CN101897289A - 一种植生型生态混凝土及其制备方法 - Google Patents

一种植生型生态混凝土及其制备方法 Download PDF

Info

Publication number
CN101897289A
CN101897289A CN2010102180195A CN201010218019A CN101897289A CN 101897289 A CN101897289 A CN 101897289A CN 2010102180195 A CN2010102180195 A CN 2010102180195A CN 201010218019 A CN201010218019 A CN 201010218019A CN 101897289 A CN101897289 A CN 101897289A
Authority
CN
China
Prior art keywords
concrete
water
vegetation type
grass seeds
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010102180195A
Other languages
English (en)
Inventor
张静
徐文炘
董丽娟
肖筱瑜
李蘅
林达红
黎洪
程柳
白小强
李香兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guilin Minerals & Geologic Academy
Original Assignee
Guilin Minerals & Geologic Academy
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guilin Minerals & Geologic Academy filed Critical Guilin Minerals & Geologic Academy
Priority to CN2010102180195A priority Critical patent/CN101897289A/zh
Publication of CN101897289A publication Critical patent/CN101897289A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种植生型生态混凝土，它由混凝土骨架结构和培养基组成，其中，混凝土骨架结构主要由水泥、水、石渣和减水剂组成，它们的重量配比为水泥∶水∶石渣＝1∶0.28～0.45∶4～6.5；减水剂的掺入量为水泥重量的1～3％；培养基由自然土、保水剂和缓释肥组成，它们的重量配比为自然土∶保水剂∶缓释肥＝1∶0.1～0.2∶0.01～0.015。其制备方法是制作混凝土骨架结构，养护混凝土骨架结构，填充培养基，撒播草种，在草种表面覆盖培养基并压实；将预制块置于要铺设的场地，养护，直至草种根系进入混凝土下的土壤。与现有技术相比，本发明材料、结构简单，方法简单易控。

Description

一种植生型生态混凝土及其制备方法
技术领域
本发明涉及一种植被混凝土，具体涉及一种环保的植生型生态混凝土及其制备方法。
背景技术
长期以来，混凝土给人们生活带来便利的同时也对人类赖以生存的环境造成了明显的破坏。混凝土构筑物破坏了自然生态环境、摧毁动植物栖息地，同时还造成生态的荒漠，生物不能在其上生长(除苔藓植物外)，易形成城市热岛效应。此外，混凝土构筑物不具备保持水土的功能，易造成水土流失。因此，环境友好型的生态混凝土的研究也应运而生。
生态混凝土的研究在国外起步较早，特别是日本。早在1994～1995年日本混凝土工学协会设立了“生态混凝土研究委员会”，以多孔混凝土为主要课题进行了为期多年的研究工作，取得了大量的成果。成功地研究出连通孔占15～35％、结构本身利于动植物生长的多孔(大孔)混凝土。在日本，生态混凝土已应用于河堤护坡、污水净化、城市住宅绿化等工程。
在国内，对生态混凝土的研究相对较晚，但发展较迅速。2002年天津水利科学研究所发明了一种只适用于现场浇注的绿色植被混凝土，主要应用于河道提防、江湖堤坡等。随后国内纷纷研究开发环境友好型的生态混凝土，在吉林、长春、上海、南京、无锡等多地在河道护坡、城市防洪、道路边坡等工程中都应用了生态混凝土技术。
上述生态混凝土大多材料或结构较复杂，不利于推广应用。
发明内容
本发明要解决的技术问题是提供一种材料、结构简单，具有较大孔径(孔隙率20％以上)的植生型生态混凝土及其制备方法。
为解决上述技术问题，本发明采用以下技术方案：
一种植生型生态混凝土，它由混凝土骨架结构和培养基组成，其中，
混凝土骨架结构主要由水泥、水、石渣和减水剂组成，它们的重量配比为水泥∶水∶石渣＝1∶0.28～0.45∶4～6.5；减水剂的掺入量为水泥重量的1～3％；
培养基由自然土、保水剂和缓释肥组成，它们的重量配比为自然土∶保水剂∶缓释肥＝1∶0.1～0.2∶0.01～0.015。
上述混凝土骨架结构中，还可进一步包括0.05～0.18重量份的沸石；混凝土中添加一定量的沸石，对低含量的NH3-N、重金属元素等具有一定的去除作用。
上述技术方案中，
所述水泥为普通硅酸盐水泥，优选标号325#以上的水泥。
所述减水剂为NSO高效减水剂。
所述石渣的粒径优选为10～25mm。
所述保水剂优选为珍珠岩或者泥炭。
所述沸石的粒度优选为180目～200目。
本发明所述的植生型生态混凝土的制备方法，步骤如下：
①根据配比量，按水、水泥、减水剂的顺序加入至搅拌机，搅拌均匀后现场浇注成型，或注入预制模块成型，养护24h后脱模，得到植生型混凝土的骨架结构；
②在自然条件下，混凝土骨架结构洒水覆膜养护5～8天；
③将所需的培养基原材料粉碎成细小颗粒，混合均匀后灌入植生型混凝土骨架的空隙，基本灌满后撒播草种，之后在草种表面覆盖培养基并压实；
④将预制块置于要铺设的场地，洒水养护培养基，3～5天后草种即可发芽成长，继续养护，直至草种根系进入混凝土下的土壤。
上述方法中，
所述草种可以是多年生黑麦草、狗牙根、高羊茅或结缕草等。当撒播好草种后，在草种表面覆盖的培养基厚度以为0.5～2cm为宜。
与现有技术相比，本发明植生型生态混凝土材料、结构简单，制备方法简单易控，该混凝土有着良好的透水与透气性，对低含量的NH3-N、重金属元素等具有一定的去除能力。
具体实施方式
下面以具体的实施例对本发明作进一步说明，但本发明并不局限于这些实施例。
实施例1
混凝土骨架结构的组成配方：
325#水泥∶水∶粒径为10～25mm的石渣＝1∶0.3∶4.5(重量配比)；NSO高效减水剂的掺入量为水泥重量的1.5％；
培养基的组成配方：
自然土∶珍珠岩∶缓释肥(汉枫缓释肥有限公司)＝1∶0.2∶0.01(重量配比)。
植生型生态混凝土的制备方法：
①根据配比量，按水、水泥、减水剂的顺序加入至搅拌机，搅拌均匀后注入预制模块成型，养护24h后脱模，得到多种植生型混凝土的骨架结构(此时连通孔占26％)；
②在自然条件(保持温度在15℃～25℃，湿度在75～80％)下，混凝土骨架结构洒水覆膜养护7天；
③将所需的培养基原材料粉碎至50目，混合均匀后灌入植生型混凝土骨架的空隙，基本灌满后撒播多年生黑麦草草种，之后在草种表面覆盖1cm的培养基并压实；
④将预制块置于要铺设的场地，洒水养护3天后草种发芽，继续养护，直至草种根系进入混凝土下的土壤。
实施例2
混凝土骨架结构的组成配方：
425#水泥∶水∶180目的沸石∶粒径为25mm的石渣＝1∶0.38∶0.1∶5(重量配比)；NSO高效减水剂的掺入量为水泥重量的2％；
培养基的组成配方：
自然土∶珍珠岩∶缓释肥(山东鲁西化工集团股份有限公司)＝1∶0.1∶0.015(重量配比)。
植生型生态混凝土的制备方法：
①根据配比量，按水、水泥、减水剂的顺序加入至搅拌机，搅拌均匀后注入预制模块成型，养护24h后脱模，得到多种植生型混凝土的骨架结构(连通孔约占27.1％)；
②在自然条件(保持温度在25℃～35℃，湿度在85～95％)下，混凝土骨架结构洒水覆膜养护7天；
③将所需的培养基原材料粉碎至80目，混合均匀后灌入植生型混凝土骨架的空隙，基本灌满后撒播高羊茅草种，之后在草种表面覆盖1.5cm的培养基并压实；
④将预制块置于要铺设的场地，洒水养护4天后草种发芽，继续养护，直至草种根系进入混凝土下的土壤。
实施例3
混凝土骨架结构的组成配方：
425#水泥∶水∶200目的沸石∶粒径为20mm的石渣＝1∶0.45∶0.12∶4(重量配比)；NSO高效减水剂的掺入量为水泥重量的1％；
培养基的组成配方：
自然土∶泥炭∶缓释肥(山东鲁西化工集团股份有限公司)＝1∶0.15∶0.012(重量配比)。
植生型生态混凝土的制备方法：
①根据配比量，按水、水泥、减水剂的顺序加入至搅拌机，搅拌均匀后注入预制模块成型，养护24h后脱模，得到多种植生型混凝土的骨架结构(连通孔约占23.5％)；
②在自然条件(保持温度在25℃，湿度在80％)下，混凝土骨架结构洒水覆膜养护5天；
③将所需的培养基原材料粉碎至100目，混合均匀后灌入植生型混凝土骨架的空隙，基本灌满后撒播结缕草草种，之后在草种表面覆盖2cm的培养基并压实；
④将预制块置于要铺设的场地，洒水养护5天后草种发芽，继续养护，直至草种根系进入混凝土下的土壤。
实施例4
混凝土骨架结构的组成配方：
325#水泥∶水∶190目的沸石∶粒径为15mm的石渣＝1∶0.4∶0.18∶6.5(重量配比)；NSO高效减水剂的掺入量为水泥重量的3％；
培养基的组成配方：
自然土∶泥炭∶缓释肥(汉枫缓释肥有限公司)＝1∶0.15∶0.015(重量配比)。
植生型生态混凝土的制备方法：
①根据配比量，按水、水泥、减水剂的顺序加入至搅拌机，搅拌均匀后注入预制模块成型，养护24h后脱模，得到多种植生型混凝土的骨架结构(连通孔约占25.4％)；
②在自然条件(保持温度在20℃，湿度在95％)下，混凝土骨架结构洒水覆膜养护8天；
③将所需的培养基原材料粉碎至90目，混合均匀后灌入植生型混凝土骨架的空隙，基本灌满后撒播结缕草草种，之后在草种表面覆盖3cm的培养基并压实；
④将预制块置于要铺设的场地，洒水养护3天后草种发芽，继续养护，直至草种根系进入混凝土下的土壤。
实施例5
混凝土骨架结构的组成配方：
325#水泥∶水∶粒径为10mm的石渣＝1∶0.28∶6(重量配比)；NSO高效减水剂的掺入量为水泥重量的2.5％；
培养基的组成配方：
自然土∶泥炭∶缓释肥(汉枫缓释肥有限公司)＝1∶0.18∶0.01(重量配比)。
植生型生态混凝土的制备方法：
①根据配比量，按水、水泥、减水剂的顺序加入至搅拌机，搅拌均匀后注入预制模块成型，养护24h后脱模，得到多种植生型混凝土的骨架结构(连通孔约占22.8％)；
②在自然条件(保持温度在30℃，湿度在90％)下，混凝土骨架结构洒水覆膜养护6天；
③将所需的培养基原材料粉碎至60目，混合均匀后灌入植生型混凝土骨架的空隙，基本灌满后撒播狗牙根草种，之后在草种表面覆盖0.5cm的培养基并压实；
④将预制块置于要铺设的场地，洒水养护3天后草种发芽，继续养护，直至草种根系进入混凝土下的土壤。

Claims (9)

1.一种植生型生态混凝土，其特征在于：它由混凝土骨架结构和培养基组成，其中，
混凝土骨架结构主要由水泥、水、石渣和减水剂组成，它们的重量配比为水泥∶水∶石渣＝1∶0.28～0.45∶4～6.5；减水剂的掺入量为水泥重量的1～3％；
培养基由自然土、保水剂和缓释肥组成，它们的重量配比为自然土∶保水剂∶缓释肥＝1∶0.1～0.2∶0.01～0.015。
2.根据权利要求1所述的植生型生态混凝土，其特征在于：混凝土骨架结构还包括0.05～0.18重量份的沸石。
3.根据权利要求1或2所述的植生型生态混凝土，其特征在于：减水剂为NSO高效减水剂。
4.根据权利要求1或2所述的植生型生态混凝土，其特征在于：石渣的粒径为10～25mm。
5.根据权利要求1或2所述的植生型生态混凝土，其特征在于：保水剂为珍珠岩或者泥炭。
6.根据权利要求2所述的植生型生态混凝土，其特征在于：沸石的粒度为180目～200目。
7.权利要求1所述的植生型生态混凝土的制备方法，其特征在于步骤如下：
①根据配比量，按水、水泥、减水剂的顺序加入至搅拌机，搅拌均匀后现场浇注成型，或注入预制模块成型，养护24h后脱模，得到植生型混凝土的骨架结构；
②在自然条件下，混凝土骨架结构洒水覆膜养护5～8天；
③将所需的培养基原材料粉碎成细小颗粒，混合均匀后灌入植生型混凝土骨架的空隙，基本灌满后撒播草种，之后在草种表面覆盖培养基并压实；
④将预制块置于要铺设的场地，洒水养护培养基，草种发芽，继续养护，直至草种根系进入混凝土下的土壤。
8.根据权利要求7所述的植生型生态混凝土的制备方法，其特征在于：所述草种为多年生黑麦草、狗牙根、高羊茅或结缕草。
9.根据权利要求7所述的植生型生态混凝土的制备方法，其特征在于：草种表面覆盖的培养基厚度为0.5～2cm。
CN2010102180195A 2010-07-05 2010-07-05 一种植生型生态混凝土及其制备方法 Pending CN101897289A (zh)