CN106830832B - 用于污水处理的大孔型生态混凝土 - Google Patents
用于污水处理的大孔型生态混凝土 Download PDFInfo
- Publication number
- CN106830832B CN106830832B CN201710051484.6A CN201710051484A CN106830832B CN 106830832 B CN106830832 B CN 106830832B CN 201710051484 A CN201710051484 A CN 201710051484A CN 106830832 B CN106830832 B CN 106830832B
- Authority
- CN
- China
- Prior art keywords
- parts
- ecological concrete
- concrete
- macroporous
- particle size
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种用于污水处理的大孔型生态混凝土，原料按重量份包括以下组分：所述生态混凝土的孔隙率为5‑35％，所述生态混凝土内的连通孔占15‑30％，所述生态混凝土原料按重量份包括以下组分：骨料400‑500份、普通硅酸盐水泥100‑120份、赤泥20‑30份、亚硝酸钠防冻剂10‑20份、醋酸乙烯‑乙烯共聚物5‑10份、中聚羧酸减水剂0.03‑0.08份、烷基苯磺酸钙5‑15份、缓释性材料10‑20份、丙烯酸共聚物5‑15份、木质磺酸盐3‑8份、生物质焦5‑10份、稳泡剂3‑10份、水60‑80份；所述骨料为粒径为2.5‑5mm砂石、粒径为10‑25mm的花岗岩碎石和粒径为10‑25mm的粘土陶粒的混合物；能形成一个个“蜂窝状”空隙，吸附能力强，净水效果好，能够减少混凝土在流动水中钙离子的流失，提高大孔型生态混凝土的耐久性。
Description
技术领域
本发明涉及一种生态混凝土，特别涉及一种用于污水处理的大孔型生态混凝土。
背景技术
用于处理污水的生态混凝土内有大量的连通孔，具有良好的透水性，依靠大孔混凝土的物理、化学以及生物化学作用，达到净水的目的。但是，国外至今没有取得实际应用，主要原因是污水中的固体物质沉积在混凝土上，很快堵塞了大孔混凝土的孔隙，使其失去了净水功能；并且，普通大孔混凝土净水效果不够理想，混凝土在流动水中钙离子大量流失，使水泥水化产物分解，造成强度降低，直至破坏，所以混凝土的耐久性不够。
发明内容
有鉴于，本发明的目的在于提供一种用于污水处理的大孔型生态混凝土，能形成一个个“蜂窝状”空隙，吸附能力强，净水效果好，能够减少混凝土在流动水中钙离子的流失，提高大孔型生态混凝土的耐久性。
本发明的用于污水处理的大孔型生态混凝土，所述生态混凝土的孔隙率为5-35％，所述生态混凝土内的连通孔占15-30％，所述生态混凝土原料按重量份包括以下组分：骨料400-500份、普通硅酸盐水泥100-120份、赤泥20-30份、亚硝酸钠防冻剂10-20份、醋酸乙烯-乙烯共聚物5-10份、中聚羧酸减水剂0.03-0.08份、烷基苯磺酸钙5-15份、缓释性材料10-20份、丙烯酸共聚物5-15份、木质磺酸盐3-8份、生物质焦5-10份、稳泡剂3-10份、水60-80份；所述骨料为粒径为2.5-5mm砂石、粒径为10-25mm的花岗岩碎石和粒径为10-25mm的粘土陶粒的混合物；
进一步，原料按重量份包括以下组分：碎石骨料450份、普通硅酸盐水泥110份、赤泥25份、亚硝酸钠防冻剂15份、醋酸乙烯-乙烯共聚物7份、中聚羧酸减水剂0.06份、烷基苯磺酸钙10份、缓释性材料15份、丙烯酸共聚物10份、活性掺合料10份、木质磺酸盐5份、生物质焦7份、吸水树脂15份、玉米酒糟20份、稳泡剂6份、水70份；
进一步，所述稳泡剂为大豆豆柏、高碳醇、氢氧化钠、三乙醇胺和水的混合物；
进一步，所述缓释性材料为聚合氯化铝、聚合氯化铝铁、碱式氯化铝、聚丙烯酰胺、硫酸铝、硫酸亚铁中的一种或两种以上混合物。
本发明的有益效果：本发明的用于污水处理的大孔型生态混凝土，能形成一个个“蜂窝状”空隙,净水效果好，能够减少混凝土在流动水中钙离子的流失，提高大孔型生态混凝土的耐久性。采用粒径为2.5-5mm砂石、粒径为10-25mm的花岗岩碎石和粒径为10-25mm的粘土陶粒的混合物形成的孔隙率为5-35％，所述生态混凝土内的连通孔占15-30％的平均孔隙直径为1.95mm的大孔型生态混凝土与水接触的表面积是普通水泥的120倍以上，具有很好的吸附能力，且利用大孔型混凝土外表面对各种微生物的吸附,通过生物层的作用产生间接净化功能；混凝土中的镁、铝离子可以阻缓钙离子的溶出；并且镁、铝离子也可以发挥净水作用；镁离子可以同时达到去除污水中氮、磷等营养物质的作用；缓释性材料会包裹污水中的悬浮物质共同沉淀，达到净水的目的；将该大孔型混凝土用于河道中的污水处理，污水的化学需氧量和生化需氧量的去除率为65％～80％，总氮去除率为40％～50％，尤其是总磷的去除率达到85％～96％。
具体实施方式
实施例一
本实施例的用于污水处理的大孔型生态混凝土，所述生态混凝土的孔隙率为5％，所述生态混凝土内的连通孔占15％，所述生态混凝土原料按重量份包括以下组分：骨料400份、普通硅酸盐水泥100份、赤泥20份、亚硝酸钠防冻剂10份、醋酸乙烯-乙烯共聚物5份、中聚羧酸减水剂0.03份、烷基苯磺酸钙5份、缓释性材料10份、丙烯酸共聚物5份、木质磺酸盐3份、生物质焦5份、稳泡剂3份、水60份；所述骨料为粒径为2.5mm砂石、粒径为10mm的花岗岩碎石和粒径为10mm的粘土陶粒的混合物。
本实施例中，所述稳泡剂为大豆豆柏、高碳醇、氢氧化钠、三乙醇胺和水的混合物。
本实施例中，所述缓释性材料为聚合氯化铝铁，按照同等重量份将本实施例中的聚合氯化铝铁替换为聚合氯化铝、碱式氯化铝、聚丙烯酰胺、硫酸铝、硫酸亚铁中的一种，或者替换为聚合氯化铝铁与聚合氯化铝、碱式氯化铝、聚丙烯酰胺、硫酸铝、硫酸亚铁的混合物，均能实现本发明的目的。
实施例二
本实施例的用于污水处理的大孔型生态混凝土，所述生态混凝土的孔隙率为35％，所述生态混凝土内的连通孔占30％，所述生态混凝土原料按重量份包括以下组分：骨料500份、普通硅酸盐水泥120份、赤泥30份、亚硝酸钠防冻剂20份、醋酸乙烯-乙烯共聚物10份、中聚羧酸减水剂0.08份、烷基苯磺酸钙15份、缓释性材料20份、丙烯酸共聚物15份、木质磺酸盐8份、生物质焦10份、稳泡剂10份、水80份；所述骨料为粒径为5mm砂石、粒径为25mm的花岗岩碎石和粒径为25mm的粘土陶粒的混合物。
本实施例中，所述稳泡剂为大豆豆柏、高碳醇、氢氧化钠、三乙醇胺和水的混合物。
本实施例中，所述缓释性材料为碱式氯化铝，按照同等重量份将本实施例中的碱式氯化铝替换为聚合氯化铝铁、聚合氯化铝、聚丙烯酰胺、硫酸铝、硫酸亚铁中的一种，或者替换为碱式氯化铝与聚合氯化铝铁、聚合氯化铝、聚丙烯酰胺、硫酸铝、硫酸亚铁的混合物，均能实现本发明的目的。
实施例三
本实施例的用于污水处理的大孔型生态混凝土，所述生态混凝土的孔隙率为5％，所述生态混凝土内的连通孔占30％，所述生态混凝土原料按重量份包括以下组分：骨料400份、普通硅酸盐水泥120份、赤泥20份、亚硝酸钠防冻剂20份、醋酸乙烯-乙烯共聚物5份、中聚羧酸减水剂0.08份、烷基苯磺酸钙5份、缓释性材料20份、丙烯酸共聚物5份、木质磺酸盐8份、生物质焦5份、稳泡剂10份、水60份；所述骨料为粒径为5mm砂石、粒径为10mm的花岗岩碎石和粒径为25mm的粘土陶粒的混合物。
本实施例中，所述稳泡剂为大豆豆柏、高碳醇、氢氧化钠、三乙醇胺和水的混合物。
本实施例中，所述缓释性材料为聚丙烯酰胺，按照同等重量份将本实施例中的聚丙烯酰胺替换为聚合氯化铝铁、碱式氯化铝、聚合氯化铝、硫酸铝、硫酸亚铁中的一种，或者替换为聚丙烯酰胺与聚合氯化铝铁、碱式氯化铝、聚合氯化铝、硫酸铝、硫酸亚铁的混合物，均能实现本发明的目的。
实施例四
本实施例的用于污水处理的大孔型生态混凝土，所述生态混凝土的孔隙率为20％，所述生态混凝土内的连通孔占25％，所述生态混凝土原料按重量份包括以下组分：骨料450份、普通硅酸盐水泥120份、赤泥25份、亚硝酸钠防冻剂10份、醋酸乙烯-乙烯共聚物8份、中聚羧酸减水剂0.08份、烷基苯磺酸钙10份、缓释性材料10份、丙烯酸共聚物10份、木质磺酸盐8份、生物质焦7份、稳泡剂3份、水70份；所述骨料为粒径为5mm砂石、粒径为15mm的花岗岩碎石和粒径为15mm的粘土陶粒的混合物。
本实施例中，所述稳泡剂为大豆豆柏、高碳醇、氢氧化钠、三乙醇胺和水的混合物。
本实施例中，所述缓释性材料为硫酸铝，按照同等重量份将本实施例中的硫酸铝替换为聚合氯化铝铁、碱式氯化铝、聚丙烯酰胺、硫酸亚铁中的一种，或者替换为硫酸铝与聚合氯化铝铁、聚合氯化铝、碱式氯化铝、聚丙烯酰胺、聚合氯化铝、硫酸亚铁的混合物，均能实现本发明的目的。
实施例五
本实施例的用于污水处理的大孔型生态混凝土，所述生态混凝土的孔隙率为25％，所述生态混凝土内的连通孔占25％，所述生态混凝土原料按重量份包括以下组分：骨料450份、普通硅酸盐水泥110份、赤泥25份、亚硝酸钠防冻剂15份、醋酸乙烯-乙烯共聚物8份、中聚羧酸减水剂0.06份、烷基苯磺酸钙10份、缓释性材料15份、丙烯酸共聚物10份、木质磺酸盐6份、生物质焦8份、稳泡剂7份、水70份；所述骨料为粒径为4mm砂石、粒径为22mm的花岗岩碎石和粒径为22mm的粘土陶粒的混合物。
本实施例中，所述稳泡剂为大豆豆柏、高碳醇、氢氧化钠、三乙醇胺和水的混合物。
本实施例中，所述缓释性材料为硫酸亚铁，按照同等重量份将本实施例中的硫酸亚铁替换为聚合氯化铝铁、碱式氯化铝、聚丙烯酰胺、、硫酸亚铁中的一种，或者替换为硫酸铝与聚合氯化铝、聚合氯化铝铁、碱式氯化铝、聚丙烯酰胺、硫酸铝、聚合氯化铝的混合物，均能实现本发明的目的。
实施例六
本实施例的用于污水处理的大孔型生态混凝土，所述生态混凝土的孔隙率为35％，所述生态混凝土内的连通孔占15％，所述生态混凝土原料按重量份包括以下组分：骨料450份、普通硅酸盐水泥110份、赤泥20份、亚硝酸钠防冻剂20份、醋酸乙烯-乙烯共聚物8份、中聚羧酸减水剂0.04份、烷基苯磺酸钙5份、缓释性材料20份、丙烯酸共聚物6份、木质磺酸盐7份、生物质焦5份、稳泡剂10份、水70份；所述骨料为粒径为2.5mm砂石、粒径为25mm的花岗岩碎石和粒径为25mm的粘土陶粒的混合物。
本实施例中，所述稳泡剂为大豆豆柏、高碳醇、氢氧化钠、三乙醇胺和水的混合物。
本实施例中，所述缓释性材料为聚合氯化铝，按照同等重量份将本实施例中的聚合氯化铝替换为聚合氯化铝铁、碱式氯化铝、聚丙烯酰胺、硫酸铝、硫酸亚铁中的一种，或者替换为聚合氯化铝与聚合氯化铝铁、碱式氯化铝、聚丙烯酰胺、硫酸铝、硫酸亚铁的混合物，均能实现本发明的目的。
最后说明的是，以上实施例仅用以说明本发明的技术方案而非限制，尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的宗旨和范围，其均应涵盖在本发明的权利要求范围当中。
Claims (2)
1.一种用于污水处理的大孔型生态混凝土，其特征在于：所述生态混凝土具有蜂窝状空隙，所述生态混凝土的孔隙率为5 -35% ，所述生态混凝土内的连通孔占15-30% ，所述生态混凝土原料按重量份包括以下组分：骨料400-500份、普通硅酸盐水泥100-120份、赤泥20-30份、亚硝酸钠防冻剂10-20份、醋酸乙烯-乙烯共聚物5-10份、聚羧酸减水剂0.03-0.08份、烷基苯磺酸钙5-15份、缓释性材料10-20份、丙烯酸共聚物5-15份、木质磺酸盐3-8份、生物质焦5-10份、稳泡剂3-10份、水60-80份；所述骨料为粒径为2 . 5 - 5mm砂石、粒径为10-25mm的花岗岩碎石和粒径为10-25mm的粘土陶粒的混合物；所述缓释性材料为聚合氯化铝、聚合氯化铝铁、碱式氯化铝、聚丙烯酰胺、硫酸铝、硫酸亚铁中的一种或两种以上混合物，所述稳泡剂为大豆豆粕、高碳醇、氢氧化钠、三乙醇胺和水的混合物。
2.根据权利要求1所述的用于污水处理的大孔型生态混凝土，其特征在于：原料按重量份包括以下组分：骨料450份、普通硅酸盐水泥110份、赤泥25份、亚硝酸钠防冻剂15份、醋酸乙烯-乙烯共聚物8份、聚羧酸减水剂0.06份、烷基苯磺酸钙10份、缓释性材料15份、丙烯酸共聚物10份、木质磺酸盐6份、生物质焦8份、稳泡剂7份、水70份。