CN103382317A - Metal protection resin varnish - Google Patents
Metal protection resin varnish Download PDFInfo
- Publication number
- CN103382317A CN103382317A CN2013102592610A CN201310259261A CN103382317A CN 103382317 A CN103382317 A CN 103382317A CN 2013102592610 A CN2013102592610 A CN 2013102592610A CN 201310259261 A CN201310259261 A CN 201310259261A CN 103382317 A CN103382317 A CN 103382317A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal protection
- protection resin
- resin paint
- siccative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a metal protection resin varnish. The metal protection resin varnish comprises, by weight, 25 to 45 parts of an acrylic resin, 10 to 15 parts of methyl methacrylate, 30 to 40 parts of styrene, 35 to 50 parts of deionized water, 3 to 6 parts of ammonia water, 1.8 to 2.5 parts of an auxiliary agent, 18 to 42 parts of a pigment and filler and 1.5 to 2.5 parts of a dry material. The metal protection resin varnish provided by the invention has the advantages of good mechanical and physical properties, high hardness, high adhesion, good water resistance, excellent decorative and protective performance, good low temperature resistance, water resistance and wear resistance and prevention of environmental pollution due to no use of xylene as a solvent.
Description
Technical field
The present invention relates to a kind of resin paint, be specifically related to a kind of nontoxic, free from extraneous odour, incombustible metal protection resin paint.
Background technology
Existing metal protection resin paint contains the dimethylbenzene equal solvent, the healthy of construction workman that is in for a long time in operating environment is caused damage, and also pollute the environment in production process.
Summary of the invention
Goal of the invention: in order to overcome the deficiencies in the prior art, the invention provides a kind of metal protection resin paint
Technical scheme: for achieving the above object, a kind of metal protection resin paint provided by the invention, its component consists of the following composition by weight: 25～45 parts of acrylic resins, 10～15 parts of methyl methacrylates, 30～40 parts of vinylbenzene, 35～50 parts of deionized waters, 3～6 parts of ammoniacal liquor, 1.8～2.5 parts of auxiliary agents, 18～42 parts of color stuffings, 1.5～2.5 parts of siccatives;
Wherein, described auxiliary agent comprises: 0.1～0.5 part of wetting agent, 0.2～0.25 part of defoamer, help 1.5～1.8 parts of films; Described color stuffing comprises: 5～15 parts of rust-stabilising pigments, 5～15 parts of tinting pigments, 15～25 parts of fillers; Described siccative comprises: 0.5～0.7 part of zinc siccative, 0.5～0.8 part of manganese siccative, 0.5～1 part of cobalt siccative.
Preferably, described acrylic resin is 30～40 parts.
Preferably, described methyl methacrylate is 12～14 parts.
Preferably, described rust-stabilising pigment is one or several in zinc molybdate, zinc phosphate, aluminium triphosphate, barium metaborate.
Preferably, described tinting pigment is one or several in titanium dioxide, red iron oxide, carbon black, phthalocyanine blue.
Preferably, described filler be in mica powder, natural barite powder, talcum powder, process white one or several.
Preferably, the described film that helps is 2-Butoxyethyl acetate.
Preferably, described defoamer is the silicone oil defoamer.
Preferably, described wetting agent is polyether-modified alkynol.
The preparation process of above-mentioned metal protection resin paint comprises:
(1) take corresponding material component by above-mentioned weight part;
(2) acrylic resin, the bitter methyl acrylate of first, vinylbenzene, deionized water and ammoniacal liquor are added in the pot of getting the raw materials ready, mix;
(3) then add successively in the pot of getting the raw materials ready defoamer, wetting agent, help film, after mixing, add rust-stabilising pigment, tinting pigment, filler, turn 1500/per minute stirred 15 minutes, made mill base liquid;
(4) with the mill base liquid that stirs by 120 order copper mesh or nylon net filters, then add successively zinc siccative, manganese siccative and cobalt siccative, turn 500～700/the per minute rotating speed under, stir and can construct in 25 minutes.
Beneficial effect: the present invention in terms of existing technologies, have mechanical and physical performance good, hardness is high, and sticking power is high, water tolerance is strong, antiseptic property good, have good ornamental and protective, resistance to low temperature is good, and the water proof and wearable performance is good, can add as required colorant, be modulated into the product of different color, and saved dimethylbenzene as solvent, thereby avoided contaminate environment.
Embodiment
Below in conjunction with embodiment, the present invention is further described.
Embodiment 1:
A kind of metal protection resin paint, its component consists of the following composition by weight: 45 parts of acrylic resins, 15 parts of methyl methacrylates, 30 parts of vinylbenzene, 35 parts of deionized waters, 3 parts of ammoniacal liquor, 0.5 part of wetting agent, 0.25 part of silicone oil defoamer, 1.8 parts of 2-Butoxyethyl acetates, 15 parts of zinc phosphates, 15 parts of titanium dioxides, 25 parts of mica powders, 0.7 part of zinc siccative, 0.5 part of manganese siccative, 0.5 part of cobalt siccative.
The preparation process of above-mentioned metal protection resin paint comprises:
(1) take corresponding material component by above-mentioned weight part;
(2) acrylic resin, the bitter methyl acrylate of first, vinylbenzene, deionized water and ammoniacal liquor are added in the pot of getting the raw materials ready, mix;
(3) then add successively silicone oil defoamer, wetting agent, 2-Butoxyethyl acetate in the pot of getting the raw materials ready, after mixing, add zinc phosphate, titanium dioxide and mica powder, turn 1500/per minute stirred 18 minutes, made mill base liquid;
(4) with the mill base liquid that stirs by 120 order copper mesh or nylon net filters, then add successively zinc siccative, manganese siccative and cobalt siccative, turn 500～700/the per minute rotating speed under, stir and can construct in 25 minutes.
Embodiment 2:
A kind of metal protection resin paint, its component consists of the following composition by weight: 25 parts of acrylic resins, 10 parts of methyl methacrylates, 40 parts of vinylbenzene, 50 parts of deionized waters, 6 parts of ammoniacal liquor, 0.1 part of wetting agent, 0.2 part of silicone oil defoamer, 1.5 parts of 2-Butoxyethyl acetates, 5 parts of barium metaborates, 5 parts of phthalocyanine blues, 15 parts of talcum powder, zinc siccative 0.5, part, 0.5 part of manganese siccative, 1 part of cobalt siccative.
The preparation process of above-mentioned metal protection resin paint comprises:
(1) take corresponding material component by above-mentioned weight part;
(2) acrylic resin, the bitter methyl acrylate of first, vinylbenzene, deionized water and ammoniacal liquor are added in the pot of getting the raw materials ready, mix;
(3) then add successively silicone oil defoamer, wetting agent, 2-Butoxyethyl acetate in the pot of getting the raw materials ready, after mixing, add barium metaborate, phthalocyanine blue, talcum powder, turn 1500/per minute stirred 15 minutes, made mill base liquid;
(4) with the mill base liquid that stirs by 120 order copper mesh or nylon net filters, then add successively zinc siccative, manganese siccative and cobalt siccative, turn 500～700/the per minute rotating speed under, stir and can construct in 25 minutes.
Embodiment 3:
A kind of metal protection resin paint, its component consists of the following composition by weight: 30 parts of acrylic resins, 12 parts of methyl methacrylates, 35 parts of vinylbenzene, 45 parts of deionized waters, 5 parts of ammoniacal liquor, 0.3 part of wetting agent, 0.22 part of silicone oil defoamer, 1.6 parts of 2-Butoxyethyl acetates, 10 parts of aluminium triphosphates, 10 parts of red iron oxides, 20 parts of process whites; 0.6 part of zinc siccative, 0.6 part of manganese siccative, 0.8 part of cobalt siccative.
The preparation process of above-mentioned metal protection resin paint comprises:
(1) take corresponding material component by above-mentioned weight part;
(2) acrylic resin, the bitter methyl acrylate of first, vinylbenzene, deionized water and ammoniacal liquor are added in the pot of getting the raw materials ready, mix;
(3) then add successively silicone oil defoamer, wetting agent, 2-Butoxyethyl acetate in the pot of getting the raw materials ready, after mixing, add aluminium triphosphate, red iron oxide, process white, turn 1500/per minute stirred 15 minutes, made mill base liquid;
(4) with the mill base liquid that stirs by 120 order copper mesh or nylon net filters, then add successively zinc siccative, manganese siccative and cobalt siccative, turn 500～700/the per minute rotating speed under, stir and can construct in 25 minutes.
Embodiment 4:
A kind of metal protection resin paint, its component consists of the following composition by weight: 40 parts of acrylic resins, 14 parts of methyl methacrylates, 32 parts of vinylbenzene, 40 parts of deionized waters, 4 parts of ammoniacal liquor, 0.4 part of wetting agent, 0.24 part of defoamer, 1.7 parts of 2-Butoxyethyl acetates, 12 parts of zinc molybdates, 12 parts of carbon blacks, 18 parts, natural barite powder, 0.6 part of zinc siccative, 0.7 part of manganese siccative, 0.9 part of cobalt siccative.
The preparation process of above-mentioned metal protection resin paint comprises:
(1) take corresponding material component by above-mentioned weight part;
(2) acrylic resin, the bitter methyl acrylate of first, vinylbenzene, deionized water and ammoniacal liquor are added in the pot of getting the raw materials ready, mix;
(3) then add successively silicone oil defoamer, wetting agent, 2-Butoxyethyl acetate in the pot of getting the raw materials ready, after mixing, add three zinc molybdates, carbon black, natural barite powder, turn 1500/per minute stirred 15 minutes, made mill base liquid;
(4) with the mill base liquid that stirs by 120 order copper mesh or nylon net filters, then add successively zinc siccative, manganese siccative and cobalt siccative, turn 500～700/the per minute rotating speed under, stir and can construct in 25 minutes.
Embodiment 5:
A kind of metal protection resin paint, its component consists of the following composition by weight: 38 parts of acrylic resins, 13 parts of methyl methacrylates, 36 parts of vinylbenzene, 42 parts of deionized waters, 5 parts of ammoniacal liquor, 0.2 part of wetting agent, 0.21 part of defoamer, 1.6 parts of 2-Butoxyethyl acetates, 8 parts of barium metaborates, 8 parts of red iron oxides, 17 parts, natural barite powder, 0.6 part of zinc siccative, 0.6 part of manganese siccative, 0.9 part of cobalt siccative.
The preparation process of above-mentioned metal protection resin paint comprises:
(1) take corresponding material component by above-mentioned weight part;
(2) acrylic resin, the bitter methyl acrylate of first, vinylbenzene, deionized water and ammoniacal liquor are added in the pot of getting the raw materials ready, mix;
(3) then add successively silicone oil defoamer, wetting agent, 2-Butoxyethyl acetate in the pot of getting the raw materials ready, after mixing, add barium metaborate, red iron oxide, natural barite powder, turn 1500/per minute stirred 15 minutes, made mill base liquid;
(4) with the mill base liquid that stirs by 120 order copper mesh or nylon net filters, then add successively zinc siccative, manganese siccative and cobalt siccative, turn 500～700/the per minute rotating speed under, stir and can construct in 25 minutes.
The above is only the preferred embodiment of the present invention; be noted that for those skilled in the art; under the prerequisite that does not break away from the principle of the invention, can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (9)
1. metal protection resin paint, it is characterized in that: its component consists of the following composition by weight: 25～45 parts of acrylic resins, 10～15 parts of methyl methacrylates, 30～40 parts of vinylbenzene, 35～50 parts of deionized waters, 3～6 parts of ammoniacal liquor, 1.8～2.5 parts of auxiliary agents, 18～42 parts of color stuffings, 1.5～2.5 parts of siccatives;
Wherein, described auxiliary agent comprises: 0.1～0.5 part of wetting agent, 0.2～0.25 part of defoamer, help 1.5～1.8 parts of films; Described color stuffing comprises: 5～15 parts of rust-stabilising pigments, 5～15 parts of tinting pigments, 15～25 parts of fillers; Described siccative comprises: 0.5～0.7 part of zinc siccative, 0.5～0.8 part of manganese siccative, 0.5～1 part of cobalt siccative.
2. metal protection resin paint according to claim 1, it is characterized in that: described acrylic resin is 30～40 parts.
3. a kind of metal protection resin paint according to claim 1, it is characterized in that: described methyl methacrylate is 12～14 parts.
4. a kind of metal protection resin paint according to claim 1, it is characterized in that: described rust-stabilising pigment is one or several in zinc molybdate, zinc phosphate, aluminium triphosphate, barium metaborate.
5. a kind of metal protection resin paint according to claim 1, it is characterized in that: described tinting pigment is one or several in titanium dioxide, red iron oxide, carbon black, phthalocyanine blue.
6. a kind of metal protection resin paint according to claim 1 is characterized in that: described filler be in mica powder, natural barite powder, talcum powder, process white one or several.
7. a kind of metal protection resin paint according to claim 1, it is characterized in that: the described film that helps is 2-Butoxyethyl acetate.
8. a kind of metal protection resin paint according to claim 1, it is characterized in that: described defoamer is the silicone oil defoamer.
9. a kind of metal protection resin paint according to claim 1, it is characterized in that: described wetting agent is polyether-modified alkynol.