CN106760233A - Composite anti-corrosion chlorine oxygen magnesium watt - Google Patents
Composite anti-corrosion chlorine oxygen magnesium watt Download PDFInfo
- Publication number
- CN106760233A CN106760233A CN201510836701.3A CN201510836701A CN106760233A CN 106760233 A CN106760233 A CN 106760233A CN 201510836701 A CN201510836701 A CN 201510836701A CN 106760233 A CN106760233 A CN 106760233A
- Authority
- CN
- China
- Prior art keywords
- watt
- composite anti
- corrosion
- chlorine oxygen
- magnesium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the composite anti-corrosion chlorine oxygen magnesium watt that a kind of building roof or facade are used.Belong to New Building Materials field.Composite anti-corrosion chlorine oxygen magnesium watt is made up of surface layer, intermediate layer, bottom;Its surface layer 1 is made up of the texture paint of silicon third, and middle level is by three layers of magnesium oxychloride cementing material of layer of non-woven fabric, two-layer medium-alkali glass fibre grid cloth composition;Bottom is made up of BOPP adhesive tapes.Composite anti-corrosion chlorine oxygen magnesium watt has resistance to A grade noninflammability, a strong alkali-acid resistance salt corrosion, UV resistant irradiates, with bending and compressive strength is high, soaking-resistant, good toughness, small lower rain noise, environmental protection, the feature of insulation.Composite anti-corrosion chlorine oxygen magnesium watt is produced using mechanization wrapping process, without trimming, does not produce industrial waste.Tilt sickness 3-6mm, 800--1050mm wide, length 2000-8000mm, weight 6-12KG, particularly suitable chemical industry, metallurgy, ceramics, large-scale country fair use.
Description
Technical field
The present invention relates to the composite anti-corrosion chlorine oxygen magnesium watt that building roof or facade are used, belong to building material field.
Background technology
Current building roof market sale using it is most be color steel tile, magnesite tile, PET aluminium foils anticorrosive heat insulating watt, resin
Watt.The deficiency of color steel tile be bending and compressive strength it is low, not acid-alkali-corrosive-resisting, thermal insulation separation heat differential, rain noise it is very big, use the longevity
Order general 2-5.Magnesite tile poor water resistance, easily returns the numerous frost of halogen, not acid and alkali-resistance, ornamental poor.Although PET aluminium foil anticorrosive heat insulatings watt
Heat insulation property is good, but 5 years or so PET film life-span, and PET film is once aging, and its performance is identical with magnesite tile.In the market
Magnesite tile, PET aluminium foils anticorrosive heat insulating watt use trimming technology, produce solid waste and dust polluting environment.General insatiable hunger
Do not prevented fires with resin tile, low intensity, production process has infringement to human body, price is high.And composite anti-corrosion chlorine oxygen magnesium watt overcomes
The shortcoming of the said goods, with A grades of noninflammability, strong alkali-acid resistance salt corrosion, UV resistant irradiation, with bending and compressive strength
Height, soaking-resistant, good toughness, small lower rain noise, environmental protection, insulation, cost and PET aluminium foils anti-corrosion are every watt holding
It is flat.Composite anti-corrosion chlorine oxygen magnesium watt, without trimming, does not produce industrial waste using the production of mechanization wrapping process.
The content of the invention
It is an object of the invention to provide a kind of corrosion of strong alkali-acid resistance, the composite anti-corrosion with various designs and varieties
Chlorine oxygen magnesium watt.The present invention watt except surface can in addition to strong alkali-acid resistance, to watt the acid and alkali-resistance formula improvement that is also carried out of material of main part, make
Also there is certain decay resistance inside it.Dripped to product of the present invention with 20% hydrochloric acid or sulfuric acid solution are continual
Upper and lower surface 72 hours, product is not any change.Product of the present invention is immersed in 20% with pure magnesite tile and PET aluminium foil watt entirety
Hydrochloric acid or sulfuric acid solution in, composite anti-corrosion chlorine oxygen magnesium (plate) is slower than latter two product by the corrosion rate of acid solution
50%-60%.
The present invention is achieved through the following technical solutions above-mentioned purpose:
Composite anti-corrosion chlorine oxygen magnesium watt is made up of surface layer, middle level (main body) and bottom, it is characterised in that:Surface layer be by
The spraying of the texture paint of silicon third is formed, and middle level is by layer of non-woven fabric, three layers of magnesium oxychloride cementing material, two-layer medium-alkali glass fibre grid cloth
Constitute, bottom is made up of BOPP adhesive tapes.
The texture paint of silicon third is made up of priming paint, thick matter texture paint, three layers of finishing varnish, and priming paint adds alkali resistance thing by pure-acrylic emulsion
Matter constitute, thick matter texture paint by silicone acrylic emulsion, coalescents, thickener, dispersant, aqueous defoamer, bactericide, water-repelling agent,
The natural colour sand composition of variable grain grade.Finishing varnish is made up of silicone acrylic emulsion, age resister.Surface layer can make granite, true
The patterns such as mineral varnish, rubble, texture paint.Surface thickness is:0.3-0.7mm.
The magnesium oxychloride cementing material in middle level is by light calcined magnesia, magnesium chloride solution, diabase flour, composite modifier group
Into.
Non-woven fabrics is high polymer fiber cloth, and its weight grams is 10-50 grams every square metre.Described middle alkali glass
Fibrous mesh cloth its alkali metal oxide total content does not have 13%, grid 3-6 millimeters very much.
Described bottom BOPP adhesive tapes are uniformly to coat the quick glue emulsion of a lamination on the polypropylene screen of biaxial tension,
Its film+latex gross thickness is 45--55 μm.
Described silicone acrylic emulsion is to use organic siliconresin modified acrylic acid emulsion, and its silicone content is 5%-10%.
The present invention has the advantages that compared with prior art:
The texture paint of silicon third used by surface layer (Environment Oriented), its film forming matter is mainly the modified acrylic acid of organic siliconresin
Emulsion, compared with pure acrylic acid, organic siliconresin is that, as major key, its bond energy will than carbon-carbon bond with siloxanes key (Si-O-Si)
High is more and long, and Si-O-Si is stereochemical structure.Therefore silicone acrylic emulsion tool can have the compliance of height, resistant of high or low temperature, excellent
Resistance to UV aging.The material of silicon third also have three significantly performance to be that oxidative resistance, low-surface-energy and base material have good viscous
Knot property, oxidative resistance shows the corrosion of resistance to strong acid, and low-surface-energy shows that surface tension is small, and water and other dirts are difficult attached
, with very strong resistance to soiling.The texture paint of silicon third is water-based material, and it does not cause any infringement pollution to human body and environment.
The magnesium oxychloride cementing material in middle level, because adding diabase flour, except remaining energy-conserving and environment-protective of magnesium oxychloride material, strong
Outside degree height, good toughness, the advantage of easy processing shaping, the acid resistance of material is greatly improved, and diabase flour main component is dioxy
SiClx and aluminum oxide, and contain a small amount of other oxides and iron oxide, calcium oxide, titanium dioxide etc..Can be configured to acidproof
(alkali) clay, decay resistance is more than 10 times of acid-resistant cement.
The polypropylene screen of the biaxial tension used by bottom (in faced chamber) BOPP adhesive tapes has impact resistance higher, strong machine
Tool, toughness, anti-various organic solvents and soda acid corrode.Surface is smooth, does not absorb water.
Brief description of the drawings
Fig. 1 is the stereogram of the embodiment of the present invention;
Fig. 2 is the A-A profiles of embodiment illustrated in fig. 1.
Specific embodiment
By light-magnesite powder (content of magnesia 85%, activated magnesia 55%) 100kg, Baume degrees is 25 degree to example 1.
Magnesium chloride solution 68kg, 180-200 mesh diabase flour 30kg, flyash 6kg, wood chip 4kg, composite modifier (orthophosphoric acid+the third
Olefin(e) acid emulsion+FDN water reducers) 2.0kg.
Technical process:Above material is successively put into mortar mixer stirring 10-15 minute as slurry, machinery into
It is molded in the following sequence on type machine:BOPP adhesive tapes → material general → fibrous mesh cloth → material general → fibrous mesh cloth → material general → nothing
Spin cloth → mould → quiet and stop the texture paint of the hardening → demoulding → sprayed silicon third (priming paint, the texture paint of middle level 2, finishing varnish) → do
Dry → inspection → storage.
The light-magnesite powder of example 2. (content of magnesia 85%, activated magnesia 60%) 100kg, Baume degrees is 28 degree
Magnesium chloride solution 71kg, 180-200 mesh diabase flour 40kg, flyash 8kg, wood chip 5kg, composite modifier (orthophosphoric acid+propylene
Yogurt liquid+FDN water reducers) 2.3kg..
Technical process is identical with example 1.
The light-magnesite powder of example 3. (content of magnesia 85%, activated magnesia 65%) 100kg, Baume degrees is 30 degree
Magnesium chloride solution 75kg, 180-200 mesh diabase flour 50kg, flyash 10kg, wood chip 6kg, composite modifier (orthophosphoric acid+the third
Olefin(e) acid emulsion+FDN water reducers) 2.5kg.
Technical process is identical with example 1.
Claims (5)
1. a kind of composite anti-corrosion chlorine oxygen magnesium watt, it is made up of surface layer (1), middle level (2), bottom (3), middle level (2) and bottom
Layer (3) is once composited on forming machine, spraying surface (1), surface layer (1), middle level (2), bottom again after it hardens demoulding
(3) closely complex superposition into an entirety.
2. composite anti-corrosion chlorine oxygen magnesium watt according to claim 1, it is characterised in that:Surface layer (1) is by the texture of silicon third
Paint structure composition, middle level (2) are made up of layer of non-woven fabric, three layers of magnesium oxychloride cementing material, two-layer medium-alkali glass fibre grid cloth, bottom
Layer (3) is made up of BOPP adhesive tapes.
3. composite anti-corrosion chlorine oxygen magnesium watt according to claim 2, it is characterised in that:The texture paint of silicon third is by alkali resistant bottom
Paint, thick matter texture middle level (2) paint and surface finishing varnish composition.
4. composite anti-corrosion chlorine oxygen magnesium watt according to claim 2, it is characterised in that:Non-woven fabrics used by intermediate layer its
Material is high polymer fiber, and grammes per square metre is 10-40 grams per square meters, and magnesium oxychloride cementing material is by light-magnesite powder, chlorination
Magnesium solution, diabase flour, flyash, wood chip, composite modifier stirring hybrid reaction are formed.
5. composite anti-corrosion chlorine oxygen magnesium watt according to claim 2, it is characterised in that:Bottom (3) BOPP adhesive tapes be by
Biaxially oriented polypropylene film and pressure-sensitive adhesive emulsion are constituted, and film+latex gross thickness is 45--55 μm.