CN106760337A - The outdoor use sheet material and its production method of a kind of waterproof anti-soil - Google Patents
The outdoor use sheet material and its production method of a kind of waterproof anti-soil Download PDFInfo
- Publication number
- CN106760337A CN106760337A CN201611100440.XA CN201611100440A CN106760337A CN 106760337 A CN106760337 A CN 106760337A CN 201611100440 A CN201611100440 A CN 201611100440A CN 106760337 A CN106760337 A CN 106760337A
- Authority
- CN
- China
- Prior art keywords
- weight
- grain slag
- color chips
- soil
- binding material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the outdoor use sheet material and its production method of a kind of waterproof anti-soil, including the sanding grain slag color chips magnesium silicon plate being made up of grain slag magnesite binding material (1), fiberglass gridding cloth (2), this color surface layer (3), sanding face (4), organic silicon water-proofing layer (5), true qualities starch adhesive material (6), anti-pollution layer (7), grain slag color chips magnesite binding material (8).The present invention is using the making for carrying out magnesite binding material as packing material by the grain slag powder of specially treated, so as to discard and easily the filter residue waste material high of environmental pollution is caused rationally to be utilized, not only accomplish the secondary utilization of waste recovery, and with preferable waterproof and dampproof performance；And there is anti-pollution layer (7) to stick to grain slag color chips magnesite binding material (8) surface, it is smooth to achieve surface, and obtains anti-soil effect；The present invention also has that thermal conductivity factor is low, heat-resist, ageing-resistant, easily cohere with other base materials, burn the excellent properties such as molten drop that do not produce.
Description
Technical field
The present invention relates to building board field, the outdoor use sheet material and its production method of a kind of waterproof anti-soil are specifically referred to.
Background technology
Conventional water-proof decoration plate is made generally with glass magnesium board as substrate in its surface mopping in the market, this
Kind of splash guard use time is long or after being clashed into, and paints easy to fall off, influences attractive in appearance, is unsuitable for interior decoration.It is waterproof and dampproof
Poor-performing, service life is shorter.
And China's building materials industry resources and energy consumption is high, gross contamination emission big, cause serious environmental pollution and
Land resource is wasted industrial residue, mine tailing " turning waste into wealth ", is made its " innoxious, resource, minimizing ", is improved people and is occupied ring
Border, promote a conservation culture, be green building material and the development of green building Industrial Convergence in the urgent need to.
At present, by JC688-2006 glass fibre and magnesium cement boards and the waterproof of JG/T414-2013 architectural magnesia-concrete decorative panel standard productions
Plate, is mainly used in waterproof finishing.The splash guard with substantial amounts of sawdust as inserts, product water absorption rate ＞ 10%, coefficient of softing
0.85, compression strength is low.Therefore, a kind of method is studied, mine tailing, blast furnace granulated slag, lightweight aggregate etc. is applied to house decorative material
Making in the middle of, the splash guard produced the preferable waterproof ability of properties and have stain resistance just seems extremely necessary.
The content of the invention
The technical problem to be solved in the present invention is to provide one kind for indoor moisture proof waterproof and possesses stain resistance and addition
A large amount of blast furnace granulated slags are a kind of outdoor use sheet material of waterproof anti-soil that inserts makes.
The present invention is achieved through the following technical solutions：A kind of outdoor use sheet material of waterproof anti-soil, including plate body, the plate body
Including upper and lower symmetrically arranged fiberglass gridding cloth 2, grain slag magnesite is filled between the upper and lower fiberglass gridding cloth 2
Binder Materials 1；The top of upper fiberglass gridding cloth 2 is sequentially provided with organic silicon water-proofing layer 5, sanding face 4, anti-pollution layer 7, institute
Fill grain slag color chips magnesite binding material 8 in the gap stated between fiberglass gridding cloth 2 and sanding face 4；The lower glass fibre
The bottom of grid cloth 2 is sequentially provided with organic silicon water-proofing layer 5, this color surface layer 3, is set between the organic silicon water-proofing layer 5 and this color surface layer 3
There is true qualities starch adhesive material 6；It is symmetrical to be provided with organic silicon water-proofing layer 5.
Further, the grain slag color chips magnesite binding material 8 is made up of grain slag, color chips, magnesite binding material 1.
Further, the color chips is made up of the magnesite binding material 1 plus pigment.
Further, the magnesite binding material 1 by plus pigment be made color chips, mica sheet, dyeing one of mica sheet or
Its combination.
Further, during the waterproof layer 5 penetrates into grain slag magnesite binding material 1.
Further, the anti-pollution layer 7 sticks to the surface of grain slag color chips magnesite binding material 8, and its action face is smooth,
Anti-soil.
Further, the total number of plies of the fiberglass gridding cloth 2 is 4~10 layers.
Further, the gross thickness of the outdoor use sheet material of whole waterproof anti-soil is 10~40mm..
The present apparatus is used in building wall to provide the sheet material of preferable decoration function, and general waterproof building plate is adopted
With waterproof gypsum board or ca silicate fibre plate, and magnesite splash guard is a kind of novel environment friendly based plate, with magnesium gelatinous material
For main body, glass fabric are that reinforcing material, light waterproof material are composited for filler, with rupture strength higher
With waterproof antifouling effect.
Other, the method for preparing this outdoor use sheet material for waterproof anti-soil, including step once：
(1) gel rubber material is prepared first：
A, 29.4 ° of B é magnesium sulfate waters of preparation：The water of a weight will be added in the epsom salt of a weight, make seven water
Magnesium sulfate is dissolved into 29.4 ° of B é magnesium sulfate waters of B é；
B, prepare color chips：29.4 ° of B é magnesium sulfate waters of a weight in step A are taken, and is added thereto to a weight
Magnesia light burnt powder, the grain slag powder of a weight, the modifying agent of a weight, the dispersible pigment color paste of a weight, mixer stirring
After uniform, it is laid in ABS templates, after reaching intensity through maintenance, is ground into sheet-like particle.
The way of C, true qualities starch adhesive material 6：Take 29.4 ° of B é magnesium sulfate waters of a weight in step A, the oxidation of a weight
Magnesium light burnt powder, the dolomite dust of a weight, the grain slag powder of a weight, the modifying agent of a weight, mixer stirs.
D, prepare grain slag magnesite binding material (1)：29.4 ° of B é magnesium sulfate waters of a weight in step A are taken, then thereto
Add the magnesia light burnt powder of a weight, the mine tailing of a weight, the grain slag of a weight, the perlite of a weight,
The modifying agent and color chips of a weight, then stir said mixture, obtain grain slag color chips magnesite binding material slurry,
And by its parts by weights at least two parts.
The way of E, grain slag color chips magnesite binding material 8：29.4 ° of B é magnesium sulfate waters of a weight step A, a weight
Magnesia light burnt powder, the dolomite dust of a weight, the grain slag powder of a weight, a weight grain slag, a weight step A
Color chips, the modifying agent of a weight, mixer stirs.
The way of F, grain slag color chips magnesite binding material 8：29.4 ° of B é magnesium sulfate waters of a weight, the oxygen of a weight
Change magnesium light burnt powder, the dolomite dust of a weight, the grain slag powder of a weight, a weight grain slag, a weight color chips, portion
Weight mica, the modifying agent of a weight, mixer stirs.
(2) the outdoor use sheet material of waterproof anti-soil is started from：
A, the outdoor use sheet material of described waterproof anti-soil are molded on waterproof board assembly line, the true qualities starch adhesive material that will be made
6 slurries are paved on PVC or ABS substrates；
B, the fiberglass gridding cloth 2 of respective numbers is pressed into the slurry of true qualities starch adhesive material 6, grain slag magnesite binding material 1
Slurry is paved on true qualities starch adhesive material 6；
C, the fiberglass gridding cloth 2 for laying respective numbers again, lay the slurry of grain slag color chips magnesite binding material 8, so
After lay non-woven fabrics；
D, cleaved, leveling, maintenance, solidification, form removal, four side Length-fixing cuttings, maintenance, sanding, form sanding face 4；
F, spraying waterproofing agent of organosilicon, baking and curing, form organosilicon waterproof layer 5；
G, spraying nanometer stain resistant material, baking and curing, form anti-pollution layer 7.
H, formation are prevented by grain slag magnesite binding material 1, fiberglass gridding cloth 2, this color surface layer 3, sanding face 4, organosilicon
Water layer 5, true qualities starch adhesive material 6, anti-pollution layer 7, the sanding grain slag color chips magnesium silicon plate of the composition of grain slag color chips magnesite binding material 8.
Wherein it is noted that described grain slag is water-granulated slag, a kind of good active mixture but because grain slag is hard
Degree is high and grindability is poor, at present, is only used as cement admixture by cement production enterprise on a small quantity, and most of steel mills all will
Grain slag is stacked as waste material, not only occupies a large amount of arable lands, and pollution environment.And grain slag powder used in the present invention is molten
The blast furnace slag of state is placed in water what is rapidly cooled down and formed, is smashed high-temperature liquid furnace slag with water quenching, is turned into loose grain slag；
Or smashed high-temperature liquid furnace slag with steam or compressed air, it is turned into fluffy slag wool.Blast furnace granulated slag is comprehensive utilization
Good method, advanced blast furnace granulated slag 100% is utilized.At present, the process equipment of punching grain slag can guarantee that grain slag
Quality, vitrifying degree can reach 90%~95%, and grain slag particle mean size is 0.2~3.0mm, and grain slag is aqueous≤and 15%.And
It is, in order to reduce product surface porosity, to facilitate vacuum cup product offline to be additionally provided with non-woven fabrics in topmost of the present invention.
The present invention compared with prior art, with advantages below and beneficial effect：
(1) present invention uses the making for carrying out magnesite binding material as packing material by the grain slag powder of specially treated,
So as to discard and easily cause the filter residue waste material high of environmental pollution rationally to be utilized, not only accomplish waste recovery two
Secondary utilization, and with preferable waterproof and dampproof performance；
(2) anti-pollution layer 7 sticks to the surface of grain slag color chips magnesite binding material 8 in the present invention, and its action face is smooth, anti-
It is dirty；
Brief description of the drawings
The detailed description made to non-limiting example with reference to the following drawings by reading, other features of the invention,
Objects and advantages will become apparent：
Fig. 1 is structural representation of the invention.
Wherein：1-grain slag magnesite binding material, 2-fiberglass gridding cloth, 3-this color surface layer, 4-sanding face, 5-
Organic silicon water-proofing layer, 6-true qualities starch adhesive material, 7-anti-pollution layer, 8-grain slag color chips magnesite binding material.
Specific embodiment
Embodiments of the invention are described below in detail, the example of the embodiment is shown in the drawings, wherein from start to finish
Same or similar label represents same or similar element or the element with same or like function.Below with reference to attached
It is exemplary to scheme the embodiment of description, is only used for explaining the present invention, and is not considered as limiting the invention.
Embodiment 1：
A kind of outdoor use sheet material of the waterproof anti-soil of the present embodiment, as shown in figure 1, including plate body, the plate body include it is upper,
Under symmetrically arranged fiberglass gridding cloth 2, between the upper and lower fiberglass gridding cloth 2 filled with grain slag magnesite be gelled material
Material 1；The top of upper fiberglass gridding cloth 2 is sequentially provided with organic silicon water-proofing layer 5, sanding face 4, anti-pollution layer 7, the glass
Fill grain slag color chips magnesite binding material 8 in gap between fibrous mesh cloth 2 and sanding face 4；The lower fiberglass gridding cloth 2
Bottom is sequentially provided with organic silicon water-proofing layer 5, this color surface layer 3, and true qualities are provided between the organic silicon water-proofing layer 5 and this color surface layer 3
Starch adhesive material 6；It is symmetrical to be provided with organic silicon water-proofing layer 5.
The grain slag color chips magnesite binding material 8 is made up of grain slag, color chips, magnesite binding material 1.The color chips is by described
Magnesite binding material 1 plus pigment are made.The magnesite binding material 1 is made color chips, mica sheet, dyeing mica sheet by adding pigment
One or a combination set of.The waterproof layer 5 is penetrated into grain slag magnesite binding material 1.The anti-pollution layer 7 sticks to grain slag color chips
The surface of magnesite binding material 8, its action face is smooth, anti-soil.The total number of plies of the fiberglass gridding cloth 2 is 4~10 layers.Entirely
The gross thickness of the outdoor use sheet material of waterproof anti-soil is 10~40mm.
The present apparatus is used in building wall to provide the sheet material of preferable water-tight device effect, general waterproof building plate
Waterproof gypsum board or ca silicate fibre plate are used, and magnesite splash guard is a kind of novel environment friendly based plate, with magnesial gelatinized
Material is that main body, glass fabric are that reinforcing material, light waterproof material are composited for filler, with anti-folding higher
Intensity and waterproof effect, but only there is single waterproof effect, and if increasing the sheet material of another antifouling effect, paint and be unfavorable for
The use of building wall, then the present invention innovation novel environment friendly grain slag magnesite binding material 1, grain slag color chips magnesite gelling material
, used as main body, obtaining can anti-soil and the sheet material of energy waterproof for material and anti-pollution layer 7.And the grain slag color chips magnesite binding material
Colored pellets is added in 1, the color chips is pigment grain slag magnesite piece, and the total number of plies of the fiberglass gridding cloth 2 is 4~10 layers, institute
The outdoor use sheet material gross thickness of waterproof anti-soil is stated between 10mm~40mm.
A kind of method of the outdoor use plate for preparing waterproof anti-soil, comprises the following steps：
(1) gel rubber material is prepared first：
A, 29.4 ° of B é magnesium sulfate waters of preparation：It is dissolved into magnesium sulfate the water that the epsom salt of 850kg adds 1000kg
29.4 ° of B é magnesium sulfate waters；
B, prepare color chips：29.4 ° of B é magnesium sulfate waters of 125kg in step A are taken, and is added thereto to the magnesia of 100kg
Light burnt powder, the dolomite dust of 4kg, the grain slag powder of 100kg, the modifying agent and the dispersible pigment color paste of 2kg of a weight, mixer are stirred
After mixing uniformly, it is laid in ABS templates, after reaching intensity through maintenance, is ground into sheet-like particle, obtains color chips；
C, preparation true qualities starch adhesive material 6：29.4 ° of B é magnesium sulfate waters of 125kg in step A are taken, then is added thereto to 100kg's
The modifying agent of magnesia light burnt powder, the dolomite dust of 4kg, the grain slag powder of 100kg and a weight, then by said mixture
Stir, obtain true qualities starch adhesive material 6；
D, prepare grain slag magnesite gel rubber material 1：29.4 ° of B é Adlerikas of 125kg in step A are taken, then is added thereto
Enter magnesia light burnt powder, 4kg dolomite dusts, 100kg grain slags powder, 180kg grain slags, the modifying agent of a weight of 100kg, then
Said mixture is stirred, grain slag lightweight aggregate magnesite binding material slurry 1 is obtained, and by its parts by weights at least two
Part；
E, prepare grain slag color chips magnesite binding material 8：29.4 ° of B é magnesium sulfate waters of 125kg in step A are taken, then thereto
Add the magnesia light burnt powder of 100kg, the dolomite dust of 4kg, the mine tailing of 100kg, the grain slag of 150kg, 30kg color chips and
The modifying agent of a weight, then stirs said mixture, obtains grain slag color chips magnesite binding material 8；
(2) the outdoor use sheet material of waterproof anti-soil is started from：
A, the outdoor use sheet material of described waterproof anti-soil are molded on waterproof board assembly line, the true qualities starch adhesive material that will be made
(6) slurry is paved on PVC or ABS substrates；
B, 2 layers of fiberglass gridding cloth (2) are pressed into true qualities starch adhesive material (6) slurries, grain slag magnesite binding material (1) slurry
Material is paved on true qualities starch adhesive material (6)；
C, again 2 layers of fiberglass gridding cloth (2) of lay, lay grain slag color chips magnesite binding material (8) slurry, Ran Houpu
Put non-woven fabrics；
D, cleaved, leveling, maintenance, solidification, form removal, four side Length-fixing cuttings, maintenance, sanding, form sanding face 4；
F, spraying waterproofing agent of organosilicon, baking and curing, form organosilicon waterproof layer 5；
G, spraying nanometer stain resistant material, baking and curing, form anti-pollution layer 7.
H, formation are prevented by grain slag magnesite binding material 1, fiberglass gridding cloth 2, this color surface layer 3, sanding face 4, organosilicon
Water layer 5, true qualities starch adhesive material 6, anti-pollution layer 7, the sanding grain slag color chips magnesium silicon plate of the composition of grain slag color chips magnesite binding material 8, always
Thickness is 10mm.
And non-woven fabrics is according to every square metre of this waterproof plate thickness different choice 9g to 100g, its Main Function reduces product table
Face porosity, facilitates vacuum cup product offline.
Embodiment 2：
The present embodiment further illustrates the consumption of fiberglass gridding cloth 2 to the present invention on the basis of above-described embodiment 1
The influence of the splash guard mechanical performance being related to.
In the middle of the present embodiment, step (2) is improved：
(2) the outdoor use sheet material of waterproof anti-soil is started from：
A, the outdoor use sheet material of described waterproof anti-soil are molded on waterproof board assembly line, the true qualities starch adhesive material that will be made
(6) slurry is paved on PVC or ABS substrates；
B, 3 layers of fiberglass gridding cloth (2) are pressed into true qualities starch adhesive material (6) slurries, grain slag magnesite binding material (1) slurry
Material is paved on true qualities starch adhesive material (6)；
C, again 3 layers of fiberglass gridding cloth (2) of lay, lay grain slag color chips magnesite binding material (8) slurry, Ran Houpu
Put non-woven fabrics；
D, cleaved, leveling, maintenance, solidification, form removal, four side Length-fixing cuttings, maintenance, sanding, form sanding face 4；
F, spraying waterproofing agent of organosilicon, baking and curing, form organosilicon waterproof layer 5；
G, spraying nanometer stain resistant material, baking and curing, form anti-pollution layer 7.
H, formation are prevented by grain slag magnesite binding material 1, fiberglass gridding cloth 2, this color surface layer 3, sanding face 4, organosilicon
Water layer 5, true qualities starch adhesive material 6, anti-pollution layer 7, the sanding grain slag color chips magnesium silicon plate of the composition of grain slag color chips magnesite binding material 8, always
Thickness is 20mm.
And non-woven fabrics is according to every square metre of this waterproof plate thickness different choice 9g to 100g, its Main Function reduces product table
Face porosity, facilitates vacuum cup product offline.
Embodiment 3：
The present embodiment further illustrates the consumption of fiberglass gridding cloth 2 to the present invention on the basis of above-described embodiment 1
The influence of the splash guard mechanical performance being related to.
In the middle of the present embodiment, step (2) is improved：
(2) the outdoor use sheet material of waterproof anti-soil is started from：
A, the outdoor use sheet material of described waterproof anti-soil are molded on waterproof board assembly line, the true qualities starch adhesive material that will be made
(6) slurry is paved on PVC or ABS substrates；
B, 4 layers of fiberglass gridding cloth (2) are pressed into true qualities starch adhesive material (6) slurries, grain slag magnesite binding material (1) slurry
Material is paved on true qualities starch adhesive material (6)；
C, again 4 layers of fiberglass gridding cloth (2) of lay, lay grain slag color chips magnesite binding material (8) slurry, Ran Houpu
Put non-woven fabrics；
D, cleaved, leveling, maintenance, solidification, form removal, four side Length-fixing cuttings, maintenance, sanding, form sanding face 4；
F, spraying waterproofing agent of organosilicon, baking and curing, form organosilicon waterproof layer 5；
G, spraying nanometer stain resistant material, baking and curing, form anti-pollution layer 7.
H, formation are prevented by grain slag magnesite binding material 1, fiberglass gridding cloth 2, this color surface layer 3, sanding face 4, organosilicon
Water layer 5, true qualities starch adhesive material 6, anti-pollution layer 7, the sanding grain slag color chips magnesium silicon plate of the composition of grain slag color chips magnesite binding material 8, always
Thickness is 40mm.
And non-woven fabrics is according to every square metre of this waterproof plate thickness different choice 9g to 100g, its Main Function reduces product table
Face porosity, facilitates vacuum cup product offline.
Embodiment 3：
The present embodiment further illustrates the consumption of fiberglass gridding cloth 2 to the present invention on the basis of above-described embodiment 1
The influence of the splash guard mechanical performance being related to.
In the middle of the present embodiment, step (2) is improved：
(2) the outdoor use sheet material of waterproof anti-soil is started from：
A, the outdoor use sheet material of described waterproof anti-soil are molded on waterproof board assembly line, the true qualities starch adhesive material that will be made
(6) slurry is paved on PVC or ABS substrates；
B, 5 layers of fiberglass gridding cloth (2) are pressed into true qualities starch adhesive material (6) slurries, grain slag magnesite binding material (1) slurry
Material is paved on true qualities starch adhesive material (6)；
C, again 5 layers of fiberglass gridding cloth (2) of lay, lay grain slag color chips magnesite binding material (8) slurry, Ran Houpu
Put non-woven fabrics；
D, cleaved, leveling, maintenance, solidification, form removal, four side Length-fixing cuttings, maintenance, sanding, form sanding face 4；
F, spraying waterproofing agent of organosilicon, baking and curing, form organosilicon waterproof layer 5；
G, spraying nanometer stain resistant material, baking and curing, form anti-pollution layer 7.
H, formation are prevented by grain slag magnesite binding material 1, fiberglass gridding cloth 2, this color surface layer 3, sanding face 4, organosilicon
Water layer 5, true qualities starch adhesive material 6, anti-pollution layer 7, the sanding grain slag color chips magnesium silicon plate of the composition of grain slag color chips magnesite binding material 8, always
Thickness is 40mm.
And non-woven fabrics is according to every square metre of this waterproof plate thickness different choice 9g to 100g, its Main Function reduces product table
Face porosity, facilitates vacuum cup product offline.
Embodiment 4
The present embodiment on the basis of above-described embodiment 1, the way of further preferred grain slag color chips magnesite binding material 8.
E steps in step (2)：
E, prepare grain slag color chips magnesite binding material 8：29.4 ° of B é magnesium sulfate waters of 125kg in step A are taken, then thereto
Add magnesia light burnt powder, the dolomite dust of 4kg, the mine tailing of 100kg, the grain slag of 150kg, 25kg color chips, the 3kg of 100kg
The modifying agent of mica and a weight, then stirs said mixture, obtains grain slag color chips magnesite binding material 8；
Learnt according to above example：Four-layer glass fibrous mesh cloth, rupture strength when this waterproof plate thickness is 10mm
＞ 30Mpa, six layers of fiberglass gridding cloth, rupture strength ＞ 25Mpa, when this waterproof thickness of slab when this waterproof plate thickness is 20mm
Eight layers of fiberglass gridding cloth when spending for 40mm, rupture strength ＞ 35Mpa, ten layers of glass fibers when this waterproof plate thickness is 40mm
Dimension grid cloth, rupture strength ＞ 40Mpa.The outdoor use sheet metal thickness of waterproof anti-soil is different, and four to ten layers of glass fibre may be selected
Grid cloth.
Although an embodiment of the present invention has been shown and described, it will be understood by those skilled in the art that：Not
Depart from and can these embodiments be carried out with various changes, modification, replacement and modification under principle of the invention and objective, it is of the invention
Scope is limited by claim and its equivalent.
Claims (9)
1. a kind of outdoor use sheet material of waterproof anti-soil, it is characterised in that：Including plate body, the plate body includes upper and lower being symmetrical arranged
Fiberglass gridding cloth (2), between the upper and lower fiberglass gridding cloth (2) be filled with grain slag magnesite binding material (1)；
Upper fiberglass gridding cloth (2) top is sequentially provided with organic silicon water-proofing layer (5), sanding face (4), anti-pollution layer (7), described
Fill grain slag color chips magnesite binding material (8) in gap between fiberglass gridding cloth (2) and sanding face (4)；The lower glass
Fibrous mesh cloth (2) bottom is sequentially provided with organic silicon water-proofing layer (5), this color surface layer (3), organic silicon water-proofing layer (5) and sheet
True qualities starch adhesive material (6) is provided between color surface layer (3)；It is symmetrical to be provided with organic silicon water-proofing layer (5).
2. the outdoor use sheet material of a kind of waterproof anti-soil according to claim 1, it is characterised in that：The grain slag color chips magnesite
Binder Materials (8) is made up of grain slag, color chips, magnesite binding material (1).
3. the outdoor use sheet material of a kind of waterproof anti-soil according to claim 2, it is characterised in that：The color chips is by the water chestnut
Magnesium Binder Materials (1) plus pigment are made.
4. the outdoor use sheet material of a kind of waterproof anti-soil according to claim 3, it is characterised in that：The magnesite binding material
(1) one or a combination set of color chips, mica sheet, dyeing mica sheet are made by adding pigment.
5. according to a kind of outdoor use sheet material of any described waterproof anti-soil of Claims 1 to 4, it is characterised in that：The anti-soil
Coating (7) is on grain slag color chips magnesite binding material (8) surface.
6. the outdoor use sheet material of a kind of waterproof anti-soil according to any one of Claims 1 to 4, it is characterised in that：The glass
The total number of plies of glass fibrous mesh cloth (2) is 4~10 layers.
7. the outdoor use sheet material of a kind of waterproof anti-soil according to any one of Claims 1 to 4, it is characterised in that：It is whole anti-
The gross thickness of the outdoor use sheet material of water anti-soil is 10~40mm.
8. the outdoor use sheet material of a kind of waterproof anti-soil according to any one of Claims 1 to 4, it is characterised in that：It is described anti-
The outdoor use sheet material of water anti-soil is used for decoration of exterior wall.
9. the production method of the outdoor use sheet material of a kind of waterproof anti-soil in claim 1~8, it is characterised in that including following
Step：
(1) gel rubber material is prepared first：
A, 29.4 ° of B é magnesium sulfate waters of preparation：The water of a weight will be added in the epsom salt of a weight, make seven water sulfuric acid
Magnesium is dissolved into 29.4 ° of B é magnesium sulfate waters of B é；
B, prepare color chips：29.4 ° of B é magnesium sulfate waters of a weight in step A are taken, and is added thereto to the oxidation of a weight
Magnesium light burnt powder, the grain slag powder of a weight, the modifying agent of a weight, the dispersible pigment color paste of a weight, mixer stir
Afterwards, it is laid in ABS templates, after reaching intensity through maintenance, is ground into sheet-like particle.
The way of C, true qualities starch adhesive material (6)：Take 29.4 ° of B é magnesium sulfate waters of a weight in step A, the magnesia of a weight
Light burnt powder, the dolomite dust of a weight, the grain slag powder of a weight, the modifying agent of a weight, mixer stirs.
D, prepare grain slag magnesite binding material (1)：29.4 ° of B é magnesium sulfate waters of a weight in step A are taken, then is added thereto to
The magnesia light burnt powder of a weight, the mine tailing of a weight, the grain slag of a weight, perlite, the portion of a weight
The modifying agent and color chips of weight, then stir said mixture, obtain grain slag color chips magnesite binding material slurry, and will
Its parts by weights is at least two parts.
The way of E, grain slag color chips magnesite binding material (8)：29.4 ° of B é magnesium sulfate waters of a weight step A, a weight
Magnesia light burnt powder, the dolomite dust of a weight, the grain slag powder of a weight, a weight grain slag, a weight step A
Color chips, the modifying agent of a weight, mixer stirs.
The way of F, grain slag color chips magnesite binding material (8)：29.4 ° of B é magnesium sulfate waters of a weight, the oxidation of a weight
Magnesium light burnt powder, the dolomite dust of a weight, the grain slag powder of a weight, a weight grain slag, a weight color chips, Yi Fenchong
Amount mica, the modifying agent of a weight, mixer stirs.
(2) the outdoor use sheet material of waterproof anti-soil is started from：
A, the outdoor use sheet material of described waterproof anti-soil are molded on fire prevention board assembly line, true qualities starch adhesive material (6) that will be made
Slurry is paved on PVC or ABS substrates；
B, by the fiberglass gridding cloth (2) of respective numbers press-in true qualities starch adhesive material (6) slurry, grain slag magnesite binding material
(1) slurry is paved on true qualities starch adhesive material (6)；
C, again lay respective numbers fiberglass gridding cloth (2, lay grain slag color chips magnesite binding material (8) slurry, then
Lay non-woven fabrics；
D, cleaved, leveling, maintenance, solidification, form removal, four side Length-fixing cuttings, maintenance, sanding, form sanding face (4)；
F, spraying waterproofing agent of organosilicon, baking and curing, form organosilicon waterproof layer (5)；
G, spraying nanometer stain resistant material, baking and curing, form anti-pollution layer (7).
H, formed by grain slag magnesite binding material (1), fiberglass gridding cloth (2), this color surface layer (3), sanding face (4), organic
Silicon waterproof layer (5), true qualities starch adhesive material (6), anti-pollution layer (7), the sanding grain slag color of grain slag color chips magnesite binding material (8) composition
Piece magnesium silicon plate.