CN106702569A - Hollowed blended yarn weaved fabric processing process - Google Patents
Hollowed blended yarn weaved fabric processing process Download PDFInfo
- Publication number
- CN106702569A CN106702569A CN201611036452.0A CN201611036452A CN106702569A CN 106702569 A CN106702569 A CN 106702569A CN 201611036452 A CN201611036452 A CN 201611036452A CN 106702569 A CN106702569 A CN 106702569A
- Authority
- CN
- China
- Prior art keywords
- sample
- yarn
- fabric
- wool
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a hollowed blended yarn weaved fabric processing process. The processing process comprises the following steps that wool fibers, bamboo carbon polyester fibers and polylactic acid fibers are re-combined to be made into wool tops; the wool tops are made into yarn through pre-spinning, yarn spinning, spooling, doubling, two-for-one twisting and yarn steaming, and woven shell fabric gray fabric is subjected to singeing, woolen cloth washing, woolen cloth boiling, drying, shaping and woolen cloth steaming, and a finished product is obtained. According to the technical scheme, comfortable and breathable hollowed fabric is obtained, meanwhile, the overall firmness of the fabric is considered, the aim of carrying out computer embroidering during cap making is achieved, and the decoration effect of a cap is effectively improved.
Description
Technical field
The present invention relates to cap manufacturing technology field, specially a kind of hollow out blended yarn weaved fabric processing technology.
Background technology
Cap is the dress ornament for being worn over head, and majority can be with the whole top of covering head.Mainly for the protection of head, part cap
Son has prominent edge, can cover sunlight.Cap such as has sunshade, decorates, heats and protect at the effect.Therefore species is a lot,
Selection is also worthy of careful study.Cap can also be used as dressing, first have to select suitable cap according to shape of face.Its it is secondary according to oneself
Stature selects cap.It is branded as wearing the clothes, maximizes favourable factors and minimizes unfavourable ones as far as possible.Form and color of cap etc. must and dress ornament
Etc. matching.Cap may also be used for protection hair style, cover bald head, or as uniform or a part for religion dress ornament.Can
Variety classes, such as cap high, sunbonnet etc..Some caps have one piece outwards the eaves that stretches it is fluffy, referred to as bongrace.It is branded as
Different culture has different ceremonys, and this is even more important among Western culture, because it is Social Identity to be branded as in the past
Symbol.
Due to cap in use, especially in summer, it is necessary to take into account ventilative, comfort level is otherwise easily had influence on,
But due to the integrally-built particularity of cap, the characteristics of fabric must also possess firm and durable, existing fabric cannot be by this
Two kinds of purposes are taken into account, and cause cap to be used under more warm environment, it is impossible to play the purpose of decoration.
The content of the invention
Comfortable, ventilative hollow-out fabric is provided it is an object of the invention to provide a kind of, while taking into account the overall jail of fabric
Solidity, carries out the purpose of computer embroidery when meeting manufacture cap, the decorative effect of cap is effectively improved, to solve above-mentioned background skill
The problem proposed in art.
To achieve the above object, the present invention provides following technical scheme:A kind of hollow out blended yarn weaved fabric processing technology, its feature
It is:The processing technology is comprised the following steps:
(1)From wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, the wool fiber is surpassed by rabbit fur fibre, beautiful promise
Fine wool fiber, the four kinds of fiber blend braidings of Angora goat wool fibre and mercerized wool fiber are formed, described blending rabbit
Percentage by weight shared by each composition is respectively in wool fiber fabric:The rabbit fur fibre accounts for 18%-22%, and the beautiful promise is ultra-fine
Wool fiber accounts for 15%-19%, and the Angora goat wool fibre accounts for 26%-30%, and the mercerized wool fiber accounts for 29%-41%;
(2)Wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic recombing are made wool top;
(3)Premenstrual spinning-spun yarn-winder-doubling-double twisting-the yarn steaming of wool top is made yarn, wherein spun yarn its number is obtained being
81Nm, 780Z twists/m of the twist;Obtained yarn its be number 80Nm double strand yarn, pool capital 810S twists/m of the twist;It is anti-transparent to wash
Weight percent content of the synthetic fibre in warp thread and weft yarn is 30;
(4)Knit and make fabric fabric and singe-braying-crabbing-drying-sizing-decatizing-finished product;Singe:Speed 90m/min, moderate heat, 1
Positive 1 is anti-;Braying:Temperature 60 C, speed 20m/min;Crabbing:Temperature is 80 DEG C, and speed is 18 ms/min;Drying:Temperature is 108
℃;Sizing:Temperature is 180 DEG C, 25 seconds time;Decatizing:Temperature is 110 DEG C, 6 minutes.
Preferably, hollow out blended yarn weaved fabric specification is:Yarn count 96/2-100/2Nm, total tightness degree 145-165, through close 615-796
Root/10 centimetre, filling density 400-358 root/10 centimetre, grammes per square metre 340-390 grams ms.
Preferably, also including hollow out blended yarn weaved fabric drying property testing procedure:
Step one:Two pieces of the sample of 10cm × 20cm is taken as test sample on the hollow out blended yarn weaved fabric sample of the logical width of 40cm;
Step 2:Sample is placed in washing appearance device, adds 300ml tetrachloro-ethylenes that dry-cleaning is put into as dry cleaning agent, after sealing
In instrument, taken out after dry-cleaning 30min, then repeated washing is twice;
Step 3:The loose wool yarn of sample selvedge, 20 ± 2 DEG C of temperature is flat on by sample after cracking-off dry-cleaning, humidity 65 ± 3%
Under environment, balance is put on balance after 12 hours and weighs, and claims to obtain the preceding weight of sample leaching;
Step 4:Reagent 500ml is added in beaker, the sample after dry-cleaning is placed in beaker abundant moisture absorption 1 minute;
Step 5:By the sample after moisture absorption, a folding is hung on airer for clothes for two along its length, and the airer for clothes that will hang with sample is placed in
20 ± 2 DEG C of temperature, under the environmental condition of humidity 65 ± 3%, and records the time, every measuring sample weight after 30 minutes, until
Untill sample recovers the preceding weight of leaching;
Step 6:Record sample recovers the time of weight before leaching, and as fabric spontaneously dries the time.
Preferably, step 4 pilot scale agent compounding method is addition 0.5ml bleeding agents FFA in 499.5ml distilled water.
Compared with prior art, the beneficial effects of the invention are as follows:Comfortable, ventilative hollow-out fabric is provided, while taking into account face
Expect overall fastness, the purpose of computer embroidery is carried out when meeting manufacture cap, effectively improve the decorative effect of cap.
Specific embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention, this area is common
The every other embodiment that technical staff is obtained under the premise of creative work is not made, belongs to the model of present invention protection
Enclose.
The present invention provides a kind of technical scheme:A kind of hollow out blended yarn weaved fabric processing technology, processing technology is comprised the following steps:
(1)From wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, the wool fiber is surpassed by rabbit fur fibre, beautiful promise
Fine wool fiber, the four kinds of fiber blend braidings of Angora goat wool fibre and mercerized wool fiber are formed, described blending rabbit
Percentage by weight shared by each composition is respectively in wool fiber fabric:The rabbit fur fibre accounts for 18%-22%, and the beautiful promise is ultra-fine
Wool fiber accounts for 15%-19%, and the Angora goat wool fibre accounts for 26%-30%, and the mercerized wool fiber accounts for 29%-41%;
(2)Wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic recombing are made wool top;
(3)Premenstrual spinning-spun yarn-winder-doubling-double twisting-the yarn steaming of wool top is made yarn, wherein spun yarn its number is obtained being
81Nm, 780Z twists/m of the twist;Obtained yarn its be number 80Nm double strand yarn, pool capital 810S twists/m of the twist;It is anti-transparent to wash
Weight percent content of the synthetic fibre in warp thread and weft yarn is 30;
(4)Knit and make fabric fabric and singe-braying-crabbing-drying-sizing-decatizing-finished product;Singe:Speed 90m/min, moderate heat, 1
Positive 1 is anti-;Braying:Temperature 60 C, speed 20m/min;Crabbing:Temperature is 80 DEG C, and speed is 18 ms/min;Drying:Temperature is 108
℃;Sizing:Temperature is 180 DEG C, 25 seconds time;Decatizing:Temperature is 110 DEG C, 6 minutes.
Also, hollow out blended yarn weaved fabric specification therein is:Yarn count 96/2-100/2Nm, total tightness degree 145-165, through close 615-
796/10 centimetres, filling density 400-358 root/10 centimetre, grammes per square metre 340-390 grams ms.
In order to further optimize the quality of the fabric, also need to carry out the survey of hollow out blended yarn weaved fabric drying property after the completion of weaving
Try is rapid:
Step one:Two pieces of the sample of 10cm × 20cm is taken as test sample on the hollow out blended yarn weaved fabric sample of the logical width of 40cm;
Step 2:Sample is placed in washing appearance device, adds 300ml tetrachloro-ethylenes that dry-cleaning is put into as dry cleaning agent, after sealing
In instrument, taken out after dry-cleaning 30min, then repeated washing is twice;
Step 3:The loose wool yarn of sample selvedge, 20 ± 2 DEG C of temperature is flat on by sample after cracking-off dry-cleaning, humidity 65 ± 3%
Under environment, balance is put on balance after 12 hours and weighs, and claims to obtain the preceding weight of sample leaching;
Step 4:Reagent 500ml is added in beaker, the sample after dry-cleaning is placed in beaker abundant moisture absorption 1 minute;
Step 5:By the sample after moisture absorption, a folding is hung on airer for clothes for two along its length, and the airer for clothes that will hang with sample is placed in
20 ± 2 DEG C of temperature, under the environmental condition of humidity 65 ± 3%, and records the time, every measuring sample weight after 30 minutes, until
Untill sample recovers the preceding weight of leaching;
Step 6:Record sample recovers the time of weight before leaching, and as fabric spontaneously dries the time.
0.5ml bleeding agents FFA is added in step 4 pilot scale agent compounding method is 499.5ml distilled water.
The technical scheme can provide comfortable, ventilative hollow-out fabric, while taking into account the overall fastness of fabric, meet manufacture
The purpose of computer embroidery is carried out during cap, the decorative effect of cap is effectively improved.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding can carry out various changes, modification, replacement to these embodiments without departing from the principles and spirit of the present invention
And modification, the scope of the present invention be defined by the appended.
Claims (4)
1. a kind of hollow out blended yarn weaved fabric processing technology, it is characterised in that:The processing technology is comprised the following steps:
(1)From wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, the wool fiber is surpassed by rabbit fur fibre, beautiful promise
Fine wool fiber, the four kinds of fiber blend braidings of Angora goat wool fibre and mercerized wool fiber are formed, described blending rabbit
Percentage by weight shared by each composition is respectively in wool fiber fabric:The rabbit fur fibre accounts for 18%-22%, and the beautiful promise is ultra-fine
Wool fiber accounts for 15%-19%, and the Angora goat wool fibre accounts for 26%-30%, and the mercerized wool fiber accounts for 29%-41%;
(2)Wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic recombing are made wool top;
(3)Premenstrual spinning-spun yarn-winder-doubling-double twisting-the yarn steaming of wool top is made yarn, wherein spun yarn its number is obtained being
81Nm, 780Z twists/m of the twist;Obtained yarn its be number 80Nm double strand yarn, pool capital 810S twists/m of the twist;It is anti-transparent to wash
Weight percent content of the synthetic fibre in warp thread and weft yarn is 30;
(4)Knit and make fabric fabric and singe-braying-crabbing-drying-sizing-decatizing-finished product;Singe:Speed 90m/min, moderate heat, 1
Positive 1 is anti-;Braying:Temperature 60 C, speed 20m/min;Crabbing:Temperature is 80 DEG C, and speed is 18 ms/min;Drying:Temperature is 108
℃;Sizing:Temperature is 180 DEG C, 25 seconds time;Decatizing:Temperature is 110 DEG C, 6 minutes.
2. a kind of hollow out blended yarn weaved fabric processing technology according to claim 1, it is characterised in that:The hollow out blended yarn weaved fabric
Specification is:Yarn count 96/2-100/2Nm, total tightness degree 145-165, through close 615-796 root/10 centimetre, filling density 400-358 root/10 li
Rice, grammes per square metre 340-390 grams ms.
3. a kind of hollow out blended yarn weaved fabric processing technology according to claim 1, it is characterised in that:Also include hollow out blending face
Material drying property testing procedure:
Step one:Two pieces of the sample of 10cm × 20cm is taken as test sample on the hollow out blended yarn weaved fabric sample of the logical width of 40cm;
Step 2:Sample is placed in washing appearance device, adds 300ml tetrachloro-ethylenes that dry-cleaning is put into as dry cleaning agent, after sealing
In instrument, taken out after dry-cleaning 30min, then repeated washing is twice;
Step 3:The loose wool yarn of sample selvedge, 20 ± 2 DEG C of temperature is flat on by sample after cracking-off dry-cleaning, humidity 65 ± 3%
Under environment, balance is put on balance after 12 hours and weighs, and claims to obtain the preceding weight of sample leaching;
Step 4:Reagent 500ml is added in beaker, the sample after dry-cleaning is placed in beaker abundant moisture absorption 1 minute;
Step 5:By the sample after moisture absorption, a folding is hung on airer for clothes for two along its length, and the airer for clothes that will hang with sample is placed in
20 ± 2 DEG C of temperature, under the environmental condition of humidity 65 ± 3%, and records the time, every measuring sample weight after 30 minutes, until
Untill sample recovers the preceding weight of leaching;
Step 6:Record sample recovers the time of weight before leaching, and as fabric spontaneously dries the time.
4. a kind of hollow out blended yarn weaved fabric processing technology according to claim 3, it is characterised in that:Reagent in the step 4
Compound method is addition 0.5ml bleeding agents FFA in 499.5ml distilled water.