CN106700915A - Preparation method of waterproof paint - Google Patents
Preparation method of waterproof paint Download PDFInfo
- Publication number
- CN106700915A CN106700915A CN201611223010.7A CN201611223010A CN106700915A CN 106700915 A CN106700915 A CN 106700915A CN 201611223010 A CN201611223010 A CN 201611223010A CN 106700915 A CN106700915 A CN 106700915A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring
- rotating speed
- paint
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of paint, in particular to a preparation method of waterproof paint. The method comprises the following steps: firstly, adding 15 parts of drier components and 10 parts of silicate cement into a stirring container, and stirring for 1h; adding 5 parts of quartz sand and 15 parts of dimethyl silicone, controlling the rotating speed to be 1000 r/min, and stirring for 1h; then adding 5 parts of ethylene-vinyl acetate copolymer and 10 parts of sodium hexametaphosphate, controlling the rotating speed to be 1000 r/min, and stirring for 1h; finally adding 5 parts of talcum powder, 5 parts of titanium dioxide and 10 parts of polyving akohol, and stirring for 2h, so as to obtain the waterproof paint. According to the method, through the adding of reasonably designed components particularly aucubin, the overall quality of the drier can be enhanced, and further the waterproof and anti-penetrability performances of the waterproof paint can be enhanced by greater than 50 percent. The production technology is simple, and paint is convenient for construction.
Description
Technical field
The present invention relates to technical field of coatings, a kind of preparation method of water-repellent paint is specifically related to.
Background technology
Water-repellent paint, as the term suggests it is exactly to make wall prevent rainwater from immersing, so as to protect the effect of wall.But, at present
Commercially available water-repellent paint is primarily present the defects such as preparation technology complexity, product water proof anti-seepage effect difference, accordingly, it would be desirable to design one kind
Meet the water-repellent paint of waterproof demand, and its impervious effect must get well.
The content of the invention
It is an object of the invention to provide a kind of water-repellent paint and preparation method thereof, the drier component for water-repellent paint
And preparation method thereof, to achieve the above object, present invention employs following technical scheme：
A kind of drier component for water-repellent paint, is made up of the component of following weight portion：
10 parts of calcium carbonate, 10 parts of active masterbatch, 10 parts of hydroxypropyl methyl celluloses, 10 parts of nano zine oxides and 5 parts of peach jaurels
Glucoside.
A kind of preparation method of drier component for water-repellent paint, step is as follows：
Calcium carbonate and active masterbatch are ground to 100 mesh, then to addition 10 parts of calcium carbonate and 10 in stirring container first
The active masterbatch of part, stirs 1 h of mixing under normal temperature；10 parts of hydroxypropyl methyl celluloses and 10 parts of nano zine oxides are subsequently adding, are risen
Warm to 50 DEG C 2 h of stirring；5 parts of Aucubins are eventually adding, 30 DEG C of 1 h of stirring are cooled to.
A kind of water-repellent paint, is made up of the component of following weight portion：
15 parts of drier components, 10 parts of portland cements, 5 parts of quartz sands, 15 parts of dimethicones, 5 parts of ethene-vinyl acetates
Copolymer, 5 parts of talcum powder, 5 parts of titanium dioxides, 10 parts of polyvinyl alcohol and 10 parts of calgons.
A kind of preparation method of water-repellent paint, step is as follows：
First to 15 parts of drier components and 10 parts of portland cements are added in stirring container, rotating speed is controlled for 800 r/min, 50
1 h is stirred at DEG C；5 parts of quartz sands and 15 parts of dimethicones are added, controls rotating speed for 1000 r/min, 1 h is stirred at 60 DEG C；
5 parts of ethylene-vinyl acetate copolymers and 10 parts of calgons are subsequently added into, control rotating speed for 1000 r/min, stirred at 50 DEG C
Mix 1 h；5 parts of talcum powder, 5 parts of titanium dioxides and 10 parts of polyvinyl alcohol are eventually adding, control rotating speed for 900 r/min, stirred at 40 DEG C
2 h are mixed, water-repellent paint is obtained.
Beneficial effects of the present invention show：
The present invention particularly adds Aucubin by adding the component for rationally designing, and can lift the overall product of drier
Matter, further enables waterproof, the anti-permeability performance lifting more than 50% of water-repellent paint.And the production technology of this water-repellent paint
Simply, coating application is convenient.
Specific embodiment
Below with reference to embodiment, the present invention is described in detail.But, embodiment content is only to this hair
Bright example and explanation, affiliated those skilled in the art do various repairing to described specific embodiment
Change or supplement or using similar mode substitute, without departing from invention design or surmount defined in the claims
Scope, all should belong to protection scope of the present invention.
Embodiment 1
A kind of drier component for water-repellent paint, is made up of the component of following weight portion：
10 parts of calcium carbonate, 10 parts of active masterbatch, 10 parts of hydroxypropyl methyl celluloses, 10 parts of nano zine oxides and 5 parts of peach jaurels
Glucoside.
A kind of preparation method of drier component for water-repellent paint, step is as follows：
Calcium carbonate and active masterbatch are ground to 100 mesh, then to addition 10 parts of calcium carbonate and 10 in stirring container first
The active masterbatch of part, stirs 1 h of mixing under normal temperature；10 parts of hydroxypropyl methyl celluloses and 10 parts of nano zine oxides are subsequently adding, are risen
Warm to 50 DEG C 2 h of stirring；5 parts of Aucubins are eventually adding, 30 DEG C of 1 h of stirring are cooled to.
Embodiment 2
A kind of water-repellent paint, is made up of the component of following weight portion：
15 parts of drier components（It is prepared by embodiment 1）, 10 parts of portland cement, 5 parts of quartz sands, 15 parts of dimethicones, 5 parts of second
Alkene-acetate ethylene copolymer, 5 parts of talcum powder, 5 parts of titanium dioxides, 10 parts of polyvinyl alcohol and 10 parts of calgons.
A kind of preparation method of water-repellent paint, step is as follows：
First to 15 parts of drier components and 10 parts of portland cements are added in stirring container, rotating speed is controlled for 800 r/min, 50
1 h is stirred at DEG C；5 parts of quartz sands and 15 parts of dimethicones are added, controls rotating speed for 1000 r/min, 1 h is stirred at 60 DEG C；
5 parts of ethylene-vinyl acetate copolymers and 10 parts of calgons are subsequently added into, control rotating speed for 1000 r/min, stirred at 50 DEG C
Mix 1 h；5 parts of talcum powder, 5 parts of titanium dioxides and 10 parts of polyvinyl alcohol are eventually adding, control rotating speed for 900 r/min, stirred at 40 DEG C
2 h are mixed, water-repellent paint is obtained.
Claims (1)
1. a kind of preparation method of water-repellent paint, it is characterised in that：Step is as follows：
First to 15 parts of drier components and 10 parts of portland cements are added in stirring container, rotating speed is controlled for 800 r/min, 50
1 h is stirred at DEG C；5 parts of quartz sands and 15 parts of dimethicones are added, controls rotating speed for 1000 r/min, 1 h is stirred at 60 DEG C；
5 parts of ethylene-vinyl acetate copolymers and 10 parts of calgons are subsequently added into, control rotating speed for 1000 r/min, stirred at 50 DEG C
Mix 1 h；5 parts of talcum powder, 5 parts of titanium dioxides and 10 parts of polyvinyl alcohol are eventually adding, control rotating speed for 900 r/min, stirred at 40 DEG C
2 h are mixed, water-repellent paint is obtained.