CN106751361A - A kind of municipal road and bridge safeguard asphalt modification inorganic agent - Google Patents
A kind of municipal road and bridge safeguard asphalt modification inorganic agent Download PDFInfo
- Publication number
- CN106751361A CN106751361A CN201611098862.8A CN201611098862A CN106751361A CN 106751361 A CN106751361 A CN 106751361A CN 201611098862 A CN201611098862 A CN 201611098862A CN 106751361 A CN106751361 A CN 106751361A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- oil
- inorganic agent
- municipal road
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Asphalt modification inorganic agent is safeguarded the present invention relates to a kind of municipal road and bridge, it is composed of the following components：SEBS thermoplastic elastomer (TPE)s, polyester urethane resin, Petropols, lemon oil, tung oil, linseed oil, sesame oil, trimethylborate, oxymatrine, the chlorine of alkynes third, calcium hypochlorite, poly (hexamethylene) hydrochloride, sodium silicoaluminate powder, diatom powder, seawood meal, andalusite powder, sierozem power, potassium feldspar powder, elbaite powder, barium sulfate powder, aluminum stearate, nano zine oxide, nano-sized magnesium hydroxide, trichloroethyl phosphate, aminoethyl piperazine, stearic amide, Carbomer, isophorone, polyoxyethylene oleic acid ester, TR sealant.Product of the present invention has more superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improves properties of product.
Description
Technical field
Asphalt modification inorganic agent is safeguarded the present invention relates to a kind of municipal road and bridge, belongs to municipal road and bridge maintenance technology field.
Background technology
The dark brown complex mixture that pitch is made up of the hydrocarbon and its non metallic derivatives of different molecular weight,
It is one kind of high viscosity organic liquid, is in a liquid state, surface is in black, dissolves in carbon disulfide.Pitch be it is a kind of waterproof and dampproof and
Corrosion-resistant organic cementing material.Pitch can be largely classified into three kinds of coal tar pitch, asphalt and bitumen：Wherein, coal tar
Pitch is the byproduct of coking.Asphalt is the residue after crude distillation.Bitumen is then to be stored at underground, some formation
Ore bed or in earth's crust surface sediment.Pitch is mainly used in the industry such as coating, plastics, rubber and surfacing etc..
The content of the invention
Asphalt modification inorganic agent is safeguarded it is an object of the invention to provide a kind of municipal road and bridge, so that municipal administration is better achieved
Road and bridge safeguard the use function of asphalt modification inorganic agent, product is had fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improve and produce
Product performance.
To achieve these goals, technical scheme is as follows.
A kind of municipal road and bridge safeguard asphalt modification inorganic agent, are made up of the component of following mass fraction：SEBS thermoplastic elastomehcs
24~28 parts of gonosome, 22~26 parts of polyester urethane resin, 22~26 parts of Petropols, 20~24 parts of lemon oil, tung oil
22~26 parts, 22~26 parts of linseed oil, 20~24 parts of sesame oil, 22~26 parts of trimethylborate, 22~26 parts of oxymatrine,
20~24 parts of the third chlorine of alkynes, 20~24 parts of calcium hypochlorite, 20~24 parts of poly (hexamethylene) hydrochloride, sodium silicoaluminate powder 22~26
Part, 20~24 parts of diatom powder, 18~22 parts of seawood meal, 22~26 parts of andalusite powder, 20~24 parts of sierozem power, potassium feldspar powder
18~22 parts, 20~24 parts of elbaite powder, 18~22 parts of barium sulfate powder, 18~22 parts of aluminum stearate, nano zine oxide 18
~22 parts, 16~20 parts of nano-sized magnesium hydroxide, 12~16 parts of trichloroethyl phosphate, 10~14 parts of aminoethyl piperazine, stearic acid
10~14 parts of acid amides, 10~14 parts of Carbomer, 10~14 parts of isophorone, 10~14 parts of polyoxyethylene oleic acid ester, TR sealant 10
~14 parts.
Further, above-mentioned municipal road and bridge safeguard asphalt modification inorganic agent, be made up of the component of following mass fraction：SEBS
24 parts of thermoplastic elastomer (TPE), 22 parts of polyester urethane resin, 22 parts of Petropols, 20 parts of lemon oil, 22 parts of tung oil, flax
22 parts of oil, 20 parts of sesame oil, 22 parts of trimethylborate, 22 parts of oxymatrine, 20 parts of the third chlorine of alkynes, 20 parts of calcium hypochlorite, poly- six
20 parts of methylene guanidine hydrochloride, 22 parts of sodium silicoaluminate powder, 20 parts of diatom powder, 18 parts of seawood meal, 22 parts of andalusite powder, grey calcium
20 parts of powder, 18 parts of potassium feldspar powder, 20 parts of elbaite powder, 18 parts of barium sulfate powder, 18 parts of aluminum stearate, nano zine oxide 18
Part, 16 parts of nano-sized magnesium hydroxide, 12 parts of trichloroethyl phosphate, 10 parts of aminoethyl piperazine, 10 parts of stearic amide, Carbomer 10
Part, 10 parts of isophorone, 10 parts of polyoxyethylene oleic acid ester, 10 parts of TR sealant.
Further, above-mentioned municipal road and bridge safeguard asphalt modification inorganic agent, be made up of the component of following mass fraction：SEBS
26 parts of thermoplastic elastomer (TPE), 24 parts of polyester urethane resin, 24 parts of Petropols, 22 parts of lemon oil, 24 parts of tung oil, flax
24 parts of oil, 22 parts of sesame oil, 24 parts of trimethylborate, 24 parts of oxymatrine, 22 parts of the third chlorine of alkynes, 22 parts of calcium hypochlorite, poly- six
22 parts of methylene guanidine hydrochloride, 24 parts of sodium silicoaluminate powder, 22 parts of diatom powder, 20 parts of seawood meal, 24 parts of andalusite powder, grey calcium
22 parts of powder, 20 parts of potassium feldspar powder, 22 parts of elbaite powder, 20 parts of barium sulfate powder, 20 parts of aluminum stearate, nano zine oxide 20
Part, 18 parts of nano-sized magnesium hydroxide, 14 parts of trichloroethyl phosphate, 12 parts of aminoethyl piperazine, 12 parts of stearic amide, Carbomer 12
Part, 12 parts of isophorone, 12 parts of polyoxyethylene oleic acid ester, 12 parts of TR sealant.
Further, above-mentioned municipal road and bridge safeguard asphalt modification inorganic agent, be made up of the component of following mass fraction：SEBS
28 parts of thermoplastic elastomer (TPE), 26 parts of polyester urethane resin, 26 parts of Petropols, 24 parts of lemon oil, 26 parts of tung oil, flax
26 parts of oil, 24 parts of sesame oil, 26 parts of trimethylborate, 26 parts of oxymatrine, 24 parts of the third chlorine of alkynes, 24 parts of calcium hypochlorite, poly- six
24 parts of methylene guanidine hydrochloride, 26 parts of sodium silicoaluminate powder, 24 parts of diatom powder, 22 parts of seawood meal, 26 parts of andalusite powder, grey calcium
24 parts of powder, 22 parts of potassium feldspar powder, 24 parts of elbaite powder, 22 parts of barium sulfate powder, 22 parts of aluminum stearate, nano zine oxide 22
Part, 20 parts of nano-sized magnesium hydroxide, 16 parts of trichloroethyl phosphate, 14 parts of aminoethyl piperazine, 14 parts of stearic amide, Carbomer 14
Part, 14 parts of isophorone, 14 parts of polyoxyethylene oleic acid ester, 14 parts of TR sealant.
Further, above-mentioned municipal road and bridge safeguard that asphalt modification inorganic agent preparation method step is as follows：
（1）By the SEBS thermoplastic elastomer (TPE)s of the mass fraction, polyester urethane resin, Petropols, lemon oil, paulownia
Oil, linseed oil, sesame oil, trimethylborate, oxymatrine, the chlorine of alkynes third, calcium hypochlorite, poly (hexamethylene) hydrochloride, silicon
Sodium aluminate powder, diatom powder, seawood meal, andalusite powder, sierozem power, potassium feldspar powder, elbaite powder, barium sulfate powder give
To mix, ultrasound is disperseed at a high speed, and ultrasonic frequency is 20~40KHz, 5000~5400r/min of rate of dispersion or so, during dispersion
Between be 30~60min；
（2）Add aluminum stearate, nano zine oxide, nano-sized magnesium hydroxide, trichloroethyl phosphate, the ammonia second of the mass fraction
Base piperazine, ultrasound is disperseed at a high speed, and ultrasonic frequency is 20~35KHz, 4800~5200r/min of rate of dispersion or so, during dispersion
Between be 30~50min；
（3）Stearic amide, Carbomer, isophorone, polyoxyethylene oleic acid ester, the TR sealant of the mass fraction are added, is surpassed
Sound pitch speed dispersion, ultrasonic frequency is 20~30KHz, 4600~4800r/min of rate of dispersion or so, jitter time is 20~
40min；This product is obtained after well mixed.
The beneficial effect of the invention is：Municipal road and bridge in the present invention safeguard asphalt modification inorganic agent, by following components
Composition：SEBS thermoplastic elastomer (TPE)s, polyester urethane resin, Petropols, lemon oil, tung oil, linseed oil, sesame oil,
Trimethylborate, oxymatrine, the chlorine of alkynes third, calcium hypochlorite, poly (hexamethylene) hydrochloride, sodium silicoaluminate powder, diatom powder,
It is seawood meal, andalusite powder, sierozem power, potassium feldspar powder, elbaite powder, barium sulfate powder, aluminum stearate, nano oxidized
Zinc, nano-sized magnesium hydroxide, trichloroethyl phosphate, aminoethyl piperazine, stearic amide, Carbomer, isophorone, oleic acid polyoxy
Vinyl acetate, TR sealant.Product of the present invention has more superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improves product
Energy.
Specific embodiment
Specific embodiment of the invention is described with reference to embodiment, to be better understood from the present invention.
Embodiment 1
Municipal road and bridge in the present embodiment safeguard asphalt modification inorganic agent, are made up of the component of following mass fraction：SEBS thermoplastics
24 parts of elastomer of property, 22 parts of polyester urethane resin, 22 parts of Petropols, 20 parts of lemon oil, 22 parts of tung oil, linseed oil 22
Part, 20 parts of sesame oil, 22 parts of trimethylborate, 22 parts of oxymatrine, 20 parts of the third chlorine of alkynes, 20 parts of calcium hypochlorite, poly- six methylene
20 parts of base guanidine hydrochloride, 22 parts of sodium silicoaluminate powder, 20 parts of diatom powder, 18 parts of seawood meal, 22 parts of andalusite powder, sierozem power 20
Part, 18 parts of potassium feldspar powder, 20 parts of elbaite powder, 18 parts of barium sulfate powder, 18 parts of aluminum stearate, 18 parts of nano zine oxide,
16 parts of nano-sized magnesium hydroxide, 12 parts of trichloroethyl phosphate, 10 parts of aminoethyl piperazine, 10 parts of stearic amide, 10 parts of Carbomer,
10 parts of isophorone, 10 parts of polyoxyethylene oleic acid ester, 10 parts of TR sealant.
Above-mentioned municipal road and bridge safeguard that asphalt modification inorganic agent preparation method step is as follows：
（1）By the SEBS thermoplastic elastomer (TPE)s of the mass fraction, polyester urethane resin, Petropols, lemon oil, paulownia
Oil, linseed oil, sesame oil, trimethylborate, oxymatrine, the chlorine of alkynes third, calcium hypochlorite, poly (hexamethylene) hydrochloride, silicon
Sodium aluminate powder, diatom powder, seawood meal, andalusite powder, sierozem power, potassium feldspar powder, elbaite powder, barium sulfate powder give
To mix, ultrasound is disperseed at a high speed, and ultrasonic frequency is 20kHz, rate of dispersion 5400r/min or so, and jitter time is 60min；
（2）Add aluminum stearate, nano zine oxide, nano-sized magnesium hydroxide, trichloroethyl phosphate, the ammonia second of the mass fraction
Base piperazine, ultrasound is disperseed at a high speed, and ultrasonic frequency is 20kHz, rate of dispersion 5200r/min or so, and jitter time is 50min；
（3）Stearic amide, Carbomer, isophorone, polyoxyethylene oleic acid ester, the TR sealant of the mass fraction are added, is surpassed
Sound pitch speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion 4800r/min or so, and jitter time is 40min；After well mixed
This product is obtained.
Embodiment 2
Municipal road and bridge in the present embodiment safeguard asphalt modification inorganic agent, are made up of the component of following mass fraction：SEBS thermoplastics
26 parts of elastomer of property, 24 parts of polyester urethane resin, 24 parts of Petropols, 22 parts of lemon oil, 24 parts of tung oil, linseed oil 24
Part, 22 parts of sesame oil, 24 parts of trimethylborate, 24 parts of oxymatrine, 22 parts of the third chlorine of alkynes, 22 parts of calcium hypochlorite, poly- six methylene
22 parts of base guanidine hydrochloride, 24 parts of sodium silicoaluminate powder, 22 parts of diatom powder, 20 parts of seawood meal, 24 parts of andalusite powder, sierozem power 22
Part, 20 parts of potassium feldspar powder, 22 parts of elbaite powder, 20 parts of barium sulfate powder, 20 parts of aluminum stearate, 20 parts of nano zine oxide,
18 parts of nano-sized magnesium hydroxide, 14 parts of trichloroethyl phosphate, 12 parts of aminoethyl piperazine, 12 parts of stearic amide, 12 parts of Carbomer,
12 parts of isophorone, 12 parts of polyoxyethylene oleic acid ester, 12 parts of TR sealant.
Above-mentioned municipal road and bridge safeguard that asphalt modification inorganic agent preparation method step is as follows：
（1）By the SEBS thermoplastic elastomer (TPE)s of the mass fraction, polyester urethane resin, Petropols, lemon oil, paulownia
Oil, linseed oil, sesame oil, trimethylborate, oxymatrine, the chlorine of alkynes third, calcium hypochlorite, poly (hexamethylene) hydrochloride, silicon
Sodium aluminate powder, diatom powder, seawood meal, andalusite powder, sierozem power, potassium feldspar powder, elbaite powder, barium sulfate powder give
To mix, ultrasound is disperseed at a high speed, and ultrasonic frequency is 30kHz, rate of dispersion 5200r/min or so, and jitter time is 45min；
（2）Add aluminum stearate, nano zine oxide, nano-sized magnesium hydroxide, trichloroethyl phosphate, the ammonia second of the mass fraction
Base piperazine, ultrasound is disperseed at a high speed, and ultrasonic frequency is 27kHz, rate of dispersion 5000r/min or so, and jitter time is 40min；
（3）Stearic amide, Carbomer, isophorone, polyoxyethylene oleic acid ester, the TR sealant of the mass fraction are added, is surpassed
Sound pitch speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion 4700r/min or so, and jitter time is 30min；After well mixed
This product is obtained.
Embodiment 3
Municipal road and bridge in the present embodiment safeguard asphalt modification inorganic agent, are made up of the component of following mass fraction：SEBS thermoplastics
28 parts of elastomer of property, 26 parts of polyester urethane resin, 26 parts of Petropols, 24 parts of lemon oil, 26 parts of tung oil, linseed oil 26
Part, 24 parts of sesame oil, 26 parts of trimethylborate, 26 parts of oxymatrine, 24 parts of the third chlorine of alkynes, 24 parts of calcium hypochlorite, poly- six methylene
24 parts of base guanidine hydrochloride, 26 parts of sodium silicoaluminate powder, 24 parts of diatom powder, 22 parts of seawood meal, 26 parts of andalusite powder, sierozem power 24
Part, 22 parts of potassium feldspar powder, 24 parts of elbaite powder, 22 parts of barium sulfate powder, 22 parts of aluminum stearate, 22 parts of nano zine oxide,
20 parts of nano-sized magnesium hydroxide, 16 parts of trichloroethyl phosphate, 14 parts of aminoethyl piperazine, 14 parts of stearic amide, 14 parts of Carbomer,
14 parts of isophorone, 14 parts of polyoxyethylene oleic acid ester, 14 parts of TR sealant.
Above-mentioned municipal road and bridge safeguard that asphalt modification inorganic agent preparation method step is as follows：
（1）By the SEBS thermoplastic elastomer (TPE)s of the mass fraction, polyester urethane resin, Petropols, lemon oil, paulownia
Oil, linseed oil, sesame oil, trimethylborate, oxymatrine, the chlorine of alkynes third, calcium hypochlorite, poly (hexamethylene) hydrochloride, silicon
Sodium aluminate powder, diatom powder, seawood meal, andalusite powder, sierozem power, potassium feldspar powder, elbaite powder, barium sulfate powder give
To mix, ultrasound is disperseed at a high speed, and ultrasonic frequency is 40kHz, and rate of dispersion 5000r/min, jitter time is 30min；
（2）Add aluminum stearate, nano zine oxide, nano-sized magnesium hydroxide, trichloroethyl phosphate, the ammonia second of the mass fraction
Base piperazine, ultrasound is disperseed at a high speed, and ultrasonic frequency is 35kHz, and rate of dispersion 4800r/min, jitter time is 30min；
（3）Stearic amide, Carbomer, isophorone, polyoxyethylene oleic acid ester, the TR sealant of the mass fraction are added, is surpassed
Sound pitch speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion 4600r/min or so, and jitter time is 20min；After well mixed
This product is obtained.
Performance measurement is carried out for the product in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available prod, it is measured
Data are as shown in table 1.Fire protection flame retarding level estimate uses UL94 standards.
The performance test results of table 1
It can be seen that, product of the present invention has preferable corrosion-resistant, fire protection flame retarding, anti-mildew, anti-microbial property.
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art
For, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications are also considered as
Protection scope of the present invention.
Claims (5)
1. a kind of municipal road and bridge safeguard asphalt modification inorganic agent, it is characterised in that：It is made up of the component of following mass fraction：SEBS
24~28 parts of thermoplastic elastomer (TPE), 22~26 parts of polyester urethane resin, 22~26 parts of Petropols, lemon oil 20~24
Part, 22~26 parts of tung oil, 22~26 parts of linseed oil, 20~24 parts of sesame oil, 22~26 parts of trimethylborate, oxymatrine 22
~26 parts, 20~24 parts of the third chlorine of alkynes, 20~24 parts of calcium hypochlorite, 20~24 parts of poly (hexamethylene) hydrochloride, aluminosilicate sodium powder
22~26 parts of end, 20~24 parts of diatom powder, 18~22 parts of seawood meal, 22~26 parts of andalusite powder, 20~24 parts of sierozem power, potassium
18~22 parts of feldspar powder, 20~24 parts of elbaite powder, 18~22 parts of barium sulfate powder, aluminum stearate 18~22 part, nanometer
18~22 parts of zinc oxide, 16~20 parts of nano-sized magnesium hydroxide, 12~16 parts of trichloroethyl phosphate, aminoethyl piperazine 10~14
Part, 10~14 parts of stearic amide, 10~14 parts of Carbomer, 10~14 parts of isophorone, 10~14 parts of polyoxyethylene oleic acid ester,
10~14 parts of TR sealant.
2. municipal road and bridge according to claim 1 safeguard asphalt modification inorganic agent, it is characterised in that：The municipal road and bridge dimension
Shield asphalt modification inorganic agent is made up of the component of following mass fraction：24 parts of SEBS thermoplastic elastomer (TPE)s, polyester urethane
22 parts of resin, 22 parts of Petropols, 20 parts of lemon oil, 22 parts of tung oil, 22 parts of linseed oil, 20 parts of sesame oil, trimethylborate 22
Part, 22 parts of oxymatrine, 20 parts of the third chlorine of alkynes, 20 parts of calcium hypochlorite, 20 parts of poly (hexamethylene) hydrochloride, sodium silicoaluminate powder
22 parts, 20 parts of diatom powder, 18 parts of seawood meal, 22 parts of andalusite powder, 20 parts of sierozem power, 18 parts of potassium feldspar powder, elbaite
20 parts of powder, 18 parts of barium sulfate powder, 18 parts of aluminum stearate, 18 parts of nano zine oxide, 16 parts of nano-sized magnesium hydroxide, trichloroethyl phosphorus
12 parts of acid esters, 10 parts of aminoethyl piperazine, 10 parts of stearic amide, 10 parts of Carbomer, 10 parts of isophorone, polyoxyethylene oleic acid ester
10 parts, 10 parts of TR sealant.
3. the municipal road and bridge according to claim 1 to 2 safeguard asphalt modification inorganic agent, it is characterised in that：The municipal road
Bridge safeguards that asphalt modification inorganic agent is made up of the component of following mass fraction：26 parts of SEBS thermoplastic elastomer (TPE)s, Amino-Polyester first
24 parts of acid ester resin, 24 parts of Petropols, 22 parts of lemon oil, 24 parts of tung oil, 24 parts of linseed oil, 22 parts of sesame oil, boric acid front three
24 parts of ester, 24 parts of oxymatrine, 22 parts of the third chlorine of alkynes, 22 parts of calcium hypochlorite, 22 parts of poly (hexamethylene) hydrochloride, sodium silicoaluminate
24 parts of powder, 22 parts of diatom powder, 20 parts of seawood meal, 24 parts of andalusite powder, 22 parts of sierozem power, 20 parts of potassium feldspar powder, lithium electricity
22 parts of gas stone flour, 20 parts of barium sulfate powder, 20 parts of aluminum stearate, 20 parts of nano zine oxide, 18 parts of nano-sized magnesium hydroxide, three chloroethenes
14 parts of base phosphate, 12 parts of aminoethyl piperazine, 12 parts of stearic amide, 12 parts of Carbomer, 12 parts of isophorone, oleic acid polyoxy second
12 parts of alkene ester, 12 parts of TR sealant.
4. the municipal road and bridge according to claims 1 to 3 safeguard asphalt modification inorganic agent, it is characterised in that：The municipal road
Bridge safeguards that asphalt modification inorganic agent is made up of the component of following mass fraction：28 parts of SEBS thermoplastic elastomer (TPE)s, Amino-Polyester first
26 parts of acid ester resin, 26 parts of Petropols, 24 parts of lemon oil, 26 parts of tung oil, 26 parts of linseed oil, 24 parts of sesame oil, boric acid front three
26 parts of ester, 26 parts of oxymatrine, 24 parts of the third chlorine of alkynes, 24 parts of calcium hypochlorite, 24 parts of poly (hexamethylene) hydrochloride, sodium silicoaluminate
26 parts of powder, 24 parts of diatom powder, 22 parts of seawood meal, 26 parts of andalusite powder, 24 parts of sierozem power, 22 parts of potassium feldspar powder, lithium electricity
24 parts of gas stone flour, 22 parts of barium sulfate powder, 22 parts of aluminum stearate, 22 parts of nano zine oxide, 20 parts of nano-sized magnesium hydroxide, three chloroethenes
16 parts of base phosphate, 14 parts of aminoethyl piperazine, 14 parts of stearic amide, 14 parts of Carbomer, 14 parts of isophorone, oleic acid polyoxy second
14 parts of alkene ester, 14 parts of TR sealant.
5. municipal road and bridge according to claim 1 safeguard asphalt modification inorganic agent, it is characterised in that：The municipal road and bridge dimension
Shield asphalt modification inorganic agent preparation method step is as follows：
（1）By the SEBS thermoplastic elastomer (TPE)s of the mass fraction, polyester urethane resin, Petropols, lemon oil, paulownia
Oil, linseed oil, sesame oil, trimethylborate, oxymatrine, the chlorine of alkynes third, calcium hypochlorite, poly (hexamethylene) hydrochloride, silicon
Sodium aluminate powder, diatom powder, seawood meal, andalusite powder, sierozem power, potassium feldspar powder, elbaite powder, barium sulfate powder give
To mix, ultrasound is disperseed at a high speed, and ultrasonic frequency is 20~40KHz, rate of dispersion about 5000~5400r/min, jitter time
It is 30~60min or so；
（2）Add aluminum stearate, nano zine oxide, nano-sized magnesium hydroxide, trichloroethyl phosphate, the ammonia second of the mass fraction
Base piperazine, ultrasound is disperseed at a high speed, and ultrasonic frequency is 20~35KHz, and rate of dispersion is for about 4800~5200r/min, during dispersion
Between for 30~50min or so；
（3）Stearic amide, Carbomer, isophorone, polyoxyethylene oleic acid ester, the TR sealant of the mass fraction are added, is surpassed
Sound pitch speed dispersion, ultrasonic frequency is 20~30KHz, and rate of dispersion is for about 4600~4800r/min, jitter time is 20~
40min or so；This product is obtained after well mixed.