CN106751465A - A kind of municipal road and bridge first-aid repair construction asphalt modification inorganic agent - Google Patents
A kind of municipal road and bridge first-aid repair construction asphalt modification inorganic agent Download PDFInfo
- Publication number
- CN106751465A CN106751465A CN201611025567.XA CN201611025567A CN106751465A CN 106751465 A CN106751465 A CN 106751465A CN 201611025567 A CN201611025567 A CN 201611025567A CN 106751465 A CN106751465 A CN 106751465A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- bridge
- inorganic agent
- aid repair
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It is composed of the following components the present invention relates to a kind of municipal road and bridge first-aid repair construction asphalt modification inorganic agent：Bisphenol A type epoxy resin, PVC resin powder, MBS resins, propylene glycol methyl ether acetate, isobutyrone, litsea citrate oil, dimethyl hydroxyl silicon oil, esterase, dibromodimethyl hydantoin, oxymatrine, the chlorine of alkynes third, calcium hypochlorite, magnesite powder, CoCL2 6H2O, aluminic acid cobalt dust, maifanite powder, wood powder, nano-carbon powder, nylon fiber, expanded vermiculite powder, HBB, sodium stannate, ammonium polyphosphate, IPPP, benzimidazole, double methyl methacrylate triethylene glycol ester, cellulose acetate, hydroxyethyl meth acrylate phosphate, vinyl acetate, paranitroanilinum.Product of the present invention has more superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improves properties of product.
Description
Technical field
The present invention relates to a kind of municipal road and bridge first-aid repair construction asphalt modification inorganic agent, belong to road and bridge repairing bitumen technology neck
Domain.
Background technology
The dark brown complex mixture that pitch is made up of the hydrocarbon and its non metallic derivatives of different molecular weight,
It is one kind of high viscosity organic liquid, is in a liquid state, surface is in black, dissolves in carbon disulfide.Pitch be it is a kind of waterproof and dampproof and
Corrosion-resistant organic cementing material.Pitch can be largely classified into three kinds of coal tar pitch, asphalt and bitumen：Wherein, coal tar
Pitch is the byproduct of coking.Asphalt is the residue after crude distillation.Bitumen is then to be stored at underground, some formation
Ore bed or in earth's crust surface sediment.Pitch is mainly used in the industry such as product, plastics, rubber and surfacing etc..On municipal road
In bridge repairing, it is often necessary to use pitch, these pitches are necessary to suitable modification agent is improved its performance.
The content of the invention
It is an object of the invention to provide a kind of municipal road and bridge first-aid repair construction asphalt modification inorganic agent, to be better achieved
The use function of municipal road and bridge first-aid repair construction asphalt modification inorganic agent, makes product have fire-retardant, acid and alkali-resistance, anti-mildew antibiotic property
Can, improve product performance.
To achieve these goals, technical scheme is as follows.
A kind of municipal road and bridge first-aid repair construction asphalt modification inorganic agent, is made up of the component of following mass fraction：Bisphenol A-type ring
26~30 parts of oxygen tree fat, 24~28 parts of PVC resin powder, 24~28 parts of MBS resins, 22~26 parts of propylene glycol methyl ether acetate, two
24~28 parts of isobutyl ketone, 24~28 parts of litsea citrate oil, 22~26 parts of dimethyl hydroxyl silicon oil, esterase 24~28
Part, 24~28 parts of dibromodimethyl hydantoin, 22~26 parts of oxymatrine, 22~26 parts of the third chlorine of alkynes, calcium hypochlorite 22~
26 parts, 24~28 parts of magnesite powder, 22~26 parts of CoCL2 6H2O, 20~24 parts of aluminic acid cobalt dust, maifanite powder 24~28
Part, 22~26 parts of wood powder, 20~24 parts of nano-carbon powder, 22~26 parts of nylon fiber, 20~24 parts of expanded vermiculite powder, HBB
20~24 parts, 22~26 parts of sodium stannate, 22~26 parts of ammonium polyphosphate, 22~26 parts of IPPP, benzimidazole
22~26 parts, 22~26 parts of double methyl methacrylate triethylene glycol ester, 22~26 parts of cellulose acetate, hydroxyethyl methyl propylene
22~26 parts of acid esters phosphate, 22~26 parts of vinyl acetate, 20~24 parts of paranitroanilinum.
Further, above-mentioned municipal road and bridge first-aid repair construction asphalt modification inorganic agent, is made up of the component of following mass fraction：
26 parts of bisphenol A type epoxy resin, 24 parts of PVC resin powder, 24 parts of MBS resins, 22 parts of propylene glycol methyl ether acetate, diisobutyl first
24 parts of ketone, 24 parts of litsea citrate oil, 22 parts of dimethyl hydroxyl silicon oil, 24 parts of esterase, 24 parts of dibromodimethyl hydantoin,
22 parts of oxymatrine, 22 parts of the third chlorine of alkynes, 22 parts of calcium hypochlorite, 24 parts of magnesite powder, 22 parts of CoCL2 6H2O, aluminic acid cobalt dust
20 parts, 24 parts of maifanite powder, 22 parts of wood powder, 20 parts of nano-carbon powder, 22 parts of nylon fiber, 20 parts of expanded vermiculite powder, hexabromo
20 parts of benzene, 22 parts of sodium stannate, 22 parts of ammonium polyphosphate, 22 parts of IPPP, 22 parts of benzimidazole, double metering systems
22 parts of sour Triethylene Glycol, 22 parts of cellulose acetate, 22 parts of hydroxyethyl meth acrylate phosphate, vinyl acetate 22
Part, 20 parts of paranitroanilinum.
Further, above-mentioned municipal road and bridge first-aid repair construction asphalt modification inorganic agent, is made up of the component of following mass fraction：
28 parts of bisphenol A type epoxy resin, 26 parts of PVC resin powder, 26 parts of MBS resins, 24 parts of propylene glycol methyl ether acetate, diisobutyl first
26 parts of ketone, 26 parts of litsea citrate oil, 24 parts of dimethyl hydroxyl silicon oil, 26 parts of esterase, 26 parts of dibromodimethyl hydantoin,
24 parts of oxymatrine, 24 parts of the third chlorine of alkynes, 24 parts of calcium hypochlorite, 26 parts of magnesite powder, 24 parts of CoCL2 6H2O, aluminic acid cobalt dust
22 parts, 26 parts of maifanite powder, 24 parts of wood powder, 22 parts of nano-carbon powder, 24 parts of nylon fiber, 22 parts of expanded vermiculite powder, hexabromo
22 parts of benzene, 24 parts of sodium stannate, 24 parts of ammonium polyphosphate, 24 parts of IPPP, 24 parts of benzimidazole, double metering systems
24 parts of sour Triethylene Glycol, 24 parts of cellulose acetate, 24 parts of hydroxyethyl meth acrylate phosphate, vinyl acetate 24
Part, 22 parts of paranitroanilinum.
Further, above-mentioned municipal road and bridge first-aid repair construction asphalt modification inorganic agent, is made up of the component of following mass fraction：
30 parts of bisphenol A type epoxy resin, 28 parts of PVC resin powder, 28 parts of MBS resins, 26 parts of propylene glycol methyl ether acetate, diisobutyl first
28 parts of ketone, 28 parts of litsea citrate oil, 26 parts of dimethyl hydroxyl silicon oil, 28 parts of esterase, 28 parts of dibromodimethyl hydantoin,
26 parts of oxymatrine, 26 parts of the third chlorine of alkynes, 26 parts of calcium hypochlorite, 28 parts of magnesite powder, 26 parts of CoCL2 6H2O, aluminic acid cobalt dust
24 parts, 28 parts of maifanite powder, 26 parts of wood powder, 24 parts of nano-carbon powder, 26 parts of nylon fiber, 24 parts of expanded vermiculite powder, hexabromo
24 parts of benzene, 26 parts of sodium stannate, 26 parts of ammonium polyphosphate, 26 parts of IPPP, 26 parts of benzimidazole, double metering systems
26 parts of sour Triethylene Glycol, 26 parts of cellulose acetate, 26 parts of hydroxyethyl meth acrylate phosphate, vinyl acetate 26
Part, 24 parts of paranitroanilinum.
Further, above-mentioned municipal road and bridge first-aid repair construction asphalt modification inorganic agent preparation method step is as follows：
（1）By the bisphenol A type epoxy resin of the mass fraction, PVC resin powder, MBS resins, propylene glycol methyl ether acetate, two
Isobutyl ketone, litsea citrate oil, dimethyl hydroxyl silicon oil, esterase, dibromodimethyl hydantoin, oxymatrine,
The chlorine of alkynes third, calcium hypochlorite, magnesite powder, CoCL2 6H2O, aluminic acid cobalt dust, maifanite powder, wood powder, nano-carbon powder, nylon
Fiber, expanded vermiculite powder are mixed, ultrasound at a high speed disperse, ultrasonic frequency be 20~40KHz, rate of dispersion 5000~
5400r/min or so, jitter time is 30~60min；
（2）HBB, sodium stannate, ammonium polyphosphate, IPPP, the benzimidazole of the mass fraction are added,
Ultrasonic to disperse at a high speed, ultrasonic frequency is 20~35KHz, 4800~5200r/min of rate of dispersion or so, jitter time is 30~
50min；
（3）Add double methyl methacrylate triethylene glycol ester, cellulose acetate, the hydroxyethyl methyl propylene of the mass fraction
Acid esters phosphate, vinyl acetate, paranitroanilinum, ultrasound are disperseed at a high speed, and ultrasonic frequency is 20~30KHz, rate of dispersion
4600~4800r/min or so, jitter time is 20~40min；This product is obtained after well mixed.
The beneficial effect of the invention is：Municipal road and bridge first-aid repair construction asphalt modification inorganic agent in the present invention, by following
Component is constituted：Bisphenol A type epoxy resin, PVC resin powder, MBS resins, propylene glycol methyl ether acetate, isobutyrone, mountain are grey
Seed oil, dimethyl hydroxyl silicon oil, esterase, dibromodimethyl hydantoin, oxymatrine, the chlorine of alkynes third, calcium hypochlorite,
Magnesite powder, CoCL2 6H2O, aluminic acid cobalt dust, maifanite powder, wood powder, nano-carbon powder, nylon fiber, expanded vermiculite powder
End, HBB, sodium stannate, ammonium polyphosphate, IPPP, benzimidazole, three second two of contracting of methacrylate two
Alcohol ester, cellulose acetate, hydroxyethyl meth acrylate phosphate, vinyl acetate, paranitroanilinum.Product of the present invention has
More superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improve properties of product.
Specific embodiment
Specific embodiment of the invention is described with reference to embodiment, to be better understood from the present invention.
Embodiment 1
Municipal road and bridge first-aid repair construction asphalt modification inorganic agent in the present embodiment, is made up of the component of following mass fraction：Bisphenol-A
26 parts of type epoxy resin, 24 parts of PVC resin powder, 24 parts of MBS resins, 22 parts of propylene glycol methyl ether acetate, isobutyrone 24
Part, 24 parts of litsea citrate oil, 22 parts of dimethyl hydroxyl silicon oil, 24 parts of esterase, 24 parts of dibromodimethyl hydantoin, oxidation
22 parts of matrine, 22 parts of the third chlorine of alkynes, 22 parts of calcium hypochlorite, 24 parts of magnesite powder, 22 parts of CoCL2 6H2O, aluminic acid cobalt dust 20
Part, 24 parts of maifanite powder, 22 parts of wood powder, 20 parts of nano-carbon powder, 22 parts of nylon fiber, 20 parts of expanded vermiculite powder, HBB
20 parts, 22 parts of sodium stannate, 22 parts of ammonium polyphosphate, 22 parts of IPPP, 22 parts of benzimidazole, methacrylate
22 parts of Triethylene Glycol, 22 parts of cellulose acetate, 22 parts of hydroxyethyl meth acrylate phosphate, vinyl acetate 22
Part, 20 parts of paranitroanilinum.
Above-mentioned municipal road and bridge first-aid repair construction asphalt modification inorganic agent preparation method step is as follows：
（1）By the bisphenol A type epoxy resin of the mass fraction, PVC resin powder, MBS resins, propylene glycol methyl ether acetate, two
Isobutyl ketone, litsea citrate oil, dimethyl hydroxyl silicon oil, esterase, dibromodimethyl hydantoin, oxymatrine,
The chlorine of alkynes third, calcium hypochlorite, magnesite powder, CoCL2 6H2O, aluminic acid cobalt dust, maifanite powder, wood powder, nano-carbon powder, nylon
Fiber, expanded vermiculite powder are mixed, and ultrasound is disperseed at a high speed, and ultrasonic frequency is 20kHz, and rate of dispersion 5400r/min is left
The right side, jitter time is 60min；
（2）HBB, sodium stannate, ammonium polyphosphate, IPPP, the benzimidazole of the mass fraction are added,
Ultrasonic to disperse at a high speed, ultrasonic frequency is 20kHz, rate of dispersion 5200r/min or so, and jitter time is 50min；
（3）Add double methyl methacrylate triethylene glycol ester, cellulose acetate, the hydroxyethyl methyl propylene of the mass fraction
Acid esters phosphate, vinyl acetate, paranitroanilinum, ultrasound are disperseed at a high speed, and ultrasonic frequency is 20kHz, rate of dispersion
4800r/min or so, jitter time is 40min；This product is obtained after well mixed.
Embodiment 2
Municipal road and bridge first-aid repair construction asphalt modification inorganic agent in the present embodiment, is made up of the component of following mass fraction：Bisphenol-A
28 parts of type epoxy resin, 26 parts of PVC resin powder, 26 parts of MBS resins, 24 parts of propylene glycol methyl ether acetate, isobutyrone 26
Part, 26 parts of litsea citrate oil, 24 parts of dimethyl hydroxyl silicon oil, 26 parts of esterase, 26 parts of dibromodimethyl hydantoin, oxidation
24 parts of matrine, 24 parts of the third chlorine of alkynes, 24 parts of calcium hypochlorite, 26 parts of magnesite powder, 24 parts of CoCL2 6H2O, aluminic acid cobalt dust 22
Part, 26 parts of maifanite powder, 24 parts of wood powder, 22 parts of nano-carbon powder, 24 parts of nylon fiber, 22 parts of expanded vermiculite powder, HBB
22 parts, 24 parts of sodium stannate, 24 parts of ammonium polyphosphate, 24 parts of IPPP, 24 parts of benzimidazole, methacrylate
24 parts of Triethylene Glycol, 24 parts of cellulose acetate, 24 parts of hydroxyethyl meth acrylate phosphate, vinyl acetate 24
Part, 22 parts of paranitroanilinum.
Above-mentioned municipal road and bridge first-aid repair construction asphalt modification inorganic agent preparation method step is as follows：
（1）By the bisphenol A type epoxy resin of the mass fraction, PVC resin powder, MBS resins, propylene glycol methyl ether acetate, two
Isobutyl ketone, litsea citrate oil, dimethyl hydroxyl silicon oil, esterase, dibromodimethyl hydantoin, oxymatrine,
The chlorine of alkynes third, calcium hypochlorite, magnesite powder, CoCL2 6H2O, aluminic acid cobalt dust, maifanite powder, wood powder, nano-carbon powder, nylon
Fiber, expanded vermiculite powder are mixed, and ultrasound is disperseed at a high speed, and ultrasonic frequency is 30kHz, and rate of dispersion 5200r/min is left
The right side, jitter time is 45min；
（2）HBB, sodium stannate, ammonium polyphosphate, IPPP, the benzimidazole of the mass fraction are added,
Ultrasonic to disperse at a high speed, ultrasonic frequency is 27kHz, rate of dispersion 5000r/min or so, and jitter time is 40min；
（3）Add double methyl methacrylate triethylene glycol ester, cellulose acetate, the hydroxyethyl methyl propylene of the mass fraction
Acid esters phosphate, vinyl acetate, paranitroanilinum, ultrasound are disperseed at a high speed, and ultrasonic frequency is 25kHz, rate of dispersion
4700r/min or so, jitter time is 30min；This product is obtained after well mixed.
Embodiment 3
Municipal road and bridge first-aid repair construction asphalt modification inorganic agent in the present embodiment, is made up of the component of following mass fraction：Bisphenol-A
30 parts of type epoxy resin, 28 parts of PVC resin powder, 28 parts of MBS resins, 26 parts of propylene glycol methyl ether acetate, isobutyrone 28
Part, 28 parts of litsea citrate oil, 26 parts of dimethyl hydroxyl silicon oil, 28 parts of esterase, 28 parts of dibromodimethyl hydantoin, oxidation
26 parts of matrine, 26 parts of the third chlorine of alkynes, 26 parts of calcium hypochlorite, 28 parts of magnesite powder, 26 parts of CoCL2 6H2O, aluminic acid cobalt dust 24
Part, 28 parts of maifanite powder, 26 parts of wood powder, 24 parts of nano-carbon powder, 26 parts of nylon fiber, 24 parts of expanded vermiculite powder, HBB
24 parts, 26 parts of sodium stannate, 26 parts of ammonium polyphosphate, 26 parts of IPPP, 26 parts of benzimidazole, methacrylate
26 parts of Triethylene Glycol, 26 parts of cellulose acetate, 26 parts of hydroxyethyl meth acrylate phosphate, vinyl acetate 26
Part, 24 parts of paranitroanilinum.
Above-mentioned municipal road and bridge first-aid repair construction asphalt modification inorganic agent preparation method step is as follows：
（1）By the bisphenol A type epoxy resin of the mass fraction, PVC resin powder, MBS resins, propylene glycol methyl ether acetate, two
Isobutyl ketone, litsea citrate oil, dimethyl hydroxyl silicon oil, esterase, dibromodimethyl hydantoin, oxymatrine,
The chlorine of alkynes third, calcium hypochlorite, magnesite powder, CoCL2 6H2O, aluminic acid cobalt dust, maifanite powder, wood powder, nano-carbon powder, nylon
Fiber, expanded vermiculite powder are mixed, and ultrasound is disperseed at a high speed, and ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, is divided
The time of dissipating is 30min；
（2）HBB, sodium stannate, ammonium polyphosphate, IPPP, the benzimidazole of the mass fraction are added,
Ultrasonic to disperse at a high speed, ultrasonic frequency is 35kHz, and rate of dispersion 4800r/min, jitter time is 30min；
（3）Add double methyl methacrylate triethylene glycol ester, cellulose acetate, the hydroxyethyl methyl propylene of the mass fraction
Acid esters phosphate, vinyl acetate, paranitroanilinum, ultrasound are disperseed at a high speed, and ultrasonic frequency is 30kHz, rate of dispersion
4600r/min or so, jitter time is 20min；This product is obtained after well mixed.
Performance measurement is carried out for the product in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available prod, it is measured
Data are as shown in table 1.Fire protection flame retarding level estimate uses UL94 standards.
The performance test results of table 1
It can be seen that, product of the present invention has preferable corrosion-resistant, fire protection flame retarding, anti-mildew, anti-microbial property.
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art
For, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications are also considered as
Protection scope of the present invention.
Claims (5)
1. a kind of municipal road and bridge first-aid repair construction asphalt modification inorganic agent, it is characterised in that：It is made up of the component of following mass fraction：
26~30 parts of bisphenol A type epoxy resin, 24~28 parts of PVC resin powder, 24~28 parts of MBS resins, propylene glycol methyl ether acetate 22
~26 parts, 24~28 parts of isobutyrone, 24~28 parts of litsea citrate oil, 22~26 parts of dimethyl hydroxyl silicon oil, rosin glycerin ester
24~28 parts of ester, 24~28 parts of dibromodimethyl hydantoin, 22~26 parts of oxymatrine, 22~26 parts of the third chlorine of alkynes, secondary chlorine
22~26 parts of sour calcium, 24~28 parts of magnesite powder, 22~26 parts of CoCL2 6H2O, 20~24 parts of aluminic acid cobalt dust, medical stone powder
24~28 parts of end, 22~26 parts of wood powder, 20~24 parts of nano-carbon powder, 22~26 parts of nylon fiber, expanded vermiculite powder 20~24
Part, 20~24 parts of HBB, 22~26 parts of sodium stannate, 22~26 parts of ammonium polyphosphate, 22~26 parts of IPPP,
22~26 parts of benzimidazole, 22~26 parts of double methyl methacrylate triethylene glycol ester, 22~26 parts of cellulose acetate, ethoxy
22~26 parts of methacrylate phosphate, 22~26 parts of vinyl acetate, 20~24 parts of paranitroanilinum.
2. municipal road and bridge first-aid repair construction asphalt modification inorganic agent according to claim 1, it is characterised in that：The municipal road
Bridge first-aid repair construction asphalt modification inorganic agent is made up of the component of following mass fraction：26 parts of bisphenol A type epoxy resin, polyvinyl chloride resin
24 parts of powder, 24 parts of MBS resins, 22 parts of propylene glycol methyl ether acetate, 24 parts of isobutyrone, 24 parts of litsea citrate oil, dimethyl
22 parts of hydroxy silicon oil, 24 parts of esterase, 24 parts of dibromodimethyl hydantoin, 22 parts of oxymatrine, 22 parts of the third chlorine of alkynes,
22 parts of calcium hypochlorite, 24 parts of magnesite powder, 22 parts of CoCL2 6H2O, 20 parts of aluminic acid cobalt dust, 24 parts of maifanite powder, wood powder 22
Part, 20 parts of nano-carbon powder, 22 parts of nylon fiber, 20 parts of expanded vermiculite powder, 20 parts of HBB, 22 parts of sodium stannate, polyphosphoric acids
22 parts of ammonium, 22 parts of IPPP, 22 parts of benzimidazole, 22 parts of double methyl methacrylate triethylene glycol ester, acetic acid
22 parts of cellulose, 22 parts of hydroxyethyl meth acrylate phosphate, 22 parts of vinyl acetate, 20 parts of paranitroanilinum.
3. the municipal road and bridge first-aid repair construction asphalt modification inorganic agent according to claim 1 to 2, it is characterised in that：The city
Political affairs road and bridge first-aid repair construction asphalt modification inorganic agent is made up of the component of following mass fraction：28 parts of bisphenol A type epoxy resin, PVC
26 parts of resin-oatmeal, 26 parts of MBS resins, 24 parts of propylene glycol methyl ether acetate, 26 parts of isobutyrone, 26 parts of litsea citrate oil, two
24 parts of methylhydroxy silicone oil, 26 parts of esterase, 26 parts of dibromodimethyl hydantoin, 24 parts of oxymatrine, the chlorine of alkynes third
24 parts, 24 parts of calcium hypochlorite, 26 parts of magnesite powder, 24 parts of CoCL2 6H2O, 22 parts of aluminic acid cobalt dust, 26 parts of maifanite powder,
It is 24 parts of wood powder, 22 parts of nano-carbon powder, 24 parts of nylon fiber, 22 parts of expanded vermiculite powder, 22 parts of HBB, 24 parts of sodium stannate, many
24 parts of APP, 24 parts of IPPP, 24 parts of benzimidazole, double methyl methacrylate triethylene glycol ester 24
Part, 24 parts of cellulose acetate, 24 parts of hydroxyethyl meth acrylate phosphate, 24 parts of vinyl acetate, 22 parts of paranitroanilinum.
4. the municipal road and bridge first-aid repair construction asphalt modification inorganic agent according to claims 1 to 3, it is characterised in that：The city
Political affairs road and bridge first-aid repair construction asphalt modification inorganic agent is made up of the component of following mass fraction：30 parts of bisphenol A type epoxy resin, PVC
28 parts of resin-oatmeal, 28 parts of MBS resins, 26 parts of propylene glycol methyl ether acetate, 28 parts of isobutyrone, 28 parts of litsea citrate oil, two
26 parts of methylhydroxy silicone oil, 28 parts of esterase, 28 parts of dibromodimethyl hydantoin, 26 parts of oxymatrine, the chlorine of alkynes third
26 parts, 26 parts of calcium hypochlorite, 28 parts of magnesite powder, 26 parts of CoCL2 6H2O, 24 parts of aluminic acid cobalt dust, 28 parts of maifanite powder,
It is 26 parts of wood powder, 24 parts of nano-carbon powder, 26 parts of nylon fiber, 24 parts of expanded vermiculite powder, 24 parts of HBB, 26 parts of sodium stannate, many
26 parts of APP, 26 parts of IPPP, 26 parts of benzimidazole, double methyl methacrylate triethylene glycol ester 26
Part, 26 parts of cellulose acetate, 26 parts of hydroxyethyl meth acrylate phosphate, 26 parts of vinyl acetate, 24 parts of paranitroanilinum.
5. municipal road and bridge first-aid repair construction asphalt modification inorganic agent according to claim 1, it is characterised in that：The municipal road
Bridge first-aid repair construction asphalt modification inorganic agent preparation method step is as follows：
（1）By the bisphenol A type epoxy resin of the mass fraction, PVC resin powder, MBS resins, propylene glycol methyl ether acetate, two
Isobutyl ketone, litsea citrate oil, dimethyl hydroxyl silicon oil, esterase, dibromodimethyl hydantoin, oxymatrine,
The chlorine of alkynes third, calcium hypochlorite, magnesite powder, CoCL2 6H2O, aluminic acid cobalt dust, maifanite powder, wood powder, nano-carbon powder, nylon
Fiber, expanded vermiculite powder are mixed, ultrasound at a high speed disperse, ultrasonic frequency be 20~40KHz, rate of dispersion about 5000~
5400r/min, jitter time is 30~60min or so；
（2）HBB, sodium stannate, ammonium polyphosphate, IPPP, the benzimidazole of the mass fraction are added,
Ultrasonic to disperse at a high speed, ultrasonic frequency is 20~35KHz, and rate of dispersion is for about 4800~5200r/min, jitter time is 30~
50min or so；
（3）Add double methyl methacrylate triethylene glycol ester, cellulose acetate, the hydroxyethyl methyl propylene of the mass fraction
Acid esters phosphate, vinyl acetate, paranitroanilinum, ultrasound are disperseed at a high speed, and ultrasonic frequency is 20~30KHz, rate of dispersion
For about 4600~4800r/min, jitter time is 20~40min or so；This product is obtained after well mixed.