CN106752220A - A kind of art painting compound propylene material and preparation method thereof - Google Patents
A kind of art painting compound propylene material and preparation method thereof Download PDFInfo
- Publication number
- CN106752220A CN106752220A CN201611021887.8A CN201611021887A CN106752220A CN 106752220 A CN106752220 A CN 106752220A CN 201611021887 A CN201611021887 A CN 201611021887A CN 106752220 A CN106752220 A CN 106752220A
- Authority
- CN
- China
- Prior art keywords
- parts
- art painting
- acrylic acid
- acid emulsion
- modified acrylic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
It is according to the primary raw material of weight portion with compound propylene material with propylene material, the art painting is combined the invention discloses a kind of art painting：30 40 parts of modified acrylic acid emulsion, 8 15 parts of guar gum, 7.5 8.0 parts of phenylalanine, 13 parts of sodium potassium tartrate tetrahydrate, 5 12 parts of tween, 18 22 parts of pigment particle；The modified acrylic acid emulsion is that after acrylic emulsion is heated, addition shaddock flesh, titanium dioxide, amylopectin carry out reaction and be obtained；Preparation technology is first, under nitrogen protection, modified acrylic acid emulsion, guar gum, phenylalanine, sodium potassium tartrate tetrahydrate, tween, pigment particle to be mixed; place in closed mixer, mixing speed is 200 300r/min, stirring to substantially uniformity; then carry out being filled into bottle, obtain final product.The art painting that the present invention is prepared has the durable effect of rapid-curing cutback with compound propylene material；The compound propylene material of art painting is rapid to be dried after being applied on paper, the performance with rapid-curing cutback；In addition the compound propylene material of art painting, still with original color representation power, and with certain antibacterial ability, prevents from going mouldy after placing 2 years.
Description
Technical field
The present invention relates to a kind of painting material field, the compound propylene material of specifically a kind of art painting.
Background technology
Acrylic paints have purposes widely in the middle of the use of pigment, can be used in the purposes such as drawing.Third
In the middle of the application of alkene pigment, there is standard higher to the rapid-curing cutback performance and endurance quality of acrylic paints.Wherein, rapid-curing cutback performance pair
The use of acrylic paints play the role of it is very big, if with good rapid-curing cutback performance, can improve acrylic paints using in the middle of
Efficiency.Meanwhile, acrylic paints possess good durability, after drawing, can for a long time keep lasting effect, keep drawing former
Some colors and expressive force.
The content of the invention
It is an object of the invention to provide a kind of art painting with compound propylene material, to solve to be carried in above-mentioned background technology
The problem for going out.
To achieve the above object, the present invention provides following technical scheme：
A kind of compound propylene material of art painting, be according to the primary raw material of weight portion：Modified acrylic acid emulsion 30-40
Part, guar gum 8-15 parts, phenylalanine 7.5-8.0 parts, sodium potassium tartrate tetrahydrate 1-3 parts, tween 5-12 parts, pigment particle 18-22 parts；
The modified acrylic acid emulsion is that after acrylic emulsion is heated, addition shaddock flesh, titanium dioxide, amylopectin carry out reaction system
.
As further scheme of the invention：Primary raw material according to weight portion is：Modified acrylic acid emulsion 33-37 parts,
Guar gum 10-14 parts, phenylalanine 7.5-8.0 parts, sodium potassium tartrate tetrahydrate 1-3 parts, tween 8-10 parts, pigment particle 18-22 parts；Institute
It is that after acrylic emulsion is heated, addition shaddock flesh, titanium dioxide, amylopectin carry out reaction system to state modified acrylic acid emulsion
.
As further scheme of the invention：Primary raw material according to weight portion is：35 parts of modified acrylic acid emulsion, Guar
12 parts of glue, 7.8 parts of phenylalanine, 2 parts of sodium potassium tartrate tetrahydrate, 9 parts of tween, 20 parts of pigment particle；The modified acrylic acid emulsion is
After acrylic emulsion is heated, addition shaddock flesh, titanium dioxide, amylopectin carry out reaction and are obtained.
A kind of art painting preparation method of compound propylene material, concretely comprises the following steps：
First, under nitrogen protection, by modified acrylic acid emulsion, guar gum, phenylalanine, sodium potassium tartrate tetrahydrate, tween, face
Material particulate is mixed, and is placed in closed mixer, and mixing speed is 200-300r/min, is stirred to substantially uniformity, is then filled
Load bottle, obtain final product.
As further scheme of the invention：Mixing speed is 250r/min in step.
Compared with prior art, the beneficial effects of the invention are as follows：
The art painting that the present invention is prepared has the durable effect of rapid-curing cutback with compound propylene material；Art painting is with again
Propylene material is closed after being applied on paper, is dried rapidly, the performance with rapid-curing cutback；In addition art painting is existed with compound propylene material
After placing 2 years, still with original color representation power, and with certain antibacterial ability, prevent from going mouldy.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment 1
A kind of compound propylene material of art painting, be according to the primary raw material of weight portion：30 parts of modified acrylic acid emulsion,
8 parts of guar gum, 7.5 parts of phenylalanine, 1 part of sodium potassium tartrate tetrahydrate, 5 parts of tween, 18 parts of pigment particle；The modified acrylic acid emulsion
It is that after acrylic emulsion is heated, addition shaddock flesh, titanium dioxide, amylopectin carry out reaction and be obtained.
A kind of art painting preparation method of compound propylene material, concretely comprises the following steps：
First, under nitrogen protection, by modified acrylic acid emulsion, guar gum, phenylalanine, sodium potassium tartrate tetrahydrate, tween, face
Material particulate is mixed, and is placed in closed mixer, and mixing speed is 200r/min, is stirred to substantially uniformity, is then filled into
Bottle, obtains final product.
Embodiment 2
A kind of compound propylene material of art painting, be according to the primary raw material of weight portion：33 parts of modified acrylic acid emulsion,
10 parts of guar gum, 7.5 parts of phenylalanine, 1 part of sodium potassium tartrate tetrahydrate, 8 parts of tween, 18 parts of pigment particle；The modified propylene yogurt
Liquid is that after acrylic emulsion is heated, addition shaddock flesh, titanium dioxide, amylopectin carry out reaction and be obtained.
A kind of art painting preparation method of compound propylene material, concretely comprises the following steps：
First, under nitrogen protection, by modified acrylic acid emulsion, guar gum, phenylalanine, sodium potassium tartrate tetrahydrate, tween, face
Material particulate is mixed, and is placed in closed mixer, and mixing speed is 230r/min, is stirred to substantially uniformity, is then filled into
Bottle, obtains final product.
Embodiment 3
A kind of compound propylene material of art painting, be according to the primary raw material of weight portion：35 parts of modified acrylic acid emulsion,
12 parts of guar gum, 7.8 parts of phenylalanine, 2 parts of sodium potassium tartrate tetrahydrate, 9 parts of tween, 20 parts of pigment particle；The modified propylene yogurt
Liquid is that after acrylic emulsion is heated, addition shaddock flesh, titanium dioxide, amylopectin carry out reaction and be obtained.
A kind of art painting preparation method of compound propylene material, concretely comprises the following steps：
First, under nitrogen protection, by modified acrylic acid emulsion, guar gum, phenylalanine, sodium potassium tartrate tetrahydrate, tween, face
Material particulate is mixed, and is placed in closed mixer, and mixing speed is 250r/min, is stirred to substantially uniformity, is then filled into
Bottle, obtains final product.
Embodiment 4
A kind of compound propylene material of art painting, be according to the primary raw material of weight portion：37 parts of modified acrylic acid emulsion,
14 parts of guar gum, 8.0 parts of phenylalanine, 3 parts of sodium potassium tartrate tetrahydrate, 10 parts of tween, 22 parts of pigment particle；The modified propylene yogurt
Liquid is that after acrylic emulsion is heated, addition shaddock flesh, titanium dioxide, amylopectin carry out reaction and be obtained.
A kind of art painting preparation method of compound propylene material, concretely comprises the following steps：
First, under nitrogen protection, by modified acrylic acid emulsion, guar gum, phenylalanine, sodium potassium tartrate tetrahydrate, tween, face
Material particulate is mixed, and is placed in closed mixer, and mixing speed is 300r/min, is stirred to substantially uniformity, is then filled into
Bottle, obtains final product.
Embodiment 5
A kind of compound propylene material of art painting, be according to the primary raw material of weight portion：40 parts of modified acrylic acid emulsion,
15 parts of guar gum, 8.0 parts of phenylalanine, 3 parts of sodium potassium tartrate tetrahydrate, 12 parts of tween, 22 parts of pigment particle；The modified propylene yogurt
Liquid is that after acrylic emulsion is heated, addition shaddock flesh, titanium dioxide, amylopectin carry out reaction and be obtained.
A kind of art painting preparation method of compound propylene material, concretely comprises the following steps：
First, under nitrogen protection, by modified acrylic acid emulsion, guar gum, phenylalanine, sodium potassium tartrate tetrahydrate, tween, face
Material particulate is mixed, and is placed in closed mixer, and mixing speed is 300r/min, is stirred to substantially uniformity, is then filled into
Bottle, obtains final product.
Test
The compound propylene material that embodiment 1, embodiment 2, embodiment 3, embodiment 4, embodiment 5 are prepared respectively is applied to
It is rapid to dry after on paper, the effect with rapid-curing cutback；Additionally, after placing 2 years, still with original color representation power, with good
Good lasting effect.
Performance test then is carried out according to GB/T 9754-2007 and QB/T 4289-2012, embodiment 1-5 is prepared respectively
Compound propylene material specific insulation be 4.8-5.3 × 10-1Ω cm, average 4200 times of wearability test, gloss 68-72,
At 5-7 grades, without mildew phenomena, the element that can move out is detection to light resistance to greatest extent.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be in other specific forms realized.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires to be limited rather than described above, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each implementation method is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should
Specification an as entirety, the technical scheme in each embodiment can also be formed into those skilled in the art through appropriately combined
May be appreciated other embodiment.
Claims (5)
1. a kind of art painting is with compound propylene material, it is characterised in that the primary raw material according to weight portion is：Modified acroleic acid
Emulsion 30-40 parts, guar gum 8-15 parts, phenylalanine 7.5-8.0 parts, sodium potassium tartrate tetrahydrate 1-3 parts, tween 5-12 parts, pigment it is micro-
18-22 parts of grain；The modified acrylic acid emulsion is addition shaddock flesh, titanium dioxide, amylopectin after acrylic emulsion is heated
Reaction is carried out to be obtained.
2. art painting according to claim 1 is used and is combined propylene material, it is characterised in that according to the main original of weight portion
Expect be：Modified acrylic acid emulsion 33-37 parts, guar gum 10-14 parts, phenylalanine 7.5-8.0 parts, sodium potassium tartrate tetrahydrate 1-3 parts, tell
It is warm 8-10 parts, pigment particle 18-22 parts；The modified acrylic acid emulsion is addition shaddock flesh, two after acrylic emulsion is heated
Titanium oxide, amylopectin carry out reaction and are obtained.
3. art painting according to claim 1 and 2 is used and is combined propylene material, it is characterised in that according to the master of weight portion
The raw material is wanted to be：35 parts of modified acrylic acid emulsion, 12 parts of guar gum, 7.8 parts of phenylalanine, 2 parts of sodium potassium tartrate tetrahydrate, 9 parts of tween, face
20 parts of particulate of material；The modified acrylic acid emulsion is that after acrylic emulsion is heated, addition shaddock flesh, titanium dioxide, side chain form sediment
Powder carries out reaction and is obtained.
4. a kind of art painting use as described in claim 1-3 is any is combined the preparation method of propylene material, it is characterised in that
Concretely comprise the following steps：
First, under nitrogen protection, it is modified acrylic acid emulsion, guar gum, phenylalanine, sodium potassium tartrate tetrahydrate, tween, pigment is micro-
Grain is mixed, and is placed in closed mixer, and mixing speed is 200-300r/min, is stirred to substantially uniformity, is then filled into
Bottle, obtains final product.
5. art painting use according to claim 4 is combined the preparation method of propylene material, it is characterised in that stirred in step
Speed is mixed for 250r/min.