CN106752615A - A kind of lac varnish high and preparation method - Google Patents
A kind of lac varnish high and preparation method Download PDFInfo
- Publication number
- CN106752615A CN106752615A CN201611179786.3A CN201611179786A CN106752615A CN 106752615 A CN106752615 A CN 106752615A CN 201611179786 A CN201611179786 A CN 201611179786A CN 106752615 A CN106752615 A CN 106752615A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- ultra
- organobentonite
- lac varnish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of lac varnish high and preparation method, it is made up of following mass fraction formula components:40~45 parts of xylene solvent, 20~25 parts of perfluoro hexyl ethyl propylene acid esters, 20~25 parts of acrylic acid, 15~20 parts of methacrylic acid, 15~20 parts of methyl methacrylate, 15~20 parts of butyl acrylate, 5~10 parts of trimellitic anhydride, 5~7 parts of rutile type titanium white, 5~7 parts of anatase thpe white powder, 3~4 parts of organobentonite, 3~4 parts of ultra-fine barium sulfate, lac varnish high of the invention have good grease proofness.
Description
Technical field
The present invention relates to chemical material technical field, in particular to a kind of lac varnish high and preparation method.
Background technology
Paint is widely used in the life of people and industrial production, plays the work of protection, decoration, mark and other specific uses
With being the indispensable material in the world today.The species that existing market is painted is various, wherein lac varnish high is with its excellent gloss
Property is favored by everybody.Traditional lac varnish high be with acrylic resin or polyurethane as base-material, be aided with various pigment, solvent,
Additive is refined to be formed, although its paint film toughness and wear-resisting, heat-resisting, resistance to persistence, glossiness are all relatively good, but it is anti-
Water, grease proofing, antifouling NBC protective performance and resistance to chemical corrosion are relatively poor, and this largely limits lac varnish high
Range of application, while shortening the service life of lac varnish high.To there is oil preventing performance poor for paint at present, makes in some special industries
The problem being restricted in.
The content of the invention
Regarding to the issue above, the invention provides a kind of lac varnish high and preparation method.
To achieve the above object, the present invention provides following technical scheme:
A kind of lac varnish high, is made up of following mass fraction formula components:
40~45 parts of xylene solvent, 20~25 parts of perfluoro hexyl ethyl propylene acid esters, 20~25 parts of acrylic acid, methyl-prop
15~20 parts of olefin(e) acid, 15~20 parts of methyl methacrylate, 15~20 parts of butyl acrylate, 5~10 parts of trimellitic anhydride, golden red
5~7 parts of stone-type titanium dioxide, 5~7 parts of anatase thpe white powder, 3~4 parts of organobentonite, 3~4 parts of ultra-fine barium sulfate.
Further, it is made up of following mass fraction formula components:
40 parts of xylene solvent, 20 parts of perfluoro hexyl ethyl propylene acid esters, 20 parts of acrylic acid, 15 parts of methacrylic acid, first
15 parts of base methyl acrylate, 15 parts of butyl acrylate, 5 parts of trimellitic anhydride, 5 parts of rutile type titanium white, anatase thpe white powder 5
Part, 3 parts of organobentonite, 3 parts of ultra-fine barium sulfate.
Further, it is made up of following mass fraction formula components:
45 parts of xylene solvent, 25 parts of perfluoro hexyl ethyl propylene acid esters, 25 parts of acrylic acid, 20 parts of methacrylic acid, first
20 parts of base methyl acrylate, 20 parts of butyl acrylate, 10 parts of trimellitic anhydride, 7 parts of rutile type titanium white, anatase thpe white powder
7 parts, 4 parts of organobentonite, 4 parts of ultra-fine barium sulfate.
Further, it is made up of following mass fraction formula components:
43 parts of xylene solvent, 23 parts of perfluoro hexyl ethyl propylene acid esters, 23 parts of acrylic acid, 17 parts of methacrylic acid, first
17 parts of base methyl acrylate, 16 parts of butyl acrylate, 8 parts of trimellitic anhydride, 6 parts of rutile type titanium white, anatase thpe white powder 6
Part, 3 parts of organobentonite, 4 parts of ultra-fine barium sulfate.
Further:Preparation method of the present invention has following steps:
Step one:Under nitrogen protection, will in xylene solvent mix add agitator in, then sequentially add perfluor oneself
Base ethyl propylene acid esters, acrylic acid, methacrylic acid, methyl methacrylate and butyl acrylate, and stirred under normal temperature condition
Mix 1~2 hour, be made intermediate blend 1;
Step 2, by trimellitic anhydride addition intermediate blend 1, is then cooled to 150~160 DEG C of reactions 1.5~2 small
When, it is made intermediate blend 2;
Step 3:During rutile type titanium white, anatase thpe white powder, organobentonite, ultra-fine barium sulfate are sequentially added
Between in mixture 2, stirring mixing is made finished product.
The beneficial effects of the invention are as follows:
1. lac varnish high of the invention has good grease proofness;
2. lac varnish high of the invention has good glossiness;
3. lac varnish high of the invention has good UV resistant performance.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment one:
A kind of lac varnish high, is made up of following mass fraction formula components:40~45 parts of xylene solvent, perfluoro hexyl ethyl
20~25 parts of acrylate, 20~25 parts of acrylic acid, 15~20 parts of methacrylic acid, 15~20 parts of methyl methacrylate, third
15~20 parts of olefin(e) acid butyl ester, 5~10 parts of trimellitic anhydride, 5~7 parts of rutile type titanium white, 5~7 parts of anatase thpe white powder, have
3~4 parts of machine bentonite, 3~4 parts of ultra-fine barium sulfate.
Embodiment two:
A kind of lac varnish high, is made up of following mass fraction formula components:40 parts of xylene solvent, perfluoro hexyl ethyl propylene
20 parts of acid esters, 20 parts of acrylic acid, 15 parts of methacrylic acid, 15 parts of methyl methacrylate, 15 parts of butyl acrylate, trimellitic acid
5 parts of acid anhydride, 5 parts of rutile type titanium white, 5 parts of anatase thpe white powder, 3 parts of organobentonite, 3 parts of ultra-fine barium sulfate.
Embodiment three:
A kind of lac varnish high, is made up of following mass fraction formula components:45 parts of xylene solvent, perfluoro hexyl ethyl propylene
25 parts of acid esters, 25 parts of acrylic acid, 20 parts of methacrylic acid, 20 parts of methyl methacrylate, 20 parts of butyl acrylate, trimellitic acid
10 parts of acid anhydride, 7 parts of rutile type titanium white, 7 parts of anatase thpe white powder, 4 parts of organobentonite, 4 parts of ultra-fine barium sulfate.
Example IV:
A kind of lac varnish high, is made up of following mass fraction formula components:43 parts of xylene solvent, perfluoro hexyl ethyl propylene
23 parts of acid esters, 23 parts of acrylic acid, 17 parts of methacrylic acid, 17 parts of methyl methacrylate, 16 parts of butyl acrylate, trimellitic acid
8 parts of acid anhydride, 6 parts of rutile type titanium white, 6 parts of anatase thpe white powder, 3 parts of organobentonite, 4 parts of ultra-fine barium sulfate.
Embodiment five:
A kind of lac varnish its preparation method high comprises the following steps:
Step one:Under nitrogen protection, will in xylene solvent mix add agitator in, then sequentially add perfluor oneself
Base ethyl propylene acid esters, acrylic acid, methacrylic acid, methyl methacrylate and butyl acrylate, and stirred under normal temperature condition
Mix 1~2 hour, be made intermediate blend 1;
Step 2, by trimellitic anhydride addition intermediate blend 1, is then cooled to 150~160 DEG C of reactions 1.5~2 small
When, it is made intermediate blend 2;
Step 3:During rutile type titanium white, anatase thpe white powder, organobentonite, ultra-fine barium sulfate are sequentially added
Between in mixture 2, stirring mixing is made finished product.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each implementation method is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should
Specification an as entirety, the technical scheme in each embodiment can also be formed into those skilled in the art through appropriately combined
May be appreciated other embodiment.
Claims (5)
1. a kind of lac varnish high, it is characterised in that:It is made up of following mass fraction formula components:
40~45 parts of xylene solvent, 20~25 parts of perfluoro hexyl ethyl propylene acid esters, 20~25 parts of acrylic acid, methacrylic acid
15~20 parts, 15~20 parts of methyl methacrylate, 15~20 parts of butyl acrylate, 5~10 parts of trimellitic anhydride, rutile-type
5~7 parts of titanium dioxide, 5~7 parts of anatase thpe white powder, 3~4 parts of organobentonite, 3~4 parts of ultra-fine barium sulfate.
2. a kind of lac varnish high according to claim 1, it is characterised in that:It is made up of following mass fraction formula components:
40 parts of xylene solvent, 20 parts of perfluoro hexyl ethyl propylene acid esters, 20 parts of acrylic acid, 15 parts of methacrylic acid, methyl-prop
15 parts of e pioic acid methyl ester, 15 parts of butyl acrylate, 5 parts of trimellitic anhydride, 5 parts of rutile type titanium white, 5 parts of anatase thpe white powder,
3 parts of organobentonite, 3 parts of ultra-fine barium sulfate.
3. a kind of lac varnish high according to claim 1, it is characterised in that:It is made up of following mass fraction formula components:
45 parts of xylene solvent, 25 parts of perfluoro hexyl ethyl propylene acid esters, 25 parts of acrylic acid, 20 parts of methacrylic acid, methyl-prop
20 parts of e pioic acid methyl ester, 20 parts of butyl acrylate, 10 parts of trimellitic anhydride, 7 parts of rutile type titanium white, 7 parts of anatase thpe white powder,
4 parts of organobentonite, 4 parts of ultra-fine barium sulfate.
4. a kind of lac varnish high according to claim 1, it is characterised in that:It is made up of following mass fraction formula components:
43 parts of xylene solvent, 23 parts of perfluoro hexyl ethyl propylene acid esters, 23 parts of acrylic acid, 17 parts of methacrylic acid, methyl-prop
17 parts of e pioic acid methyl ester, 16 parts of butyl acrylate, 8 parts of trimellitic anhydride, 6 parts of rutile type titanium white, 6 parts of anatase thpe white powder,
3 parts of organobentonite, 4 parts of ultra-fine barium sulfate.
5. the preparation method of a kind of lac varnish high according to claim 1, it is characterised in that:Comprise the following steps:
Step one:Under nitrogen protection, will mix in xylene solvent in addition agitator, then sequentially add perfluoro hexyl second
Base acrylate, acrylic acid, methacrylic acid, methyl methacrylate and butyl acrylate, and under normal temperature condition stirring 1~
2 hours, it is made intermediate blend 1;
Step 2, by trimellitic anhydride addition intermediate blend 1, is then cooled to 150~160 DEG C and reacts 1.5~2 hours,
It is made intermediate blend 2;
Step 3:Rutile type titanium white, anatase thpe white powder, organobentonite, ultra-fine barium sulfate are sequentially added middle mixed
In compound 2, stirring mixing is made finished product.