CN106633931A - Plastic product and preparation method thereof - Google Patents
Plastic product and preparation method thereof Download PDFInfo
- Publication number
- CN106633931A CN106633931A CN201611100878.8A CN201611100878A CN106633931A CN 106633931 A CN106633931 A CN 106633931A CN 201611100878 A CN201611100878 A CN 201611100878A CN 106633931 A CN106633931 A CN 106633931A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic products
- agent
- paraffin
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a plastic product and a preparation method thereof. The plastic product is prepared from the following formula ingredients in parts by mass: 11 to 13 parts of polyethylene terephthalate, 1 to 3 parts of hardening agents, 3 to 5 parts of polycarbonate, 5 to 7 parts of mountain flour, 6 to 8 parts of low molecular weight acrylic acid co-polymers, 1 to 2 parts of reinforcing agents, 1 to 3 parts of wire drawing powder materials, 12 to 14 parts of paraffin, 1 to 3 parts of coupling agents, 1 to 3 parts of stearic acid, 1 to 3 parts of antistatic agents, 6 to 8 parts of zinc silicate, 2 to 4 parts of environment-friendly plasticizing agents and 1 to 3 parts of calcium carbonate. The plastic product has the advantages that the formula is simple; the implementation is easy; the cost is very low; the prepared flat silk has higher stretch intensity, and can be used for preparing the plastic product; the manufacturing cost of the plastic product is reduced.
Description
Technical field
The present invention relates to plastic material field, in particular to a kind of plastic products and preparation method thereof.
Background technology
Polywoven Bag is mainly made up of woven cloth, and woven cloth is formed by flat filament longitude and latitude weaving, wherein the property of flat filament
Decisive role can be played to the application of Polywoven Bag.Flat filament by polypropylene or polyethylene and various auxiliary agent Jing melting extrusions into
Film, segmentation after-drawing shaping are made.Flat filament has higher tensile strength, can effectively prevent fracture of wire during braiding, makes
Woven bag toughness is high, intensity is high, it is durable.The consumption of polypropylene and polyethylene is big needed in prior art prepared by flat filament,
It is relatively costly.But the tensile strength of polypropylene and polyethylene is limited, need to add drawing of the various auxiliary combinations to improve flat filament
Intensity is stretched, causes dispensing complicated components, enforcement difficulty big, relatively costly.
The content of the invention
The invention provides a kind of plastic products and preparation method thereof, inventive formulation is simple, easily enforcement, and cost is extremely low,
And made by flat filament tensile strength it is higher, can be used in preparing plastic products, reduce the manufacturing cost of plastic products.
For achieving the above object, the present invention provides following technical scheme：
A kind of plastic products and preparation method thereof, are made up of following mass fraction formula components：Poly terephthalic acid second two
Ester 11-13 parts, curing agent 1-3 parts, Merlon 3-5 parts, stone flour 5-7 parts, low molecular weight propylene acid copolymer 6-8 parts, enhancing
Agent 1-2 parts, wire drawing powder 1-3 parts, paraffin 12-14 parts, coupling agent 1-3 parts, stearic acid 1-3 parts, antistatic additive 1-3 parts, silicic acid
Zinc 6-8 parts, environmentally friendly class plasticizer 2-4 parts, calcium carbonate 1-3 parts.
Further：It is made up of following mass fraction formula components：It is 11 parts of PET, 1 part of curing agent, poly-
3 parts of carbonic ester, 5 parts of stone flour, 6 parts of low molecular weight propylene acid copolymer, 1 part of reinforcing agent, 1 part of wire drawing powder, 12 parts of paraffin, coupling
1 part of agent, 1 part of stearic acid, 1 part of antistatic additive, 6 parts of zinc silicate, environmentally friendly 2 parts of class plasticizer, 1 part of calcium carbonate.
Further：It is made up of following mass fraction formula components：It is 12 parts of PET, 2 parts of curing agent, poly-
4 parts of carbonic ester, 6 parts of stone flour, 7 parts of low molecular weight propylene acid copolymer, 1.5 parts of reinforcing agent, 2 parts of wire drawing powder, 13 parts of paraffin, idol
2 parts of agent of connection, 2 parts of stearic acid, 2 parts of antistatic additive, 7 parts of zinc silicate, environmentally friendly 3 parts of class plasticizer, 2 parts of calcium carbonate.
Further：It is made up of following mass fraction formula components：It is 13 parts of PET, 3 parts of curing agent, poly-
5 parts of carbonic ester, 7 parts of stone flour, 8 parts of low molecular weight propylene acid copolymer, 2 parts of reinforcing agent, 3 parts of wire drawing powder, 14 parts of paraffin, coupling
3 parts of agent, 3 parts of stearic acid, 3 parts of antistatic additive, 8 parts of zinc silicate, environmentally friendly 4 parts of class plasticizer, 3 parts of calcium carbonate.
Further：Preparation method of the present invention has following steps：
Step one, various raw materials are mixed by proportioning, stirred, and stirred to 150～202 DEG C of material temperature；
Step 2, stirring cooling material reduce mixing speed, are kept stirring for, and make material temperature be down to 40～50 DEG C；
Step 3, extruder have plastified fused materials equably to be sent into calender and is rolled into after required form and cool to normal temperature
.
The invention has the beneficial effects as follows：
1st, inventive formulation simply, is easily implemented, and cost is extremely low；
2 and made by flat filament tensile strength it is higher, can be used in preparing plastic products, reduce being manufactured into for plastic products
This.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than the embodiment of whole.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment one：
A kind of plastic products are made up of following mass fraction formula components：PET 11-13 parts, hardening
Agent 1-3 parts, Merlon 3-5 parts, stone flour 5-7 parts, low molecular weight propylene acid copolymer 6-8 parts, reinforcing agent 1-2 parts, wire drawing powder
Material 1-3 parts, paraffin 12-14 parts, coupling agent 1-3 parts, stearic acid 1-3 parts, antistatic additive 1-3 parts, zinc silicate 6-8 parts, environmentally friendly class
Plasticizer 2-4 parts, calcium carbonate 1-3 parts.
Embodiment two：
A kind of plastic products are made up of following mass fraction formula components：11 parts of PET, curing agent 1
Part, 3 parts of Merlon, 5 parts of stone flour, 6 parts of low molecular weight propylene acid copolymer, 1 part of reinforcing agent, 1 part of wire drawing powder, paraffin 12
Part, 1 part of coupling agent, 1 part of stearic acid, 1 part of antistatic additive, 6 parts of zinc silicate, environmentally friendly 2 parts of class plasticizer, 1 part of calcium carbonate.
Embodiment three：
A kind of plastic products are made up of following mass fraction formula components：12 parts of PET, curing agent 2
Part, 4 parts of Merlon, 6 parts of stone flour, 7 parts of low molecular weight propylene acid copolymer, 1.5 parts of reinforcing agent, 2 parts of wire drawing powder, paraffin 13
Part, 2 parts of coupling agent, 2 parts of stearic acid, 2 parts of antistatic additive, 7 parts of zinc silicate, environmentally friendly 3 parts of class plasticizer, 2 parts of calcium carbonate.
Example IV：
A kind of plastic products are made up of following mass fraction formula components：13 parts of PET, curing agent 3
Part, 5 parts of Merlon, 7 parts of stone flour, 8 parts of low molecular weight propylene acid copolymer, 2 parts of reinforcing agent, 3 parts of wire drawing powder, paraffin 14
Part, 3 parts of coupling agent, 3 parts of stearic acid, 3 parts of antistatic additive, 8 parts of zinc silicate, environmentally friendly 4 parts of class plasticizer, 3 parts of calcium carbonate.
Embodiment five：
A kind of preparation method preparation method of plastic products comprises the steps：
Step one, various raw materials are mixed by proportioning, stirred, and stirred to 150～202 DEG C of material temperature；
Step 2, stirring cooling material reduce mixing speed, are kept stirring for, and make material temperature be down to 40～50 DEG C；
Step 3, extruder have plastified fused materials equably to be sent into calender and is rolled into after required form and cool to normal temperature
.
Moreover, it will be appreciated that although this specification is been described by according to embodiment, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity those skilled in the art should
Using specification as an entirety, the technical scheme in each embodiment can also Jing it is appropriately combined, form those skilled in the art
Understandable other embodiment.
Claims (5)
1. a kind of plastic products, it is characterised in that：It is made up of following mass fraction formula components：
PET 11-13 parts, curing agent 1-3 parts, Merlon 3-5 parts, stone flour 5-7 parts, low-molecular-weight third
Olefin(e) acid copolymer 6-8 parts, reinforcing agent 1-2 parts, wire drawing powder 1-3 parts, paraffin 12-14 parts, coupling agent 1-3 parts, stearic acid 1-3
Part, antistatic additive 1-3 parts, zinc silicate 6-8 parts, environmentally friendly class plasticizer 2-4 parts, calcium carbonate 1-3 parts.
2. a kind of plastic products according to claim 1, it is characterised in that：It is made up of following mass fraction formula components：
11 parts of PET, 1 part of curing agent, 3 parts of Merlon, 5 parts of stone flour, low molecular weight propylene acid copolymer
6 parts, 1 part of reinforcing agent, 1 part of wire drawing powder, 12 parts of paraffin, 1 part of coupling agent, 1 part of stearic acid, 1 part of antistatic additive, 6 parts of zinc silicate,
2 parts of environmentally friendly class plasticizer, 1 part of calcium carbonate.
3. a kind of plastic products according to claim 1, it is characterised in that：It is made up of following mass fraction formula components：
12 parts of PET, 2 parts of curing agent, 4 parts of Merlon, 6 parts of stone flour, low molecular weight propylene acid copolymer
7 parts, 1.5 parts of reinforcing agent, 2 parts of wire drawing powder, 13 parts of paraffin, 2 parts of coupling agent, 2 parts of stearic acid, 2 parts of antistatic additive, zinc silicate 7
Part, environmentally friendly 3 parts of class plasticizer, 2 parts of calcium carbonate.
4. a kind of plastic products according to claim 1, it is characterised in that：It is made up of following mass fraction formula components：
13 parts of PET, 3 parts of curing agent, 5 parts of Merlon, 7 parts of stone flour, low molecular weight propylene acid copolymer
8 parts, 2 parts of reinforcing agent, 3 parts of wire drawing powder, 14 parts of paraffin, 3 parts of coupling agent, 3 parts of stearic acid, 3 parts of antistatic additive, 8 parts of zinc silicate,
4 parts of environmentally friendly class plasticizer, 3 parts of calcium carbonate.
5. a kind of a kind of preparation method of plastic products according to claim 1, it is characterised in that：Comprise the steps：
Step one, various raw materials are mixed by proportioning, stirred, and stirred to 150～202 DEG C of material temperature；
Step 2, stirring cooling material reduce mixing speed, are kept stirring for, and make material temperature be down to 40～50 DEG C；
Step 3, extruder have plastified fused materials equably to be sent into calender and is rolled into after required form and cool to normal temperature i.e.
Can.