CN1055278C - Method for making colour glaze natural leaf figure ceramic product - Google Patents
Method for making colour glaze natural leaf figure ceramic product Download PDFInfo
- Publication number
- CN1055278C CN1055278C CN 96111457 CN96111457A CN1055278C CN 1055278 C CN1055278 C CN 1055278C CN 96111457 CN96111457 CN 96111457 CN 96111457 A CN96111457 A CN 96111457A CN 1055278 C CN1055278 C CN 1055278C
- Authority
- CN
- China
- Prior art keywords
- leaf
- coat enamel
- glaze
- natural
- ground
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses a method for making color glaze natural leaf pattern ceramics. Natural leaves or plant leaves are stuck to a blank coated with base glaze after particularly treated, and a layer of surface glaze is coated on the blank. Then, the blank is put in a kiln to be burned to obtain a ceramic finished product. The present invention uses ceramics as a carrier, and natural leaf patterns are burned on the ceramics. The leaf patterns are clear, natural and vivid and have beauty sense and very high appreciation and collection value. The present invention has no particular requirements for conditions of the base glaze, the blank, combusting atmospheres, etc. and has the advantages of simple preparation process and easy operation.
Description
The present invention relates to ceramic, especially relate to a kind of method for making colour glaze natural leaf figure ceramic product.
The coloured glaze pottery occupies great proportion in Production of Ceramics, it is wide in variety, rich color, with a long history, but the coloured glaze pottery exists great limitation on performance concrete image and content, it is difficult to image is done careful delineation, thus the coloured glaze pottery of seeing usually be thick lines, arbitrarily, the pattern of irregularity.
The object of the present invention is to provide a kind of be carrier with the pottery, be manifestation with the coloured glaze, be method of producing, finally obtain the natural leaf line pottery of the coloured glaze of nature natural leaf line pattern true to nature processing and fabricating method with natural leaf.
The object of the present invention is achieved like this:
One, processing and fabricating method of the present invention:
1, plucks natural leaf or leaf;
2, remove the chlorophyll of leaf;
(3) preparation ground-coat enamel;
(4) the preparation cover-coat enamel different with the ground-coat enamel color;
(5) on the embryo of moulding, execute ground-coat enamel;
(6) leaf is attached on the vessel of executing ground-coat enamel;
(7) execute one deck cover-coat enamel again;
(8) vessel of executing cover-coat enamel are put into kiln and fire, promptly get the ceramic product of natural leaf line.
Two, the prescription of cover-coat enamel (by weight percentage) is:
Feldspar: 7～13% quartz: 3～10% porcelain mud: 20～30%
Glaze fruit: 20～30% glaze ashes, 15～25% colorants: 3～7%
Three, remove chlorophyllous method and have three kinds:
First kind: boiled natural leaf 20～30 minutes with rice washing water, take out the back and brush away chlorophyll with hairbrush;
Second kind: add 40 parts of natural leaves of poach 20～30 minutes with 1 part of caustic soda, take out the back and brush away chlorophyll with hairbrush;
The third: the natural leaf that is soaked in water brushes away chlorophyll to rotting, take out the back with hairbrush.
The present invention is carrier with the pottery, be manifestation with the coloured glaze, be method of producing with natural leaf, the natural leaf line of the coloured glaze of producing pottery, Ye Wen is clear, natural, true to nature, is rich in aesthetic feeling, and can produce shades of colour as required.This ceramic is given a kind of novelty of people, elegance, the unique sensation that clears away heart-fire, and has very high appreciation reserve value.The present invention all has no special requirements to the prescription of the prescription of mold, ground-coat enamel and moulding, combustion atmosphere etc., has that manufacture craft is simple, the advantage of processing ease.
Below in conjunction with embodiment the present invention is described in further detail.
Embodiment one:
With at the bottom of making cyan, yellow leaf line is example.
1, plucks natural leaf;
2, leaf is put into pot and added rice washing water and boiled 30 minutes, take out the back and brushes away chlorophyll with hairbrush;
3, preparation cyan ground-coat enamel: take by weighing rhombspar 7 and restrain, glaze fruit 90 grams, bright material 3 grams of pearl, levigate standby after mixing;
4, prepare cover-coat enamel: take by weighing feldspar 13 grams, quartzy 10 grams, porcelain mud 30 grams, glaze really 20 grams, glaze ash 20 grams, titanium 7 grams, the mixing back is levigate standby;
5, on the embryo of moulding, execute the cyan ground-coat enamel;
6, leaf is attached on the vessel of executing the cyan ground-coat enamel;
7, execute one deck cover-coat enamel again;
8, the vessel of executing cover-coat enamel are put into kiln and fire, can obtain a pottery that in the cyan glaze, shows a slice or several pieces yellow natural leaf lines.
Embodiment two:
At the bottom of making black, the green leaf line is an example.
1, plucks natural plant leaves;
2, get 500 gram caustic soda and add in 20 kg water, leaf is put into wherein boiled 20 minutes again, take out the back and brush away chlorophyll with hairbrush;
3, preparation black ground-coat enamel: take by weighing ferric oxide 40.2 grams, manganese oxide 20 grams, glaze really 30 grams, glaze ash 9.8 grams, levigate standby after mixing;
4, prepare cover-coat enamel: take by weighing feldspar 7 grams, quartzy 3 grams, porcelain mud 30 grams, glaze really 30 grams, glaze ash 25 grams, cupric chloride 5 grams, the mixing back is levigate standby.
5, on the embryo of moulding, execute the black ground-coat enamel;
6, leaf is attached on the vessel of executing the black ground-coat enamel;
7, execute one deck cover-coat enamel again;
8, the vessel of executing cover-coat enamel are put into kiln and fire, can obtain a pottery that in the black glaze, presents a slice or several pieces green natural leaf lines.
Embodiment three:
With make the red end, blue leaf line is an example.
1, plucks natural leaf.
2, be soaked in water leaf to rotting, take out the back and brush away chlorophyll with hairbrush.
3, prepare red ground-coat enamel: take by weighing copper and spend 10 grams, hydrophite 60 grams, glass 30 grams, levigate standby after mixing.
4, prepare cover-coat enamel: take by weighing feldspar 12 grams, quartzy 8 grams, porcelain mud 28 grams, glaze really 30 grams, glaze ash 15 grams, cobalt 7 grams, the mixing back is levigate standby.
5, on the embryo of moulding, execute red ground-coat enamel;
6, leaf is attached on the vessel of executing red ground-coat enamel;
7, execute one deck cover-coat enamel again;
8, the vessel of executing cover-coat enamel are put into kiln and fire, can obtain a pottery that in red glaze, shows a slice or several pieces blue natural leaf lines.
Claims (2)
1, a kind of method for making colour glaze natural leaf figure ceramic product is characterized in that:
(1) plucks natural leaf or leaf;
(2) remove the chlorophyll of leaf;
(3) preparation ground-coat enamel;
(4) the preparation cover-coat enamel different with the ground-coat enamel color;
(5) on the embryo of moulding, execute ground-coat enamel;
(6) leaf is attached on the vessel of executing ground-coat enamel;
(7) execute one deck cover-coat enamel again;
(8) vessel of executing cover-coat enamel are put into kiln and fire, promptly get the ceramic product of natural leaf line.
2, a kind of method for making colour glaze natural leaf figure ceramic product as claimed in claim 1 is characterized in that: the prescription of cover-coat enamel (by weight percentage) is:
Feldspar: 7～13% quartz: 3～10% porcelain mud: 20～30%
Glaze fruit: 20～30% glaze ashes, 15～25% colorants: 3～7%