CN106699067A - Method for producing concrete product from ceramic waste residues - Google Patents

Method for producing concrete product from ceramic waste residues Download PDF

Info

Publication number
CN106699067A
CN106699067A CN201710012884.6A CN201710012884A CN106699067A CN 106699067 A CN106699067 A CN 106699067A CN 201710012884 A CN201710012884 A CN 201710012884A CN 106699067 A CN106699067 A CN 106699067A
Authority
CN
China
Prior art keywords
ceramic
waste residue
ceramic waste
waste residues
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710012884.6A
Other languages
Chinese (zh)
Inventor
许刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710012884.6A priority Critical patent/CN106699067A/en
Publication of CN106699067A publication Critical patent/CN106699067A/en
Pending legal-status Critical Current

Abstract

The invention provides a method for producing a concrete product from ceramic waste residues. The production method comprises the following steps: A, smashing reclaimed ceramic defectives or leftover materials into ceramic particles with the particle size of 1-10mm; B, preparing all raw materials by percentage; C, pouring all the raw materials obtained in Step B except the ceramic particles into a stirrer, adding water with 23% of the amount of cement and stirring for 8min, so as to form cement mortar; adding the ceramic particles and uniformly stirring the mixture, so as to form concrete slurry with the ceramic waste residues; D, pouring the concrete slurry with the ceramic waste residues into a product mold, placing for 24h and demolding; E, soaking in clear water for 7 days after demolding. A metal product manufactured with the method is nice in appearance and reliable in quality.

Description

The production method of ceramic waste residue concrete product
Technical field
The present invention relates to the production method of ceramic waste residue concrete product.
Background technology
Traditional desk, chair, light fixture is all manufactured using metal, glass or plastic material and formed, and not only external form is common, raw Can be used in the relatively costly and production process of product and waste more raw material, cost not only be increased, while also generating Many garbage wastes.
The content of the invention
In order to overcome the deficiencies in the prior art, the present invention to provide a kind of production method of ceramic waste residue concrete product.
The technical solution adopted for the present invention to solve the technical problems is：
The production method of ceramic waste residue concrete product, step is as follows：
A, the ceramic particle that the ceramic substandard products for reclaiming or leftover pieces are ground into 1~10mm；
B, prepare each raw material by following percentage：The class g cement 30% of A Erbo boards 525, the quartz sand 15%, step of 40~100 mesh Ceramic particle 53%, the sincere work(building materials WRA-2 types polycarboxylate water-reducer 0.2%, Beijing of the silicon ash 1.5%, Shenzhen of 5000 mesh that A is obtained The defoamer 0.3% of city Chao Hengyuan chemical plant production；
C, the raw material that step B is obtained all are poured into mixer in addition to ceramic particle, added equivalent to cement amount 23% Stirred after water 8 minutes and form cement mortar, ceramic waste residue concrete grout is mixing uniformly to form after then adding ceramic particle Material；
D, the ceramic waste residue concrete slurry for obtaining step C are poured into product mold, can the demoulding after placing 24 hours；
Clear water is steeped after E, the demoulding to conserve 7 days.
The beneficial effects of the invention are as follows：Reasonable in design, energy-conserving and environment-protective of the invention, make full use of discarded ceramic substandard products or side Corner material not only efficiently solves building waste, and low production cost as main raw material(s), while being produced by the present invention The product for coming is sturdy and durable, the rub resistance of resistance to decay, and UV resistant irradiation, weatherability is strong.
Specific embodiment
The production method of ceramic waste residue concrete product, its step is as follows：
A, the ceramic particle that the ceramic substandard products for reclaiming or leftover pieces are ground into 1~10mm；
B, prepare each raw material by following percentage：The class g cement 30% of A Erbo boards 525, the quartz sand 15%, step of 40~100 mesh Ceramic particle 53%, the sincere work(building materials WRA-2 types polycarboxylate water-reducer 0.2%, Beijing of the silicon ash 1.5%, Shenzhen of 5000 mesh that A is obtained The defoamer 0.3% of city Chao Hengyuan chemical plant production；
C, the raw material that step B is obtained all are poured into mixer in addition to ceramic particle, added equivalent to cement amount 23% Stirred after water 8 minutes and form cement mortar, ceramic waste residue concrete grout is mixing uniformly to form after then adding ceramic particle Material；
D, the ceramic waste residue concrete slurry for obtaining step C are poured into product mold, can the demoulding after placing 24 hours；
Clear water is steeped after E, the demoulding to conserve 7 days.
Reasonable in design, energy-conserving and environment-protective of the invention, make full use of discarded ceramic substandard products or leftover pieces as main raw material(s), Building waste, and low production cost are not only efficiently solved, at the same it is sturdy and durable by product that the present invention makes, it is resistance to Decay rub resistance, UV resistant irradiation, weatherability is strong.

Claims (1)

1. the production method of ceramic waste residue concrete product, it is characterised in that step is as follows：
A, the ceramic particle that the ceramic substandard products for reclaiming or leftover pieces are ground into 1~10mm；
B, prepare each raw material by following percentage：The class g cement 30% of A Erbo boards 525, the quartz sand 15%, step of 40~100 mesh Ceramic particle 53%, the sincere work(building materials WRA-2 types polycarboxylate water-reducer 0.2%, Beijing of the silicon ash 1.5%, Shenzhen of 5000 mesh that A is obtained The defoamer 0.3% of city Chao Hengyuan chemical plant production；
C, the raw material that step B is obtained all are poured into mixer in addition to ceramic particle, added equivalent to cement amount 23% Stirred after water 8 minutes and form cement mortar, ceramic waste residue concrete grout is mixing uniformly to form after then adding ceramic particle Material；
D, the ceramic waste residue concrete slurry for obtaining step C are poured into product mold, can the demoulding after placing 24 hours；
Clear water is steeped after E, the demoulding to conserve 7 days.
CN201710012884.6A 2017-01-09 2017-01-09 Method for producing concrete product from ceramic waste residues Pending CN106699067A (en)