CN106633600A - Toy resin capable of being processed easily - Google Patents

Abstract

The invention discloses a toy resin capable of being processed easily. The toy resin is prepared from the following raw materials in parts by weight: 70 to 90 parts of ABS, 1 to 3 parts of corncob supported antibacterial material, 0.3 to 0.5 part of natural rubber, 0.3 to 0.5 part of acetylsalicylic acid, 15 to 17 parts of palygorskite powder, 1.6 to 2.8 parts of chlorinated paraffin, 2 to 4 parts of nano alumina, 1 to 2 parts of aluminum hydroxide, 0.3 to 0.5 part of crystal of silica sand, 0.2 to 0.4 part of propanediol butyl ether, 0.3 to 0.5 part of silane coupling agent KH-560, 2 to 5 parts of magnesium hydroxide, 2 to 4 parts of polypropylene resin, 1.5 to 2.5 parts of SBS, 1 to 3 parts of alkyl glucoside, 3 to 5 parts of anhydrous ethanol, and 0.1 to 0.2 part of epoxy flaxseed oil.

Description

A kind of toy resin easy to process

Technical field

The present invention relates to toy material technical field, more particularly to a kind of toy resin easy to process.

Background technology

Toy is that especially children play the product of happy game for people.In ancient Egypt's historical relic away from modern about more than 5000 years There is the doll made by material such as clay, timber, beast bone and ivory, there is small-sized kitchenware and life appliance in children grave.Away from the present about Find there is the pull toy for dividing into circle wheel in the Persian historical relic of 3000.Sound-emitting top and animal that the useful cotton rope of ancient Greek is started The toy of image.Be unearthed the movable ivory carving portrait of four limbs in ancient Roman's mausoleum.18 th Century German Nuremburges become European toy The production center.Doll adopts stamping process, vivo devices mechanical part, the action such as can perform crying, walk.Also been produced music Toy and winding-up toy etc..19th century, scientific and technical New TownMovement was applied to toy designs and production, the development for promoting toy to produce, The optical toys such as appearance activity picture, raree show, magic lantern.American scientist T.A. Edison in 1878 is made using gramophone and can be said Words, the doll sung.The nineties in 19th century, the U.S. produces electronic small fan and the electronic mini train of rail in succession.Chinese toy Also there is long history.Find there is small-sized pottery pig away from modern about 5500 Shandong Ningyang Dawenkou ruins.Away from about 3800 the presents Also there are ceramic toy and jingle bell in Qijia culture remains.Kite and ball game also have the history of more than 2000.Diabolo, wind Car, rolling ring, seven-piece puzzle, Chinese puzzle ring etc. become the folk toys of Chinese tradition, and after 20th century, toy manufacturing industry becomes important Industry.The German Toy production thirties and outlet occupy first place in the world.The forties, toy production in the U.S.'s was developed rapidly, is produced, is consumed With the hat that import leaps to the world.The fifties, Japan's toy industry emerged, and export amount catches up with Germany.Chinese toy industry at the end of the fifties Formed, with Beijing, Shanghai as major production areas.Toy kind is up to kind more than 7000.The sixties Hong Kong Toy industry rise, the eighties with Afterwards Taiwan toy industry has very big development.

Current China is toy big producing country, and the toy of global 70-80% is by domestic product.With China market Constantly improve and specification, add inclination of the country in policy to toy, animation, game etc. " creative industry " and help energetically Hold, domestic toy industry will be lifted into a unprecedented golden period, trend pickup, industry benefit.

Children are the main consumer groups of toy, and underproof toy material can endanger the healthy and life peace of children Entirely.The main component of plastics is synthetic resin.Resin accounts for the 40-100% of plastics gross weight.The key property of plastics is mainly determined Also play an important role due to the person's character of resin, but additive.However, existing plastic toys performance is not good, it is impossible to meet day The market demand that benefit increases.

The B of patent CN 103965576, a kind of antibiotic toy plastics, it is compounded using ABS and PVC, and a kind of antibacterial modeling is obtained Expect that, for toy, PVC material Long-Time Service is dangerous, have potential hazard to the health of children, and the antiseptic for using is pure Chemical antiseptic, inadequate environmental protection, it is therefore desirable to a kind of toy resin of more environmental protection safety..

The content of the invention

The object of the invention is exactly to make up the defect of prior art, there is provided a kind of toy resin easy to process.

The present invention is achieved by the following technical solutions：

A kind of toy resin easy to process, it is obtained by the raw material of following weight parts：ABS70-90, corncob load are anti- Bacterium material 1-3, natural rubber 0.3-0.5, acetylsalicylic acid 0.3-0.5, palygorskite powder 15-17, chlorinated paraffin 1.6-2.8, receive Rice aluminum oxide 2-4, aluminium hydroxide 1-2, chalazie 0.3-0.5, propandiol butyl ether 0.2-0.4, silane coupler KH-560 0.3- 0.5th, magnesium hydroxide 2-5 parts, acrylic resin 2-4, SBS1.5-2.5, APG 1-3, absolute ethyl alcohol 3-5, epoxidized linseed oil 0.1-0.2；

Described corncob load anti-biotic material is obtained by the raw material of following weight parts：Linseed oil 0.1-0.2, APG 0.1-0.3, lecithin 0.1-0.2, citric acid 0.01-0.04, shitosan 1-2, polyglycol ether 0.3-0.4, irgasfos 168 0.1-0.2, corncob 2-4, silver nitrate 0.2-0.5.

Described toy resin a kind of easy to process, preparation method is comprised the following steps：

（1）Prepare corncob load anti-biotic material；

Described corncob loads the preparation method of anti-biotic material：

Add water in corncob equivalent to the water of 0.8-1.5 times of above-mentioned raw materials, after mixing, anaerobic fermentation is cleaned after 1-2 days, is air-dried, It is dried, then steam blasting is carried out to it, explosion water vapour pressure is 0.05-0.3Mpa, and blasting time is 1-3s, produces thing Jing and take off It is dried after water process, obtains xeraphium standby；Citric acid adds suitable quantity of water, after being configured to the citric acid solution that concentration is 2-5%, adds Xeraphium, after stirring 0.5-1h at 40-60 DEG C, adds remaining needed for silver nitrate and corncob load anti-biotic material preparation Raw material, after stirring, filters, and with distillation water washing filter residue, to filtrate in neutrality, filter residue is added into concentration for the carbonic acid of 1-2% In hydrogen sodium solution, 1-2h is stirred at 30-50 DEG C, filtered, with distillation water washing filter residue, to filtrate in neutrality, filter residue is in 60-80 After being dried at DEG C, corncob load anti-biotic material is obtained final product standby；

（2）After absolute ethyl alcohol, silane coupler KH-560 stir, nano aluminium oxide, chalazie, ultrasonic vibration 1-2h are added Afterwards, dry, obtain modified powder standby；

（3）Natural rubber, acetylsalicylic acid, palygorskite powder, chlorinated paraffin are put into reactor, with 400-500 rev/min of rotating speed Clock is stirred mixing 3-6 minutes, adds modified powder, corncob load anti-biotic material and remaining raw material, and 700-900 turns/ Minute sends into screw extruder melting mixing after being well mixed；

(4) screw speed is 300-400rpm, after extruding pelletization, is obtained final product.

It is an advantage of the invention that：（1）Rationally, materials safety has no toxic side effect inventive formulation, with the addition of corncob, becomes useless For treasured, environmental protection and energy saving green non-pollution；With the addition of various kinds of resin complex compounding so that the present invention is easily processed into type into various shapes Shape, is easy to make the toy of variously-shaped performance.

（2）Present invention adds corncob load antibacterial powder, bio-carrier can load antiseptic, slow to discharge, antibacterial Effect is strong, and lasting effect is good, have broad spectrum activity and good advantage compatible with fabricated product, all has to various bacteriums, mould fine Killing inhibitory action, to environment without any pollution.Make use of corncob as bio-carrier, turn waste into wealth.The present invention is adopted Steam explosion technology, the acute expansion of the gas in hole, produces " explosion " effect, is fiber fines by raw material tear, by increasing capacitance it is possible to increase raw The load capacity of thing carrier.

（3）Attapulgite is modified using coupling agent, while the compatibility for increasing raw material the strong of raw material is increased Degree and impact resistance, can effectively improve the service life using the toy of the resin manufacture..

Specific embodiment

A kind of toy resin easy to process, it is obtained by the raw material of following weight parts：ABS70, corncob load Anti-biotic material 1, natural rubber 0.3, acetylsalicylic acid 0.3, palygorskite powder 15, chlorinated paraffin 1.6, nano aluminium oxide 2, hydroxide Aluminium 1, chalazie 0.3, propandiol butyl ether 0.2, silane coupler KH, 2 parts of magnesium hydroxide, acrylic resin 2, SBS1.5, alkyl Glucosides 1, absolute ethyl alcohol 3, epoxidized linseed oil 0.1；

Described corncob load anti-biotic material is obtained by the raw material of following weight parts：Linseed oil 0.1, APG 0.1, ovum Phosphatidase 0 .1, citric acid 0.01, shitosan 1, polyglycol ether 0.3, irgasfos 168 0.1, corncob 2, silver nitrate 0.2.

Described toy resin a kind of easy to process, preparation method is comprised the following steps：

（1）Prepare corncob load anti-biotic material；

Described corncob loads the preparation method of anti-biotic material：

Add water in corncob equivalent to the water of 0.8 times of above-mentioned raw materials, after mixing, anaerobic fermentation is cleaned after 1 day, is air-dried, and is dried, Carry out steam blasting to it again, explosion water vapour pressure is 0.05Mpa, and blasting time is 1s, produce thing and do Jing after processed It is dry, obtain xeraphium standby；Citric acid adds suitable quantity of water, after being configured to the citric acid solution that concentration is 2%, xeraphium is added, at 40 DEG C After lower stirring 0.5h, add silver nitrate and corncob load anti-biotic material prepares required remaining raw material, after stirring, mistake Filter, is in 1% sodium bicarbonate solution, at 30 DEG C by filter residue addition concentration to filtrate in neutrality with distillation water washing filter residue Stirring 1h, filters, and with distillation water washing filter residue, to filtrate in neutrality, after filter residue is dried at 60 DEG C, obtains final product corncob load anti- Bacterium materials for later use；

（2）After absolute ethyl alcohol, silane coupler KH stir, nano aluminium oxide, chalazie are added, after ultrasonic vibration 1h, dried It is dry, obtain modified powder standby；

（3）Natural rubber, acetylsalicylic acid, palygorskite powder, chlorinated paraffin are put into reactor, with rotating speed, 400 revs/min are entered Row stirring mixing 3 minutes, adds modified powder, corncob load anti-biotic material and remaining raw material, and 700 revs/min of mixing are equal Screw extruder melting mixing is sent into after even；

(4) screw speed is 300rpm, after extruding pelletization, is obtained final product.

(1) antibacterial test：

Using conventional method by obtained resin forming, it is prepared into 50mm × 50mm × 4mm's respectively

Sample, carries out antibacterial test, antibacterial test standard：

QB/T2591-2003 antibiotic plastic Anti-microbial Performance Tests methods and antibacterial effect.

Escherichia coli sterilizing rate：98.8%；Staphylococcus aureus sterilizing rate:98.7%；

(2) toxotest：The antibiotic toy plastics of enforcement, Jing acute toxicity tests show, the LD50 ＞ to small white mouse 10000mg/kg, true border innocuous substance.

Claims (2)

1. a kind of toy resin easy to process, it is characterised in that：It is obtained by the raw material of following weight parts：ABS70- 90th, corncob load anti-biotic material 1-3, natural rubber 0.3-0.5, acetylsalicylic acid 0.3-0.5, palygorskite powder 15-17, chlorination Paraffin 1.6-2.8, nano aluminium oxide 2-4, aluminium hydroxide 1-2, chalazie 0.3-0.5, propandiol butyl ether 0.2-0.4, silane idol Connection agent KH-560 0.3-0.5, magnesium hydroxide 2-5 parts, acrylic resin 2-4, SBS1.5-2.5, APG 1-3, anhydrous second Alcohol 3-5, epoxidized linseed oil 0.1-0.2；

Described corncob load anti-biotic material is obtained by the raw material of following weight parts：Linseed oil 0.1-0.2, APG 0.1-0.3, lecithin 0.1-0.2, citric acid 0.01-0.04, shitosan 1-2, polyglycol ether 0.3-0.4, irgasfos 168 0.1-0.2, corncob 2-4, silver nitrate 0.2-0.5.

2. a kind of toy resin easy to process according to claim 1, it is characterised in that：Preparation method includes following Step：

（1）Prepare corncob load anti-biotic material；

Described corncob loads the preparation method of anti-biotic material：

Add water in corncob equivalent to the water of 0.8-1.5 times of above-mentioned raw materials, after mixing, anaerobic fermentation is cleaned after 1-2 days, is air-dried, It is dried, then steam blasting is carried out to it, explosion water vapour pressure is 0.05-0.3Mpa, and blasting time is 1-3s, produces thing Jing and take off It is dried after water process, obtains xeraphium standby；Citric acid adds suitable quantity of water, after being configured to the citric acid solution that concentration is 2-5%, adds Xeraphium, after stirring 0.5-1h at 40-60 DEG C, adds remaining needed for silver nitrate and corncob load anti-biotic material preparation Raw material, after stirring, filters, and with distillation water washing filter residue, to filtrate in neutrality, filter residue is added into concentration for the carbonic acid of 1-2% In hydrogen sodium solution, 1-2h is stirred at 30-50 DEG C, filtered, with distillation water washing filter residue, to filtrate in neutrality, filter residue is in 60-80 After being dried at DEG C, corncob load anti-biotic material is obtained final product standby；

（2）After absolute ethyl alcohol, silane coupler KH-560 stir, nano aluminium oxide, chalazie, ultrasonic vibration 1-2h are added Afterwards, dry, obtain modified powder standby；

（3）Natural rubber, acetylsalicylic acid, palygorskite powder, chlorinated paraffin are put into reactor, with 400-500 rev/min of rotating speed Clock is stirred mixing 3-6 minutes, adds modified powder, corncob load anti-biotic material and remaining raw material, and 700-900 turns/ Minute sends into screw extruder melting mixing after being well mixed；

(4) screw speed is 300-400rpm, after extruding pelletization, is obtained final product.