CN106674763A - 一种空调压缩机三元乙丙橡胶三层垫配方 - Google Patents
一种空调压缩机三元乙丙橡胶三层垫配方 Download PDFInfo
- Publication number
- CN106674763A CN106674763A CN201611146360.8A CN201611146360A CN106674763A CN 106674763 A CN106674763 A CN 106674763A CN 201611146360 A CN201611146360 A CN 201611146360A CN 106674763 A CN106674763 A CN 106674763A
- Authority
- CN
- China
- Prior art keywords
- parts
- formula
- accelerant
- ethylene
- accelerator
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种空调压缩机三元乙丙橡胶三层垫配方,该配方包括有三元乙丙橡胶120份、N550炭黑50份、N990炭黑30份、硅藻土20份、环保石蜡油30份、环保氧化锌3份、硬脂酸1份、硫磺0.5份、促进剂TP/S 2份、促进剂ZBEC 0.7份、促进剂MBT0.8份、RN75抗静电剂1份、发泡剂1份、防老剂RD 2份,合计262份;本发明全部使用环保体系,无毒害,N990炭黑的使用提高了制品的弹性与减震效果,硅藻土的使用降低了三层垫制品使用过程的生热问题,环保促进剂TP/S,ZBEC提高了胶料的交联程度,耐热性,提高了制品的压缩永久变形性能,可以替代价格昂贵的硅胶垫使用。
Description
技术领域
本发明涉及橡胶技术领域,尤其涉及一种空调压缩机三元乙丙橡胶三层垫配方。
背景技术
三元乙丙橡胶是乙烯、丙烯和少量的非共轭二烯烃的共聚物,是乙丙橡胶的一种,其耐臭氧、耐热、耐候等耐老化性能优异,可广泛用于汽车部件、建筑用防水材料、电线电缆护套、耐热胶管、胶带、汽车密封件等领域,目前大多数空调压缩机的垫板也采用硅胶垫,但是,传统三元乙丙橡胶的弹性和减震效果不够理想,因此,解决这一类的问题显得尤为重要。
发明内容
针对现有技术的不足,本发明提供了一种空调压缩机三元乙丙橡胶三层垫配方,通过本发明制得的胶三层垫有着很好的弹性和减震效果。
为了解决上述问题,本发明提供了一种空调压缩机三元乙丙橡胶三层垫配方,该配方包括有:三元乙丙橡胶120-175份、N550炭黑50-70份、N990炭黑30-40份、硅藻土20-30份、环保石蜡油30-50份、环保氧化锌3-7份、硬脂酸1份、硫磺0.5份、促进剂TP/S 2份、促进剂ZBEC 0.7份、促进剂MBT0.8份、RN75抗静电剂1-8份、发泡剂1-4份、防老剂RD 2份。
进一步改进在于:该配方包括有三元乙丙橡胶150份、N550炭黑60份、N990炭黑35份、硅藻土25份、环保石蜡油40份、环保氧化锌5份、硬脂酸1份、硫磺0.5份、促进剂TP/S 2份、促进剂ZBEC 0.7份、促进剂MBT0.8份、RN75抗静电剂4份、发泡剂2份、防老剂RD 2份。
进一步改进在于:所述发泡剂碳酸氢钠或偶氮二甲酰胺。
本发明的有益效果是:本发明全部使用环保体系,无毒害,N990炭黑的使用提高了制品的弹性与减震效果,硅藻土的使用降低了三层垫制品使用过程的生热问题,环保促进剂TP/S,ZBEC提高了胶料的交联程度,耐热性,提高了制品的压缩永久变形性能,可以替代价格昂贵的硅胶垫使用。
具体实施方式
为了加深对本发明的理解,下面将结合实施例对本发明做进一步详述,本实施例仅用于解释本发明,并不构成对本发明保护范围的限定。
实施例一
本发明提供了一种空调压缩机三元乙丙橡胶三层垫配方,该配方包括有三元乙丙橡胶120份、N550炭黑50份、N990炭黑30份、硅藻土20份、环保石蜡油30份、环保氧化锌3份、硬脂酸1份、硫磺0.5份、促进剂TP/S 2份、促进剂ZBEC 0.7份、促进剂MBT0.8份、RN75抗静电剂1份、发泡剂1份、防老剂RD 2份,合计262份。所述发泡剂碳酸氢钠或偶氮二甲酰胺。
实施例二
本发明提供了一种空调压缩机三元乙丙橡胶三层垫配方,该配方包括有三元乙丙橡胶175份、N550炭黑70份、N990炭黑40份、硅藻土30份、环保石蜡油50份、环保氧化锌7份、硬脂酸1份、硫磺0.5份、促进剂TP/S 2份、促进剂ZBEC 0.7份、促进剂MBT0.8份、RN75抗静电剂8份、发泡剂4份、防老剂RD 2份,合计391份。所述发泡剂碳酸氢钠或偶氮二甲酰胺。
实施例三
本发明提供了一种空调压缩机三元乙丙橡胶三层垫配方,该配方包括有三元乙丙橡胶150份、N550炭黑60份、N990炭黑35份、硅藻土25份、环保石蜡油40份、环保氧化锌5份、硬脂酸1份、硫磺0.5份、促进剂TP/S 2份、促进剂ZBEC 0.7份、促进剂MBT0.8份、RN75抗静电剂4份、发泡剂2份、防老剂RD 2份,合计328份。所述发泡剂碳酸氢钠或偶氮二甲酰胺。
本发明全部使用环保体系,无毒害,N990炭黑的使用提高了制品的弹性与减震效果,硅藻土的使用降低了三层垫制品使用过程的生热问题,环保促进剂TP/S,ZBEC提高了胶料的交联程度,耐热性,提高了制品的压缩永久变形性能,可以替代价格昂贵的硅胶垫使用。
Claims (3)
1.一种空调压缩机三元乙丙橡胶三层垫配方,其特征在于,该配方包括有:三元乙丙橡胶120-175份、N550炭黑50-70份、N990炭黑30-40份、硅藻土20-30份、环保石蜡油30-50份、环保氧化锌3-7份、硬脂酸1份、硫磺0.5份、促进剂TP/S 2份、促进剂ZBEC 0.7份、促进剂MBT0.8份、RN75抗静电剂1-8份、发泡剂1-4份、防老剂RD 2份。
2.如权利要求1所述的一种空调压缩机三元乙丙橡胶三层垫配方,其特征在于:该配方包括有三元乙丙橡胶150份、N550炭黑60份、N990炭黑35份、硅藻土25份、环保石蜡油40份、环保氧化锌5份、硬脂酸1份、硫磺0.5份、促进剂TP/S 2份、促进剂ZBEC 0.7份、促进剂MBT0.8份、RN75抗静电剂4份、发泡剂2份、防老剂RD 2份。
3.如权利要求1和2任意所述的一种空调压缩机三元乙丙橡胶三层垫配方,其特征在于:所述发泡剂碳酸氢钠或偶氮二甲酰胺。