor product caking occur causes porcelain to cause decrease in yield with backing plate adhesion, and can obtain bottom edge has had
The tea set of whole glaze paint, the quality of tea set is improved, make tea set glaze paint more complete, improve the integrated ornamental of tea set, save simultaneously
The operation on polishing tea set bottom edge has been omited, has reduced the production process of tea set, reduces cost.
Brief description of the drawings：
Fig. 1 is the structural representation of the present invention.
Embodiment：
Reference picture 1, the method for cooking after the ceramic utensil glazing, be that the tea set 1 for having soaked glaze water is placed on base, base with
Located at the projection 3 of the bottom of tea set 1 it is integral by bonding agent bonding after be fired again, base is tapped after the completion of firing makes it de-
Fall.
The ceramic utensil glazing firing base, including circular heelpiece 2 and connected unit 4, the connected unit 4 are located at heelpiece
At the center of 2 upper surfaces.The connected unit 4 is in truncated cone.
The preparation method of above-mentioned base is：Rolling mill or slip casting are first passed through to complete the shaping of base substrate branch, drying after forming makes
Its moisture content is consistent with tea set base substrate moisture content, after binding agent is applied on supporting post top.
It is only present pre-ferred embodiments in summary, all equivalent modification done according to the application and prior art additions are equal
It is considered as the technology of the present invention category.
Claims (4)
- A kind of 1. method for cooking after ceramic utensil glazing, it is characterised in that：The tea set 1 for having soaked glaze water is placed on base, Base with located at the bottom of tea set 1 projection 3 by bonding agent it is Nian Jie integrally after be fired again, base is tapped after the completion of firing It is made to come off.
- A kind of 2. ceramic utensil glazing firing base, it is characterised in that：The base includes circular heelpiece 2 and connected unit 4, The connected unit 4 is at the center of the upper surface of heelpiece 2.
- A kind of 3. ceramic utensil glazing firing base as claimed in claim 2, it is characterised in that：The connected unit 4 is in circle Taper type.
- A kind of 4. preparation method of ceramic utensil glazing firing base, it is characterised in that：The disposable roll forming of base or hand Dried after the completion of work slip casting.