CN106522494A - Outdoor fireproof plate and manufacturing method thereof - Google Patents
Outdoor fireproof plate and manufacturing method thereof Download PDFInfo
- Publication number
- CN106522494A CN106522494A CN201611100429.3A CN201611100429A CN106522494A CN 106522494 A CN106522494 A CN 106522494A CN 201611100429 A CN201611100429 A CN 201611100429A CN 106522494 A CN106522494 A CN 106522494A
- Authority
- CN
- China
- Prior art keywords
- layer
- plastic laminated
- outdoor use
- grain slag
- binding material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an outdoor fireproof plate and a manufacturing method thereof. The outdoor fireproof plate is characterized in that the outdoor fireproof plate comprises a water granulated slag magnesite cementing material, a glass fiber grid cloth, a mass-colour surface layer, a non-woven fabric, an organosilicon waterproof layer and a mass-colour surface slurry layer; and the glass fiber grid cloth has two layers; one layer in the two-layer glass fiber grid cloth is provided with a layer of non-woven fabric and an organosilicon waterproof layer form inside to outside, and the exterior of the other layer in the glass fiber grid cloth is sequentially provided with an organosilicon waterproof layer and a mass-colour surface layer. Compared with a common fireproof plate, the outdoor fireproof plate is advantaged in that the water absorption is lower than 8%, the softening coefficient is 1, the compressive strength is larger than 40 Mpa, and the outdoor fireproof plate is light in weight and high in strength and can be widely applied to outdoor decoration.
Description
Technical field
The present invention relates to building material field, is related specifically to a kind of PLASTIC LAMINATED of outdoor use and preparation method thereof.
Background technology
China's building materials industry resources and energy consumption is high, gross contamination emission is big, at present, mainly takes and cheats in surrounding city
The mode that depression band is set up interim eliminate-incorporate-land and carries out simply filling is disposed, and causes serious environmental pollution and land resource wave
Take.
Industrial residue, mine tailing " turning waste into wealth " so as to " innoxious, resource, minimizing ", improve human settlement, build
If conservation culture, be green building material and green building Industrial Convergence development in the urgent need to.
At present, by the fire prevention of JC688-2006 glass fibre and magnesium cement boards and JG/T414-2013 architectural magnesia-concrete decorative panel standard productions
Plate, is mainly used in fire prevention finishing.The PLASTIC LAMINATED with substantial amounts of sawdust as inserts, product water absorption rate > 10%, coefficient of softing
0.85, compression strength is low.
The content of the invention
The invention solves the problems that a technical problem be:One kind is provided with magnesite material as gelling agent, a large amount of blast furnaces are added
Grain slag, lightweight aggregate are inserts, organic and inorganic short fibre enhancing, a kind of PLASTIC LAMINATED of outdoor use of green building material of making, gram
Take the deficiency of existing PLASTIC LAMINATED, product water absorption rate < 8%, coefficient of softing 1, compression strength > 40Mpa, product according to the present invention
For a kind of PLASTIC LAMINATED of outdoor use.
The technical solution adopted for the present invention to solve the technical problems:
A kind of PLASTIC LAMINATED of outdoor use, a kind of PLASTIC LAMINATED of outdoor use, it is characterised in that:Including grain slag magnesite gelling material
Material, fiberglass gridding cloth, this color surface layer, non-woven fabrics, organic silicon water-proofing layer and the true qualities starch adhesive bed of material;Described glass fibre
Grid cloth is two-layer;One layer in the layer glass fibrous mesh cloth be provided with from inside to outside layer of non-woven fabric, one layer it is organic
Silicon waterproof layer, another layer of outside of the fiberglass gridding cloth are sequentially provided with one layer of organic silicon water-proofing layer and one layer of true qualities face
Layer.
Preferably, the grain slag magnesite binding material is made up of grain slag, magnesite binding material.
Preferably, described color surface layer is magnesite binding material, the surface layer of grain slag powder self color.
Preferably, the non-woven fabrics is per square metre of 9g to 100g.
Preferably, the total tablet number of the fiberglass gridding cloth is 2 to 10.
The invention solves the problems that another technical problem be:One kind is provided with magnesite material as gelling agent, is added a large amount of high
Stove grain slag, lightweight aggregate are inserts, overcome the shortcomings of existing fire prevention board manufacturing method, a kind of simple, the easy to make room of method
The preparation method of the PLASTIC LAMINATED of external application.
The technical solution adopted for the present invention to solve the technical problems:
A kind of preparation method of the PLASTIC LAMINATED of outdoor use, comprises the following steps:
A, mixer stir out the slurry of true qualities starch adhesive material and grain slag magnesite binding material respectively, then produce in PLASTIC LAMINATED
It is molded on line;
B, true qualities starch adhesive material are paved on PVC or ABS substrates, in fiberglass gridding cloth press-in true qualities starch adhesive material;
C, fiber grain slag magnesite binding material slurry are paved on true qualities starch adhesive material, lay fiberglass gridding cloth again,
Grain slag magnesite binding material slurry is laid again, is then laid nonwoven layer, is then covered with grain slag magnesite binding material slurry by nothing
Spin cloth to cement;
D, cleaved, leveling, maintenance, solidification, form removal, conserve again, four side Length-fixing cuttings, two big faces spraying organosilicons are prevented
Aqua, drying, are molded a kind of PLASTIC LAMINATED of outdoor use.
Preferably, the mixing time of true qualities starch adhesive material is three minutes in described step a.
Preferably, in described step d, cutting is using sliding knife cutting automatically.
Present invention has the advantages that:The PLASTIC LAMINATED of a kind of outdoor use of the present invention, by grain slag magnesite binding material, glass
The cooperation of fibrous mesh cloth, this color surface layer and nonwoven layer, compared with common fire prevention panel products water absorption rate < 8%, softening system
Number 1, compression strength > 40Mpa, high-strength light are widely used in interior decoration.It should be noted that a kind of fire prevention of outdoor use
Plate consumes a large amount of blast furnace granulated slags, reduces pollution, improves human settlement.
Description of the drawings
The present invention is further described with reference to the accompanying drawings and examples.
Fig. 1 is a kind of structural representation of the PLASTIC LAMINATED of outdoor use of the present invention;
Fig. 2 is cross-sectional schematics of the Fig. 1 along A-A;
In figure, 1 grain slag magnesite binding material, 2 fiberglass gridding cloths, 3 color surface layers, 4 nonwoven layers,
5 organic silicon water-proofing layers, the 6 true qualities starch adhesive bed of materials.
Specific embodiment
In order that the objects, technical solutions and advantages of the present invention become more apparent, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that specific embodiment described herein is not used to only to explain the present invention
Limit the present invention.
Embodiment 1:
A kind of PLASTIC LAMINATED of outdoor use, including grain slag magnesite binding material 1, fiberglass gridding cloth 2, this color surface layer 3, nothing
Spin cloth 4, organic silicon water-proofing layer 5 and the true qualities starch adhesive bed of material 6;Described fiberglass gridding cloth 2 is two-layer, and the PLASTIC LAMINATED is also interior
Portion is provided with one layer of true qualities starch adhesive bed of material 6, and the PLASTIC LAMINATED is additionally provided with grain slag magnesite binding material 1;The layer glass fleece
One layer in lattice cloth 2 is provided with 4, one layer of organic silicon water-proofing layer 5 of layer of non-woven fabric, the fiberglass gridding cloth 2 from inside to outside
Another layer of outside be sequentially provided with one layer of organic silicon water-proofing layer 5 and one layer of this color surface layer 3.A kind of fire prevention of the outdoor use of the present invention
Plate, by the cooperation of grain slag magnesite binding material 1, fiberglass gridding cloth 2, this color surface layer 3 and non-woven fabrics 4, compared with common
Fire prevention panel products water absorption rate < 8%, coefficient of softing 1, compression strength > 40Mpa, high-strength light are widely used in outdoor dress
Decorations.It should be noted that a kind of PLASTIC LAMINATED of outdoor use consumes a large amount of blast furnace granulated slags, pollution is reduced, improve people and occupy ring
Border.
Embodiment 2:
Used as preferred, the grain slag magnesite binding material 1 is made up of grain slag, magnesite binding material.It is noticeable
It is, the mixture unrelated component in the present embodiment, only to think about it that expression grain slag magnesite binding material 1 includes grain slag, magnesite gelling material
The obsolete materials such as material, the component of each material is not as technical characteristic.
Embodiment 3:
Used as preferred, described color surface layer 3 is magnesite binding material, the surface layer of grain slag powder self color.This color surface layer 3
Way:29.4 ° of B é magnesium sulfate waters of 125kg, the magnesia light burnt powder of 100kg, the dolomite dust of 4kg, the grain slag of 100kg
Powder, the modifying agent of a weight, mixer stir and obtain.
Embodiment 4:
Used as preferred, the non-woven fabrics 4 is per square metre of 9g to 100g.It should be noted that be molded on a production line,
True qualities starch adhesive material 6 is paved on PVC or ABS substrates, in the press-in true qualities starch adhesive of fiberglass gridding cloth 2 material 6;Fiber grain slag magnesite
1 slurry of Binder Materials is paved on true qualities starch adhesive material 6, lays fiberglass gridding cloth 2 again, lays the gelling of grain slag magnesite again
1 slurry of material, then lays non-woven fabrics 4, is then covered with 1 slurry of grain slag magnesite binding material and cements non-woven fabrics 4;It is cleaved, whole
Flat, maintenance, solidification, form removal, conserve again, four side Length-fixing cuttings, two big faces spray waterproofing agent of organosilicon 5, dry, and form this
Grain slag magnesite binding material, fiberglass gridding cloth, this color surface layer, nonwoven layer, organic silicon water-proofing layer and true qualities in bright figure
A kind of PLASTIC LAMINATED of the outdoor use of starch adhesive bed of material composition.
Embodiment 5:
It should be noted that when a kind of fire prevention plate thickness of outdoor use is 8mm 2 layers of fiberglass gridding cloth 2, anti-folding is strong
Degree > 12Mpa, 4 layers of fiberglass gridding cloth 2 when a kind of fire prevention plate thickness of outdoor use is 8mm, rupture strength > 25Mpa,
4 layers of fiberglass gridding cloth 2 when a kind of fire prevention plate thickness of outdoor use is 10mm, rupture strength > 25Mpa, when a kind of outdoor
4 layers of fiberglass gridding cloth 2 when fire prevention plate thickness is 12mm, rupture strength > 20Mpa, when a kind of PLASTIC LAMINATED of outdoor use
6 layers of fiberglass gridding cloth 2 when thickness is 16mm, rupture strength > 25Mpa, when a kind of fire prevention plate thickness of outdoor use is 20mm
When 9 layers of fiberglass gridding cloth 2, rupture strength > 30Mpa, when a kind of outdoor use fire prevention plate thickness be 20mm when 10 layers of glass
Fibrous mesh cloth 2, rupture strength > 35Mpa, 10 layers of fiberglass gridding when a kind of fire prevention plate thickness of outdoor use is 40mm
Cloth 2, rupture strength > 25Mpa.A kind of fire prevention plate thickness of outdoor use is different, and 2 to 10 layers of fiberglass gridding cloth 2 may be selected.
It should be noted that the proportioning of described grain slag magnesite binding material 1 is:29.4 ° of B é magnesium sulfate waters of 125kg,
The magnesia light burnt powder of 100kg, the dolomite dust of 4kg, the grain slag powder of 100kg, 180kg grain slags, the modifying agent of a weight are produced
Product density 1.4.
The proportioning of this color surface layer 3:29.4 ° of B é magnesium sulfate waters of 125kg, the magnesia light burnt powder of 100kg, 4kg's is white
Marble dust, the grain slag powder of 100kg, the modifying agent of a weight, to 30 DEG C, its drying shrinkage value is minimum, stability for 25 DEG C of room temperature
Most preferably.
A kind of fire prevention plate thickness different choice 9g to 100g per square metre of the non-woven fabrics 4 according to outdoor use, its Main Function
Product surface porosity is reduced, facilitates vacuum cup product offline.
Semi-finished product Jing leveling, maintenance, solidification, form removal, reach intensity after by production line enter four side sizing cutting machines, enter
Row Length-fixing cutting, product are offline.
Embodiment 8:
A kind of preparation method of the PLASTIC LAMINATED of outdoor use, comprises the following steps:
A, mixer stir out 1 slurry of true qualities starch adhesive material 6 and grain slag magnesite binding material respectively, then produce in PLASTIC LAMINATED
It is molded on line;
B, true qualities starch adhesive material 6 are paved on PVC or ABS substrates, in the press-in true qualities starch adhesive of fiberglass gridding cloth 2 material 6;
C, 1 slurry of fiber grain slag magnesite binding material are paved on true qualities starch adhesive material 6, lay fiberglass gridding cloth again
2,1 slurry of grain slag magnesite binding material is laid again, then lays non-woven fabrics 4, being then covered with 1 slurry of grain slag magnesite binding material will
Non-woven fabrics 4 is cemented;
D, cleaved, leveling, maintenance, solidification, form removal, conserve again, four side Length-fixing cuttings, two big faces spraying organosilicons are prevented
Aqua 5, drying, are molded a kind of PLASTIC LAMINATED of outdoor use.
The method takes full advantage of the characteristic of every aspect material, pointedly takes corresponding PROCESS FOR TREATMENT, not only method
Simply, it is and easy to make, save cost.
Embodiment 9:
In described step a, the mixing time of true qualities starch adhesive material is three minutes.
Embodiment 10:
In described step d, cutting while cutting can be reduced burr, be improved using sliding knife cutting automatically, the knife
Product quality.
Presently preferred embodiments of the present invention is the foregoing is only, not to limit the present invention, all essences in the present invention
Any modification, equivalent and improvement made within god and principle etc., should be included within the scope of the present invention.
Claims (7)
1. a kind of PLASTIC LAMINATED of outdoor use, it is characterised in that:Including grain slag magnesite binding material (1), fiberglass gridding cloth
(2), this color surface layer (3), non-woven fabrics (4), organic silicon water-proofing layer (5) and the true qualities starch adhesive bed of material (6);Described glass fiber mesh
Ge Bu (2) is two-layer;
Be provided with the from inside to outside layer of non-woven fabric (4), one layer of organosilicon of a layer in the layer glass fibrous mesh cloth (2) is prevented
Water layer (5), another layer of outside of the fiberglass gridding cloth (2) are sequentially provided with one layer of organic silicon water-proofing layer (5) and one layer of sheet
Color surface layer (3).
2. the PLASTIC LAMINATED of a kind of outdoor use according to claim 1, it is characterised in that:The grain slag magnesite binding material
(1) it is made up of grain slag, magnesite binding material.
3. the PLASTIC LAMINATED of a kind of outdoor use according to claim 1 and 2, it is characterised in that:The non-woven fabrics (4) be 9g extremely
Per square metre of 100g.
4. the PLASTIC LAMINATED of a kind of outdoor use according to claim 1, it is characterised in that:The fiberglass gridding cloth (2)
Total tablet number be 2 to 10.
5. prepare claim 1-4 described in a kind of outdoor use PLASTIC LAMINATED preparation method, it is characterised in that:Including following step
Suddenly:
A, mixer stir out true qualities starch adhesive material (6) and grain slag magnesite binding material (1) slurry respectively, then produce in PLASTIC LAMINATED
It is molded on line;
B, true qualities starch adhesive material (6) are paved on PVC or ABS substrates, in fiberglass gridding cloth (2) press-in true qualities starch adhesive material (6);
C, fiber grain slag magnesite binding material (1) slurry are paved in true qualities starch adhesive material (6), lay fiberglass gridding cloth again
(2) grain slag magnesite binding material (1) slurry is laid again, is then laid non-woven fabrics (4), is then covered with grain slag magnesite binding material
(1) non-woven fabrics (4) is cemented by slurry;
D, cleaved, leveling, maintenance, solidification, form removal, conserve again, four side Length-fixing cuttings, two big faces spray waterproofing agent of organosilicon
(5), dry, be molded a kind of PLASTIC LAMINATED of outdoor use.
6. the preparation method of the PLASTIC LAMINATED of a kind of outdoor use according to claim 5, it is characterised in that:Described step a
The mixing time of middle true qualities starch adhesive material (6) is three minutes.
7. the preparation method of the PLASTIC LAMINATED of a kind of outdoor use according to claim 5 or 6, it is characterised in that:Described step
In rapid d, cutting is using sliding knife cutting automatically.