CN1066641A - Coloured glass tile and production technique thereof - Google Patents
Coloured glass tile and production technique thereof Download PDFInfo
- Publication number
- CN1066641A CN1066641A CN 91106109 CN91106109A CN1066641A CN 1066641 A CN1066641 A CN 1066641A CN 91106109 CN91106109 CN 91106109 CN 91106109 A CN91106109 A CN 91106109A CN 1066641 A CN1066641 A CN 1066641A
- Authority
- CN
- China
- Prior art keywords
- glass
- agglutinant
- minutes
- time
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of architectural decoration coloured glass tile, the surface of buildings and ground decoration generally are to adopt ceramic tile or glass Mosaic at present, the dull coloring of these two kinds of article, and since production technique and intensity own limit, can not the production bulk, very hard so inlay, production technique is more complicated also, and cost is higher.Coloured glass tile provided by the invention is spraying one deck glass pigment agglutinant on glass basis, forms through high bake then.This coloured glass tile production technique is simple, and cost is low, and surface-brightening, and is bright in luster, and intensity is big, be difficult for broken, can the production bulk, be easier to so inlay.
Description
The present invention relates to a kind of architectural decoration coloured glass tile and production technique thereof.
The decoration on building wall and ground generally is to adopt ceramic tile or glass Mosaic at present, and the piece of glass Mosaic is little, so inlay inconvenience, the surface of glass Mosaic is brightless, and dull coloring is so outward appearance is very not attractive in appearance, and because being shaped as of its section is inner small and outside big, so be easy to come off, the product percent of pass of ceramic tile is lower, the production cost height, though piece is big, but shaky, frangible, the production technique of glass Mosaic and ceramic tile is more complicated all.
The object of the present invention is to provide a kind of building decorative material-coloured glass tile and production technique thereof, it can overcome existing shortcoming in the prior art.
The object of the present invention is achieved like this: coloured glass tile is to make matrix with glass, is coated with the glass agglutinant on its surface, forms through high bake, and its section form is trapezoidal, and interior big, outer little, the production technique of coloured glass tile is as follows:
One, peach latex and water are pressed 1-2.5: 100 mixed, make agglutinant.
Two, with above-mentioned agglutinant and glass pigment in 5-15: 100 ratio is mixed into glass pigment agglutinant.
Three, the glass pigment agglutinant of working good is sprayed on glass surface, required thickness is at the 0.1-0.2 millimeter.
Four, it is roasting that the glass that the surface is coated with glass pigment agglutinant is gone into kilning, and whole bake process is divided into three phases:
1, the temperature rise period, the time is 15-25 minute, and temperature is increased to 600 ℃ from envrionment temperature.
2, holding stage, the time is 30 minutes, temperature is 600 ℃.
3, temperature-fall period, the time is 55-65 minute, temperature is reduced to envrionment temperature from 600 ℃.
Five, kiln temperature gets final product kiln discharge below reducing to the environment temperature.
Coloured glass tile surface-brightening provided by the present invention, color glow, and also intensity is big, and non-friable, can make bigger piece, inlay easily, and also difficult drop-off, coloured glass tile production technique of the present invention is simple, and cost is low.
Below in conjunction with implementation column and accompanying drawing thereof, the present invention is done further detailed narration.
Fig. 1 is the sectional schematic diagram of coloured glass tile of the present invention.
The glass basis section of coloured glass tile is shown in Figure 1 trapezoidal, interior big, outer little, and ash mouthful is left in the centre.Because above-mentioned this shape and structure, so can not come off, 1 is coloured glass tile among the figure, and 2 is the ash mouth, and 3 is wall.
The production technique of coloured glass tile is provided by following examples:
Embodiment one
1, in 1: 100 ratio peach latex and water are mixed into agglutinant.
2, the ratio of agglutinant and glass pigment is 12: 100, makes glass pigment agglutinant.
3, glass pigment agglutinant is sprayed on the glass basis surface, its thickness is the 0.1-0.2 millimeter.
4, baking, envrionment temperature is 28 ℃, kiln temperature was increased to 600 ℃ in 15 minutes, was incubated 15 minutes, began cooling then, reduced to below the envrionment temperature at 55 minutes.
5, kiln discharge.
Embodiment two
1, the ratio of peach latex and water is 2.5: 100, makes agglutinant.
2, the ratio of agglutinant and glass pigment I be 15: 100, make glass pigment agglutinant.
3, spraying, thickness requirement 0.1-0.2 millimeter.
4, baking, envrionment temperature is 20 ℃.
Heating-up time is 25 minutes;
Soaking time is 30 minutes;
Temperature fall time is 65 minutes.
5, kiln discharge.
Embodiment three
1, the ratio of peach latex and water is 1.7: 100.
2, the ratio of agglutinant and glass pigment is 5: 100 in the glass pigment agglutinant.
3, spraying, thickness requirement 0.1-0.2 millimeter.
4, baking, envrionment temperature is 25 ℃.
Heating-up time is 20 minutes;
Soaking time is 30 minutes;
Temperature fall time is 60 minutes.
5, kiln discharge.
Claims (5)
1, a kind of coloured glass tile is made matrix with glass, and the section form that it is characterized in that glass basis is trapezoidal, and the surface is coated with the glass agglutinant, forms through high bake.
2, a kind of coloured glass tile production technique is characterized in that its technical process is as follows:
One, peach latex and water are pressed 1-2.5: 100 mixed, make agglutinant.
Two, with above-mentioned agglutinant and glass pigment in 5-15: 100 ratio is mixed into glass pigment agglutinant.
Three, the glass pigment agglutinant of working good is sprayed on glass surface, required thickness is at the 0.1-0.2 millimeter.
Four, it is roasting that the glass that the surface is coated with glass pigment agglutinant is gone into kilning, and whole bake process is divided into three phases:
(1), the temperature rise period, the time is 15-25 minute, temperature is increased to 600 ℃ from envrionment temperature;
(2), holding stage, the time is 30 minutes, temperature is 600 ℃;
(3), temperature-fall period, the time is 55-65 minute, temperature is reduced to below the envrionment temperature from 600 ℃;
Five, kiln discharge.
3, coloured glass tile production technique according to claim 2 is characterized in that:
One, the ratio of peach latex and water is 1: 100
Two, the ratio of agglutinant and glass pigment is 12: 100
Three, baking
Heating-up time is 15 minutes
Soaking time is 30 minutes
Between producing during cooling is 55 minutes.
4, coloured glass tile production technique according to claim 2 is characterized in that:
One, the ratio of peach latex and water is 2.5: 100
Two, the ratio of agglutinant and water is 15: 100
Three, baking
Heating-up time is 25 minutes
Soaking time is 30 minutes
Temperature fall time is 65 minutes.
5, coloured glass tile production technique according to claim 2 is characterized in that:
One, the ratio of peach latex and water is 1.7: 100
Two, the ratio of agglutinant and water is 5: 100
Three, baking
Heating-up time is 20 minutes
Soaking time is 30 minutes
Temperature fall time is 60 minutes.