CN103254580A - Abrasion-resistant polyethylene glycol terephthalate molding plastic - Google Patents
Abrasion-resistant polyethylene glycol terephthalate molding plastic Download PDFInfo
- Publication number
- CN103254580A CN103254580A CN2013101681640A CN201310168164A CN103254580A CN 103254580 A CN103254580 A CN 103254580A CN 2013101681640 A CN2013101681640 A CN 2013101681640A CN 201310168164 A CN201310168164 A CN 201310168164A CN 103254580 A CN103254580 A CN 103254580A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear
- polyethylene terephthalate
- moulding compound
- compound according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an abrasion-resistant polyethylene glycol terephthalate molding plastic, and belongs to the technical field of high polymer materials. The abrasion-resistant polyethylene glycol terephthalate molding plastic comprises the following raw materials in parts by weight: 28 to 36 parts of polyethylene glycol terephthalate resin, 8 to 15 parts of uncrystallized polyester resin, 9 to 16 parts of olefin resin, 6 to 12 parts of compatilizer, 20 to 29 parts of filling material, 0.5 to 1.2 parts of antioxidant, 9 to 17 parts of reinforced fibers, 4 to 8 parts of an abrasion-resistant agent and 0.7 to 1.3 parts of carbon black. According to the testing, the abrasion-resistant polyethylene glycol terephthalate molding plastic has the following performance indexes: the tensile strength is from 165 to 178MPa; the bending strength is from 230 to 255MPa; the bending modulus is from 9000 to 12000MPa; the notch impact strength is from 67 to 88j/m; and the heat deflection temperature is from 205 to 226 DEG C. In addition, all the raw materials are wide in resource and low in cost.
Description
Technical field
The invention belongs to technical field of polymer materials, be specifically related to a kind of wear-resisting polyethylene terephthalate moulding compound.
Background technology
Because polyethylene terephthalate has excellent intensity and resistance toheat, thereby is widely used in fields such as automobile, electronics, machinery, instrument.But, because automotive field requires higher and more harsh to fatigue performance, resistance toheat and wear resisting property to this strength of materials, therefore common polyethylene terephthalate moulding compound also is difficult to adapt to this harsh requirement, must further improve its intensity, temperature tolerance etc. by modification.Chinese patent publication number CN102311616A discloses carbon fiber reinforced polyester, still, owing to raw material sources are restricted, thereby can not form scale production.In view of this, be necessary to be explored, the applicant does actively and good try has formed technical scheme described below finally for this reason.
Summary of the invention
Task of the present invention is to provide a kind of raw material sources extensively and cheap, as to have good intensity and wear-resisting effect wear-resisting polyethylene terephthalate moulding compound.
Task of the present invention is finished like this, a kind of wear-resisting polyethylene terephthalate moulding compound, and its raw material by following parts by weight is formed:
In one embodiment of the invention, described pet resin be fusing point at 260 ℃ and limiting viscosity index is the polyethylene terephthalate of 0.65dl/g.
In another embodiment of the present invention, described noncrystalline polyester resin is softening temperature at 130 ℃ saturated polyester resin.
In yet another embodiment of the present invention, described olefin resin is the Co-polypropylene resin of 170 ℃ of fusing points.
In another embodiment of the present invention, described compatilizer is the acrylic resin of maleic anhydride graft.
Also have among the embodiment of the present invention, described filler is polynite.
More of the present invention and among embodiment, described oxidation inhibitor is 2, the 5-ditert-butylhydro quinone.
In of the present invention and then embodiment, described fortifying fibre is the alkali free glass fibre of length 12mm.
Of the present invention again more and among embodiment, described anti-wear agent is graphite.
In again of the present invention and then embodiment, described carbon black is the carbon black that channel process is produced.
Wear-resisting polyethylene terephthalate moulding compound provided by the invention has following performance index after tested: tensile strength 165~178MPa, flexural strength 230~255MPa, modulus in flexure 9000~12000MPa, notched Izod impact strength 67~88j/m, 205~226 ℃ of heat-drawn wires; And all raw material sources are extensive and cheap.
Embodiment
Embodiment 1:
Embodiment 2:
Embodiment 3:
Embodiment 4:
The wear-resisting polyethylene terephthalate moulding compound that is obtained by above-described embodiment 1 to 4 has the technique effect shown in the following table after tested:
Test event | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 |
Tensile strength MPa | 166 | 170 | 173 | 178 |
Flexural strength MPa | 230 | 238 | 247 | 255 |
Modulus in flexure MPa | 9050 | 10280 | 11190 | 11960 |
Notched Izod impact strength j/m | 67.5 | 72.6 | 79.8 | 87.4 |
Heat-drawn wire ℃ | 206 | 213 | 219 | 225 |
Claims (10)
1. wear-resisting polyethylene terephthalate moulding compound is characterized in that its raw material by following parts by weight forms:
28~36 parts of pet resins;
8~15 parts of non-crystalline polyester resin;
9~16 parts of olefin resins;
6 ~ 12 parts of compatilizers;
20 ~ 29 parts of fillers;
0.5 ~ 1.2 part in oxidation inhibitor;
9 ~ 17 parts of fortifying fibres;
4 ~ 8 parts of anti-wear agents;
0.7 ~ 1.3 part of carbon black.
2. wear-resisting polyethylene terephthalate moulding compound according to claim 1 is characterized in that described pet resin be fusing point at 260 ℃ and limiting viscosity index is the polyethylene terephthalate of 0.65dl/g.
3. wear-resisting polyethylene terephthalate moulding compound according to claim 1 is characterized in that described noncrystalline polyester resin is softening temperature at 130 ℃ saturated polyester resin.
4. wear-resisting polyethylene terephthalate moulding compound according to claim 1 is characterized in that described olefin resin is the Co-polypropylene resin of 170 ℃ of fusing points.
5. wear-resisting polyethylene terephthalate moulding compound according to claim 1 is characterized in that described compatilizer is the acrylic resin of maleic anhydride graft.
6. wear-resisting polyethylene terephthalate moulding compound according to claim 1 is characterized in that described filler is polynite.
7. wear-resisting polyethylene terephthalate moulding compound according to claim 1 is characterized in that described oxidation inhibitor is 2,5-ditert-butylhydro quinone.
8. wear-resisting polyethylene terephthalate moulding compound according to claim 1 is characterized in that described fortifying fibre is the alkali free glass fibre of length 12mm.
9. wear-resisting polyethylene terephthalate moulding compound according to claim 1 is characterized in that described anti-wear agent is graphite.
10. wear-resisting polyethylene terephthalate moulding compound according to claim 1 is characterized in that described carbon black is the carbon black that channel process is produced.