CN106118342A - A kind of municipal administration road and bridge safeguard asphalt modification inorganic agent - Google Patents

A kind of municipal administration road and bridge safeguard asphalt modification inorganic agent Download PDF

Info

Publication number
CN106118342A
CN106118342A CN201610551448.1A CN201610551448A CN106118342A CN 106118342 A CN106118342 A CN 106118342A CN 201610551448 A CN201610551448 A CN 201610551448A CN 106118342 A CN106118342 A CN 106118342A
Authority
CN
China
Prior art keywords
parts
tert
methyl
butyl
inorganic agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610551448.1A
Other languages
Chinese (zh)
Inventor
王根夫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610551448.1A priority Critical patent/CN106118342A/en
Publication of CN106118342A publication Critical patent/CN106118342A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of municipal administration road and bridge safeguards asphalt modification inorganic agent, composed of the following components: calcium acetate, diethylene glycol monoethyl ether, Bravo, Oleum Bulbus Allii, dual-tert-butyl peroxy isopropyl base benzene, Zinc Pyrithione, carbolineum, methyl isobutyl carbinol, amino resins, a olefin elastomer, phenolic aldehyde vinylite, hydrogenated nitrile-butadiene rubber, ammonium polyphosphate, nano-sized magnesium hydroxide, TDE, prestox silicone oil, Brazil wax, methyl benzoylformate, magnesium sulfate, aluminium triphosphate, chromic oxide powder, chromic acid powder, Orthophosphoric acid Ferrum, polyether modified silicon oil, methylisobutylketone, methyl borate., tert-butyl hydroperoxide, double stearic acid aluminium, butyl titanate, double imidazolidinyl urea.Product of the present invention has the most superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improves properties of product.

Description

A kind of municipal administration road and bridge safeguard asphalt modification inorganic agent
Technical field
The present invention relates to a kind of municipal administration road and bridge safeguards asphalt modification inorganic agent, belongs to municipal administration road and bridge maintenance technology field.
Background technology
The pitchy complex mixture that Colophonium is made up of Hydrocarbon and the nonmetal derivant thereof of different molecular weight, Being the one of high viscosity organic liquid, be in a liquid state, surface is black, dissolves in Carbon bisulfide.Colophonium be a kind of waterproof and dampproof and Antiseptical organic gel gel material.Colophonium can be largely classified into coal tar pitch, asphalt and bitumen three kinds: wherein, coal tar Colophonium is the side-product of coking.Asphalt is the residue after crude distillation.Bitumen is then to be stored at underground, some formation Ore bed or at earth's crust surface sediment.Colophonium is mainly used in industry and the surfacings etc. such as coating, plastics, rubber.
Summary of the invention
It is an object of the invention to provide a kind of municipal administration road and bridge safeguards asphalt modification inorganic agent, in order to municipal administration is better achieved Road and bridge safeguard the use function of asphalt modification inorganic agent, make product have fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improve and produce Product serviceability.
To achieve these goals, technical scheme is as follows.
A kind of municipal administration road and bridge safeguard asphalt modification inorganic agent, are made up of the component of following mass fraction: calcium acetate 10～14 Part, diethylene glycol monoethyl ether 8～12 parts, Bravo 8～12 parts, Oleum Bulbus Allii 6～10 parts, dual-tert-butyl peroxy isopropyl base benzene 8～ 12 parts, Zinc Pyrithione 8～12 parts, carbolineum 6～10 parts, methyl isobutyl carbinol 8～12 parts, amino resins 8～12 parts, a-alkene Olefin elastomer 6～10 parts, phenolic aldehyde vinylite 6～10 parts, hydrogenated nitrile-butadiene rubber 6～10 parts, ammonium polyphosphate 8～12 parts, Nano-sized magnesium hydroxide 6～10 parts, TDE 4～8 parts, prestox silicone oil 8～12 parts, Brazil wax 6～10 parts, benzene GA methyl ester 4～8 parts, magnesium sulfate 6～10 parts, aluminium triphosphate 4～8 parts, chromic oxide powder 4～8 parts, three oxidations 6～10 parts of chromium powder end, Orthophosphoric acid Ferrum 6～10 parts, polyether modified silicon oil 6～10 parts, methylisobutylketone 6～10 parts, boric acid front three Ester 6～10 parts, tert-butyl hydroperoxide 6～10 parts, double stearic acid aluminium 6～10 parts, butyl titanate 6～10 parts, double imidazolidine Base urea 4～8 parts.
Further, above-mentioned municipal administration road and bridge safeguard asphalt modification inorganic agent, are made up of the component of following mass fraction: acetic acid Calcium 10 parts, diethylene glycol monoethyl ether 8 parts, Bravo 8 parts, Oleum Bulbus Allii 6 parts, dual-tert-butyl peroxy isopropyl base benzene 8 parts, pyrithione 8 parts of zinc, carbolineum 6 parts, methyl isobutyl carbinol 8 parts, 8 parts of amino resins, a-olefin elastomer 6 parts, phenolic aldehyde vinylite 6 Part, hydrogenated nitrile-butadiene rubber 6 parts, ammonium polyphosphate 8 parts, nano-sized magnesium hydroxide 6 parts, TDE 4 parts, prestox silicone oil 8 Part, Brazil wax 6 parts, methyl benzoylformate 4 parts, 6 parts of magnesium sulfate, aluminium triphosphate 4 parts, 4 parts of chromic oxide powder, 6 parts of chromic acid powder, Orthophosphoric acid Ferrum 6 parts, polyether modified silicon oil 6 parts, methylisobutylketone 6 parts, methyl borate. 6 parts, tertiary fourth Base hydrogen peroxide 6 parts, double stearic acid aluminium 6 parts, butyl titanate 6 parts, double imidazolidinyl urea 4 parts.
Further, above-mentioned municipal administration road and bridge safeguard asphalt modification inorganic agent, are made up of the component of following mass fraction: acetic acid Calcium 12 parts, diethylene glycol monoethyl ether 10 parts, Bravo 10 parts, Oleum Bulbus Allii 8 parts, dual-tert-butyl peroxy isopropyl base benzene 10 parts, pyridine 10 parts of thioketone zinc, carbolineum 8 parts, methyl isobutyl carbinol 10 parts, 10 parts of amino resins, a-olefin elastomer 8 parts, phenolic aldehyde vinyl Resin 8 parts, hydrogenated nitrile-butadiene rubber 8 parts, ammonium polyphosphate 10 parts, nano-sized magnesium hydroxide 8 parts, TDE 6 parts, prestox Silicone oil 10 parts, Brazil wax 8 parts, methyl benzoylformate 6 parts, 8 parts of magnesium sulfate, aluminium triphosphate 6 parts, chromic oxide powder 6 parts of end, 8 parts of chromic acid powder, Orthophosphoric acid Ferrum 8 parts, polyether modified silicon oil 8 parts, methylisobutylketone 8 parts, methyl borate. 8 Part, tert-butyl hydroperoxide 8 parts, double stearic acid aluminium 8 parts, butyl titanate 8 parts, double imidazolidinyl urea 6 parts.
Further, above-mentioned municipal administration road and bridge safeguard asphalt modification inorganic agent, are made up of the component of following mass fraction: acetic acid Calcium 14 parts, diethylene glycol monoethyl ether 12 parts, Bravo 12 parts, Oleum Bulbus Allii 10 parts, dual-tert-butyl peroxy isopropyl base benzene 12 parts, pyridine 12 parts of thioketone zinc, carbolineum 10 parts, methyl isobutyl carbinol 12 parts, 12 parts of amino resins, a-olefin elastomer 10 parts, phenolic aldehyde ethylene Base resin 10 parts, hydrogenated nitrile-butadiene rubber 10 parts, ammonium polyphosphate 12 parts, nano-sized magnesium hydroxide 10 parts, TDE 8 parts, Prestox silicone oil 12 parts, Brazil wax 10 parts, methyl benzoylformate 8 parts, 10 parts of magnesium sulfate, aluminium triphosphate 8 parts, three oxygen Change two chromium powders end 8 parts, 10 parts of chromic acid powder, Orthophosphoric acid Ferrum 10 parts, polyether modified silicon oil 10 parts, methylisobutylketone 10 parts, Methyl borate. 10 parts, tert-butyl hydroperoxide 10 parts, double stearic acid aluminium 10 parts, butyl titanate 10 parts, double imidazolidinyl urea 8 Part.
Further, above-mentioned municipal administration road and bridge safeguard that asphalt modification inorganic agent preparation method step is as follows:
(1) by different to the calcium acetate of described mass fraction, diethylene glycol monoethyl ether, Bravo, Oleum Bulbus Allii, dual-tert-butyl peroxide Propylbenzene, Zinc Pyrithione, carbolineum, methyl isobutyl carbinol, amino resins, a-olefin elastomer, phenolic aldehyde vinylite, hydrogen Change nitrile rubber, ammonium polyphosphate, nano-sized magnesium hydroxide, TDE, prestox silicone oil, Brazil wax, benzoyl Methyl formate, magnesium sulfate, aluminium triphosphate are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20～40KHz, dispersion speed Degree 5000～about 5400r/min, jitter time is 30～60min；
(2) the chromic oxide powder of described mass fraction, chromic acid powder, Orthophosphoric acid Ferrum, polyether-modified silicon are added Oil, methylisobutylketone, ultrasonic high speed dispersion, ultrasonic frequency is 20～35KHz, rate of dispersion 4800～about 5200r/min, Jitter time is 30～50min；
(3) add the methyl borate. of described mass fraction, tert-butyl hydroperoxide, double stearic acid aluminium, butyl titanate, Double imidazolidinyl urea, ultrasonic high speed dispersion, ultrasonic frequency is 20～30KHz, rate of dispersion 4600～about 4800r/min, Jitter time is 20～40min；This product is prepared after mix homogeneously.
This beneficial effect of the invention is: the municipal road and bridge in the present invention safeguard asphalt modification inorganic agent, by following components Composition: calcium acetate, diethylene glycol monoethyl ether, Bravo, Oleum Bulbus Allii, dual-tert-butyl peroxy isopropyl base benzene, Zinc Pyrithione, anthracene Oil, methyl isobutyl carbinol, amino resins, a-olefin elastomer, phenolic aldehyde vinylite, hydrogenated nitrile-butadiene rubber, polyphosphoric acids Ammonium, nano-sized magnesium hydroxide, TDE, prestox silicone oil, Brazil wax, methyl benzoylformate, magnesium sulfate, trimerization Aluminum phosphate, chromic oxide powder, chromic acid powder, Orthophosphoric acid Ferrum, polyether modified silicon oil, methylisobutylketone, boric acid front three Ester, tert-butyl hydroperoxide, double stearic acid aluminium, butyl titanate, double imidazolidinyl urea.Product of the present invention has the most superior Fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improve properties of product.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is described, in order to be better understood from the present invention.
Embodiment 1
Municipal road and bridge in the present embodiment safeguard asphalt modification inorganic agent, are made up of the component of following mass fraction: acetic acid Calcium 10 parts, diethylene glycol monoethyl ether 8 parts, Bravo 8 parts, Oleum Bulbus Allii 6 parts, dual-tert-butyl peroxy isopropyl base benzene 8 parts, pyrithione 8 parts of zinc, carbolineum 6 parts, methyl isobutyl carbinol 8 parts, 8 parts of amino resins, a-olefin elastomer 6 parts, phenolic aldehyde vinylite 6 Part, hydrogenated nitrile-butadiene rubber 6 parts, ammonium polyphosphate 8 parts, nano-sized magnesium hydroxide 6 parts, TDE 4 parts, prestox silicone oil 8 Part, Brazil wax 6 parts, methyl benzoylformate 4 parts, 6 parts of magnesium sulfate, aluminium triphosphate 4 parts, 4 parts of chromic oxide powder, 6 parts of chromic acid powder, Orthophosphoric acid Ferrum 6 parts, polyether modified silicon oil 6 parts, methylisobutylketone 6 parts, methyl borate. 6 parts, tertiary fourth Base hydrogen peroxide 6 parts, double stearic acid aluminium 6 parts, butyl titanate 6 parts, double imidazolidinyl urea 4 parts.
Above-mentioned municipal administration road and bridge safeguard that asphalt modification inorganic agent preparation method step is as follows:
(1) by different to the calcium acetate of described mass fraction, diethylene glycol monoethyl ether, Bravo, Oleum Bulbus Allii, dual-tert-butyl peroxide Propylbenzene, Zinc Pyrithione, carbolineum, methyl isobutyl carbinol, amino resins, a-olefin elastomer, phenolic aldehyde vinylite, hydrogen Change nitrile rubber, ammonium polyphosphate, nano-sized magnesium hydroxide, TDE, prestox silicone oil, Brazil wax, benzoyl Methyl formate, magnesium sulfate, aluminium triphosphate are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20kHz, rate of dispersion About 5400r/min, jitter time is 60min；
(2) the chromic oxide powder of described mass fraction, chromic acid powder, Orthophosphoric acid Ferrum, polyether-modified silicon are added Oil, methylisobutylketone, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min；
(3) add the methyl borate. of described mass fraction, tert-butyl hydroperoxide, double stearic acid aluminium, butyl titanate, Double imidazolidinyl urea, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is 40min；This product is prepared after mix homogeneously.
Embodiment 2
Municipal road and bridge in the present embodiment safeguard asphalt modification inorganic agent, are made up of the component of following mass fraction: acetic acid Calcium 12 parts, diethylene glycol monoethyl ether 10 parts, Bravo 10 parts, Oleum Bulbus Allii 8 parts, dual-tert-butyl peroxy isopropyl base benzene 10 parts, pyridine 10 parts of thioketone zinc, carbolineum 8 parts, methyl isobutyl carbinol 10 parts, 10 parts of amino resins, a-olefin elastomer 8 parts, phenolic aldehyde vinyl Resin 8 parts, hydrogenated nitrile-butadiene rubber 8 parts, ammonium polyphosphate 10 parts, nano-sized magnesium hydroxide 8 parts, TDE 6 parts, prestox Silicone oil 10 parts, Brazil wax 8 parts, methyl benzoylformate 6 parts, 8 parts of magnesium sulfate, aluminium triphosphate 6 parts, chromic oxide powder 6 parts of end, 8 parts of chromic acid powder, Orthophosphoric acid Ferrum 8 parts, polyether modified silicon oil 8 parts, methylisobutylketone 8 parts, methyl borate. 8 Part, tert-butyl hydroperoxide 8 parts, double stearic acid aluminium 8 parts, butyl titanate 8 parts, double imidazolidinyl urea 6 parts.
Above-mentioned municipal administration road and bridge safeguard that asphalt modification inorganic agent preparation method step is as follows:
(1) by different to the calcium acetate of described mass fraction, diethylene glycol monoethyl ether, Bravo, Oleum Bulbus Allii, dual-tert-butyl peroxide Propylbenzene, Zinc Pyrithione, carbolineum, methyl isobutyl carbinol, amino resins, a-olefin elastomer, phenolic aldehyde vinylite, hydrogen Change nitrile rubber, ammonium polyphosphate, nano-sized magnesium hydroxide, TDE, prestox silicone oil, Brazil wax, benzoyl Methyl formate, magnesium sulfate, aluminium triphosphate are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 30kHz, rate of dispersion About 5200r/min, jitter time is 45min；
(2) the chromic oxide powder of described mass fraction, chromic acid powder, Orthophosphoric acid Ferrum, polyether-modified silicon are added Oil, methylisobutylketone, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min；
(3) add the methyl borate. of described mass fraction, tert-butyl hydroperoxide, double stearic acid aluminium, butyl titanate, Double imidazolidinyl urea, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is 30min；This product is prepared after mix homogeneously.
Embodiment 3
Municipal road and bridge in the present embodiment safeguard asphalt modification inorganic agent, are made up of the component of following mass fraction: acetic acid Calcium 14 parts, diethylene glycol monoethyl ether 12 parts, Bravo 12 parts, Oleum Bulbus Allii 10 parts, dual-tert-butyl peroxy isopropyl base benzene 12 parts, pyridine 12 parts of thioketone zinc, carbolineum 10 parts, methyl isobutyl carbinol 12 parts, 12 parts of amino resins, a-olefin elastomer 10 parts, phenolic aldehyde ethylene Base resin 10 parts, hydrogenated nitrile-butadiene rubber 10 parts, ammonium polyphosphate 12 parts, nano-sized magnesium hydroxide 10 parts, TDE 8 parts, Prestox silicone oil 12 parts, Brazil wax 10 parts, methyl benzoylformate 8 parts, 10 parts of magnesium sulfate, aluminium triphosphate 8 parts, three oxygen Change two chromium powders end 8 parts, 10 parts of chromic acid powder, Orthophosphoric acid Ferrum 10 parts, polyether modified silicon oil 10 parts, methylisobutylketone 10 parts, Methyl borate. 10 parts, tert-butyl hydroperoxide 10 parts, double stearic acid aluminium 10 parts, butyl titanate 10 parts, double imidazolidinyl urea 8 Part.
Above-mentioned municipal administration road and bridge safeguard that asphalt modification inorganic agent preparation method step is as follows:
(1) by different to the calcium acetate of described mass fraction, diethylene glycol monoethyl ether, Bravo, Oleum Bulbus Allii, dual-tert-butyl peroxide Propylbenzene, Zinc Pyrithione, carbolineum, methyl isobutyl carbinol, amino resins, a-olefin elastomer, phenolic aldehyde vinylite, hydrogen Change nitrile rubber, ammonium polyphosphate, nano-sized magnesium hydroxide, TDE, prestox silicone oil, Brazil wax, benzoyl Methyl formate, magnesium sulfate, aluminium triphosphate are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, jitter time is 30min；
(2) the chromic oxide powder of described mass fraction, chromic acid powder, Orthophosphoric acid Ferrum, polyether-modified silicon are added Oil, methylisobutylketone, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min；
(3) add the methyl borate. of described mass fraction, tert-butyl hydroperoxide, double stearic acid aluminium, butyl titanate, Double imidazolidinyl urea, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is 20min；This product is prepared after mix homogeneously.
Performance measurement is carried out for the product in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available prod, measured Data are as shown in table 1.Fire protection flame retarding level estimate uses UL94 standard.
Table 1 the performance test results
Visible, product of the present invention has the most corrosion-resistant, fire protection flame retarding, anti-mildew, anti-microbial property.
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art For, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications are also considered as Protection scope of the present invention.

Claims (5)

1. municipal road and bridge safeguard asphalt modification inorganic agent, it is characterised in that: it is made up of the component of following mass fraction: acetic acid Calcium 10～14 parts, diethylene glycol monoethyl ether 8～12 parts, Bravo 8～12 parts, Oleum Bulbus Allii 6～10 parts, dual-tert-butyl peroxy isopropyl Base benzene 8～12 parts, Zinc Pyrithione 8～12 parts, carbolineum 6～10 parts, methyl isobutyl carbinol 8～12 parts, amino resins 8～12 Part, a-olefin elastomer 6～10 parts, phenolic aldehyde vinylite 6～10 parts, hydrogenated nitrile-butadiene rubber 6～10 parts, ammonium polyphosphate 8 ～12 parts, nano-sized magnesium hydroxide 6～10 parts, TDE 4～8 parts, prestox silicone oil 8～12 parts, Brazil wax 6～ 10 parts, methyl benzoylformate 4～8 parts, magnesium sulfate 6～10 parts, aluminium triphosphate 4～8 parts, chromic oxide powder 4～8 Part, chromic acid powder 6～10 parts, Orthophosphoric acid Ferrum 6～10 parts, polyether modified silicon oil 6～10 parts, methylisobutylketone 6～10 parts, Methyl borate. 6～10 parts, tert-butyl hydroperoxide 6～10 parts, double stearic acid aluminium 6～10 parts, butyl titanate 6～10 parts, Double imidazolidinyl urea 4～8 parts.
Municipal administration road and bridge the most according to claim 1 safeguard asphalt modification inorganic agent, it is characterised in that: described municipal administration road and bridge dimension Protect asphalt modification inorganic agent to be made up of the component of following mass fraction: calcium acetate 10 parts, diethylene glycol monoethyl ether 8 parts, Bravo 8 Part, Oleum Bulbus Allii 6 parts, dual-tert-butyl peroxy isopropyl base benzene 8 parts, Zinc Pyrithione 8 parts, carbolineum 6 parts, methyl isobutyl carbinol 8 parts, 8 parts of amino resins, a-olefin elastomer 6 parts, phenolic aldehyde vinylite 6 parts, hydrogenated nitrile-butadiene rubber 6 parts, ammonium polyphosphate 8 parts, Nano-sized magnesium hydroxide 6 parts, TDE 4 parts, prestox silicone oil 8 parts, Brazil wax 6 parts, methyl benzoylformate 4 Part, 6 parts of magnesium sulfate, aluminium triphosphate 4 parts, 4 parts of chromic oxide powder, 6 parts of chromic acid powder, Orthophosphoric acid Ferrum 6 parts, polyethers Modified silicon oil 6 parts, methylisobutylketone 6 parts, methyl borate. 6 parts, tert-butyl hydroperoxide 6 parts, double stearic acid aluminium 6 parts, metatitanic acid Four butyl esters 6 parts, double imidazolidinyl urea 4 parts.
3. safeguard asphalt modification inorganic agent according to the municipal road and bridge described in claim 1 to 2, it is characterised in that: described municipal administration road Bridge safeguards that asphalt modification inorganic agent is made up of the component of following mass fraction: calcium acetate 12 parts, diethylene glycol monoethyl ether 10 parts, hundred Clear 10 parts of bacterium, Oleum Bulbus Allii 8 parts, dual-tert-butyl peroxy isopropyl base benzene 10 parts, Zinc Pyrithione 10 parts, carbolineum 8 parts, methyl-isobutyl Methanol 10 parts, 10 parts of amino resins, a-olefin elastomer 8 parts, phenolic aldehyde vinylite 8 parts, hydrogenated nitrile-butadiene rubber 8 parts, poly 10 parts of ammonium phosphate, nano-sized magnesium hydroxide 8 parts, TDE 6 parts, prestox silicone oil 10 parts, Brazil wax 8 parts, benzene first Acyl methyl formate 6 parts, 8 parts of magnesium sulfate, aluminium triphosphate 6 parts, 6 parts of chromic oxide powder, 8 parts of chromic acid powder, positive phosphorus Acid ferrum 8 parts, polyether modified silicon oil 8 parts, methylisobutylketone 8 parts, methyl borate. 8 parts, tert-butyl hydroperoxide 8 parts, double tristearin Acid 8 parts of aluminum, butyl titanate 8 parts, double imidazolidinyl urea 6 parts.
4. safeguard asphalt modification inorganic agent according to the municipal road and bridge described in claims 1 to 3, it is characterised in that: described municipal administration road Bridge safeguards that asphalt modification inorganic agent is made up of the component of following mass fraction: calcium acetate 14 parts, diethylene glycol monoethyl ether 12 parts, hundred Clear 12 parts of bacterium, Oleum Bulbus Allii 10 parts, dual-tert-butyl peroxy isopropyl base benzene 12 parts, Zinc Pyrithione 12 parts, carbolineum 10 parts, methyl tert-butyl Base methanol 12 parts, 12 parts of amino resins, a-olefin elastomer 10 parts, phenolic aldehyde vinylite 10 parts, hydrogenated nitrile-butadiene rubber 10 parts, Ammonium polyphosphate 12 parts, nano-sized magnesium hydroxide 10 parts, TDE 8 parts, prestox silicone oil 12 parts, Brazil wax 10 Part, methyl benzoylformate 8 parts, 10 parts of magnesium sulfate, aluminium triphosphate 8 parts, 8 parts of chromic oxide powder, chromic acid powder 10 parts, Orthophosphoric acid Ferrum 10 parts, polyether modified silicon oil 10 parts, methylisobutylketone 10 parts, methyl borate. 10 parts, tert-butyl hydroperoxide Hydrogen 10 parts, double stearic acid aluminium 10 parts, butyl titanate 10 parts, double imidazolidinyl urea 8 parts.
Municipal administration road and bridge the most according to claim 1 safeguard asphalt modification inorganic agent, it is characterised in that: described municipal administration road and bridge dimension Protect asphalt modification inorganic agent preparation method step as follows:
(1) by the calcium acetate of described mass fraction, diethylene glycol monoethyl ether, Bravo, Oleum Bulbus Allii, dual-tert-butyl peroxy isopropyl base Benzene, Zinc Pyrithione, carbolineum, methyl isobutyl carbinol, amino resins, a-olefin elastomer, phenolic aldehyde vinylite, hydrogenation fourth Nitrile rubber, ammonium polyphosphate, nano-sized magnesium hydroxide, TDE, prestox silicone oil, Brazil wax, benzoyl formic acid Methyl ester, magnesium sulfate, aluminium triphosphate are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20～40KHz, and rate of dispersion is about 5000～5400r/min, jitter time is 30～about 60min；
(2) the chromic oxide powder of described mass fraction, chromic acid powder, Orthophosphoric acid Ferrum, polyether modified silicon oil, first are added Base isobutyl ketone, ultrasonic high speed dispersion, ultrasonic frequency is 20～35KHz, and rate of dispersion is about 4800～5200r/min, dispersion Time is 30～about 50min；
(3) methyl borate. of described mass fraction, tert-butyl hydroperoxide, double stearic acid aluminium, butyl titanate, double miaow are added Oxazolidinyl urea, ultrasonic high speed dispersion, ultrasonic frequency is 20～30KHz, and rate of dispersion is about 4600～4800r/min, dispersion Time is 20～about 40min；This product is prepared after mix homogeneously.
CN201610551448.1A 2016-07-12 2016-07-12 A kind of municipal administration road and bridge safeguard asphalt modification inorganic agent Pending CN106118342A (en)