CN106699063A - 一种低灰砂比电瓷专用胶合剂 - Google Patents

一种低灰砂比电瓷专用胶合剂 Download PDF

Info

Publication number
CN106699063A
CN106699063A CN201611259978.5A CN201611259978A CN106699063A CN 106699063 A CN106699063 A CN 106699063A CN 201611259978 A CN201611259978 A CN 201611259978A CN 106699063 A CN106699063 A CN 106699063A
Authority
CN
China
Prior art keywords
parts
cement
sand
adhesive
ratio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611259978.5A
Other languages
English (en)
Inventor
姚绍明
薛征峰
罗汉英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHONGQING GEPAI ELECTRIC PORCELAIN Co Ltd
Original Assignee
CHONGQING GEPAI ELECTRIC PORCELAIN Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHONGQING GEPAI ELECTRIC PORCELAIN Co Ltd filed Critical CHONGQING GEPAI ELECTRIC PORCELAIN Co Ltd
Priority to CN201611259978.5A priority Critical patent/CN106699063A/zh
Publication of CN106699063A publication Critical patent/CN106699063A/zh
Pending legal-status Critical Current

Abstract

本发明一种低灰砂比电瓷专用胶合剂，涉及到绝缘子生产用料，由以下质量份的组分混合构成：白色硅酸盐水泥80～120份，胶装石英砂100～150份，自来水30～40份，减水剂0.3～0.5份。改变了组分中的灰砂比，将砂的比例大幅度提高，灰砂比为1：0.8～1.5，将可以得到两个明显的效果：一是胶合剂的收缩率低，而抗压强度基本保持不变；二是胶合剂的成本大为降低，价格上砂比水泥低廉很多。该胶合剂已成功运用于生产中，稳定性较好，运行良好。

Description

一种低灰砂比电瓷专用胶合剂
技术领域
本发明涉及一种绝缘子生产用料，具体涉及一种在抗压强度保持不变的条件下收缩率低的胶合剂的配方。
背景技术
电工陶瓷简称电瓷。广义而言，电瓷涵盖了各种电工用陶瓷制品，包括绝缘用陶瓷、半导体陶瓷等等。侠义的电瓷仅指以铝矾土、高岭土、长石等天然矿物为主要原料经高温烧制而成的一类应用于电力工业系统的瓷绝缘子，包括各种线路绝缘子和电站电器用绝缘子，以及其它带电体隔离或支持用的绝缘部件。电瓷是电力工业的重要基础器件，是应用于电力系统中主要起支持和绝缘作用的部件，有时兼做其它电气部件的容器。因此，对其机械性能、电气性能、耐环境性能(冷热、抗污秽、老化等)有较高的要求。
电瓷胶合剂是电瓷产品的重要组成部分，它起着将瓷件与金属附件结成一整体的作用。现有技术中，在传统电瓷胶合剂中的灰砂比为2：1，高灰砂比能产生高的抗折强度，但也带来了较高的收缩率。在电瓷行业中，电瓷胶合剂的高收缩率会导致产品在运行过程中性能下降，例如钢脚松动。
发明内容
本发明的目的在于提供一种低灰砂比电瓷专用胶合剂，用于降低胶合剂的收缩率，保持抗压强度不变。
为达到上述目的，本发明的技术方案是：一种低灰砂比电瓷专用胶合剂，由以下质量份的组分混合构成：白色硅酸盐水泥80～120份，胶装石英砂100～150份，自来水30～40份，减水剂0.3～0.5份。
采用上述技术方案时，改变了组分中的灰砂比，将砂的比例大幅度提高，灰砂比为1：0.8～1.5，将可以得到两个明显的效果：一是胶合剂的收缩率低，而抗压强度基本保持不变；二是胶合剂的成本大为降低，价格上砂比水泥低廉很多。该胶合剂已成功运用于生产中，稳定性较好，运行良好。
进一步改进方案，由以下质量份的组分混合构成：白色硅酸盐水泥80份，胶装石英砂100份，自来水30份，减水剂0.3份。
进一步改进方案，由以下质量份的组分混合构成：白色硅酸盐水泥120份，胶装石英砂150份，自来水40份，减水剂0.5份。
进一步改进方案，由以下质量份的组分混合构成：白色硅酸盐水泥100份，胶装石英砂120份，自来水35份，减水剂0.4份。
具体实施方式
实施例1
本发明一种低灰砂比电瓷专用胶合剂，由以下质量份的组分混合构成：白色硅酸盐水泥80份，胶装石英砂100份，自来水30份，减水剂0.3份。
实施例1胶合剂检验数据
其中，灰砂比指白色硅酸盐水泥和胶装石英砂的质量份数比。水灰比指白色硅酸盐水泥和自来水的质量份数比。
实施例2
本发明一种低灰砂比电瓷专用胶合剂，由以下质量份的组分混合构成：白色硅酸盐水泥120份，胶装石英砂150份，自来水40份，减水剂0.5份。
实施例2胶合剂检验数据
其中，灰砂比指白色硅酸盐水泥和胶装石英砂的质量份数比。水灰比指白色硅酸盐水泥和自来水的质量份数比。
实施例3
本发明一种低灰砂比电瓷专用胶合剂，由以下质量份的组分混合构成：白色硅酸盐水泥100份，胶装石英砂120份，自来水35份，减水剂0.4份。
实施例3胶合剂检验数据
其中，灰砂比指白色硅酸盐水泥和胶装石英砂的质量份数比。水灰比指白色硅酸盐水泥和自来水的质量份数比。
以上所述的仅是本发明的优选实施方式，应当指出，对于本领域的技术人员来说，在不脱离本发明构思的前提下，还可以作出若干变形和改进，这些也应该视为本发明的保护范围，这些都不会影响本发明实施的效果和专利的实用性。本发明所省略描述的技术、形状、构造部分均为公知技术。

Claims (4)

1.一种低灰砂比电瓷专用胶合剂，其特征在于，由以下质量份的组分混合构成：白色硅酸盐水泥80～120份，胶装石英砂100～150份，自来水30～40份，减水剂0.3～0.5份。
2.根据权利要求1所述的一种低灰砂比电瓷专用胶合剂，其特征在于，由以下质量份的组分混合构成：白色硅酸盐水泥80份，胶装石英砂100份，自来水30份，减水剂0.3份。
3.根据权利要求1所述的一种低灰砂比电瓷专用胶合剂，其特征在于，由以下质量份的组分混合构成：白色硅酸盐水泥120份，胶装石英砂150份，自来水40份，减水剂0.5份。
4.根据权利要求1所述的一种低灰砂比电瓷专用胶合剂，其特征在于，由以下质量份的组分混合构成：白色硅酸盐水泥100份，胶装石英砂120份，自来水35份，减水剂0.4份。
CN201611259978.5A 2016-12-30 2016-12-30 一种低灰砂比电瓷专用胶合剂 Pending CN106699063A (zh)