CN105906991A - Asphalt modifying treating agent for municipal road and bridge repair construction - Google Patents

Asphalt modifying treating agent for municipal road and bridge repair construction Download PDF

Info

Publication number
CN105906991A
CN105906991A CN201610492698.2A CN201610492698A CN105906991A CN 105906991 A CN105906991 A CN 105906991A CN 201610492698 A CN201610492698 A CN 201610492698A CN 105906991 A CN105906991 A CN 105906991A
Authority
CN
China
Prior art keywords
parts
powder
bridge
repair construction
oxide powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610492698.2A
Other languages
Chinese (zh)
Inventor
龚灿锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610492698.2A priority Critical patent/CN105906991A/en
Publication of CN105906991A publication Critical patent/CN105906991A/en
Pending legal-status Critical Current

Abstract

The invention relates to an asphalt modifying treating agent for municipal road and bridge repair construction. The asphalt modifying treating agent consists of the following components: sorbitan anhydride oleate, trichloromethane, aluminum oxide powder, polybutylene terephthalate, polyvinyl chloride, microcrystalline wax, 2-mercapto benzimidazole, magnesium oxide powder, dicumyl peroxide, basalt fiber, nano carbon powder, diisocyanate, chrome green powder, artificial mica, glycerin monostearate, molybdenum oxide powder, medical stone powder, barium sulfate, polyvinyl butyral, dimethyl amino propane, amino acid, chlorothalonil, ammonium chloride, panax notoginseng saponins, eugenol, polyvinylpyrrolidone and acetylspiramycin. The product has relatively excellent flame resistance, acid and alkaline resistance, and anti-mildew antibacterial performances, so that the product performances are improved.

Description

A kind of municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent
Technical field
The present invention relates to a kind of municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent, belong to road and bridge repairing bitumen technology neck Territory.
Background technology
The pitchy complex mixture that pitch is made up of hydrocarbon and the nonmetal derivative thereof of different molecular weight, Being the one of high viscosity organic liquid, be in a liquid state, surface is black, dissolves in carbon disulfide.Pitch be a kind of waterproof and dampproof and Corrosion-resistant organic gel gel material.Pitch can be largely classified into coal tar pitch, asphalt and bitumen three kinds: wherein, coal tar Pitch is the byproduct of coking.Asphalt is the residue after crude distillation.Bitumen is then to be stored at underground, some formation Ore bed or at earth's crust surface sediment.Pitch is mainly used in industry and the surfacings etc. such as product, plastics, rubber.On municipal administration road In bridge repairing, it is often necessary to using pitch, these pitches are necessary to suitable modification agent and are improved its performance.
Summary of the invention
It is an object of the invention to provide a kind of municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent, in order to be better achieved The process function of municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent.
To achieve these goals, technical scheme is as follows.
A kind of municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent, is made up of the component of following mass fraction: Sorbitan Alcohol acid anhydride oleate 18～22 parts, chloroform 20～24 parts, alumina powder 16～20 parts, polybutylene terephthalate (PBT) 14 ～18 parts, polyvinyl chloride 20～24 parts, microwax 16～20 parts, 2-mercaptobenzimidazole 14～18 parts, magnesium oxide powder 20～ 24 parts, cumyl peroxide 16～20 parts, basalt fibre 14～18 parts, nano-carbon powder 20～24 parts, diisocyanate 16 ～20 parts, chrome green powder 16～20 parts, artificial mica 14～18 parts, glycerin monostearate 20～24 parts, molybdenum oxide powder 16 ～20 parts, maifanite powder 14～18 parts, barium sulfate 20～24 parts, polyvinyl butyral resin 16～20 parts, dimethylamino-propane 14～18 parts, amino acid 20～24 parts, daconil M 16～20 parts, ammonium chloride 14～18 parts, arasaponin 20～24 Part, eugenol 16～20 parts, polyvinylpyrrolidone 16～20 parts, acetyl spiramycin 16～20 parts.
Further, above-mentioned municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent, it is made up of the component of following mass fraction: Anhydrous sorbitol acid anhydride oleate 18 parts, chloroform 20 parts, alumina powder 16 parts, polybutylene terephthalate (PBT) 14 parts, Polyvinyl chloride 20 parts, microwax 16 parts, 2-mercaptobenzimidazole 14 parts, magnesium oxide powder 20 parts, cumyl peroxide 16 parts, Basalt fibre 14 parts, nano-carbon powder 20 parts, diisocyanate 16 parts, 16 parts of chrome green powder, artificial mica 14 parts, monostearate Glyceride 20 parts, 16 parts of molybdenum oxide powder, maifanite powder 14 parts, 20 parts of barium sulfate, polyvinyl butyral resin 16 parts, diformazan ammonia 14 parts of base propane, 20 parts of amino acid, daconil M 16 parts, ammonium chloride 14 parts, arasaponin 20 parts, eugenol 16 parts, Polyvinylpyrrolidone 16 parts, acetyl spiramycin 16 parts.
Further, above-mentioned municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent, it is made up of the component of following mass fraction: Anhydrous sorbitol acid anhydride oleate 20 parts, chloroform 22 parts, alumina powder 18 parts, polybutylene terephthalate (PBT) 16 parts, Polyvinyl chloride 22 parts, microwax 18 parts, 2-mercaptobenzimidazole 16 parts, magnesium oxide powder 22 parts, cumyl peroxide 18 parts, Basalt fibre 16 parts, nano-carbon powder 22 parts, diisocyanate 18 parts, 18 parts of chrome green powder, artificial mica 16 parts, monostearate Glyceride 22 parts, 18 parts of molybdenum oxide powder, maifanite powder 16 parts, 22 parts of barium sulfate, polyvinyl butyral resin 18 parts, diformazan ammonia 16 parts of base propane, 22 parts of amino acid, daconil M 18 parts, ammonium chloride 16 parts, arasaponin 22 parts, eugenol 18 parts, Polyvinylpyrrolidone 18 parts, acetyl spiramycin 18 parts.
Further, above-mentioned municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent, it is made up of the component of following mass fraction: Anhydrous sorbitol acid anhydride oleate 22 parts, chloroform 24 parts, alumina powder 20 parts, polybutylene terephthalate (PBT) 18 parts, Polyvinyl chloride 24 parts, microwax 20 parts, 2-mercaptobenzimidazole 18 parts, magnesium oxide powder 24 parts, cumyl peroxide 20 parts, Basalt fibre 18 parts, nano-carbon powder 24 parts, diisocyanate 20 parts, 20 parts of chrome green powder, artificial mica 18 parts, monostearate Glyceride 24 parts, 20 parts of molybdenum oxide powder, maifanite powder 18 parts, 24 parts of barium sulfate, polyvinyl butyral resin 20 parts, diformazan ammonia 18 parts of base propane, 24 parts of amino acid, daconil M 20 parts, ammonium chloride 18 parts, arasaponin 24 parts, eugenol 20 parts, Polyvinylpyrrolidone 20 parts, acetyl spiramycin 20 parts.
Further, above-mentioned municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent preparation method step is as follows:
(1) by the anhydrous sorbitol acid anhydride oleate of described mass fraction, chloroform, alumina powder, poly terephthalic acid fourth Diol ester, polyvinyl chloride, microwax, basalt fibre, nano-carbon powder, molybdenum oxide powder, maifanite powder, barium sulfate, poly-second Enol butyral, dimethylamino-propane, amino acid, daconil M, ammonium chloride, arasaponin, eugenol, polyethylene pyrrole Pyrrolidone, acetyl spiramycin are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20～40KHz, rate of dispersion 5000～ About 5400r/min, jitter time is 30～60min；
(2) diisocyanate of described mass fraction, chrome green powder, artificial mica, glycerin monostearate, ultrasonic high speed are added Dispersion, ultrasonic frequency is 20～35KHz, rate of dispersion 4800～about 5200r/min, and jitter time is 30～50min；
(3) adding the 2-mercaptobenzimidazole of described mass fraction, magnesium oxide powder, cumyl peroxide, ultrasonic high speed is divided Dissipating, ultrasonic frequency is 20～30KHz, rate of dispersion 4600～about 4800r/min, and jitter time is 20～40min；Mixing This product is prepared after uniformly.
This beneficial effect of the invention is: the present invention relates to a kind of municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent, by Following components forms: anhydrous sorbitol acid anhydride oleate, chloroform, alumina powder, polybutylene terephthalate (PBT), polychlorostyrene Ethene, microwax, 2-mercaptobenzimidazole, magnesium oxide powder, cumyl peroxide, basalt fibre, nano-carbon powder, two different Cyanate, chrome green powder, artificial mica, glycerin monostearate, molybdenum oxide powder, maifanite powder, barium sulfate, polyvinyl alcohol Butyral, dimethylamino-propane, amino acid, daconil M, ammonium chloride, arasaponin, eugenol, polyvinylpyrrolidine Ketone, acetyl spiramycin.This municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent process of preparing is simple, prepared product There is the most superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improve properties of product.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is described, in order to be better understood from the present invention.
Embodiment 1
Municipal road and bridge first-aid repair construction asphalt modification inorganic agent in the present embodiment, is made up of the component of following mass fraction: dehydration Sorbitan oleate 18 parts, chloroform 20 parts, alumina powder 16 parts, polybutylene terephthalate (PBT) 14 parts, polychlorostyrene Ethene 20 parts, microwax 16 parts, 2-mercaptobenzimidazole 14 parts, magnesium oxide powder 20 parts, cumyl peroxide 16 parts, the Black Warrior Rock fiber 14 parts, nano-carbon powder 20 parts, diisocyanate 16 parts, 16 parts of chrome green powder, artificial mica 14 parts, glycerol monostearate Ester 20 parts, 16 parts of molybdenum oxide powder, maifanite powder 14 parts, 20 parts of barium sulfate, polyvinyl butyral resin 16 parts, dimethylamino third 14 parts of alkane, 20 parts of amino acid, daconil M 16 parts, ammonium chloride 14 parts, arasaponin 20 parts, eugenol 16 parts, poly-second Alkene pyrrolidone 16 parts, acetyl spiramycin 16 parts.
Above-mentioned municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent preparation method step is as follows:
(1) by the anhydrous sorbitol acid anhydride oleate of described mass fraction, chloroform, alumina powder, poly terephthalic acid fourth Diol ester, polyvinyl chloride, microwax, basalt fibre, nano-carbon powder, molybdenum oxide powder, maifanite powder, barium sulfate, poly-second Enol butyral, dimethylamino-propane, amino acid, daconil M, ammonium chloride, arasaponin, eugenol, polyethylene pyrrole Pyrrolidone, acetyl spiramycin are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20kHz, rate of dispersion 5400r/min Left and right, jitter time is 60min；
(2) diisocyanate of described mass fraction, chrome green powder, artificial mica, glycerin monostearate, ultrasonic high speed are added Dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min；
(3) adding the 2-mercaptobenzimidazole of described mass fraction, magnesium oxide powder, cumyl peroxide, ultrasonic high speed is divided Dissipating, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is 40min；This is prepared after mixing Product.
Embodiment 2
Municipal road and bridge first-aid repair construction asphalt modification inorganic agent in the present embodiment, is made up of the component of following mass fraction: dehydration Sorbitan oleate 20 parts, chloroform 22 parts, alumina powder 18 parts, polybutylene terephthalate (PBT) 16 parts, polychlorostyrene Ethene 22 parts, microwax 18 parts, 2-mercaptobenzimidazole 16 parts, magnesium oxide powder 22 parts, cumyl peroxide 18 parts, the Black Warrior Rock fiber 16 parts, nano-carbon powder 22 parts, diisocyanate 18 parts, 18 parts of chrome green powder, artificial mica 16 parts, glycerol monostearate Ester 22 parts, 18 parts of molybdenum oxide powder, maifanite powder 16 parts, 22 parts of barium sulfate, polyvinyl butyral resin 18 parts, dimethylamino third 16 parts of alkane, 22 parts of amino acid, daconil M 18 parts, ammonium chloride 16 parts, arasaponin 22 parts, eugenol 18 parts, poly-second Alkene pyrrolidone 18 parts, acetyl spiramycin 18 parts.
Above-mentioned municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent preparation method step is as follows:
(1) by the anhydrous sorbitol acid anhydride oleate of described mass fraction, chloroform, alumina powder, poly terephthalic acid fourth Diol ester, polyvinyl chloride, microwax, basalt fibre, nano-carbon powder, molybdenum oxide powder, maifanite powder, barium sulfate, poly-second Enol butyral, dimethylamino-propane, amino acid, daconil M, ammonium chloride, arasaponin, eugenol, polyethylene pyrrole Pyrrolidone, acetyl spiramycin are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 30kHz, rate of dispersion 5200r/min Left and right, jitter time is 45min；
(2) diisocyanate of described mass fraction, chrome green powder, artificial mica, glycerin monostearate, ultrasonic high speed are added Dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min；
(3) adding the 2-mercaptobenzimidazole of described mass fraction, magnesium oxide powder, cumyl peroxide, ultrasonic high speed is divided Dissipating, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is 30min；This is prepared after mixing Product.
Embodiment 3
Municipal road and bridge first-aid repair construction asphalt modification inorganic agent in the present embodiment, is made up of the component of following mass fraction: dehydration Sorbitan oleate 22 parts, chloroform 24 parts, alumina powder 20 parts, polybutylene terephthalate (PBT) 18 parts, polychlorostyrene Ethene 24 parts, microwax 20 parts, 2-mercaptobenzimidazole 18 parts, magnesium oxide powder 24 parts, cumyl peroxide 20 parts, the Black Warrior Rock fiber 18 parts, nano-carbon powder 24 parts, diisocyanate 20 parts, 20 parts of chrome green powder, artificial mica 18 parts, glycerol monostearate Ester 24 parts, 20 parts of molybdenum oxide powder, maifanite powder 18 parts, 24 parts of barium sulfate, polyvinyl butyral resin 20 parts, dimethylamino third 18 parts of alkane, 24 parts of amino acid, daconil M 20 parts, ammonium chloride 18 parts, arasaponin 24 parts, eugenol 20 parts, poly-second Alkene pyrrolidone 20 parts, acetyl spiramycin 20 parts.
Above-mentioned municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent preparation method step is as follows:
(1) by the anhydrous sorbitol acid anhydride oleate of described mass fraction, chloroform, alumina powder, poly terephthalic acid fourth Diol ester, polyvinyl chloride, microwax, basalt fibre, nano-carbon powder, molybdenum oxide powder, maifanite powder, barium sulfate, poly-second Enol butyral, dimethylamino-propane, amino acid, daconil M, ammonium chloride, arasaponin, eugenol, polyethylene pyrrole Pyrrolidone, acetyl spiramycin are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, Jitter time is 30min；
(2) diisocyanate of described mass fraction, chrome green powder, artificial mica, glycerin monostearate, ultrasonic high speed are added Dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min；
(3) adding the 2-mercaptobenzimidazole of described mass fraction, magnesium oxide powder, cumyl peroxide, ultrasonic high speed is divided Dissipating, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is 20min；This is prepared after mixing Product.
Performance measurement is carried out for the product in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available prod, measured Data are as shown in table 1.Fire protection flame retarding level estimate uses UL94 standard.
Table 1 the performance test results
Visible, product of the present invention has the most corrosion-resistant, fire protection flame retarding, anti-mildew, anti-microbial property.
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art For, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications are also considered as Protection scope of the present invention.

Claims (5)

1. a municipal road and bridge first-aid repair construction asphalt modification inorganic agent, it is characterised in that: it is made up of the component of following mass fraction: Anhydrous sorbitol acid anhydride oleate 18～22 parts, chloroform 20～24 parts, alumina powder 16～20 parts, poly terephthalic acid fourth Diol ester 14～18 parts, polyvinyl chloride 20～24 parts, microwax 16～20 parts, 2-mercaptobenzimidazole 14～18 parts, magnesia Powder 20～24 parts, cumyl peroxide 16～20 parts, basalt fibre 14～18 parts, nano-carbon powder 20～24 parts, two different Cyanate 16～20 parts, chrome green powder 16～20 parts, artificial mica 14～18 parts, glycerin monostearate 20～24 parts, oxidation Molybdenum powder 16～20 parts, maifanite powder 14～18 parts, barium sulfate 20～24 parts, polyvinyl butyral resin 16～20 parts, diformazan Aminopropane 14～18 parts, amino acid 20～24 parts, daconil M 16～20 parts, ammonium chloride 14～18 parts, the total soap of pseudo-ginseng Glycosides 20～24 parts, eugenol 16～20 parts, polyvinylpyrrolidone 16～20 parts, acetyl spiramycin 16～20 parts.
Municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent the most according to claim 1, it is characterised in that: described municipal administration road Bridge first-aid repair construction asphalt modification inorganic agent is made up of the component of following mass fraction: anhydrous sorbitol acid anhydride oleate 18 parts, trichlorine 20 parts of methane, alumina powder 16 parts, polybutylene terephthalate (PBT) 14 parts, polyvinyl chloride 20 parts, microwax 16 parts, 2-mercapto Base benzimidazole 14 parts, magnesium oxide powder 20 parts, cumyl peroxide 16 parts, basalt fibre 14 parts, nano-carbon powder 20 parts, Diisocyanate 16 parts, 16 parts of chrome green powder, artificial mica 14 parts, glycerin monostearate 20 parts, 16 parts of molybdenum oxide powder, wheat Between meal stone powder 14 parts, 20 parts of barium sulfate, polyvinyl butyral resin 16 parts, dimethylamino-propane 14 parts, 20 parts of amino acid, tetrachloro Benzene dinitrile 16 parts, ammonium chloride 14 parts, arasaponin 20 parts, eugenol 16 parts, polyvinylpyrrolidone 16 parts, acetyl spiral are mould Element 16 parts.
3. according to the municipal road and bridge first-aid repair construction asphalt modification inorganic agent described in claim 1 to 2, it is characterised in that: described city Political affairs road and bridge first-aid repair construction asphalt modification inorganic agent is made up of the component of following mass fraction: anhydrous sorbitol acid anhydride oleate 20 parts, Chloroform 22 parts, alumina powder 18 parts, polybutylene terephthalate (PBT) 16 parts, polyvinyl chloride 22 parts, microwax 18 parts, 2-mercaptobenzimidazole 16 parts, magnesium oxide powder 22 parts, cumyl peroxide 18 parts, basalt fibre 16 parts, nano-carbon powder 22 parts, diisocyanate 18 parts, 18 parts of chrome green powder, artificial mica 16 parts, glycerin monostearate 22 parts, molybdenum oxide powder 18 Part, maifanite powder 16 parts, 22 parts of barium sulfate, polyvinyl butyral resin 18 parts, dimethylamino-propane 16 parts, 22 parts of amino acid, Daconil M 18 parts, ammonium chloride 16 parts, arasaponin 22 parts, eugenol 18 parts, polyvinylpyrrolidone 18 parts, acetyl Spiramvcin 18 parts.
4. according to the municipal road and bridge first-aid repair construction asphalt modification inorganic agent described in claims 1 to 3, it is characterised in that: described city Political affairs road and bridge first-aid repair construction asphalt modification inorganic agent is made up of the component of following mass fraction: anhydrous sorbitol acid anhydride oleate 22 parts, Chloroform 24 parts, alumina powder 20 parts, polybutylene terephthalate (PBT) 18 parts, polyvinyl chloride 24 parts, microwax 20 parts, 2-mercaptobenzimidazole 18 parts, magnesium oxide powder 24 parts, cumyl peroxide 20 parts, basalt fibre 18 parts, nano-carbon powder 24 parts, diisocyanate 20 parts, 20 parts of chrome green powder, artificial mica 18 parts, glycerin monostearate 24 parts, molybdenum oxide powder 20 Part, maifanite powder 18 parts, 24 parts of barium sulfate, polyvinyl butyral resin 20 parts, dimethylamino-propane 18 parts, 24 parts of amino acid, Daconil M 20 parts, ammonium chloride 18 parts, arasaponin 24 parts, eugenol 20 parts, polyvinylpyrrolidone 20 parts, acetyl Spiramvcin 20 parts.
Municipal administration road and bridge first-aid repair construction asphalt modification inorganic agent the most according to claim 1, it is characterised in that: described municipal administration road Bridge first-aid repair construction asphalt modification inorganic agent preparation method step is as follows:
(1) by the anhydrous sorbitol acid anhydride oleate of described mass fraction, chloroform, alumina powder, poly terephthalic acid fourth Diol ester, polyvinyl chloride, microwax, basalt fibre, nano-carbon powder, molybdenum oxide powder, maifanite powder, barium sulfate, poly-second Enol butyral, dimethylamino-propane, amino acid, daconil M, ammonium chloride, arasaponin, eugenol, polyethylene pyrrole Pyrrolidone, acetyl spiramycin are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20～40KHz, rate of dispersion about 5000 ～5400r/min, jitter time is 30～about 60min；
(2) diisocyanate of described mass fraction, chrome green powder, artificial mica, glycerin monostearate, ultrasonic high speed are added Dispersion, ultrasonic frequency is 20～35KHz, and rate of dispersion is about 4800～5200r/min, and jitter time is 30～50min left sides Right；
(3) adding the 2-mercaptobenzimidazole of described mass fraction, magnesium oxide powder, cumyl peroxide, ultrasonic high speed is divided Dissipating, ultrasonic frequency is 20～30KHz, and rate of dispersion is about 4600～4800r/min, and jitter time is 20～about 40min； This product is prepared after mixing.
CN201610492698.2A 2016-06-29 2016-06-29 Asphalt modifying treating agent for municipal road and bridge repair construction Pending CN105906991A (en)